CN101826418A - 重叠软连接薄片与接触块的焊接技术 - Google Patents

重叠软连接薄片与接触块的焊接技术 Download PDF

Info

Publication number
CN101826418A
CN101826418A CN200910102458A CN200910102458A CN101826418A CN 101826418 A CN101826418 A CN 101826418A CN 200910102458 A CN200910102458 A CN 200910102458A CN 200910102458 A CN200910102458 A CN 200910102458A CN 101826418 A CN101826418 A CN 101826418A
Authority
CN
China
Prior art keywords
contact block
flexible coupling
thin slice
welding
overlapping
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN200910102458A
Other languages
English (en)
Other versions
CN101826418B (zh
Inventor
田景彩
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guizhou Tianyi Electrical Appliances Co Ltd
Original Assignee
Guizhou Tianyi Electrical Appliances Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guizhou Tianyi Electrical Appliances Co Ltd filed Critical Guizhou Tianyi Electrical Appliances Co Ltd
Priority to CN2009101024587A priority Critical patent/CN101826418B/zh
Publication of CN101826418A publication Critical patent/CN101826418A/zh
Application granted granted Critical
Publication of CN101826418B publication Critical patent/CN101826418B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

重叠软连接薄片与接触块的焊接技术，该技术包括下述两个步骤：第一步，选8-30块干净完整的软连接薄片，先用钨铜制成两块电极头，然后在软连接薄片两端用90KVA以上的逆变直流电源点焊机进行点焊，一次性点焊成型即为重叠软连接片；第二步，选1块干净完整的接触块，先用钨铜制成两块电极头，然后在接触块与成型重叠软连接薄片两端用90KVA以上的逆变直流电源点焊机采用点钎焊法焊接即成，在此步骤中，焊料选用银铜；在上述步骤中，焊接熔和处为长方形。本发明能降低零件之间的接触压降，减少连接处的发热量，从而提高产品的使用性能和使用寿命，推动产品的高端发展。

Description

重叠软连接薄片与接触块的焊接技术
技术领域
本发明涉及一种焊接技术，尤其涉及一种重叠软连接薄片与接触块的焊接技术。
技术背景
目前，在密封的大功率接触器生产中，常常需要进行重叠软连接薄片与接触块的连接，从而达到引流或分流的作用。然而重叠软连接薄片，其两端与接触块或与别的零件的连接处的结构是非常重要的，能直接影响到产品的使用性能和使用寿命。
在以往的产品生产中，其软连接薄片两端的成型，基本上都是采用铆接方式，然后再与接触块的连接仍是采用铆接方式。从而导致产品的使用性能达不到要求，或使用寿命的缩短。也正是这种原因而竭力制约了大量接触器的高端发展。
发明内容
本发明的所要解决的技术问题是降低零件之间的接触压降，减少连接处的发热量，从而提高产品的使用性能和使用寿命，推动产品的高端发展。
为解决上述技术问题本发明所采用的技术方案是：
重叠软连接薄片与接触块的焊接技术，该技术包括下述两个步骤：
第一步，选8-30块干净完整的软连接薄片，先用钨铜制成两块电极头，然后在软连接薄片两端用90KVA以上的逆变直流电源点焊机进行点焊，一次性点焊成型即为重叠软连接片。
第二步，选1块干净完整的接触块，先用钨铜制成两块电极头，然后在接触块与成型重叠软连接薄片两端用90KVA以上的逆变直流电源点焊机采用点钎焊法焊接即成，在此步骤中，焊料选用HIAgCu80-5。
在上述步骤中，焊接熔和处为长方形。
所述软连接薄片为铜或铜合金。
所述接触块为黄铜。
所述焊料为片状银铜。
采用上述技术方案的有益效果是：
降低零件之间的接触压降，减少连接处的发热量，从而提高产品的使用性能和使用寿命，推动产品的高端发展。
具体实施方式
现对重叠软连接薄片与接触块的焊接技术，作进一步详细说明：
实施例1：
第一步，选15块干净完整的软连接薄片，先用钨铜制成两块电极头，然后在软连接薄片两端用100KVA以上的逆变直流电源点焊机进行点焊，一次性点焊成型即为重叠软连接片。
第二步，选1块干净完整的接触块，先用钨铜制成两块电极头，然后在接触块与成型重叠软连接薄片两端用100KVA以上的逆变直流电源点焊机采用点钎焊法焊接即成。在此步骤中焊料选用HIAgCu80-5。
在上述步骤中，焊接熔和处为长方形。
实施例2：
第一步，选20块干净完整的软连接薄片，先用钨铜制成两块电极头，然后在软连接薄片两端用110KVA以上的逆变直流电源点焊机进行点焊，一次性点焊成型即为重叠软连接片。
第二步，选1块干净完整的接触块，先用钨铜制成两块电极头，然后在接触块与成型重叠软连接薄片两端用110KVA以上的逆变直流电源点焊机采用点钎焊法焊接即成。在此步骤中焊料选用HIAgCu80-5。
在上述步骤中，焊接熔和处为长方形。
所述软连接薄片材质为铜或铜合金。
所述接触块材质为黄铜。
所述焊料为片状银铜。

Claims (5)

1.重叠软连接薄片与接触块的焊接技术，其特征在于：该技术包括下述两个步骤：
第一步，选8-30块干净完整的软连接薄片，先用钨铜制成两块电极头，然后在软连接薄片两端用90KVA以上的逆变直流电源点焊机进行点焊，一次性点焊成型即为重叠软连接片；
第二步，选1块干净完整的接触块，先用钨铜制成两块电极头，然后在接触块与成型重叠软连接薄片两端用90KVA以上的逆变直流电源点焊机采用点钎焊法焊接即成，在此步骤中，焊料选用HIAgCu80-5；
在上述步骤中，焊接熔和处为长方形。
2.根据权利要求1所述的重叠软连接薄片与接触块的焊接技术，其特征在于：所述软连接薄片为铜或铜合金。
3.根据权利要求1所述的重叠软连接薄片与接触块的焊接技术，其特征在于：所述接触块为黄铜。
4.根据权利要求1所述的重叠软连接薄片与接触块的焊接技术，其特征在于：所述焊料为银铜。
5.根据权利要求1或4所述的重叠软连接薄片与接触块的焊接技术，其特征在于：所述焊料为片状。
CN2009101024587A 2009-03-05 2009-03-05 重叠软连接薄片与接触块的焊接方法 Active CN101826418B (zh)