CN102029718B - Agate-jade artificial composite material decorating plate and processing method - Google Patents
Agate-jade artificial composite material decorating plate and processing method Download PDFInfo
- Publication number
- CN102029718B CN102029718B CN200910246577.XA CN200910246577A CN102029718B CN 102029718 B CN102029718 B CN 102029718B CN 200910246577 A CN200910246577 A CN 200910246577A CN 102029718 B CN102029718 B CN 102029718B
- Authority
- CN
- China
- Prior art keywords
- kilograms
- polyester resin
- unsaturated polyester
- fine powder
- grams
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses an agate-jade artificial composite material decorating plate and a processing method. The surface of the conventional decorating plate is not provided with emulational pattern, the surface finish is undesirable and certain decorating plates contain toxic and harmful substances and cause great damage to the using environment. The processing method of the agate-jade artificial composite material decorating plate comprises the following steps of: preparing 1 kilogram of unsaturated polyester resin and color paste based on a square meter of finished product, wherein the using amount of the color paste is determined according to the color desired by a user; preparing 1 kilogram of unsaturated polyester resin fine powder, 1.3 kilograms of aluminum hydroxide fine powder and white paste, wherein the using amount of the white paste is determined according to field condition; and preparing 6.5 to 6 kilograms of unsaturated polyester resin, 6 to 5.5 kilograms of aluminum hydroxide coarse powder, 5.5 to 6 kilograms of aluminum hydroxide fine powder, 5 to 2.8 grams of methyl ethyl ketone peroxide and 5 to 2.8 grams of cobalt naphthenate, wherein processing temperature is between 5 and 2.8 DEG C. The product is applied to interior decoration.
Description
Technical field:
The present invention relates to imitative agate-jade artificial composite material decorating plate material and processing method that a kind of resin composite materials is made.
Background technology:
Decorative panel, the important materials as house decoration is generally applied.Complaint according to Decoration Industry is added up, and 70% about decoration panel, and case hardness is low, fineness is also undesirable, bulk strength is poor, does not often reach the satisfaction of user, and some decorative panel is owing to the addition of the harmful substances such as benzene, containing poisonous and harmful substances, very large harm is caused to environment for use.
Summary of the invention:
The object of this invention is to provide artificial compounded material decorating plate and processing method that height that a kind of, fine powder thick by unsaturated polyester resin and Aluminium Hydroxide Powder(to make Alum.Sulfate) powder be composited imitates agate jade material.
Above-mentioned object is realized by following technical scheme:
Agate-jade artificial composite material decorating plate processing method:
The first step: get unsaturated polyester resin 1 kilogram, according to user want color to add the mill base amount of supporting color, Homogeneous phase mixing, be the first material, the first described material be spread out on off-the-shelf workbench equably, leave standstill 1-5 minute;
Second step: get unsaturated polyester resin fine powder 1 kilogram and add aluminium hydroxide powder and fine powder 1.3 kilograms, adding stock white is the second material, described the second material Homogeneous phase mixing is pressed the pattern of often row diamond block, is arranged in order and is poured, and leaves standstill 3-8 minute;
3rd step: get unsaturated polyester resin 6.5---6 kilogram, aluminium hydroxide meal and each 6---5.5 kilogram of fine powder, pour in mixer and stir, and is the third material;
The third material is cast on the second material, leaves standstill 10-30 minute;
Add man-hour, temperature, between 5 DEG C-28 DEG C, on mounted workbench, reserves temperature, treats to add cobalt naphthenate 5---2.8 gram and peroxidating first and second bronze medal 5---2.8 gram in materials in proportion to above three kinds;
4th step: towards the direction of workbench, by extruding, the decorative pattern as leaf of self-assembling formation uniqueness, leaves standstill 5-10 hour coagulation forming.Play platform, check the quality of the products, after up-to-standard, pack, dispatch from the factory.
An agate-jade artificial composite material decorating plate for above-mentioned method processing, its composition comprises: base plate, the base plate described in making with said method and pass through the very high dapple surface layer of band of the fineness of said method compound.
Beneficial effect of the present invention:
1. the hardness of artificial compounded material decorating plate of the present invention is good, surface smoothness is very high, and decorative pattern is unique, is applicable to various decoration occasions and uses.
2. the surface color of artificial compounded material decorating plate of the present invention is soft, and color is warm, and clear transparent, brings people warming sense.
3. artificial compounded material decorating plate waterproof of the present invention, protection against the tide, can according to, can bore, can glue, processing technology is simple.
4. nontoxic, tasteless, the environmental protection of artificial compounded material decorating plate of the present invention, harmless.
Accompanying drawing illustrates:
Accompanying drawing 1 is structural representation of the present invention.
Detailed description of the invention:
Embodiment 1:
Agate-jade artificial composite material decorating plate, its composition comprises: base plate, described base plate is compounded with the dapple surface layer of the very high band of fineness.
Embodiment 2:
Agate-jade artificial composite material decorating plate processing technology described in embodiment 1, described formula calculates by weight per square meter:
First, consumption is unsaturated polyester resin and mill base 1 kilogram, the consumption of mill base according to user want color and determine.
Secondly, consumption is unsaturated polyester resin fine powder 1 kilogram, aluminium hydroxide powder and fine powder 1.3 kilograms, stock white, and the consumption of stock white according to the situation.
Then, following consumption is determined by variations in temperature:
When processing temperature is at 7 DEG C-8 DEG C, unsaturated polyester resin 6.5 kilograms, aluminium hydroxide meal 6 kilograms, aluminium hydroxide fine powder 5.5 kilograms, peroxidating first and second bronze medal (plain boiled water) 4.8 grams, cobalt naphthenate (purple water) 4.8 grams;
When processing temperature is at 9 DEG C-10 DEG C, unsaturated polyester resin 6.5 kilograms, aluminium hydroxide meal 6 kilograms, aluminium hydroxide fine powder 5.5 kilograms, peroxidating first and second bronze medal (plain boiled water) 4.6 grams, cobalt naphthenate (purple water) 4.6 grams;
When processing temperature is at 11 DEG C-12 DEG C, unsaturated polyester resin 6.5 kilograms, aluminium hydroxide meal 6 kilograms, aluminium hydroxide fine powder 5.5 kilograms, peroxidating first and second bronze medal (plain boiled water) 4.4 grams, cobalt naphthenate (purple water) 4.4 grams;
When processing temperature is at 13 DEG C-14 DEG C, unsaturated polyester resin 6.5 kilograms, aluminium hydroxide meal 6 kilograms, aluminium hydroxide fine powder 5.5 kilograms, peroxidating first and second bronze medal (plain boiled water) 4.7 grams, cobalt naphthenate (purple water) 4.7 grams;
When processing temperature is at 15 DEG C-16 DEG C, unsaturated polyester resin 6 kilograms, aluminium hydroxide meal 6 kilograms, aluminium hydroxide fine powder 6 kilograms, peroxidating first and second bronze medal (plain boiled water) 4 grams, cobalt naphthenate (purple water) 4 grams;
When processing temperature is at 17 DEG C-18 DEG C, unsaturated polyester resin 6 kilograms, aluminium hydroxide meal 6 kilograms, aluminium hydroxide fine powder 6 kilograms, peroxidating first and second bronze medal (plain boiled water) 3.8 grams, cobalt naphthenate (purple water) 3.8 grams;
When processing temperature is at 19 DEG C-20 DEG C, unsaturated polyester resin 6 kilograms, aluminium hydroxide meal 5.5 kilograms, aluminium hydroxide fine powder 6 kilograms, peroxidating first and second bronze medal (plain boiled water) 3.6 grams, cobalt naphthenate (purple water) 3.6 grams;
When processing temperature is at 21 DEG C-22 DEG C, unsaturated polyester resin 6 kilograms, aluminium hydroxide meal 5.5 kilograms, aluminium hydroxide fine powder 6 kilograms, peroxidating first and second bronze medal (plain boiled water) 3.5 grams, cobalt naphthenate (purple water) 3.5 grams;
When processing temperature is at 23 DEG C-24 DEG C, unsaturated polyester resin 6 kilograms, aluminium hydroxide meal 5.5 kilograms, aluminium hydroxide fine powder 6 kilograms, peroxidating first and second bronze medal (plain boiled water) 3.1 grams, cobalt naphthenate (purple water) 3.1 grams;
When processing temperature is at 25 DEG C-26 DEG C, unsaturated polyester resin 6 kilograms, aluminium hydroxide meal 5.5 kilograms, aluminium hydroxide fine powder 6 kilograms, peroxidating first and second bronze medal (plain boiled water) 3 grams, cobalt naphthenate (purple water) 3 grams.
When processing temperature is at 27 DEG C-28 DEG C, unsaturated polyester resin 6 kilograms, aluminium hydroxide meal 5.5 kilograms, aluminium hydroxide fine powder 6 kilograms, peroxidating first and second bronze medal (plain boiled water) 2.8 grams, cobalt naphthenate (purple water) 2.8 grams.
Embodiment 3:
Agate-jade artificial composite material decorating plate processing method, is characterized in that:
The first step: get unsaturated polyester resin 1 kilogram, according to user want color to add to overlap the mill base amount that mixes colours, Homogeneous phase mixing, is the first material, is spread out on off-the-shelf workbench equably by the first described material, leaves standstill 1-5 minute;
Second step: get unsaturated polyester resin fine powder 1 kilogram and add aluminium hydroxide powder and fine powder 1.3 kilograms, adding stock white is the second material, described the second material Homogeneous phase mixing is pressed the pattern of often row diamond block, is arranged in order and is poured, and leaves standstill 3-8 minute;
3rd step: get unsaturated polyester resin 6.5---6 kilogram, aluminium hydroxide meal and each 6---5.5 kilogram of fine powder, pour in mixer and stir, and is the third material;
The third material is cast on the second material, leaves standstill 10-30 minute;
Add man-hour, temperature, between 5 DEG C-28 DEG C, on mounted workbench, reserves temperature, treats to add cobalt naphthenate 5---2.8 gram and peroxidating first and second bronze medal 5---2.8 gram in materials in proportion to above three kinds;
4th step: towards the direction of workbench, by extruding, the decorative pattern as leaf of self-assembling formation uniqueness, leaves standstill 5-10 hour coagulation forming.
Claims (1)
1.
a kind of agate-jade artificial composite material decorating plate processing method, is characterized in that:
the first step: get unsaturated polyester resin 1 kilogram, according to user want color to add the mill base amount of supporting color, Homogeneous phase mixing, be the first material, the first described material be spread out on off-the-shelf workbench equably, leave standstill 1-5 minutes;
second step: get unsaturated polyester resin fine powder 1 kilogram and add aluminium hydroxide powder and fine powder 1.3 kilograms, adding stock white is the second material, described the second material Homogeneous phase mixing is pressed the pattern of often row diamond block, is arranged in order and is poured, and leaves standstill 3-8 minutes;
3rd step: get unsaturated polyester resin 6.5-6 kilograms, aluminium hydroxide meal and each 6-5.5 kilograms of fine powder, pour in mixer and stir, and is the third material;
the third material is cast on the second material, leaves standstill 10-30 minutes;
add man-hour, temperature, between 5 DEG C-28 DEG C, on mounted workbench, reserves temperature, treats to add cobalt naphthenate 5-2.8 grams and peroxidating first and second bronze medal 5-2.8 grams in materials in proportion to above three kinds;
4th step: towards the direction of workbench, by extruding, the decorative pattern as leaf of self-assembling formation uniqueness, leaves standstill 5-10 hours coagulation formings.