CN101879793A - 超薄石材酚醛复合成品保温装饰板 - Google Patents
超薄石材酚醛复合成品保温装饰板 Download PDFInfo
- Publication number
- CN101879793A CN101879793A CN 201010209984 CN201010209984A CN101879793A CN 101879793 A CN101879793 A CN 101879793A CN 201010209984 CN201010209984 CN 201010209984 CN 201010209984 A CN201010209984 A CN 201010209984A CN 101879793 A CN101879793 A CN 101879793A
- Authority
- CN
- China
- Prior art keywords
- phenolic aldehyde
- dimensional sandwich
- finished product
- thermal insulation
- decorating plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及超薄石材酚醛复合成品保温装饰板,包括酚醛泡沫填充的三维夹芯层,胶水粘结层和超薄石材层,所述的超薄石材层通过胶水粘结层与酚醛泡沫填充的三维夹芯层复合,所述的酚醛泡沫填充的三维夹芯层包括上织物面,中间芯材结构和下织物面,所述中间芯材结构以三维夹芯织物材料为支撑体,酚醛泡沫为填充基体,所述的中间芯材连接上织物面和下织物面,所述的下织物面为几何面结构。本发明具有重量轻,强度高、抗污染能力强,更易控制色差、安装方便及安全可靠、保温效果佳、防火性能优异、良好的隔音防潮功能,性价比高。
Description
技术领域
本发明涉及一种板材结构,尤其是一种超薄石材酚醛复合成品保温装饰板。
背景技术
目前市场上保温装饰板,其保温层以矿棉、泡沫玻璃、聚苯乙烯泡沫、聚氨酯泡沫等保温材料为主。这其中,无机材料的防火性能好,但是导热系数大,节能效果不理想。有机材料的保温隔热效果相对有很大的优势,但是这种保温材料的防火性能很差,易燃烧,并且产生大量的有毒烟雾。
普通保温装饰板装饰层主要以石材特别是大理石薄板为主,但由于市场上能生产超薄石材的企业不多,而且现有设备及工艺技术都处在一个探索、摸索的阶段,还需要一个技术改进与工艺提高的过程。超薄石材因受到机械设备、辅助材料、石材性质(易碎易断裂)的影响,目前只能生产较薄(8mm-12mm厚)小规格板材,而生产大批量超薄板材还有一定的局限性。
传统的保温装饰板虽具有标准化、组合多样化、装饰性好、保温等特点,但由于其重量不够轻、防火性能差、导热系数大、节能效果不理想等缺点,影响了其应用范围,特别是在高层建筑墙体外保温领域的应用。
发明内容
为了克服以上缺陷,本发明要解决的技术问题是:提出一种具有重量轻、防火性能好、强度高、保温效果佳、阻燃性好、节能、维护方便、应用范围广的超薄石材酚醛复合成品保温装饰板。
本发明所采用的技术方案为:一种超薄石材酚醛复合成品保温装饰板,包括酚醛泡沫填充的三维夹芯层,胶水粘结层和超薄石材层,所述的超薄石材层通过胶水粘结层与酚醛泡沫填充的三维夹芯层复合,所述的酚醛泡沫填充的三维夹芯层包括上织物面,中间芯材结构和下织物面,所述中间芯材结构以三维夹芯织物材料为支撑体,酚醛泡沫为填充基体,所述的中间芯材连接上织物面和下织物面,所述的下织物面为几何面结构。
根据本发明的另外一个实施例,超薄石材酚醛复合成品保温装饰板进一步包括所述的胶水粘结层的厚度为0.1~1mm。
根据本发明的另外一个实施例,超薄石材酚醛复合成品保温装饰板进一步包括所述的超薄石材为大理石,花岗石中的一种。
根据本发明的另外一个实施例,超薄石材酚醛复合成品保温装饰板进一步包括所述的超薄石材的厚度为2~10mm。
根据本发明的另外一个实施例,超薄石材酚醛复合成品保温装饰板进一步包括所述的三维夹芯织物材料为玻纤维三维夹芯织物、碳纤维三维夹芯织物或芳纶纤维三维夹芯织物中的一种。
根据本发明的另外一个实施例,酚醛填充的三维夹芯与超薄石材复合的保温装饰一体化板进一步包括所述酚醛泡沫填充的三维夹芯层的厚度为5~50mm。
根据本发明的另外一个实施例,一种酚醛填充的三维夹芯与超薄石材复合的保温装饰一体化板进一步包括所述的下织物面得几何面结构为平面或凹凸面结构。
根据本发明的另外一个实施例,一种超薄石材酚醛复合成品保温装饰板进一步包括所述的凹凸面结构的凸面高度为0.5-20mm,凹面宽度为10-600mm。
与现有技术相比,本发明的有益效果是:
1、由于本发明提出的一种超薄石材酚醛复合成品保温装饰板是由酚醛三维夹芯板通过胶水粘结层与超薄石材复合,三维酚醛夹芯板具有高阻燃、低烟、低毒、重量轻、强度高、刚性好、吸水率低等独特优势,才能支撑起石材的切割、打磨、水冷却等工序,而一般普通保温材料的特性是无法达到这个要求,使石材的厚度一般在5mm以下,最薄可以达到2mm厚,本发明将酚醛三维夹芯板与超薄石材通过胶粘剂复合在一起,将普通的石材经过特殊的技术工艺制成超薄型石材。
2、本发明提出的所述的下织物面为平面或凹凸面,采用凹凸面时可使粘结面增大,抗压强度增大,横面剪切力增大。
3、传统的保温装饰成品板用特殊技术将瓷砖、保温材料、硅酸钙材料等与石材复合而成,其结构一般有4层以上材料组合构成,本发明克服了传统石材与保温材料结合的复杂结构形式,革命性的创造出只有两层结构的保温装饰一体化成品板。
4、本发明提出超薄石材酚醛复合成品保温装饰板具有重量轻,强度高、抗污染能力强,更易控制色差、安装方便及安全可靠、保温效果佳、防火性能优异、良好的隔音防潮功能,性价比高。
附图说明
图1是本发明的优选实施例的结构示意图;
图2是本发明的另一优选实施例的结构示意图。
具体实施方式
现在结合附图和优选实施例对本发明作进一步详细的说明。这些附图均为简化的示意图,仅以示意方式说明本发明的基本结构,因此其仅显示与本发明有关的构成。
实施例1
如附图1所示,一种超薄石材酚醛复合成品保温装饰板,包括酚醛泡沫填充的三维夹芯层6,胶水粘结层2和超薄石材层1,胶水粘结层的厚度为0.1~1mm,超薄石材层1通过胶水粘结层2与酚醛泡沫填充的三维夹芯层6复合,所述的酚醛泡沫填充的三维夹芯层6包括上织物面3,中间芯材结构4和下织物面5,中间芯材结构4以三维夹芯织物材料为支撑体,酚醛泡沫为填充基体,三维夹芯层6材料为玻纤维三维夹芯织物、碳纤维三维夹芯织物或芳纶纤维三维夹芯织物中的一种。酚醛泡沫填充的三维夹芯层6的厚度为5~50mm。中间芯材4连接上织物面3和下织物面5,所述的上织物面3为平面结构,所述的下织物面5为平面结构。超薄石材层1采用的材料为大理石或花岗石中的一种,厚度为2~10mm。
实施例2
如附图2所示,一种酚醛填充的三维夹芯与超薄石材复合的保温装饰一体化板,包括酚醛泡沫填充的三维夹芯层6,胶水粘结层2和超薄石材层1,胶水粘结层的厚度为0.1~1mm,超薄石材层1通过胶水粘结层2与酚醛泡沫填充的三维夹芯层6复合,所述的酚醛泡沫填充的三维夹芯层6包括上织物面3,中间芯材结构4和下织物面7,中间芯材结构4以三维夹芯织物材料为支撑体,酚醛泡沫为填充基体,三维夹芯层6材料为玻纤维三维夹芯织物、碳纤维三维夹芯织物或芳纶纤维三维夹芯织物中的一种。酚醛泡沫填充的三维夹芯层的厚度为5~50mm。中间芯材4连接上织物面3和下织物面5,所述的上织物面3为平面结构,所述的下织物面5为凹凸面结构,凹凸面结构的凸面高度为0.5-20mm,凹面宽度为10-600mm。采用凹凸面时可使粘结面增大,抗压强度增大,横面剪切力增大。超薄石材层1采用的材料为大理石或花岗石中的一种,厚度为2~10mm。
以上述依据本发明的理想实施例为启示,通过上述的说明内容,相关工作人员完全可以在不偏离本项发明技术思想的范围内,进行多样的变更以及修改。本项发明的技术性范围并不局限于说明书上的内容,必须要根据权利要求范围来确定其技术性范围。
Claims (8)
1.一种超薄石材酚醛复合成品保温装饰板,其特征在于包括酚醛泡沫填充的三维夹芯层,胶水粘结层和超薄石材层,所述的超薄石材层通过胶水粘结层与酚醛泡沫填充的三维夹芯层复合,所述的酚醛泡沫填充的三维夹芯层包括上织物面,中间芯材结构和下织物面,所述中间芯材结构以三维夹芯织物材料为支撑体,酚醛泡沫为填充基体,所述的中间芯材连接上织物面和下织物面,所述的下织物面为几何面结构。
2.根据权利要求1所述的超薄石材酚醛复合成品保温装饰板,其特征在于所述的胶水粘结层的厚度为0.1~1mm。
3.根据权利要求1所述的超薄石材酚醛复合成品保温装饰板,其特征在于所述的超薄石材为大理石,花岗石中的一种。
4.根据权利要求2所述的超薄石材酚醛复合成品保温装饰板,其特征在于所述的超薄石材的厚度为2~10mm。
5.根据权利要求1所述的超薄石材酚醛复合成品保温装饰板,其特征在于所述的三维夹芯织物材料为玻纤维三维夹芯织物、碳纤维三维夹芯织物或芳纶纤维三维夹芯织物中的一种。
6.根据权利要求1所述的超薄石材酚醛复合成品保温装饰板,其特征在于所述酚醛泡沫填充的三维夹芯层的厚度为5~50mm。
7.根据权利要求1所述的超薄石材酚醛复合成品保温装饰板,其特征在于所述的下织物面得几何面结构为平面或凹凸面结构。
8.根据权利要求6所述的超薄石材酚醛复合成品保温装饰板,其特征在于所述的凹凸面结构的凸面高度为0.5-20mm,凹面宽度为10-600mm。