CN102231311A - 一种用聚酯无纺布单面补强少胶云母带的生产方法 - Google Patents
一种用聚酯无纺布单面补强少胶云母带的生产方法 Download PDFInfo
- Publication number
- CN102231311A CN102231311A CN 201110103581 CN201110103581A CN102231311A CN 102231311 A CN102231311 A CN 102231311A CN 201110103581 CN201110103581 CN 201110103581 CN 201110103581 A CN201110103581 A CN 201110103581A CN 102231311 A CN102231311 A CN 102231311A
- Authority
- CN
- China
- Prior art keywords
- woven fabric
- polyester non
- mica tape
- production method
- low resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种用聚酯无纺布单面补强少胶云母带的生产方法，包括以下步骤：1）聚酯无纺布浸渍；2）复合；3）烘焙；4）冷却制成胚料；5）分切收卷；本发明，制得的聚酯无纺布单面补强少胶云母带，柔软性好，包扎工艺性好，透气性高，可用于2兆瓦及2兆瓦以下容量的风力发电机的定子线圈绝缘，也可用于3000V、6000V电压等级的高压电机定子线圈绝缘。
Description
技术领域
本发明属于云母带制造技术领域，涉及到用无纺布作为补强材料制造的单面补强少胶云母带的生产工艺。
技术背景
云母带是电机特别是大型、高压电机中不可替代的最为关键的绝缘材料，但云母的机械强度太低，不能满足电机制造过程中和电机实际运行中对机械强度的要求，必须使用补强材料予以增强。目前，国家标准、行业标准、各个云母带生产企业的企业标准中所用的补强材料都是电工用无碱玻璃纤维布、绝缘纸、塑料薄膜。为使少胶云母带具有更好的性能和降低成本，根据少胶云母带某些特定用途，选用聚酯无纺布做为补强材料制造单面补强少胶云母带成为可能。
发明内容
针对云母带结构中必须用补强材料存在胶的问题，本发明的目的在于提供一种用聚酯无纺布单面补强少胶云母带的生产工艺，是用聚酯无纺布做为补强材料制造单面补强少胶云母带。
本发明的技术方案是通过以下方式实现的：一种用聚酯无纺布单面补强少胶云母带的生产方法，包括以下步骤：1）、聚酯无纺布浸渍；2）复合；3）、烘焙；4）、冷却制成胚料；5）、分切收卷；其特征在于：
1）、聚酯无纺布浸渍；将0.025～0.060mm厚的聚酯无纺布开卷，过装有浸渍胶黏剂的胶槽，胶液的固体含量按少胶云母带的胶含量20～30%wt要求进行控制。
所述的浸渍胶黏剂为环氧型胶粘剂或聚酯环氧型胶粘剂；
2）复合：将0.05～0.08mm厚的云母纸开卷并复合在涂了胶黏剂的聚酯无纺布上，用滚筒将二者压合在一起形成云母带胚带；
3）、烘焙：将上述云母带胚带通过烘箱烘焙，烘箱的温度由室温逐渐升高到40℃～80℃，烘焙3～8min；
4）、冷却制成胚料:出烘焙后在室温空气中冷却2～3min，冷却后将制成的云母带胚料进行收卷；
5）、分切收卷：将云母带胚料装置在分切机上，按客户要求的宽度进行分切成带状并收卷，即制成用聚酯无纺布单面补强少胶云母带。
本发明，制得的聚酯无纺布单面补强少胶云母带，柔软性好，包扎工艺性好，透气性高，真空压力浸渍时树脂更容易浸透，更有助于实现电机无气隙绝缘，保证电机的电热老化寿命，同时降低电机成本，减少污染、节省能源。本发明产品各项性能都达到和超过“GB/T5019-2009—以云母为基的绝缘材料”的有关要求，并且还要高于电工用无碱玻璃纤维布补强单面少胶云母带的性能。本发明产品聚酯无纺布单面补强少胶云母带可用于2兆瓦及2兆瓦以下容量的风力发电机的定子线圈绝缘，也可用于3000V、6000V电压等级的高压电机定子线圈绝缘。
附图说明
图1是本发明的工艺流程图。
具体实施方式
一种用聚酯无纺布单面补强少胶云母带的生产方法，包括以下步骤：
1、聚酯无纺布浸渍；将0.025mm厚的聚酯无纺布开卷，经过装有浸渍胶黏剂（环氧型或聚酯环氧型）胶槽，胶液的固体含量按少胶云母带的胶含量20～30%wt要求进行控制。
2、复合；将0.05mm厚的云母纸开卷并复合在涂了胶黏剂的聚酯无纺布上。
3、烘焙；将步骤2的云母纸和涂了胶黏剂的聚酯无纺布通过烘箱烘焙，烘箱的温度由室温逐渐升高到40℃～80℃，烘焙3～8min。
4、冷却制成胚料；出烘箱后在室温下冷却2～3min，冷却后制成云母带的胚料卷，便制成少胶云母带的胚料。
5、分切收卷：将云母带胚料装置在分切机上，按客户要求的宽度进行分切成带状并收卷，即制成聚酯无纺布单面补强少胶云母带。检验、包装、入库。
本发明产品聚酯无纺布单面补强少胶云母带柔软性好，包扎工艺性好，透气性高，真空压力浸渍时树脂更容易浸透，更有助于实现电机无气隙绝缘，保证电机的电热老化寿命，同时降低电机成本，减少污染、节省能源。
Claims (2)
1.一种用聚酯无纺布单面补强少胶云母带的生产方法，包括以下步骤：1）、聚酯无纺布浸渍；2）复合；3）、烘焙；4）、冷却制成胚料；5）、分切收卷；其特征在于：
1）、聚酯无纺布浸渍；将0.025～0.060mm厚的聚酯无纺布开卷，过装有浸渍胶黏剂的胶槽，胶液的固体含量按少胶云母带的胶含量20～30%wt要求进行控制；
2）复合：将0.05～0.08mm厚的云母纸开卷并复合在涂了胶黏剂的聚酯无纺布上，用滚筒将二者压合在一起形成云母带胚带；
3）、烘焙：将上述云母带胚带通过烘箱烘焙，烘箱的温度由室温逐渐升高到40℃～80℃，烘焙3～8min；
4）、冷却制成胚料:出烘焙后在室温空气中冷却2～3min，冷却后将制成的云母带胚料进行收卷；
5）、分切收卷：将云母带胚料装置在分切机上，按客户要求的宽度进行分切成带状并收卷，即制成用聚酯无纺布单面补强少胶云母带。
2.根据权利要求1所述的一种用聚酯无纺布单面补强少胶云母带的生产方法，其特征在于：所述的步骤1）中浸渍胶黏剂为环氧型胶粘剂或聚酯环氧型胶粘剂。