CN101948599A - 一种热塑性弹性体的制备方法 - Google Patents
一种热塑性弹性体的制备方法 Download PDFInfo
- Publication number
- CN101948599A CN101948599A CN 201010503090 CN201010503090A CN101948599A CN 101948599 A CN101948599 A CN 101948599A CN 201010503090 CN201010503090 CN 201010503090 CN 201010503090 A CN201010503090 A CN 201010503090A CN 101948599 A CN101948599 A CN 101948599A
- Authority
- CN
- China
- Prior art keywords
- thermoplastic elastomer
- polypropylene
- preparation
- vinyl acetate
- ethylene vinyl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | |
乙烯醋酸乙烯酯橡胶 | 70 | 70 | 70 | 70 | 70 |
均聚聚丙烯 | 30 | 15 | 15 | - | - |
共聚聚丙烯 | - | - | - | 30 | 15 |
聚丙烯接枝马来酸酐 | - | 15 | 15 | - | 15 |
过氧化二异丙苯 | 1.5 | 1.5 | 1.5 | 1.5 | 1.5 |
丙烯酸锌 | - | - | 8 | - | - |
实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | |
拉伸强度/MPa | 4.6 | 8.4 | 13.3 | 10.8 | 13.0 |
断裂伸长率/% | 63 | 302 | 403 | 359 | 376 |
Claims (7)