CN102078794B - 一种除砷矿物材料及其制备方法 - Google Patents

一种除砷矿物材料及其制备方法 Download PDF

Info

Publication number
CN102078794B
CN102078794B CN200910238483.8A CN200910238483A CN102078794B CN 102078794 B CN102078794 B CN 102078794B CN 200910238483 A CN200910238483 A CN 200910238483A CN 102078794 B CN102078794 B CN 102078794B
Authority
CN
China
Prior art keywords
arsenic
siderite
kaolin
pore
activation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN200910238483.8A
Other languages
English (en)
Other versions
CN102078794A (zh
Inventor
冯流
刘欣
陈明
赵青涛
高峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beijing University of Chemical Technology
Original Assignee
Beijing University of Chemical Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beijing University of Chemical Technology filed Critical Beijing University of Chemical Technology
Priority to CN200910238483.8A priority Critical patent/CN102078794B/zh
Publication of CN102078794A publication Critical patent/CN102078794A/zh
Application granted granted Critical
Publication of CN102078794B publication Critical patent/CN102078794B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开一种用于水中砷吸附去除的矿物材料及其制备方法，该矿物材料采用高岭土、菱铁矿等矿物作为原料，以花生壳等果壳作为造孔剂，并适当添加少量粘结材料，经化学和高温煅烧活化制备得到。所包含的原料重量配比为：高岭土35～40％；菱铁矿35～40％；造孔材料10～20％；粘结材料5～10％。本发明中，除砷材料的制备方法简单易行，制造成本低，实际应用试验结果表明该除砷材料具有较好的吸附除砷效果。

Description

一种除砷矿物材料及其制备方法
技术领域
本发明涉及一种用于水中砷去除的矿物材料及其制备方法。
背景技术
在自然界中，砷含量平均为1.8mg/kg，其中一般岩石均含量在1～2mg/kg之间；土壤均含量约为5mg/kg，但有些土壤可达几百mg/kg；粘土层含量约为13mg/kg，但我国沿海有些地方松散沉积层中的粘土层，含量高达20mg/kg以上。
饮用水中过量砷可导致慢性中毒。最初，世界各国基于防治经饮用水过量摄砷导致的慢性砷中毒而制订了0.05mg/L的饮用水砷卫生标准。近年来，大量的流行病学调查显示：砷可能致人群皮肤癌、膀胱癌与肺癌等多种癌症，所以砷已被国际癌症组织确定为人类致癌物，且研究表明与其它一些疾病亦有较高的相关性。世界卫生组织(WHO)于1993年将饮用水砷卫生标准提高至0.01mg/L。日本和德国也分别于1993年和1996年将饮水砷标准提高至0.01mg/L。加拿大为0.025mg/L。美国环保局(USEPA)根据人群流行病学研究结果，于2001年1月公布了新标准中最大沾染物水平(maximum contaminantlevel，MCL)或最大沾染物水平目标(maximum contaminant level goal，MCLG)10μg/L的建议值，2002年10月对饮用水中砷卫生标准修订为10μg/L做出最终决定，2006年该标准在美国正式实施。美国有些州甚至把标准提高至0.002mg/L。我国最新的《生活饮用水卫生标准GB5749-2006》修订稿中砷的最大限值为0.01mg/L，但对于农村小型集中式供水和分散式供水部分仍沿用了以往0.05mg/L的规定(《生活饮用水卫生标准GB5749-85》)。
但就目前的研究成果来看，我国的除砷技术都过于繁琐，原材料、制作工艺成本较高，并不能广泛应用于饮用水含砷超标的贫困地区，对我国治理含砷饮用水的工程作用不大。因此，研究一种可以廉价的高效吸附水中砷的吸附材料来解决我国地方性慢性砷中毒已经势在必行。本发明制备的砷吸附材料主要原料为菱铁矿和高岭土，它们是天然的地质材料，价廉易得，具有一定的吸附性能，经过一系列的化学和高温煅烧活化处理后，对砷有很好的去除效果。
发明内容
本发明的目的是提供一种除砷效果好，并能投入使用的一种用于地下水砷去除的矿物材料及其制备方法。
地下水砷去除的矿物材料以下述技术方案实现：
先将高岭土、菱铁矿、造孔材料、粘结材料粉碎，将高岭土和菱铁矿用氢氧化钾活化，造孔材料用磷酸活化，再将材料用水洗至中性，按一定比例混合，压制成型，放入马弗炉高温活化，制得除砷材料。
质量百分含量为：高岭土35～40％；菱铁矿35～40％；造孔剂(花生壳等)10～20％；粘接材料(碎玻璃等)5～10％；
高岭土、菱铁矿粒径小于140目，造孔材料、粘结材料粒径小于40目。
氢氧化钾浓度为0.1mol/L～0.5mol/L。
磷酸浓度为40～60％，浸泡时间为4～7h。
高温活化温度为800～1000℃。
本发明特点：本发明提供一种用于地下水砷去除的矿物材料及其制备方法。该方法与以往方法相比具有除砷效果好、制备工艺简单、易于制备、方法简便可行、可重复利用、成本低等特点。
具体实施方式
以下结合具体实施方式对本发明作进一步详细说明：
实施例1
将高岭土、菱铁矿、造孔材料、粘结材料粉碎，将高岭土和菱铁矿用0.1mol/L氢氧化钾浸泡，花生壳用40％磷酸浸泡3h，再将材料用水洗至中性，按比例高岭土40％；菱铁矿40％；造孔材料15％；粘结材料5％混合，压制成型，放入马弗炉800℃活化，制得除砷材料，其静态试验除砷率为85％。
实施例2
将高岭土、菱铁矿、造孔材料、粘结材料粉碎，将高岭土和菱铁矿用0.3mol/L氢氧化钾浸泡，花生壳用60％磷酸浸泡6h，再将材料用水洗至中性，按比例高岭土35％；菱铁矿40％；造孔材料25％混合，压制成型，放入马弗炉1000℃活化，制得除砷材料，其静态试验除砷率为92％。
实施例3
将高岭土、菱铁矿、造孔材料、粘结材料粉碎，将高岭土和菱铁矿用0.2mol/L氢氧化钾浸泡，花生壳用50％磷酸浸泡5h，再将材料用水洗至中性，按比例高岭土40％；菱铁矿40％；造孔材料15％；粘结材料5％混合，压制成型，放入马弗炉900℃活化，制得除砷材料，其静态试验除砷率为93％。

Claims (2)

1.一种用于水中砷去除的矿物材料，其特征在于：以高岭土和菱铁矿为主要原材料，使用花生壳作为造孔材料，并辅以碎玻璃作为粘接材料，通过化学活化和高温煅烧，制备得到除砷材料；
具体步骤是：先将高岭土、菱铁矿、造孔材料、粘接材料粉碎，将高岭土和菱铁矿用氢氧化钾活化，造孔材料用磷酸活化，再将材料用水洗至中性，按一定比例混合，压制成型，放入马弗炉高温活化，制得除砷材料；
采用氢氧化钾和磷酸进行化学活化中，氢氧化钾浓度为0.1mol／L～0.5mol／L；磷酸浓度为40～60％，浸泡时间4～7h；
所述高温煅烧的活化温度为800～1000℃；
2.根据权利要求1所述的矿物材料，其特征是：主要原料高岭土和菱铁矿粒径小于140目，造孔材料和粘接材料粒径小于40目。
CN200910238483.8A 2009-11-27 2009-11-27 一种除砷矿物材料及其制备方法 Expired - Fee Related CN102078794B (zh)