CN105385266A - Environment-friendly indoor multifunctional diatomite wall paint - Google Patents
Environment-friendly indoor multifunctional diatomite wall paint Download PDFInfo
- Publication number
- CN105385266A CN105385266A CN201510893444.7A CN201510893444A CN105385266A CN 105385266 A CN105385266 A CN 105385266A CN 201510893444 A CN201510893444 A CN 201510893444A CN 105385266 A CN105385266 A CN 105385266A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- wall paint
- diatomite
- environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environment-friendly indoor multifunctional diatomite wall paint. The wall paint is composed of the following components in parts by weight: 200 to 400 parts of high elasticity acrylic emulsion, 30 to 70 parts of water, 50 to 100 parts of diatomite, 5 to 25 parts of bamboo charcoal fiber powder, 1 to 10 parts of talcum powder, 10 to 30 parts of wollastonite, 1 to 10 parts of thickening agent, 0.1 to 10 parts of levelling agent, 0.1 to 10 parts of organic silicon hydrophobic agent, 0.1 to 10 parts of antifoaming agent, 0.1 to 10 parts of hydroxyethyl cellulose, 0.1 to 10 parts of emulsified wax, 0.1 to 10 parts of wetting agent, 0.1 to 10 parts of dispersant, 0.1 to 10 parts of alumina, and 0.1 to 10 parts of sodium nitrate. The wall paint has the advantages that the wall paint can absorb substances that are harmful to human body such as formaldehyde, benzene, and the like; the wall paint can adjust the concavity and convexity of wall, and can create different patterns on the wall; and the wall paint has the characteristics of scrub resistance, environment-friendliness, and high bonding strength.
Description
Technical field
The present invention relates to a kind of coating, be specifically related to a kind of environment-friendly type Multi-functional indoor diatom wall paint.
Background technology
At present, market utilizes mostly containing poisonous and hazardous material paint vehicles such as methyl alcohol as the material beautifying furniture, house etc., thus injury greatly can be produced to human body.
The existing coating for smearing indoor and outdoor wall, wear resistance is poor, not environmentally, constrains the application of coating widely.
Summary of the invention
The object of this invention is to provide a kind of environment-friendly type Multi-functional indoor diatom wall paint.
The technical solution used in the present invention is a kind of environment-friendly type Multi-functional indoor diatom wall paint, described wall paint is made up of the component of following parts by weight: tenacity acrylic's emulsion 200 ~ 400 parts, 30 ~ 70 parts, water, 50 ~ 100 parts, diatomite, 5 ~ 25 parts, bamboo-carbon fibre powder, talcum powder 1 ~ 10 part, wollastonite 10 ~ 30 parts, thickening material 1 ~ 10 part, flow agent 0.1 ~ 10 part, silicone based hydrophobizing agent 0.1 ~ 10 part, defoamer 0.1 ~ 10 part, Natvosol 0.1 ~ 10 part, emulsifying wax 0.1 ~ 10 part, wetting agent 0.1 ~ 10 part, dispersion agent 0.1 ~ 10 part, 0.1 ~ 10 part, aluminum oxide and SODIUMNITRATE 0.1 ~ 10 part.
As preferably, described wall paint is made up of the component of following parts by weight: tenacity acrylic's emulsion 250 ~ 350 parts, 40 ~ 60 parts, water, 60 ~ 80 parts, diatomite, 10 ~ 20 parts, bamboo-carbon fibre powder, talcum powder 3 ~ 7 parts, wollastonite 15 ~ 25 parts, thickening material 3 ~ 7 parts, flow agent 0.5 ~ 5 part, silicone based hydrophobizing agent 0.5 ~ 5 part, defoamer 0.5 ~ 5 part, Natvosol 0.5 ~ 5 part, emulsifying wax 0.5 ~ 5 part, wetting agent 0.5 ~ 5 part, dispersion agent 0.5 ~ 5 part, 0.5 ~ 5 part, aluminum oxide and SODIUMNITRATE 0.5 ~ 5 part.
As preferably, described wall paint is made up of the component of following parts by weight: tenacity acrylic's emulsion 300 parts, 50 parts, water, 70 parts, diatomite, 15 parts, bamboo-carbon fibre powder, talcum powder 5 parts, wollastonite 20 parts, thickening material 4 parts, flow agent 2 parts, silicone based hydrophobizing agent 1.5 parts, defoamer 1.5 parts, Natvosol 1.5 parts, emulsifying wax 1 part, wetting agent 1 part, dispersion agent 1 part, 1 part, aluminum oxide and SODIUMNITRATE 1 part.
As preferably, described water is deionized water; Described defoamer is selected from the one in polydimethylsiloxane or polyether-modified polydimethylsiloxane, or their arbitrary proportion mixture; Described wetting agent is selected from acetylenic diols or Siloxane-Oxyalkylene Copolymers class, or their arbitrary proportion mixture.
A kind of method preparing described water-miscible paint, comprise the following steps: by weight ratio, dispersion agent, wetting agent, defoamer is first soluble in water, then add Natvosol mixing, add diatomite, bamboo-carbon fibre powder, talcum powder, wollastonite co-ground subsequently; Add tenacity acrylic's emulsion, thickening material, flow agent, silicone based hydrophobizing agent, emulsifying wax, aluminum oxide and SODIUMNITRATE again, homogeneous, filter, obtain finished product.
In the present invention, each component is all by commercially available acquisition.
Beneficial effect of the present invention is: scrubbing resistance, environmental protection, and bonding strength is high.
Embodiment
For making those skilled in the art understand production technique of the present invention and technique effect in detail, introduce application of the present invention and technique effect further with concrete production instance below.
Embodiment 1
By weight ratio, 10 parts of dispersion agents, 10 parts of acetylenic diols, 10 parts of polydimethylsiloxanes are first dissolved in 70 parts of deionized waters, add 10 parts of Natvosol mixings again, add 100 parts of diatomite, 25 parts of bamboo-carbon fibre powder, 10 parts of talcum powder, 30 parts of wollastonite co-ground subsequently; Add 400 parts of tenacity acrylic's emulsions, 10 parts of thickening materials, 10 parts of flow agents, 10 parts of silicone based hydrophobizing agents, 10 parts of emulsifying waxs, 10 parts of aluminum oxide and 10 parts of SODIUMNITRATE again, homogeneous, filter, obtain finished product.
Embodiment 2
By weight ratio, 0.1 part of dispersion agent, 0.1 part of acetylenic diols, 0.1 part of polydimethylsiloxane are first dissolved in 30 parts of deionized waters, add 0.1 part of Natvosol mixing again, add 50 parts of diatomite, 5 parts of bamboo-carbon fibre powder, 1 part of talcum powder, 10 parts of wollastonite co-ground subsequently; Add 200 parts of tenacity acrylic's emulsions, 1 part of thickening material, 0.1 part of flow agent, 0.1 part of silicone based hydrophobizing agent, 0.1 part of emulsifying wax, 0.1 part of aluminum oxide and 0.1 part of SODIUMNITRATE again, homogeneous, filter, obtain finished product.
Embodiment 3
By weight ratio, 0.5 part of dispersion agent, 0.5 part of Siloxane-Oxyalkylene Copolymers class, 5 parts of polyether-modified polydimethylsiloxanes are first dissolved in 40 parts of deionized waters, add 5 parts of Natvosol mixings again, add 80 parts of diatomite, 10 parts of bamboo-carbon fibre powder, 3 parts of talcum powder, 25 parts of wollastonite co-ground subsequently; Add 250 parts of tenacity acrylic's emulsions, 5 parts of thickening materials, 5 parts of flow agents, 5 parts of silicone based hydrophobizing agents, 5 parts of emulsifying waxs, 5 parts of aluminum oxide and 0.5 part of SODIUMNITRATE again, homogeneous, filter, obtain finished product.
Embodiment 4
By weight ratio, 5 parts of dispersion agents, 5 parts of Siloxane-Oxyalkylene Copolymers classes, 0.5 part of polyether-modified polydimethylsiloxane are first dissolved in 60 parts of deionized waters, add 0.5 part of Natvosol mixing again, add 60 parts of diatomite, 20 parts of bamboo-carbon fibre powder, 7 parts of talcum powder, 15 parts of wollastonite co-ground subsequently; Add 350 parts of tenacity acrylic's emulsions, 0.5 part of thickening material, 0.5 part of flow agent, 0.5 part of silicone based hydrophobizing agent, 0.5 part of emulsifying wax, 0.5 part of aluminum oxide and 5 parts of SODIUMNITRATE again, homogeneous, filter, obtain finished product.
Embodiment 5
By weight ratio, 1 part of dispersion agent, 0.5 part of acetylenic diols, 0.5 part of Siloxane-Oxyalkylene Copolymers class, 1 part of dimethyl siloxane, 0.5 part of polyether-modified polydimethylsiloxane are first dissolved in 50 parts of deionized waters, add 0.1 ~ 10 part of Natvosol mixing again, add 70 parts of diatomite, 15 parts of bamboo-carbon fibre powder, 5 parts of talcum powder, 20 parts of wollastonite co-ground subsequently; Add 300 parts of tenacity acrylic's emulsions, 4 parts of thickening materials, 2 parts of flow agents, 1.5 parts of silicone based hydrophobizing agents, 1 part of emulsifying wax, 1 part of aluminum oxide and 1 part of SODIUMNITRATE again, homogeneous, filter, obtain finished product.
Comparative example 1
Reduce aluminum oxide, all the other carry out according to the mode of embodiment 5 completely.
Comparative example 2
Reduce SODIUMNITRATE, all the other carry out according to the mode of embodiment 5 completely.
Comparative example 3
Reduce talcum powder, all the other carry out according to the mode of embodiment 5 completely.
Comparative example 4
Reduce silicone based hydrophobizing agent, all the other carry out according to the mode of embodiment 5 completely.
For verifying technique effect of the present invention, the performance of the test method specified according to GB/T1729, GB1723, GB1732, GB1731, GB9286 to above-described embodiment and comparative example products obtained therefrom detects.
As seen from the above table, change component of the present invention, can directly cause the performance of product to have larger difference.The present invention is by the interaction of each component, and each index performance is remarkable, achieves significant progress.
Because component of the present invention is not containing benzene,toluene,xylene, formaldehyde, free TDI toxic heavy metal, nontoxic non-stimulated smell, harmless, can be applicable on indoor and outdoor or other article, environmental protection, safe and reliable.Also there is scrubbing resistance, the feature that bonding strength is high.
Owing to have employed the composition such as diatomite, bamboo-carbon fibre powder, go back the material that the human bodies such as Absorbable rod indoor formaldehyde, benzene are harmful, the style pattern of the concavity and convexity of metope, intention and moulding and collocation, the various style of engraving can also be adjusted.
Embodiment of the present invention 1-5 wall paint purifying formaldehyde rate detects, purifying formaldehyde efficiency >=81%; Purifying formaldehyde effect persistence >=75%, equal conformance with standard requirement.
Finally it should be noted that, above embodiment is the unrestricted technical scheme of the present invention in order to explanation only, although with reference to above-described embodiment to invention has been detailed description, those skilled in the art are to be understood that, still can modify to the present invention or equivalent replacement, and not departing from any modification or partial replacement of the spirit and scope of the present invention, it all should be encompassed in right of the present invention.
Claims (5)
1. an environment-friendly type Multi-functional indoor diatom wall paint, it is characterized in that, described wall paint is made up of the component of following parts by weight: tenacity acrylic's emulsion 200 ~ 400 parts, 30 ~ 70 parts, water, 50 ~ 100 parts, diatomite, 5 ~ 25 parts, bamboo-carbon fibre powder, talcum powder 1 ~ 10 part, wollastonite 10 ~ 30 parts, thickening material 1 ~ 10 part, flow agent 0.1 ~ 10 part, silicone based hydrophobizing agent 0.1 ~ 10 part, defoamer 0.1 ~ 10 part, Natvosol 0.1 ~ 10 part, emulsifying wax 0.1 ~ 10 part, wetting agent 0.1 ~ 10 part, dispersion agent 0.1 ~ 10 part, 0.1 ~ 10 part, aluminum oxide and SODIUMNITRATE 0.1 ~ 10 part.
2. a kind of environment-friendly type Multi-functional indoor diatom wall paint according to claim 1, it is characterized in that, described wall paint is made up of the component of following parts by weight: tenacity acrylic's emulsion 250 ~ 350 parts, 40 ~ 60 parts, water, 60 ~ 80 parts, diatomite, 10 ~ 20 parts, bamboo-carbon fibre powder, talcum powder 3 ~ 7 parts, wollastonite 15 ~ 25 parts, thickening material 3 ~ 7 parts, flow agent 0.5 ~ 5 part, silicone based hydrophobizing agent 0.5 ~ 5 part, defoamer 0.5 ~ 5 part, Natvosol 0.5 ~ 5 part, emulsifying wax 0.5 ~ 5 part, wetting agent 0.5 ~ 5 part, dispersion agent 0.5 ~ 5 part, 0.5 ~ 5 part, aluminum oxide and SODIUMNITRATE 0.5 ~ 5 part.
3. a kind of environment-friendly type Multi-functional indoor diatom wall paint according to claim 2, it is characterized in that, described wall paint is made up of the component of following parts by weight: tenacity acrylic's emulsion 300 parts, 50 parts, water, 70 parts, diatomite, 15 parts, bamboo-carbon fibre powder, talcum powder 5 parts, wollastonite 20 parts, thickening material 4 parts, flow agent 2 parts, silicone based hydrophobizing agent 1.5 parts, defoamer 1.5 parts, Natvosol 1.5 parts, emulsifying wax 1 part, wetting agent 1 part, dispersion agent 1 part, 1 part, aluminum oxide and SODIUMNITRATE 1 part.
4. the self-cleaning aqueous paint of a kind of environment protection type high-strength for indoor and outdoor according to claim 1, is characterized in that, described water is deionized water; Described defoamer is selected from the one in polydimethylsiloxane or polyether-modified polydimethylsiloxane, or their arbitrary proportion mixture; Described wetting agent is selected from acetylenic diols or Siloxane-Oxyalkylene Copolymers class, or their arbitrary proportion mixture.
5. prepare the method for water-miscible paint described in any one of claim 1-4 for one kind, it is characterized in that, comprise the following steps: by weight ratio, dispersion agent, wetting agent, defoamer is first soluble in water, add Natvosol mixing again, add diatomite, bamboo-carbon fibre powder, talcum powder, wollastonite co-ground subsequently; Add tenacity acrylic's emulsion, thickening material, flow agent, silicone based hydrophobizing agent, emulsifying wax, aluminum oxide and SODIUMNITRATE again, homogeneous, filter, obtain finished product.