CN102126324B - 复合塑料板材及其玻璃钢增强结构 - Google Patents
复合塑料板材及其玻璃钢增强结构 Download PDFInfo
- Publication number
- CN102126324B CN102126324B CN201010566107.4A CN201010566107A CN102126324B CN 102126324 B CN102126324 B CN 102126324B CN 201010566107 A CN201010566107 A CN 201010566107A CN 102126324 B CN102126324 B CN 102126324B
- Authority
- CN
- China
- Prior art keywords
- layer
- plastic
- fiber
- board
- fibrage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种复合塑料板材及其生产工艺，所述复合塑料板材包括塑料板材层，塑料板材层上依次复合有纤维/塑料混合层和纤维层；所述复合塑料板材的生产工艺包括下述步骤：将纤维层通过热压使其下部嵌入到塑料板材层中，使得嵌入到塑料板材层中的纤维层与塑料板材层形成纤维/塑料混合层。本发明的复合塑料板材能使纤维/塑料混合层与塑料板材层机械牢固结合，该生产工艺生产的复合塑料板材无损伤、变形小，在复合塑料板材增强形成复合塑料板材玻璃钢增强结构时，界面粘接强度高，扩大了非极性塑料在工业中的应用范围，该板材减薄塑料板层厚度，减小了塑料板与玻璃钢间温差应力，增加了用该板材制作设备的使用寿命。
Description
技术领域
本发明涉及一种复合塑料板材、生产工艺及其玻璃钢增强结构，特别涉及一种塑料板材表面热压复合有纤维层的复合塑料板材及其工艺。
背景技术
现有工业生产中塑料板材以其优良的耐腐蚀性能得到广泛应用，塑料板材复合玻璃钢技术的引进又提高了设备的耐温和耐压性能，但聚丙烯、聚乙烯、聚偏氟乙烯、聚四氟乙烯、聚全氟乙丙烯等属于非极性塑料，因为分子结构差异的原因，这两种材料膨胀系数相差较大，界面粘接强度较小，无法很好地解决这些板材与玻璃钢的界面连接问题。目前国内这些板材如果复合玻璃钢主要采用表面机械打磨、火烧烫压玻纤布、涂刷粘接剂等方法，这些方法的不足之处有：
1）塑料板材与玻璃钢界面粘接强度不足；
2）在板材的制作过程中塑料板材易损伤、变形；
3）该板材制作的设备用于温差较大场合时热应力大，易造成分层、渗漏，使设备无法正常使用；
4）该板材制作的设备不可用于微负压场合；
5）将该板材用于大型设备制作筒体内壁时，还需要利用圈板、竖筋联合加强；
6）该板材制作的设备使用寿命短。
发明内容
本发明所要解决的技术问题是提供一种复合塑料板材及其生产工艺，使用该工艺生产的复合塑料板材能解决以往塑料板材和玻璃钢界面粘接强度不足而造成的上述问题。
为解决上述问题，本发明的技术方案是：
一种复合塑料板材，包括塑料板材层，所述塑料板材层上依次复合有纤维/塑料混合层和纤维层，纤维/塑料混合层处于塑料板材层和纤维层之间；所述复合塑料板材采用下述生产工艺制备：将纤维层通过热压使其下部嵌入到塑料板材层中，使得嵌入到塑料板材层中的纤维层与塑料板材层形成纤维/塑料混合层。
优选地，所述纤维层中纤维在厚度方向上连续。
优选地，所述塑料板材层材质为聚丙烯板材、聚乙烯板材、聚偏氟乙烯板材、聚四氟乙烯板材或聚全氟乙丙烯板材。
优选地，所述纤维层材质为玻璃纤维或化学纤维。
一种复合塑料板材玻璃钢增强结构，包括塑料板材层，所述塑料板材层上依次复合有纤维/塑料混合层、纤维层和玻璃钢层，纤维层和玻璃钢层通过树脂粘接；所述复合塑料板材采用下述生产工艺制备：将纤维层通过热压使其下部嵌入到塑料板材层中，使得嵌入到塑料板材层中的纤维层与塑料板材层形成纤维/塑料混合层。
本发明所提供的复合塑料板材能使纤维/塑料混合层与塑料板材层机械牢固结合，该生产工艺生产的复合塑料板材无损伤、变形小，在复合塑料板材增强形成复合塑料板材玻璃钢增强结构时，纤维层能与玻璃钢层粘接牢固，扩大了非极性塑料在工业中的应用范围，并且使用该增强复合塑料板材制作的设备可用于温差较大场合或是负压场合，该设备内侧可少设或不设加强圈和加强筋，节省了资源，由于该增强板材中塑料板材层、纤维层和玻璃钢层之间的粘接强度高，塑料板材层与玻璃钢层形成一体，塑料板材层能起耐腐蚀层的作用，因此还可减薄塑料板层厚度，同时也减小了塑料板与玻璃钢间温差应力，增加了该设备的使用寿命。
附图说明
图1是本发明复合塑料板材结构示意图。
图2是本发明复合塑料板材的生产装置结构示意图。
图3是本发明复合塑料板材玻璃钢增强结构示意图。
具体实施方式
下面结合附图和实施例进一步详细说明本发明，但本发明的保护范围并不限于此。
参照图1，本发明的复合塑料板材，包括塑料板材层1，塑料板材层1上依次复合有纤维/塑料混合层2和纤维层3，纤维/塑料混合层2处于塑料板材层1和纤维层3之间，该混合层是将纤维通过将热压使其下部嵌入塑料板材层1中而形成，裸露在上部的纤维形成纤维层3，在该混合层内塑料会将嵌入的纤维包裹住，由于纤维层3中纤维在厚度方向上连续，这样纤维层3就无法从塑料板材层1上剥离。
参照图2，本发明的生产装置结构示意图，图中辊筒5、板材挤出机模头6、辊筒7、辊筒8和加热装置9形成了通用塑料板材的生产装置，通用塑料板材的生产装置、导向辊10和纤维布架11形成了本发明复合塑料板材的生产装置。在该生产装置上，使用板材挤出机模头6挤出的板料经过辊筒5和辊筒7定型冷却，在塑料板材经过辊筒7时，通过调高加热装置9发热量使塑料板材的表面熔融，通过导向辊10将安放在纤维布架11上的纤维层导向并进入辊筒7和辊筒8间，此时与塑料板接触的纤维层被压入表面熔融的塑料板材层1中形成纤维/塑料混合层2，再经过切边和定长切割即完成本发明复合塑料板材的生产。
参照图3，利用本发明工艺所得复合塑料板材进行增强，在该复合塑料板材上通过树脂粘接玻璃钢层，得到复合塑料板材玻璃钢增强结构，该增强板材界面粘接强度高，扩大了非极性塑料在工业中的应用范围，复合塑料板材玻璃钢增强结构从下到上依次为塑料板材层1，纤维/塑料混合层2、纤维层3和玻璃钢层4。
Claims (4)
1.一种复合塑料板材，包括塑料板材层，其特征在于，所述塑料板材层上依次复合有纤维/塑料混合层和纤维层，纤维/塑料混合层处于塑料板材层和纤维层之间，所述纤维层中纤维在厚度方向上连续；所述复合塑料板材采用下述生产工艺制备：使用板材挤出机模头（6）挤出的板料经过第一辊筒（5）和第二辊筒（7）定型冷却，在塑料板材经过第二辊筒（7）时，通过调高加热装置（9）发热量使塑料板材的表面熔融，通过导向辊（10）将安放在纤维布架（11）上的纤维层导向并进入第二辊筒（7）和第三辊筒（8）间，此时与塑料板接触的纤维层被压入表面熔融的塑料板材层（1）中形成纤维/塑料混合层（2），再经过切边和定长切割即完成复合塑料板材的生产。
2.根据权利要求1所述的复合塑料板材，其特征在于，所述塑料板材层材质为聚丙烯板材、聚乙烯板材、聚偏氟乙烯板材、聚四氟乙烯板材或聚全氟乙丙烯板材。
3.根据权利要求1所述的复合塑料板材，其特征在于，所述纤维层材质为玻璃纤维或化学纤维。
4.一种复合塑料板材玻璃钢增强结构，包括塑料板材层，其特征在于，所述塑料板材层上依次复合有纤维/塑料混合层、纤维层和玻璃钢层，所述纤维层中纤维在厚度方向上连续，纤维层和玻璃钢层通过树脂粘接；所述复合塑料板材采用下述生产工艺制备：使用板材挤出机模头（6）挤出的板料经过第一辊筒（5）和第二辊筒（7）定型冷却，在塑料板材经过第二辊筒（7）时，通过调高加热装置（9）发热量使塑料板材的表面熔融，通过导向辊（10）将安放在纤维布架（11）上的纤维层导向并进入第二辊筒（7）和第三辊筒（8）间，此时与塑料板接触的纤维层被压入表面熔融的塑料板材层（1）中形成纤维/塑料混合层（2），再经过切边和定长切割即完成复合塑料板材的生产。