CN102206932A - 一种具有被动调温性能的透水砖 - Google Patents
一种具有被动调温性能的透水砖 Download PDFInfo
- Publication number
- CN102206932A CN102206932A CN 201110081534 CN201110081534A CN102206932A CN 102206932 A CN102206932 A CN 102206932A CN 201110081534 CN201110081534 CN 201110081534 CN 201110081534 A CN201110081534 A CN 201110081534A CN 102206932 A CN102206932 A CN 102206932A
- Authority
- CN
- China
- Prior art keywords
- permeable brick
- particle layer
- water
- layer
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明请求保护一种具有被动调温性能的透水砖,所述透水砖的骨料选用粗0.8-1.2mm、中0.3-0.8mm、细0.1-0.3mm三种颗粒的石粉,水泥选用32.5R复合硅酸盐水泥,将三种颗粒的石粉分别和水泥加水后混合(混合比例为3.17:1:0.44),分布层装入模具中压制成型、晾晒,形成具有粗颗粒层、中颗粒层和细颗粒层三层结构的透水砖。其粗颗粒层主要解决雨水迅速向下渗透的问题,避免路面积水,其含水率相对较低;中颗粒层同时具备较好渗透性和较高的含水率,它是上下层的过渡层;最下层的细颗粒层的主要功能是保持雨水不会迅速流失,其自身的含水率较高,但是在雨量大、长时间下雨的情况下,细颗粒层达到饱和后,雨水将继续通过细颗粒层向下渗透,从而保证了路面不积水,同时又具有很高的含水率,以提供给被动蒸发调温使用。
Description
技术领域
本发明涉及一种路面铺设用的地砖,其同时具有温度调节能力和透水能力。
背景技术
目前城市道路铺设用的地砖绝大部分为非透水地砖,由于没有透水性能,雨水只能沿城市雨水******流失,从而直接阻断了雨水向地下的渗透,导致城市地下水源得不到补充。同时,在夏季的暴雨时节,由于城市雨水******容量的限制,还可能导致城市水涝。近年来,有地方少量的使用了透水地砖,解决了部分雨水向地下渗透的问题。但是在夏季,由于太阳辐射强度大,路面温度高的问题没有得到解决,从而加重了城市热岛效应。近年来相关的透水砖的研究,都将重点放在了雨水的渗透问题上。因此,本发明提出了一种同时兼顾透水功能和调温功能的透水砖。
发明内容
本发明的目的在于提供一种具有被动调温性能的透水砖,其同时具有高含水率和透水率,能在降雨时吸收雨水,并将多余的雨水向地下渗透。在强烈的太阳辐射情况下,通过透水砖的蒸发冷却作用,调节自身的温度,再通过与周围空气的对流换热,从而实现调节透水砖周围的空气环境温度。
本发明的方案如下:
一种具有被动调温性能的透水砖, 所述透水砖的骨料选用粗0.8-1.2mm、中0.3-0.8mm、细0.1-0.3mm三种颗粒的石粉,水泥选用32.5R复合硅酸盐水泥,将三种颗粒的石粉分别和水泥加水后混合,分层装入模具中,底层为细颗粒石粉的混合料,中层为中颗粒石粉的混合料,上层为粗颗粒石粉的混合料,然后压制成型、晾晒,形成具有粗颗粒层、中颗粒层和细颗粒层三层结构的透水砖。
本发明提出的透水砖,其粗颗粒层主要解决雨水迅速向下渗透的问题,避免路面积水,其含水率相对较低;中颗粒层同时具备较好渗透性和较高的含水率,它是上下层的过渡层;最下层的细颗粒层的主要功能是保持雨水不会迅速流失,其自身的含水率较高,但是在雨量大、长时间下雨的情况下,细颗粒层达到饱和后,雨水将继续通过细颗粒层向下渗透,从而保证了路面不积水,同时又具有很高的含水率,以提供给被动蒸发调温使用。
本发明的三种粗细不同的骨料的体积构成比例为1:1:1,综合体积含水率35-40%,综合透水率达到1mm/sec,能够满足常规情况下的雨水渗透率,同时具备较高的蒸发调温能力。
附图说明
图1是本发明的结构示意图。
具体实施方式
本发明所用骨料为普通石粉,其主要成分为碳酸盐。用筛分机将石粉分为粗(0.8-1.2mm)、中(0.3-0.8mm)、细(0.1-0.3mm)三种颗粒,粘接用水泥为32.5R复合硅酸盐水泥。
本发明的制造工序如下:⑴将骨料筛分为粗、中、细三种类型;⑵将三种类型的普通石粉骨料分别和水泥加水后混合;⑶分层装入模具压制成型,下层为细混合料,中层为中混合料,上层为粗混合料;⑷制成晾晒3天。
本发明的构造简图如图1所示,其构造分为三层:粗颗粒层1、中颗粒层2和细颗粒层3。
Claims (2)
1.一种具有被动调温性能的透水砖, 所述透水砖的骨料选用粗0.8-1.2mm、中0.3-0.8mm、细0.1-0.3mm三种颗粒的石粉,水泥选用32.5R复合硅酸盐水泥,将三种颗粒的石粉分别和水泥加水后混合,分层装入模具中,底层为细颗粒石粉的混合料,中层为中颗粒石粉的混合料,上层为粗颗粒石粉的混合料,然后压制成型、晾晒,形成具有粗颗粒层、中颗粒层和细颗粒层三层结构的透水砖。
2.根据权利要求1所述的具有被动调温性能的透水砖,其特征在于:所述三种粗细不同的石粉的体积构成比例为1:1:1。