CN102002769A - 超高分子量聚乙烯纤维制备方法 - Google Patents
超高分子量聚乙烯纤维制备方法 Download PDFInfo
- Publication number
- CN102002769A CN102002769A CN 201010533593 CN201010533593A CN102002769A CN 102002769 A CN102002769 A CN 102002769A CN 201010533593 CN201010533593 CN 201010533593 CN 201010533593 A CN201010533593 A CN 201010533593A CN 102002769 A CN102002769 A CN 102002769A
- Authority
- CN
- China
- Prior art keywords
- molecular weight
- ultra
- fiber
- high molecular
- weight polyethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (3)