CN102311704A - 展柜用高丰满型环保亮光白面漆 - Google Patents
展柜用高丰满型环保亮光白面漆 Download PDFInfo
- Publication number
- CN102311704A CN102311704A CN201110064894A CN201110064894A CN102311704A CN 102311704 A CN102311704 A CN 102311704A CN 201110064894 A CN201110064894 A CN 201110064894A CN 201110064894 A CN201110064894 A CN 201110064894A CN 102311704 A CN102311704 A CN 102311704A
- Authority
- CN
- China
- Prior art keywords
- environmental protection
- finish paint
- adopts
- light white
- protection light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种展柜用合成酯肪酸类高丰满型环保亮光白面漆,是由主漆、固化剂、稀释剂等三组份按1:0.8:0.5比例配制而成,其中主漆的配比如下为:合成酯肪酸类醇酸树酯60%、钛白粉35%、消泡剂0.2%、流平剂0.5%、湿润剂0.5%、复合环保溶剂3.7%、催干剂0.1%;固化剂组份为多异氰酸酯固化剂;稀释剂组份为复合环保溶剂混合而成。本发明是一种干速快、性价比高,符合环保健康要求,且具有高丰满度、流平性好、附着力强、硬度高、高光泽、防踏陷性好等特点的展柜用亮光白面漆。
Description
技术领域
本发明涉及一种油漆,特别涉及一种展柜用合成酯肪酸类高丰满型环保亮光白面漆。
背景技术
木器涂料中亮光白面漆问题是难点之一。而亮光白面漆一直存在有较难克服的耐黄变性能、丰满度和清晰度等技术问题;同时,亮光白面漆又是亮光类产品,因而它的硬度、光泽、起泡性、踏陷性是否能够满足要求也是一个很大技术问题。现有技术中,亮光白面漆主要应用在橱柜和展柜上,这些地方都是需要大面积和立面混合喷涂,因此在流平和立面流平上又要面临一大难题。众所周知,亮光白面漆里面含有25-30%的钛白粉,其树脂含量本身很低,要把丰满度和光泽很难达到要求,而且就算满足了丰满度和光泽的要求,其硬度也会变得很差。因此,有些好的白面漆喷涂起来表面油光水滑,而有一些则没有一点油性。还有白色漆如果喷涂薄,对遮盖力不好,如喷涂比较厚,特别在温度高的环境下,很容易起泡。现有的高档亮光白面漆采用合成酯肪酸与丙稀酸体系性能好,但成本高,市场难于接受;其它体系价格有优势,但涂膜性能一般,施工问题较多。
发明内容
本发明的目的是提供一种性价比高,符合环保健康要求,具有一种干速快、性价比高,且具有高丰满度、流平性好、附着力强、硬度高、高光泽、防踏陷性好等特点的展柜用高丰满型环保亮光白面漆。
本发明是采用如下的配方来实现上述目的的,一种展柜用高丰满型环保亮光白面漆,该油漆是由主漆、固化剂、稀释剂共三组份按1:0.8:0.5比例,以一般亮光漆的制作工艺配制而成,其中主漆、固化剂、稀释剂三种组份具体成分及配比按质量百分比如下:
主漆:
合成酯肪酸类醇酸树酯 60%
钛白粉 35%
消泡剂 0.2%
流平剂 0.5%
湿润剂 0.5%
催干剂 0.1%
复合环保溶剂 3.7%
其中,钛白粉采用金红石型钛白粉;消泡剂采用聚氨酯专用消泡剂,主要成份是改性硅酮类;流平剂采用聚丙烯酸酯共聚体或氟碳改性聚丙烯酸酯类;湿润剂采用具有酸性基团的共聚体溶液;催干剂采用有机锡化合物溶液;复合环保溶剂采用醋酸丁酯、丙二醇甲醚醋酸酯、二价酸酯、混酸甲酯混合配制。
固化剂为多异氰酸酯,主要成份是芳香族二异氰酸酯类和六亚甲基二异氰酸酯类。
稀释剂为复合环保溶剂,采用醋酸丁酯、丙二醇甲醚醋酸酯、二价酸酯、混酸甲酯配制而成。
本发明是针对现有亮光白面漆的缺陷而加以改进,经过大量的实验筛选出各种材料组配,采用多因素实验设计方法,正交试验设计法确定组分及其重量百分比,采用上述配方的其与现有技术相比,有如下优点:
1)配方中的合成脂肪酸类醇酸树酯采用了当今的最新先进技术,具有性价比高、高丰满度、高固含(高达90%,一般普通的产品只有80%)、流平性好、附着力强、硬度高、高光泽、防踏陷性好等特点;与固化剂芳香族二异氰酸酯类和六亚甲基二异氰酸酯类搭配涂膜质量更好,性能更佳;
2)采用了世界上最先进消泡剂、流平剂、湿润剂等助剂 ,满足了目前亮光白面漆的生产及施工要求;
3)复合环保溶剂毒性低、气味小,无毒性,可完全生物降解,绝对无苯且voc 含量符合健康要求;
4) 固化剂组份:固化剂游离TDI含量<0.5%,达到欧盟标准,高于国家GB18581—2009行业标准。
具体实施方式
下面对本发明作进一步的描述:
一种展柜用高丰满型环保亮光白面漆,该油漆是由主漆、固化剂、稀释剂共三组份按1:0.8:0.5比例,以一般亮光漆的制作工艺配制而成,其中主漆、固化剂、稀释剂三种组份具体成分及配比按质量百分比如下:
主漆:
合成酯肪酸类醇酸树酯 60%
钛白粉 35%
消泡剂 0.2%
流平剂 0.5%
湿润剂 0.5%
催干剂 0.1%
复合环保溶剂 3.7%
其中,钛白粉采用金红石型钛白粉;消泡剂采用聚氨酯专用消泡剂,主要成份是改性硅酮类;流平剂采用聚丙烯酸酯共聚体或氟碳改性聚丙烯酸酯类;湿润剂采用具有酸性基团的共聚体溶液;催干剂采用有机锡化合物溶液;复合环保溶剂采用醋酸丁酯、丙二醇甲醚醋酸酯、二价酸酯、混酸甲酯混合配制。
固化剂为多异氰酸酯,主要成份是芳香族二异氰酸酯类和六亚甲基二异氰酸酯类。
稀释剂为复合环保溶剂,采用醋酸丁酯、丙二醇甲醚醋酸酯、二价酸酯、混酸甲酯配制而成。
该高性能的展柜用高丰满型环保亮光白面漆各项性能指标和技术指标如下各表所示:
表一高性能展柜用高丰满型环保亮光白面漆性能指标
项 目 | 单位 | HG/T2454-2006标准中的技术指标 | 实测值 |
在容器中状态 | 搅拌后均匀无硬块 | 符含 | |
施工性 | 施涂无障碍 | 符合 | |
干燥时间 | H | 表干≤1H,实干≤24H | 表干≤1H,实干≤24H |
涂膜外观 | 正常 | 正常 | |
贮存稳定性(50℃/7d) | 无异常 | 无异常 | |
光泽(60°) | 商定 | 105 | |
铅笔硬度(擦伤)≥ | H | 2H | |
附着力(划格间距2mm)≤ | 1 | 1 | |
耐干热性﹙90±2〕℃,15min≤ | 级 | 2 | 2 |
耐磨性(750g/500r) ≤ | g | 0.050 | 0.045 |
耐水性(24h) | 无异常 | 无异常 | |
耐碱性(2h) | 无异常 | 无异常 | |
耐醇性(8h) | 无异常 | 无异常 | |
耐污染性(1h) 茶和醋 | 无异常 | 无异常 |
从表一可明显看出,本发明的各项性能均达到或高于国标标准,确认了本发明的高性能。
表二高性能展柜用高丰满型环保亮光白面漆技术要求
主漆组份
项 目 | 技术要求 |
固含量 | 88±2% |
外观 | 白色粘液 |
粘度(NDJ-1,25℃) | 5000±1000cps |
施工比例 | 主漆:固化剂:稀释剂=1:0.8:0.5 |
胶化时间(25℃,75%) | 4小时以上 |
固化剂组份
项 目 | 技术要求 |
固含量 | 50±2% |
外观 | 清澈透明 |
粘度(涂-4,30℃) | 13-16秒 |
游离TDI含量 | <0.5% |
稀释剂组份
项 目 | 技术要求 |
苯含量 | ≤0.1% |
外观 | 清澈透明 |
甲苯、二甲苯含量 | ≤0.1% |
溶解力 | 强 |
表二技术要求表明,VOC含量及游离TDI含量达到或优于GB18581-2009标准,符合环保健康要求,使用安全可靠。
尽管对本发明已作了详细的说明并提供了一些具体实例,但对本领域熟练技术人员来说,只要不离开本发明的精神和范围可作各种变化或修正是显然的。
Claims (9)
1.一种展柜用高丰满型环保亮光白面漆,其特征在于:该油漆是由主漆、固化剂、稀释剂共三组份按1:0.8:0.5比例,以一般亮光漆的制作工艺配制而成,其中主漆的具体成分及配比按质量百分比如下:
合成酯肪酸类醇酸树酯 60%
钛白粉 35%
消泡剂 0.2%
流平剂 0.5%
湿润剂 0.5%
催干剂 0.1%
复合环保溶剂 3.7%。
2.根据权利要求1所述的展柜用高丰满型环保亮光白面漆,其特征在于:所述固化剂为多异氰酸酯,主要成份是芳香族二异氰酸酯类和六亚甲基二异氰酸酯类。
3.根据权利要求1所述的展柜用高丰满型环保亮光白面漆,其特征在于:所述稀释剂为复合环保溶剂,采用醋酸丁酯、丙二醇甲醚醋酸酯、二价酸酯、混酸甲酯配制而成。
4.根据权利要求1所述的展柜用高丰满型环保亮光白面漆,其特征在于:所述钛白粉采用金红石型钛白粉。
5.根据权利要求1所述的展柜用高丰满型环保亮光白面漆,其特征在于:所述消泡剂采用聚氨酯专用消泡剂,主要成份是改性硅酮类。
6.根据权利要求1所述的展柜用高丰满型环保亮光白面漆,其特征在于:所述流平剂采用聚丙烯酸酯共聚体或氟碳改性聚丙烯酸酯类。
7.根据权利要求1所述的展柜用高丰满型环保亮光白面漆,其特征在于:所述湿润剂采用具有酸性基团的共聚体溶液。
8.根据权利要求1所述的展柜用高丰满型环保亮光白面漆,其特征在于:所述催干剂采用有机锡化合物溶液。
9.根据权利要求1所述的展柜用高丰满型环保亮光白面漆,其特征在于:所述复合环保溶剂采用醋酸丁酯、丙二醇甲醚醋酸酯、二价酸酯、混酸甲酯混合配制。