CN102181618A - Protective gas for annealing of metal materials - Google Patents
Protective gas for annealing of metal materials Download PDFInfo
- Publication number
- CN102181618A CN102181618A CN2011100967603A CN201110096760A CN102181618A CN 102181618 A CN102181618 A CN 102181618A CN 2011100967603 A CN2011100967603 A CN 2011100967603A CN 201110096760 A CN201110096760 A CN 201110096760A CN 102181618 A CN102181618 A CN 102181618A
- Authority
- CN
- China
- Prior art keywords
- annealing
- protective gas
- hydrogen
- metal materials
- ratio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses protective gas for the annealing of metal materials. In the protective gas, mixed gas comprises 75 percent of hydrogen and 25 percent of nitrogen, and a ratio of the mixed gas containing the hydrogen and the nitrogen is appropriate; and the protective gas is easy and convenient to prepare and high in quality after annealing.
Description
Affiliated technical field
The present invention relates to a kind of thermal treatment process technology, particularly a kind of metallic substance annealed shielding gas that is used for is suitable for the protective atmosphere shield type bright annealing oven that circulates by force.
Background technology
At present, during the shield type bright annealing oven that circulates by force work, need to charge into shielding gas in the stove, originally the nitrogen Hydrogen shielding gas of Ying Yonging contains nitrogen 96~98%, hydrogen 2~4%.Product behind the clean annealing exists surface quality undesirable, and mechanical property is even inadequately, and the annealing cycle is long partially, the problem of the higher aspect of energy consumption.
Summary of the invention
Problem to be solved by this invention is, overcomes the deficiency of existing proportioning, and a kind of metallic substance annealed shielding gas that is used for is provided.This shielding gas is not only filled a prescription rationally, and preparation is simple, and the good product quality of producing.
The technical solution used in the present invention is:
The ratio of mixed gas is: hydrogeneous ratio is 75%, nitrogenous ratio is 25%.
The invention has the beneficial effects as follows, prescription rationally, preparation is simple, adopts high hydrogen decomposed ammonia as shielding gas, has significantly improved heat transfer efficiency, the annealing cycle has shortened about 10%, has improved anneal capability, has reduced energy consumption; Improve temperature uniformity, guaranteed the mechanical property of product; The inner quality and the surface quality of product all are improved.
Embodiment
Adopt the ammonia resolving device, prepare hydrogeneous ratio 75%, the hydrogen of nitrogenous ratio 25%, nitrogen mixed gas are used through can be used as shielding gas after purification system drying, the purification.
The density of hydrogen is 1/14 of nitrogen, and the thermal conductivity of hydrogen is 7 times of nitrogen.Hydrogen quality is light, and seepage force is strong, can infiltrate the coil of strip interlayer, gives full play to the big characteristics of thermal conductivity, significantly improves heat transfer efficiency.Hydrogen is reducing gas, and at high temperature can make iron oxide reduction is iron.
Make full use of and bring into play advantage and the potential of hydrogen in annealing, improve the annealing product quality, shorten the annealing cycle.
Claims (1)
1. one kind is used for metallic substance annealed shielding gas, and it is characterized in that: the ratio of mixed gas is: hydrogeneous ratio is 75%, nitrogenous ratio is 25%.