CN102061555A - Flame-retardant fabric and manufacture process thereof - Google Patents
Flame-retardant fabric and manufacture process thereof Download PDFInfo
- Publication number
- CN102061555A CN102061555A CN 201010617553 CN201010617553A CN102061555A CN 102061555 A CN102061555 A CN 102061555A CN 201010617553 CN201010617553 CN 201010617553 CN 201010617553 A CN201010617553 A CN 201010617553A CN 102061555 A CN102061555 A CN 102061555A
- Authority
- CN
- China
- Prior art keywords
- retardant
- flame
- fire
- static
- yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a flame-retardant fabric, which is blended by electrostatic flame-retardant yarns and non-electrostatic flame-retardant yarns, wherein the non-electrostatic flame-retardant yarns comprise the following components in percentage by mass: 55%-80% of flame-retardant acrylon, 15%-40% of combed cotton and 5% of flame-retardant nylon, and the non-electrostatic flame-retardant yarns comprise the following components in percentage by mass: 55%-80% of flame-retardant acrylon, 13%-38% of combed cotton, 5% of flame-retardant nylon and 2% of electrostatic fiber. The invention also discloses a spinning process of the electrostatic flame-retardant yarns and the non-electrostatic flame-retardant yarns, and a manufacture process of the flame-retardant fabric. The invention adopts the reasonable combination of the flame-retardant acrylon, the combed cotton, the flame-retardant nylon, and the electrostatic fiber, and adopts an antistat. Meanwhile, the invention adjusts equipment of a spinning machine, and overcomes the defect of poor spinnability of the flame-retardant acrylon.
Description
Technical field
The present invention relates to the textile weaving field, be specifically related to a kind of fire-retardant lining and manufacturing technique thereof.
Background technology
Fire-retardant in the market lining is divided into two kinds of permanent fire retardant and disposable fire-retardant linings, its application prospect is very wide, except the effect that performances such as fabrics for industrial use, building interior trim, vehicles interior trim can not be substituted, also bringing into play many effects in the protective clothing field, the fire retardant protective clothing that fire-retardant lining is made has good washing durability, nonpoisonous and tasteless nonirritant, safe and reliable to human body, air-moisture-permeable, soft, comfortable and easy to wear.The problem that mainly exists for existing fire-retardant lining is easy to generate to drip to melt and causes the secondary injury because it weaves yarn is the polymer plastic material.
Application number is to disclose a kind of substrate-free flame retardant material in 200510012019.9 the Chinese invention patent, and it is formed and weight ratio is: colloid 40-70%, azo crosslinking agent 3-10%, efficient flame-retarding agent 20-50%.This substrate-free flame retardant material is made film, soft, and can be washable wear-resisting attached to the fireproof outside composite of making on the lining, and reach the difficult combustion of B1 grade standard.This kind lining be not permanent fire retardant along with its anti-flammability of long-term use will reduce gradually.
Summary of the invention
The invention provides a kind of permanent fire retardant, comfortable and easy to wear, COLOR FASTNESS superior performance, fire-retardant lining and manufacturing technique thereof that the feature of environmental protection is strong.
A kind of fire-retardant lining is formed by static flame-retardant yarn and the blending of non-static flame-retardant yarn, and described non-static flame-retardant yarn comprises following component by mass percent: 55%~80% flame-retardant acrylic fibre, 15%~40% combed cotton and 5% fire-retardant nylon; Described static flame-retardant yarn comprises following component by mass percent: 55%~80% flame-retardant acrylic fibre, 13%~38% combed cotton, 5% fire-retardant nylon and 2% electrostatic fibre.Adopt the blending structure of static flame-retardant yarn and non-static flame-retardant yarn not only to reduce the electrostatic effect of lining, and reduced manufacturing cost.The content that above-mentioned static flame-retardant yarn and non-its component of static flame-retardant yarn have reduced flame-retardant acrylic fibre has as much as possible kept the flame-retarding characteristic standard of lining simultaneously.
The spinning process of above-mentioned static flame-retardant yarn comprises:
With mass percent is 55%-80% flame-retardant acrylic fibre, 15%-38% combed cotton, 5% fire-retardant nylon fibrous raw material spinning machine mixed textile static flame-retardant yarn, and to add mass percent concentration in above-mentioned blended fiber raw material per ton be 45 kilograms in 2% antistatic additive, the Speed frames revolution is set at 3500 to be changeed, the fine spining machine revolution is set at 6300 changes, and incorporates mass ratio into by doubling frame at last and accounts for 2% electrostatic fibre long filament and be made into the static flame-retardant yarn.
The spinning process of above-mentioned non-static flame-retardant yarn comprises:
With mass percent is 55%~80% flame-retardant acrylic fibre, 15%~40% combed cotton, the 5% fire-retardant nylon fibrous raw material non-static flame-retardant yarn of spinning machine mixed textile, and to add mass percent concentration in above-mentioned blended fiber raw material per ton be 45 kilograms in 2% antistatic additive, the Speed frames revolution is set at 3500 commentaries on classics, the fine spining machine revolution is set at 6300 changes, and is made into non-static flame-retardant yarn.
Above-mentioned static flame-retardant yarn that makes or non-static flame-retardant yarn are permanent fire retardant, its main component flame-retardant acrylic fibre refers to fiber under middle-size and small-size burning things which may cause a fire disaster is lighted, and is difficult for flame combustion takes place, in case burning things which may cause a fire disaster is withdrawn, the flame that fiber produces is just quickly from horizontal blanking, and can not spreading causes disaster has anti-flammability.Nylon fiber is intensity and the toughness that a kind of high-intensity chemical fibre silk can increase flame-retardant yarn, but because its fire resistance is relatively poor, in combustion process, produce drippage, belong to combustible material, adopt fire-retardant nylon to strengthen anti-flammability and in flame-retardant acrylic fibre, combed cotton is compound makes it not produce drippage in combustion process, avoids the human body skin of burning.Electrostatic fibre can reduce the electrostatic effect of flame-retardant yarn.13%~40% or 13%~38% combed cotton has not only reduced the weaving cost but also has made the spinnability of yarn improve.
A kind of manufacturing technique of above-mentioned fire-retardant lining, with 7 non-static flame-retardant yarns at interval the flame-retardant yarn of 1 static enter large circle machine, revolution 280 changes, and weaves the typing of dyeing behind the fire-retardant lining.It has avoided electrostatic effect preferably with the 1 woven lining of static flame-retardant yarn in 7 non-static flame-retardant yarns intervals.Described dyeing setting process is: the fire-retardant lining that will weave adds color pond, and in dye solution per ton, add retarding agents (grand its dyeing and finishing auxiliaries for textile Co., Ltd., Factory production model in Dongguan: HONG QI-1227-214-3) reduce the colouring speed of flame-retardant acrylic fibre of concentration 0.3%, temperature curve 40 degree begin colouring, per minute intensification 2 degree arrive 80 degree, begin to boost to temperature 160 degree; Be incubated 30 minutes, be depressured to temperature 80 degree, be incubated natural cooling and shaping after 30 minutes.Adopting this kind dyeing to avoid painting because of flame-retardant acrylic fibre is the dyeing flower phenomenon that high-temperature pressure dyeing causes for normal temperature and pressure dyeing fire-retardant nylon soon, adopt curvilinear motion dyeing to make the lining expansion and contraction reach in 3%, 4 grades of color and luster fastness, the fire-retardant EN571 standard that reaches, static reaches the EN1149 standard.
The present invention adopts the reasonable combination of flame-retardant acrylic fibre, combed cotton, fire-retardant nylon, electrostatic fibre and adopts antistatic additive to regulate spinning machine simultaneously, overcomes the defective of flame-retardant acrylic fibre spinnability difference.Fire-retardant lining of the present invention is comfortable feel, permanent fire retardant and economical and practical not only, is fit to the large-scale application in market.
The specific embodiment
Embodiment 1
A kind of fire-retardant lining comprises by static flame-retardant yarn and the blending of non-static flame-retardant yarn and forming that described non-static flame-retardant yarn comprises following component by mass percent: 55% flame-retardant acrylic fibre, 40% combed cotton and 5% fire-retardant nylon; Described static flame-retardant yarn comprises following component by mass percent: 80% flame-retardant acrylic fibre, 13% combed cotton, 5% fire-retardant nylon and 2% electrostatic fibre.
With above-mentioned mass percent static flame-retardant yarn fibrous raw material spinning machine mixed textile static flame-retardant yarn, and to add mass percent concentration in above-mentioned blended fiber raw material per ton be 45 kilograms in 2% antistatic additive, the Speed frames revolution is set at 3500 to be changeed, the fine spining machine revolution is set at 6300 changes, and incorporates mass ratio into by doubling frame at last and accounts for 2% electrostatic fibre long filament and be made into the static flame-retardant yarn.
With the non-static flame-retardant yarn of the above-mentioned mass percent fibrous raw material non-static flame-retardant yarn of spinning machine mixed textile, and to add mass percent concentration in above-mentioned blended fiber raw material per ton be 45 kilograms in 2% antistatic additive, the Speed frames revolution is set at 3500 commentaries on classics, the fine spining machine revolution is set at 6300 changes, and is made into non-static flame-retardant yarn.
Embodiment 2
A kind of fire-retardant lining comprises by static flame-retardant yarn and the blending of non-static flame-retardant yarn and forming that non-static flame-retardant yarn comprises following component by mass percent: 60% flame-retardant acrylic fibre, 35% combed cotton and 5% fire-retardant nylon; Described static flame-retardant yarn comprises following component by mass percent: 75% flame-retardant acrylic fibre, 18% combed cotton, 5% fire-retardant nylon and 2% electrostatic fibre.The spinning process of static flame-retardant yarn and non-static flame-retardant yarn is with embodiment 1.
Embodiment 3
A kind of fire-retardant lining comprises by static flame-retardant yarn and the blending of non-static flame-retardant yarn and forming that non-static flame-retardant yarn comprises following component by mass percent: 65% flame-retardant acrylic fibre, 30% combed cotton and 5% fire-retardant nylon; Described static flame-retardant yarn comprises following component by mass percent: 70% flame-retardant acrylic fibre, 23% combed cotton, 5% fire-retardant nylon and 2% electrostatic fibre.The spinning process of static flame-retardant yarn and non-static flame-retardant yarn is with embodiment 1.
Embodiment 4
A kind of fire-retardant lining comprises by static flame-retardant yarn and the blending of non-static flame-retardant yarn and forming that non-static flame-retardant yarn comprises following component by mass percent: 70% flame-retardant acrylic fibre, 25% combed cotton and 5% fire-retardant nylon; Described static flame-retardant yarn comprises following component by mass percent: 65% flame-retardant acrylic fibre, 28% combed cotton, 5% fire-retardant nylon and 2% electrostatic fibre.The spinning process of static flame-retardant yarn and non-static flame-retardant yarn is with embodiment 1.
Embodiment 5
A kind of fire-retardant lining comprises by static flame-retardant yarn and the blending of non-static flame-retardant yarn and forming that non-static flame-retardant yarn comprises following component by mass percent: 75% flame-retardant acrylic fibre, 20% combed cotton and 5% fire-retardant nylon; Described static flame-retardant yarn comprises following component by mass percent: 60% flame-retardant acrylic fibre, 33% combed cotton, 5% fire-retardant nylon and 2% electrostatic fibre.The spinning process of static flame-retardant yarn and non-static flame-retardant yarn is with embodiment 1.
Embodiment 6
A kind of fire-retardant lining comprises by static flame-retardant yarn and the blending of non-static flame-retardant yarn and forming that non-static flame-retardant yarn comprises following component by mass percent: 80% flame-retardant acrylic fibre, 15% combed cotton and 5% fire-retardant nylon; Described static flame-retardant yarn comprises following component by mass percent: 55% flame-retardant acrylic fibre, 38% combed cotton, 5% fire-retardant nylon and 2% electrostatic fibre.The spinning process of static flame-retardant yarn and non-static flame-retardant yarn is with embodiment 1.
Embodiment 7
The manufacturing technique of the arbitrary fire-retardant lining of the foregoing description 1-6, enter large circle machine with the 1 static flame-retardant yarn in 7 non-static flame-retardant yarns intervals, revolution 280 changes weaves fire-retardant lining, and it has avoided electrostatic effect preferably with the 1 woven lining of static flame-retardant yarn in 7 non-static flame-retardant yarns intervals.
Embodiment 8
A kind of dyeing that is applied to above-mentioned fire-retardant lining, described fire-retardant lining is added color pond, and in dye solution per ton, add retarding agents (grand its dyeing and finishing auxiliaries for textile Co., Ltd., Factory production model in Dongguan: HONG QI-1227-214-3) of concentration 0.3%, reduce the colouring speed of flame-retardant acrylic fibre, temperature curve 40 degree begin colouring, per minute intensification 2 degree arrive 80 degree, begin to boost to temperature 160 degree; Be incubated 30 minutes, be depressured to temperature 80 degree, be incubated natural cooling and shaping after 30 minutes.Adopting this kind dyeing to avoid painting because of flame-retardant acrylic fibre is the dyeing flower phenomenon that high-temperature pressure dyeing causes for normal temperature and pressure dyeing fire-retardant nylon soon, adopt curvilinear motion dyeing to make the lining expansion and contraction reach in 3%, 4 grades of color and luster fastness, the fire-retardant EN571 standard that reaches, static reaches the EN1149 standard.
Claims (5)
1. fire-retardant lining, it is characterized in that: formed by static flame-retardant yarn and the blending of non-static flame-retardant yarn, described non-static flame-retardant yarn comprises following component by mass percent: 55%~80% flame-retardant acrylic fibre, 15%~40% combed cotton and 5% fire-retardant nylon; Described static flame-retardant yarn comprises following component by mass percent: 55%~80% flame-retardant acrylic fibre, 13%~38% combed cotton, 5% fire-retardant nylon and 2% electrostatic fibre.
2. fire-retardant lining according to claim 1 is characterized in that: the spinning process of described static flame-retardant yarn comprises:
With mass percent is 55%-80% flame-retardant acrylic fibre, 15%-38% combed cotton, 5% fire-retardant nylon fibrous raw material spinning machine mixed textile static flame-retardant yarn, and to add mass percent concentration in above-mentioned blended fiber raw material per ton be 45 kilograms in 2% antistatic additive, the Speed frames revolution is set at 3500 to be changeed, the fine spining machine revolution is set at 6300 changes, and incorporates mass ratio into by doubling frame at last and accounts for 2% electrostatic fibre long filament and be made into the static flame-retardant yarn.
3. fire-retardant lining according to claim 1 is characterized in that: the spinning process of described non-static flame-retardant yarn comprises:
With mass percent is 55%~80% flame-retardant acrylic fibre, 15%~40% combed cotton, the 5% fire-retardant nylon fibrous raw material non-static flame-retardant yarn of spinning machine mixed textile, and to add mass percent concentration in above-mentioned blended fiber raw material per ton be 45 kilograms in 2% antistatic additive, the Speed frames revolution is set at 3500 commentaries on classics, the fine spining machine revolution is set at 6300 changes, and is made into non-static flame-retardant yarn.
4. manufacturing technique of making fire-retardant lining as claimed in claim 1 is characterized in that: with 7 non-static flame-retardant yarns at interval the flame-retardant yarn of 1 static enter large circle machine, revolution 280 changes, and weaves the typing of dyeing behind the fire-retardant lining.
5. the manufacturing technique of fire-retardant lining according to claim 4, it is characterized in that: described dyeing setting process is: the fire-retardant lining that will weave adds color pond, and in dye solution per ton, add the retarding agents of concentration 0.3%, temperature curve 40 degree begin colouring, per minute intensification 2 degree arrive 80 degree, begin to boost to temperature 160 degree; Be incubated 30 minutes, be depressured to temperature 80 degree, be incubated natural cooling and shaping after 30 minutes.