CN101870189A - Fabrication process of multilayer PET (Polyethylene Terephthalate) protective film - Google Patents
Fabrication process of multilayer PET (Polyethylene Terephthalate) protective film Download PDFInfo
- Publication number
- CN101870189A CN101870189A CN201010201239A CN201010201239A CN101870189A CN 101870189 A CN101870189 A CN 101870189A CN 201010201239 A CN201010201239 A CN 201010201239A CN 201010201239 A CN201010201239 A CN 201010201239A CN 101870189 A CN101870189 A CN 101870189A
- Authority
- CN
- China
- Prior art keywords
- pet film
- pet
- glue
- mother roll
- multilayer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a fabrication process of a multilayer PET (Polyethylene Terephthalate) protective film, comprising the following steps of: firstly, carrying out corona treatment on one surface of a prepared PET film; secondly, coating gluewater on the corona surface of the PET film by using a coating machine, and then feeding the PET film coated with the gluewater into an oven; thirdly, directly winding the PET film taken out of the oven into a mother roll; fourthly, after encoding the wound mother roll, feeding the mother roll into a curing chamber for curing; and fifthly, feeding the cured mother roll into a multi-shaft laminating machine according to a first-in first-out principle for multi-layer lamination, wherein during lamination, one PET film is firstly tiled and laminated on the mother roll without air bubbles, the other PET film is laminated on the PET film without air bubbles, and then repeated lamination is carried out. The fabrication process of the multilayer PET film changes the traditional process, reduces the fabrication hour consumption when repeating the process, also reduces the waste of waste materials, lowers cost and improves product competitiveness.
Description
Technical field
The present invention relates to the manufacture craft of PET diaphragm, special design has the manufacture craft of the multilayer PET diaphragm of multilayer PET film.
Background technology
Former individual layer applying die-cutting process PET diaphragm covers release liners, and the scope of application is extensive in the market, is used in the protection working of plastics more and is fitted in notebook computer upper cover and multiple electronic goods.But single-layer PET diaphragm (as shown in Figure 1) has just slatterned as waste material with the release liners of covering that the PET film is fitted in use, and so producing single-layer PET diaphragm and waste material has consuming timely, so lacks a kind of manufacture craft of production multilayer PET diaphragm.
Summary of the invention
Be to solve the problems referred to above that prior art exists, the present invention proposes a kind of manufacture craft of multilayer PET diaphragm, and this process exploitation purpose is to reduce consume in man-hour that iterative process makes and the waste that reduces waste material, and reaches and reduce cost, and promotes product competitiveness.
The present invention can be solved by the following technical programs:
The manufacture craft of multilayer PET diaphragm of the present invention, this technology may further comprise the steps:
The first step is a surface corona of ready PET film;
Second step, on the corona surface of described PET film by a coating machine cementing, the speed of service of this coating machine be 10-15 rice/minute, the described PET film that coats glue is sent into baking box;
The 3rd step, compound the PET film that comes out from baking box with yellow two single silicon release liners, and be wound into parent roll;
In the 4th step, behind the described parent roll coding after the rolling, send into the curing chamber slaking;
The 5th step, described parent roll after the slaking is sent into the multiaxis make-up machine by first in first out, carries out lamination coating, at first the tiling of PET film be there is no bubble during applying and fits in described parent roll, again with another PET film bubble-free laminating on described PET film, so repeat to fit.
The proportioning of glue of the present invention is: 100% acrylic glue: 1.5% bridging agent: 50% ethyl acetate.
Glue-spread is 30g/m2 in second step of the present invention.
The two single silicon release liners of described Huang have 50 gram off-type forces.
Owing to adopt above technical scheme, the manufacture craft of multilayer PET diaphragm of the present invention by repeating still coating technique, generates the multilayer PET diaphragm and replaces original single-layer PET diaphragm, not only saves resource but also save man-hour.
Description of drawings
Fig. 1 is original single-layer PET diaphragm
Fig. 2 is the multilayer PET diaphragm that the present invention produces
Among the figure 1, release liners; 2, glue; 3, the PET diaphragm.
The specific embodiment
Below in conjunction with the specific embodiment, further set forth the present invention:
The manufacture craft of multilayer PET diaphragm of the present invention, this technology may further comprise the steps:
The first step, a surface corona of ready PET film, this PET film is about 0.1 millimeters thick;
Second step, on the corona surface of described PET film by a coating machine cementing, the speed of service of this coating machine be 10-15 rice/minute, the described PET film that coats glue is sent into baking box;
The 3rd step, compound the PET film that comes out from baking box with yellow two single silicon release liners, and be wound into parent roll;
In the 4th step, behind the described parent roll coding after the rolling, send into the curing chamber slaking;
The 5th step, described parent roll after the slaking is sent into the multiaxis make-up machine by first in first out, carries out lamination coating, at first the tiling of PET film be there is no bubble during applying and fits in described parent roll, again with another PET film bubble-free laminating on described PET film, so repeat to fit.
The proportioning of the glue in above-mentioned second step of the present invention is: 100% acrylic glue: 1.5% bridging agent: 50% ethyl acetate.Joining glue is in proper order: put into A glue, 40% ethyl acetate, 1.5%CA, remaining 10% ethyl acetate successively, stirred for several minute obtains required glue.
Glue-spread is 30g/m2 in above-mentioned second step.
Yellow two single silicon release liners in above-mentioned the 3rd step are that 140g has 50 gram off-type forces.
The multilayer PET diaphragm (as shown in Figure 2) that generates through above-mentioned steps also needs the process die cutting technique multilayer PET diaphragm that generates to be cut into the PET diaphragm of needs size.Substitute original single-layer PET diaphragm by this manufacture craft production multilayer PET diaphragm, both having saved man-hour has the saving resource.
But the above-mentioned specific embodiment is exemplary, is to be the restriction that this patent is comprised scope in order better to make those skilled in the art can understand this patent, can not to be interpreted as; So long as according to spirit that this patent discloses done anyly be equal to change or modify, all fall into the scope that this patent comprises.
Claims (3)
1. the manufacture craft of multilayer PET diaphragm is characterized in that, this technology may further comprise the steps:
The first step is a surface corona of ready PET film;
In second step, on the corona surface of described PET film,, the described PET film that coats glue is sent into baking box by a coating machine cementing;
In the 3rd step, the PET film that comes out from baking box directly is wound into parent roll;
In the 4th step, behind the described parent roll coding after the rolling, send into the curing chamber slaking;
The 5th step, described parent roll after the slaking is sent into the multiaxis make-up machine by first in first out, carries out lamination coating, at first the tiling of PET film be there is no bubble during applying and fits in described parent roll, again with another PET film bubble-free laminating on described PET film, so repeat to fit.
2. manufacture craft as claimed in claim 1 is characterized in that, the proportioning of described glue is: 100% acrylic glue: 1.5% bridging agent: 50% ethyl acetate.
3. manufacture craft as claimed in claim 1 or 2 is characterized in that, glue-spread is 30g/m in described second step
2