CN1020430C - 复合铝箔防护材料及其技术 - Google Patents
复合铝箔防护材料及其技术 Download PDFInfo
- Publication number
- CN1020430C CN1020430C CN 88100696 CN88100696A CN1020430C CN 1020430 C CN1020430 C CN 1020430C CN 88100696 CN88100696 CN 88100696 CN 88100696 A CN88100696 A CN 88100696A CN 1020430 C CN1020430 C CN 1020430C
- Authority
- CN
- China
- Prior art keywords
- weight
- adhesive
- cloth
- protective material
- epoxy resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
复合铝箔防护材料,由铝箔、阻火纸和玻纤布(或无纺布等)为基材其中的玻纤布(或无纺布)可以是一层,也可以是几层,布的最下层还可以是铝箔(两层铝箔之间夹阻火纸和布)。各层材料之间以粘合剂粘接。整个工艺由粘合剂配制、投料、浸胶、烘干、压合和检验包装六道工序构成。这种防护材料保温隔热效果好、节约能源,安装维修方便,耐腐蚀、使用寿命长。这种材料适用做各种热力管道和露天容器的保温防护材料。
Description
本发明属于建材制造技术领域。主要用做石油、化工、冶金、电力等热力管道和露天容器的保温防护材料。
目前国内外用做热力管道和露天容器的保温防护材料的种类很多,如毛毡、麻、玻璃丝、玻纤布、石棉灰、白灰、草绳、油毡等等,根据需要可将其中几种材料组合使用。上述保温防护材料虽然被普遍采用,但效果不够理想,使用寿命也较短。
本发明的目的是,提供一种致密性好,隔热保温,耐腐节能的管道、容器防护材料及其技术。
本发明以铝箔、阻火纸(牛皮纸浸上加有阻火剂的粘合剂)和玻纤布(或无纺布等)为基材,各层之间以粘合剂粘接后,压合而成。这种复合铝箔防护材料一般为三层,即铝箔、阻火纸和玻纤布(或无纺布)各为一层。也可以是多层,办法是增加玻纤布(或无纺布等)的层数,最后一层还可以是铝箔(即两层铝箔中间夹阻火纸和布)。铝箔厚度为0.02-0.10毫米,以0.02-0.04毫米为宜,阻火纸(牛皮纸)和布为一般市售商品。复合铝箔防护材料,分卷材和板材两种。
复合铝箔防护材料的生产工艺如附图所示:由粘合剂配制、投料、浸胶(浸粘合剂)、烘干、压合和检验包装工序构成。现将各工序分叙如下:
1、粘合剂的配制
按配比将所需原料投入反应釜中,在常温常压下,搅拌均匀即可。
粘合剂配方如下:
卷材用粘合剂配方
原料名称 原料配比 最佳原料配比
环氧树脂 15-30%(重量) 20±3%(重量)
固化剂 环氧树脂的4-7%(重量) 环氧树脂的5±0.5%(重量)
偶联剂 1-3%(重量) 2±0.2%(重量)
防老化剂 1-4%(重量) 3%(重量)
天然胶、溶剂油 60-80%(重量) 70±5%(重量)
天然胶与溶剂油的重量比为1∶8~10,其中以1∶9为佳
各组份总合为100%(重量)
板材用粘合剂两种配方(生产板材时任选其一)
(1)
原料名称 原料配比 最佳原料配比
环氧树脂 100重量份 100重量份
固化剂 10-20重量份 15±2重量份
偶联剂 1-3重量份 2重量份
(2)
原料名称 原料配比 最佳原料配比
聚酯树脂 100重量份 100重量份
固化剂 3-5重量份 4重量份
促进剂 1-4重量份 2重量份
2、投料
材料经筛选后,由机械输送投料。
3、浸胶(浸粘合剂)
将玻纤布(或无纺布等)、阻火纸,在浸胶槽内进行单面浸胶(卷材、板财用不同的胶)。
4、烘干
浸胶后的半成品,送入烘干室在30-100℃条件下,烘至半固态(夏季不需烘干,可自然干燥)。
5、压合
将铝箔及干燥至半固态的材料,按要求的层次用对辊压合成复合铝箔防护材料。
6、检验包装
产品达到质量标准后,剪裁包装即为成品。
产品经实测,达到如下指标:
指标名称 单位 数据
热辐射系数 KJ/米2时K47.54
反射系数 % 80-90
导热系数 KJ/米时℃ 0.188
蓄热系数 KJ/米2时℃ 2.30
比热容 KJ/公斤℃ 1.13
吸水率 % ≤0.5
氧指数 >26
剥离强度 N/cm21.90
使用温度 ℃ 60-120
复合铝箔防护材料的使用方法:
1、卷材(用于管道的防护)使用时采用缠绕粘接的方法。
2、板材(用于露天大型容器)使用时采用镶嵌铆固的方法。
复合铝箔防护材料的优点是,隔热效果好、节约能源,安装维修方便,使用寿命长,耐腐蚀。
附图说明
附图为本发明生产工艺流程框图
实施方案
按如上所叙述的工艺,使用如上述所叙述的粘合剂,即可实施本发明。实施时,各工序可以是单元操作,最好是建成生产线进行连续生产。
Claims (7)
1、复合铝箔防护材料,其特征在于以铝箔、阻火纸、玻纤布或无纺布为基材,用相应的粘合剂将三种材料粘接在一起,铝箔、阻火纸各为一层,玻纤布或无纺布,可以是一层,也可以是几层,布的下面还可以加一层铝箔(即两层铝箔中夹阻火纸和布)。
2、根据权利要求1所叙述的复合铝箔防护材料,其特征在于铝箔的厚度为0.02-0.1毫米。
3、根据权利要求2所述的复合铝箔防护材料,其特征在于铝箔的厚度为0.02~0.04毫米。
4、根据权利要求1所叙述的复合铝箔防护材料,其特征在于粘接卷材的粘合剂的配方是,
环氧树脂 15-30% (重量)
固化剂 环氧树脂的4-7% (重量)
偶联剂 1-3% (重量)
防老化剂 1-4% (重量)
天然胶、溶剂油 60-80%(重量)
天然胶与溶剂油的重量比为1∶8-10
各组份总和为100%(重量)
粘接板材的粘合剂配方分别是,
(1)
环氧树脂 100份 (重量)
固化剂 10-20份 (重量)
偶联剂 1-3份 (重量)
(2)
聚酯树脂 100份 (重量)
固化剂 3-5份 (重量)
促进剂 1-4份 (重量)
5、根据权利要求4所述的复合铝箔防护材料,其特征在于粘接卷材的粘合剂的配方是,
环氧树脂 20±3% (重量)
固化剂 环氧树脂重的5±0.5% (重量)
偶联剂 2±0.2% (重量)
防老化剂 3±0.2% (重量)
天然胶、溶剂油 70±5% (重量)
天然胶与溶剂油的重量比为1∶9
各组份总和为100% (重量)
粘接板材粘合剂的配方(1)是,
环氧树脂 100份 (重量)
固化剂 15±2份 (重量)
偶联剂 2份 (重量)
6、制造复合铝箔防护材料的技术,其特征在于由粘合剂配制、投料、浸胶、烘干、压合、检验、包装六道工序组成。
7、根据权利要求6所叙述的技术,其特征在于粘合剂配制在反应釜中,在常温常压下搅拌均匀即可,材料经筛选后用机械输送投料,阻火纸、玻纤布或无纺布在浸胶槽进行单面浸胶,浸胶后的半成品送至干燥室在30-100℃条件下烘至半固态,夏季不需烘干,可在空间自然干燥,铝箔及干燥至半固态的阻火纸和布用对辊压合成一体,经剪裁包装即为成品。