CN102079931A - Industrial antirust coating - Google Patents
Industrial antirust coating Download PDFInfo
- Publication number
- CN102079931A CN102079931A CN2009102255150A CN200910225515A CN102079931A CN 102079931 A CN102079931 A CN 102079931A CN 2009102255150 A CN2009102255150 A CN 2009102255150A CN 200910225515 A CN200910225515 A CN 200910225515A CN 102079931 A CN102079931 A CN 102079931A
- Authority
- CN
- China
- Prior art keywords
- proof paint
- industrial
- rust proof
- agent
- paint according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an industrial antirust coating which comprises the following components in percentage by mass: 2-4% of butanediol, 7-9% of titanium white powder, 0.3-0.5% of dispersing agent, 6-8% of aluminium phosphate, 1-3% of zinc oxide, 8-10% of talcum powder, 40-50% of acrylate emulsion, 0.05-0.25% of preservative, 0.3-0.5% of defoaming agent, 1-3% of film forming assistant, 0.4-0.6% of petroleum sulfonate type composite antirusting agent and the balance of deionized water. No organic solvent is used, and the industrial antirust coating is environmental friendly and nontoxic and has good antirust property and low cost.
Description
Technical field
The present invention relates to paint field, especially a kind of industrial rust proof paint.
Background technology
Rust proof paint is to be used for the metallic surface coated with preventing that metal is oxidated and get rusty at life-time service, and its major requirement paint adhesion is strong, good water-proof effect, fast drying.Industrial widely used rust proof paint, its rust-stabilising pigment component is generally the chromic salt of red lead, lead powder and zinc, lead or barium.These pigment all have very strong toxicity, can serious environment pollutions in the production of coating and use, and healthy with the constructing operation personnel produced in infringement.Therefore, many countries have all banned use of by legislation and have contained red lead, lead powder etc. and be the coating material production and the use of rust-stabilising pigment component.
At present, people successively develop the rust proof paint with rust-stabilising pigment components such as zinc phosphate, aluminum phosphate, zinc molybdate, lime borates, and these coating have the low characteristics of toxicity, but rust-proof effect is bad, and the color development of film-forming resin and stability are not good enough yet.
On the other hand, contain toluene, dimethylbenzene in the normally used oiliness rust proof paint and with heavy metal lead, cobalt, manganese as poisonous and harmful elements such as catalyzer, these compositions will bring great harm to construction and user of service healthy.
Summary of the invention
The objective of the invention is at above-mentioned deficiency of the prior art, a kind of have well antirust, water resistance, harmless, environment-friendly antirust coating that cost performance is high are provided.
For achieving the above object, the technical solution adopted for the present invention to solve the technical problems is:
A kind of industrial rust proof paint comprises according to mass percent, butyleneglycol 2-4%, titanium dioxide 7-9%, dispersion agent 0.3-0.5%, aluminum phosphate 6-8%, zinc oxide 1-3%, talcum powder 8-10%, CALCIUM ACRYLATE emulsion 40-50%, sanitas 0.05-0.25%, defoamer 0.3-0.5%, film coalescence aid 1-3%, mahogany acid salt composite antirust agent 0.4-0.6%, surplus deionized water.
The agent of described mahogany acid salt composite antirust contains mahogany acid potassium, barium mahogany sulfonate.
Described sanitas is selected from a kind of among K-10, the P-840 or their mixture.
Described defoamer is a kind of among F-111, the NXZ or their mixture.
Described film coalescence aid is the ethylene glycol methyl-n-butyl ether.
Described dispersion agent is a carboxylate salt.
Rust proof paint of the present invention contains resin and the agent of activated feedstock mahogany acid salt composite antirust; active iron rust is lost activity, iron rust is separated to be enclosed in film, make deleterious iron rust be converted into useful protective layer; firmly, form persistent rustproof layer attached to the metallic surface.
Compared with prior art, the invention has the beneficial effects as follows: the present invention not with an organic solvent, environmental protection, nontoxic, good antirust property, with low cost.
Embodiment
Disclosed all features in this specification sheets, or the step in disclosed all methods or the process except mutually exclusive feature and/or step, all can make up by any way.
Disclosed arbitrary feature in this specification sheets is unless special narration all can be replaced by other equivalences or the alternative features with similar purpose.That is, unless special narration, each feature is an example in a series of equivalences or the similar characteristics.
Embodiment 1: a kind of industrial rust proof paint comprises butyleneglycol 3% according to mass percent, titanium dioxide 9%, dispersion agent (carboxylate salt) 0.3%, aluminum phosphate 7%, zinc oxide 17%, talcum powder 10%, CALCIUM ACRYLATE emulsion 40%, sanitas (K-10) 0.05%, defoamer (F-111) 0.3%, film coalescence aid (ethylene glycol methyl-n-butyl ether) 2%, mahogany acid salt composite antirust agent 0.4%, surplus deionized water.
Embodiment 2: a kind of industrial rust proof paint comprises mahogany acid salt composite antirust agent 0.6% according to mass percent, sanitas (P-840) 0.25%, defoamer (F-111, NXZ) 0.4%, film coalescence aid (ethylene glycol methyl-n-butyl ether) 1%, butyleneglycol 2%, dispersion agent (carboxylate salt) 0.4%, aluminum phosphate 6%, zinc oxide 3%, titanium dioxide 8%, talcum powder 8%, CALCIUM ACRYLATE emulsion 50%, surplus deionized water.
Embodiment 3: a kind of industrial rust proof paint comprises mahogany acid salt composite antirust agent 0.5% according to mass percent, sanitas (K-10, P-840) 0.15%, defoamer (NXZ) 0.5%, film coalescence aid (ethylene glycol methyl-n-butyl ether) 3%, butyleneglycol 4%, dispersion agent (carboxylate salt) 0.5%, aluminum phosphate 8%, zinc oxide 2%, titanium dioxide 7%, talcum powder 9%, CALCIUM ACRYLATE emulsion 45%, surplus deionized water.
The present invention is not limited to aforesaid embodiment.The present invention expands to any new feature or any new combination that discloses in this manual, and the arbitrary new method that discloses or step or any new combination of process.
Claims (6)
1. an industrial rust proof paint is characterized in that: comprise butyleneglycol 2-4% according to mass percent, titanium dioxide 7-9%, dispersion agent 0.3-0.5%, aluminum phosphate 6-8%, zinc oxide 1-3%, talcum powder 8-10%, CALCIUM ACRYLATE emulsion 40-50%, sanitas 0.05-0.25%, defoamer 0.3-0.5%, film coalescence aid 1-3%, mahogany acid salt composite antirust agent 0.4-0.6%, surplus deionized water.
2. industrial rust proof paint according to claim 1 is characterized in that: the agent of described mahogany acid salt composite antirust contains mahogany acid potassium, barium mahogany sulfonate.
3. industrial rust proof paint according to claim 1 is characterized in that: described defoamer is a kind of among F-111, the NXZ or their mixture.
4. industrial rust proof paint according to claim 1 is characterized in that: described film coalescence aid is the ethylene glycol methyl-n-butyl ether.
5. industrial rust proof paint according to claim 1 is characterized in that: described dispersion agent is a carboxylate salt.
6. industrial rust proof paint according to claim 1 is characterized in that: described sanitas is selected from a kind of among K-10, the P-840 or their mixture.