CN101984005A - Single-component water-based semi-matt varnish for woodware - Google Patents
Single-component water-based semi-matt varnish for woodware Download PDFInfo
- Publication number
- CN101984005A CN101984005A CN 201010532246 CN201010532246A CN101984005A CN 101984005 A CN101984005 A CN 101984005A CN 201010532246 CN201010532246 CN 201010532246 CN 201010532246 A CN201010532246 A CN 201010532246A CN 101984005 A CN101984005 A CN 101984005A
- Authority
- CN
- China
- Prior art keywords
- water
- agent
- component water
- based semi
- woodware
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a single-component water-based semi-matt varnish for woodware, which comprises AC2524, a defoamer, a dispersant, extinction powder, a substrate wetting agent, a flatting agent, a film forming assistant, wax emulsion, a thickening agent, water and bactericidal preservatives. The single-component water-based semi-matt varnish provided by the invention has the advantages of low free formaldehyde content, no benzene and fine water resistance and chemical resistance.
Description
Technical field
The present invention relates to a kind of single-component water-based woodenware half mute clear finish, be a kind of be the single-component water-based wood lacquer of main raw material composition with the nucleocapsid structure ACRYLIC EMULSION.
Background technology
Present prior art, single-component water-based woodenware half mute clear finish is a kind of over-all properties and the good Clear paint of environmental-protecting performance, is widely used in wood decoration, on the market the single-component water-based wood lacquer of some of Xiao Shouing, reason such as water-fast and chemical resistance difference because of it greatly reduces the usability of furniture.
Summary of the invention
The objective of the invention is to solve the existing problems of above-mentioned varnish, a kind of low content of free formaldehyde content that has is provided, do not contain benzene, water tolerance, a kind of single-component water-based woodenware half mute clear finish that chemical-resistant is good.
The present invention is achieved in that a kind of single-component water-based woodenware half mute clear finish, and its weight percent is:
AC2524 78%-82% deaerating agent 0.1%-0.3%
Dispersion agent 0.1%-0.3% flatting silica 0.6%-1.0%
Ground wetting agent 0.1%-0.3% flow agent 0.2%-0.5%
Film coalescence aid 7%-9% wax emulsion 1%-2%
Thickening material 0.3%-0.5% water 8%-10%
Fungicidal preservative 0.1%-0.2%
Its compound method: take by weighing raw material in proportion, add raw material successively, be dispersed to fineness≤25um, viscosity controller (is coated with 4 at 60-70s
#The cup survey) promptly makes finished product.
Embodiment
Below in conjunction with embodiment the present invention is further described.
Embodiment 1
A kind of single-component water-based woodenware half mute clear finish, its weight percent is:
AC2524 82% deaerating agent 0.1%
Dispersion agent 0.1% flatting silica 0.6%
Ground wetting agent 0.1% flow agent 0.2%
Film coalescence aid 7% wax emulsion 1%
Thickening material 0.3% water 8.5%
Fungicidal preservative 0.1%
Its preparation method is as follows:
Take by weighing raw material successively by above-mentioned weight percent:
AC2524 82kg deaerating agent 0.1kg
Dispersion agent 0.1kg flatting silica 0.6kg
Ground wetting agent 0.1kg flow agent 0.2kg
Film coalescence aid 7kg wax emulsion 1kg
Thickening material 0.3kg water 8.5kg
Fungicidal preservative 0.1kg
Pan feeding successively is dispersed to fineness≤25um then, and viscosity controller (is coated with 4 at 60-70s
#Cup is surveyed), make finished product.
In use, the weight ratio according to main lacquer and water is: main lacquer: water=1: 0.05-0.1.
The product that described main lacquer is promptly produced according to this patent method.
AC2524 is an ACRYLIC EMULSION
Produced by German Aberdeen gram, it contains admittedly is 48%.
Film coalescence aid:
Produced by U.S. vitrification chemical company, dipropylene glycol butyl ether, its refractive index are 1.4230, water content＜0.2%.
Embodiment 2;
A kind of single-component water-based woodenware half mute clear finish, its weight percent is:
AC2524 78% deaerating agent 0.3%
Dispersion agent 0.3% flatting silica 1.0%
Ground wetting agent 0.3% flow agent 0.4%
Film coalescence aid 9% wax emulsion 2%
Thickening material 0.5% water 8%
Fungicidal preservative 0.2%
Its preparation method is as follows:
Take by weighing raw material successively by above-mentioned weight percent:
AC2524 78kg deaerating agent 0.3kg
Dispersion agent 0.3kg flatting silica 1.0kg
Ground wetting agent 0.3kg flow agent 0.4kg
Film coalescence aid 9kg wax emulsion 2kg
Thickening material 0.5kg water 8kg
Fungicidal preservative 0.2kg
Pan feeding successively is dispersed to fineness≤25um then, and viscosity controller (is coated with 4 at 60-70s
#Cup is surveyed), make finished product.
The every performance index and the thing of limiting the quantity of of single-component water-based woodenware of the present invention half mute clear face beech are as follows:
Detection method: performance index can be with reference to GB/T23999-2009, and the thing of limiting the quantity of is with reference to GB24410-2009.
Clear finish of the present invention compares with the performance of the clear finish of buying back on the market, sees the following form:
Interventions Requested sample of the present invention
Surface drying 20min 26min
Do solid work 4h 5h
Water tolerance is no abnormal turns white
Resistance to boiling water is no abnormal to turn white
Hardness HB B
The no abnormal foaming of alkali resistance
The no abnormal foaming of alcohol resistance
Free formaldehyde content/(mg/kg) 11 56
Benzene series thing content/(mg/kg) do not have 23
Above-described only is preferential embodiment of the present invention.Should be pointed out that for the person of ordinary skill of the art under the situation that does not break away from the principle of the invention, can also make some improvement and modification, this also is considered as protection scope of the present invention.
Claims (1)
1. a single-component water-based woodenware half mute clear finish, its weight percent is:
AC2524 78%-82% deaerating agent 0.1%-0.3%
Dispersion agent 0.1%-0.3% flatting silica 0.6%-1.0%
Ground wetting agent 0.1%-0.3% flow agent 0.2%-0.5%
Film coalescence aid 7%-9% wax emulsion 1%-2%
Thickening material 0.3%-0.5% water 8%-10%
Fungicidal preservative 0.1%-0.2%
Its compound method: take by weighing raw material in proportion, add raw material successively, be dispersed to fineness≤25um, viscosity controller (is coated with 4 at 60-70s
#The cup survey) promptly makes finished product.