CN102014575A - 局部镀金板的制作工艺 - Google Patents

局部镀金板的制作工艺 Download PDF

Info

Publication number
CN102014575A
CN102014575A CN 201010557087 CN201010557087A CN102014575A CN 102014575 A CN102014575 A CN 102014575A CN 201010557087 CN201010557087 CN 201010557087 CN 201010557087 A CN201010557087 A CN 201010557087A CN 102014575 A CN102014575 A CN 102014575A
Authority
CN
China
Prior art keywords
gold
plated
circuit board
wire
manufacture craft
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 201010557087
Other languages
English (en)
Other versions
CN102014575B (zh
Inventor
刘宝林
罗斌
崔荣
武凤伍
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shennan Circuit Co Ltd
Original Assignee
Shennan Circuit Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shennan Circuit Co Ltd filed Critical Shennan Circuit Co Ltd
Priority to CN2010105570874A priority Critical patent/CN102014575B/zh
Publication of CN102014575A publication Critical patent/CN102014575A/zh
Application granted granted Critical
Publication of CN102014575B publication Critical patent/CN102014575B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种局部镀金板的制作工艺，包括如下步骤：在电路板上一次性做出具有镀金区域和非镀金区域的所有板内图形；同时制作外层引线和导电辅助边作为镀金导线，并且使外层引线的两端与导电辅助边和镀金区域连接；在非镀金区域和外层引线上贴上保护干膜进行保护；用外层引线作为镀金导线，对镀金区域进行镀金；去掉非镀金区域的保护干膜；采用激光定点熔线工艺去除外层引线，所述激光定点熔线的温度为1100度。本发明通过一次性蚀刻出电路板内所有图形，并做成外层引线作为镀金导线，在完成对电路板的局部镀金工序后，通过激光熔蚀掉，如此在电路板上就不会存在镀金区域和非镀金区域之间出现对位精度偏差的情况。

Description

局部镀金板的制作工艺
技术领域
本发明涉及一种线路板加工工艺，尤其涉及一种局部镀金板的制作工艺。
背景技术
现有的局部镀金板的制作工艺流程如下：下料-内层加工-层压-钻孔-沉铜-电镀-第一次外层图形(将镀金区域显影出来进行镀金)-根据第一次外层图形用电路板的大铜面做镀金导线，对基板进行局部镀金做成镀金区域图形-去膜(去掉镀金保护干膜)-第二次外层图形做成非镀金区域图形-对第二次外层图形部位进行碱性蚀刻、酸性蚀刻(制作板内图形)-外检-阻焊-印刷字符-表面涂覆-外形-电测-成检-包装。
然而，上述现有局部镀金板的制作工艺中第一次图形和第二次图形时存在如下缺陷：
1、图形对位困难：在镀金区域和非镀金区域的连接处，因为有第一次图形制作出镀金区域图形和第二次图形制作出非镀金区域图形之间存在2～4mil的对位精度偏差；
2、镀金质量差：由于镀金周围区域和图层连接，当进行外蚀刻制作板内图形时，容易出现镀金层下面的铜层被咬蚀掉，出现镀金面塌陷的情况。
发明内容
本发明主要解决的技术问题是提供一种局部镀金板的制作工艺，可避免图形出现对位偏差和提高镀金质量的情况。
为解决上述技术问题，本发明采用的一个技术方案是：提供一种局部镀金板的制作工艺，包括如下步骤：
在电路板上一次性做出具有镀金区域和非镀金区域的所有板内图形；同时制作外层引线和导电辅助边作为镀金导线，并且使外层引线的两端与导电辅助边和镀金区域连接；
在非镀金区域和外层引线上贴上保护干膜进行保护；
用外层引线作为镀金导线，对镀金区域进行镀金；
去掉非镀金区域的保护干膜；
采用激光定点熔线工艺去除外层引线，所述激光定点熔线的温度为1100度。
其中，所述在电路板上一次性制作出板内图形的步骤包括：在电路板上进行外层图形和进行图形蚀刻，制作出所有板内图形。
其中，所述在电路板上一次性制作出板内图形的步骤之前包括步骤：对电路板进行沉铜、电镀。
其中，所述在对电路板进行沉铜、电镀的步骤之前包括步骤：对电路板进行层压、钻孔。
其中，所述在对电路板进行层压、钻孔步骤之前包括步骤：对构成电路板的基板进行内层加工。
其中，所述在一次性做出所有板内图形和在做出的板内图形的非镀金区域贴上保护干膜的步骤之间包括步骤：对做出的所有板内图形进行外检。
其中，所述在采用激光定点熔线去除外层引线的步骤之后包括步骤：进行阻焊、印刷字符。
其中，所述在印刷字符的步骤之后包括步骤：外形检测、进行电测试。
其中，所述在外形检测、进行电测试的步骤之后包括步骤：进行成品检测。
本发明的有益效果是：区别于现有技术的局部镀金板二次图形对位困难和镀金质量差的情况，本发明通过一次性蚀刻出电路板内所有图形，并做成外层引线作为镀金导线，在完成对电路板的局部镀金工序后，通过激光熔蚀掉，如此在电路板上就不会存在镀金区域和非镀金区域之间出现对位精度偏差的情况。
附图说明
图1是本发明局部镀金板的制作工艺的流程图；
图2是本发明局部镀金板蚀刻出板内所有图形的结构示意图；
图3是将图2中非镀金区域保护起来的结构示意图；
图4是对图2中镀金区域进行镀金的结构示意图；
图5是去掉图3中非镀金区域保护膜的结构示意图；
图6是采用激光熔线法去掉外层引线的结构示意图。
具体实施方式
为详细说明本发明的技术内容、构造特征、所实现目的及效果，以下结合实施方式并配合附图详予说明。
请参阅图1，本发明局部镀金板的制作工艺，包括如下步骤：
下料，即选取构成电路板的基板；
对构成电路板的基板进行内层加工；
对电路板进行层压、钻孔；
对层压、钻孔后的电路板上进行沉铜、电镀；
请参阅图2，在电路板上一次性做出具有镀金区域和非镀金区域的所有板内图形100；即在电路板上需要进行制作板内图形100的区域进行外层图形，并蚀刻出所有板内图形；同时制作外层引线10和导电辅助边20作为镀金导线，并且使外层引线10的两端与导电辅助边20连接；
对蚀刻出的所有板内图形进行外检；
请参阅图3，将非镀金区域和外层引线贴上保护干膜进行保护；
请参阅图4，用外层引线10作为镀金导线，对镀金区域进行镀金；
请参阅图5，去掉非镀金区域的保护干膜；
请参阅图6，采用激光定点熔线工艺去除外层引线10，所述激光熔线温度为具体1100度，具体包括步骤通过侧面切断铜线和镀金区域的连接，时间为1min能点断300个点；
进行阻焊；
然后进行印刷字符；
整平电路板；
对电路板进行外形检测；
对电路板进行电测试；
成品检测；
包装。
本发明通过一次性蚀刻出电路板内所有图形，如此在电路板上就不会存在镀金区域和非镀金区域之间出现对位精度偏差的情况，并且本发明通过一次性蚀刻出电路板内所有图形100，并用外层引线10和导电辅助边20作为镀金导线，可以在镀金区域四周均镀上镍金层，这样能保护镀金区域，提高镀金质量，同时在镀金后只需要通过激光熔蚀掉外层引线，不需要进行大量的蚀刻工艺，镀金层下的沉铜不会被咬蚀掉，从而不会出现镀金面塌陷的情况。
区别于现有技术的局部镀金板在进行两次图形时存在对位困难和镀金质量差的情况，本发明通过一次性蚀刻出电路板内所有图形，并做成外层引线10作为镀金导线，在完成对电路板的局部镀金工序后，通过激光熔蚀掉外层引线10，如此在电路板上就不会存在镀金区域和非镀金区域之间出现对位精度偏差的情况。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书及附图内容所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (9)

1.一种局部镀金板的制作工艺，其特征在于，包括如下步骤：
在电路板上一次性做出具有镀金区域和非镀金区域的所有板内图形；同时制作外层引线和导电辅助边作为镀金导线，并且使外层引线的两端与导电辅助边和镀金区域连接；
在非镀金区域和外层引线上贴上保护干膜进行保护；
用外层引线作为镀金导线，对镀金区域进行镀金；
去掉非镀金区域的保护干膜；
采用激光定点熔线工艺去除外层引线，所述激光定点熔线的温度为1100度。
2.根据权利要求1所述的局部镀金板的制作工艺，其特征在于：在电路板上一次性制作出板内图形的步骤包括：在电路板上进行外层图形和进行图形蚀刻，制作出所有板内图形。
3.根据权利要求2所述的局部镀金板的制作工艺，其特征在于：在电路板上一次性制作出板内图形的步骤之前包括步骤：对电路板进行沉铜、电镀。
4.根据权利要求2所述的局部镀金板的制作工艺，其特征在于：在对电路板进行沉铜、电镀的步骤之前包括步骤：对电路板进行层压、钻孔。
5.根据权利要求3所述的局部镀金板的制作工艺，其特征在于：在对电路板进行层压、钻孔步骤之前包括步骤：对构成电路板的基板进行内层加工。
6.根据权利要求1所述的局部镀金板的制作工艺，其特征在于：在一次性做出所有板内图形和在做出的板内图形的非镀金区域贴上保护干膜的步骤之间包括步骤：对做出的所有板内图形进行外检。
7.根据权利要求1所述的局部镀金板的制作工艺，其特征在于：在采用激光定点熔线去除外层引线的步骤之后包括步骤：进行阻焊、印刷字符。
8.根据权利要求7所述的局部镀金板的制作工艺，其特征在于：在印刷字符的步骤之后包括步骤：外形检测、进行电测试。
9.根据权利要求8所述的局部镀金板的制作工艺，其特征在于：在外形检测、进行电测试的步骤之后包括步骤：进行成品检测。
CN2010105570874A 2010-11-24 2010-11-24 局部镀金板的制作工艺 Expired - Fee Related CN102014575B (zh)