CN101798480A - Preparation method of highlight wear-resistant water-based glaze oil - Google Patents
Preparation method of highlight wear-resistant water-based glaze oil Download PDFInfo
- Publication number
- CN101798480A CN101798480A CN200910230221A CN200910230221A CN101798480A CN 101798480 A CN101798480 A CN 101798480A CN 200910230221 A CN200910230221 A CN 200910230221A CN 200910230221 A CN200910230221 A CN 200910230221A CN 101798480 A CN101798480 A CN 101798480A
- Authority
- CN
- China
- Prior art keywords
- parts
- deionized water
- alkali soluble
- acrylic emulsion
- oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a preparation method of highlight wear-resistant water-based glaze oil. The highlight wear-resistant water-based glaze oil is prepared from raw materials such as acrylic emulsion, an alkali soluble resin solution, wax emulsion, a defoaming agent, a wetting agent, a film forming agent, deionized water and the like. The preparation method comprises the following steps of: adding the acrylic emulsion in a vessel equipped with a high-speed dispersion machine according to the formula proportion; adding one third of deionized water for uniformly mixing; adding the alkali soluble resin solution after dispersing for 10 minutes at the rotating speed of 800r/min; improving the rotating speed to 1,200r/min; adding the wax emulsion, the defoaming agent, the film forming agent and residual deionized water in sequence according to the proportion after dispersing for 10 minutes; and improving the revolution to 2,000r/min, dispersing for 1 hour at a high speed and filtering by a screen mesh with 200 meshes to obtain the highlight wear-resistant water-based glaze oil.
Description
Technical field
The present invention relates to a kind of preparation method of coating, specifically a kind of preparation method of highlight wear-resistant water-based glaze oil.
Background technology
Since the eighties in 20th century, fast development along with opening and commodity economy, print product is superior day by day, colorize and variation, various glazing technologies have obtained development rapidly, glazing processing is universal day by day, the year application quantity of present domestic printed matter glazing paint (oil polish) surpasses ten thousand tons, has become a key areas of printing post-treatment.Early stage glazing paint kind is few, technology is simple and crude.Nowadays glazing paint has formed the series product of variation, many kinds, is broadly divided into solvent-borne type oil polish, oiliness oil polish, UV oil polish and water lustering oil.
The solvent-borne type oil polish adopts benzene class, ester class and alcoholic solvent, and solvent evaporates or remain on the printed matter all can cause the pollution to environment, and is harmful, therefore uses to be restricted, and the trend that is substituted and eliminates is arranged.Oiliness oil polish glossiness is general, and anti-physics and chemistry degree is relatively poor, and coating is understood yellowing, is not suitable for the glazing of high-grade printed matter.UV oil polish laser curing velocity is fast, glossiness is high, wear resistance good, does not have solvent evaporates in last photoreduction process, hundred-percent participation reaction, thus can not cause environmental pollution, harmless.But the quality control of UV glazing is than other glazing process complexity, and it is big that difficulty is wanted, and cost is than other glazing paint height.Water lustering oil is colourless, tasteless, transparency is good, the glossiness height; Solvent-free volatilization, nontoxic, non-stimulated, harmless, compliance with environmental protection requirements; Rate of drying is fast, stable performance, not yellowing of coating, nondiscoloration; Flexible, wear resistance, high temperature resistant, heat sealability is good, and post-press finishing adaptability is good; Cost is low, convenient transportation, safe and reliable.
Along with more and more higher to the printed matter performance demands, the water lustering oil of high gloss, high abrasion has become glazing Development of Materials direction, only the glossiness that provides by emulsion can not meet the demands, so the preparation process at water lustering oil can add a large amount of water-base resins to increase the glossiness and the wear resistance of gloss oil, and in order to improve the rate of drying of water-based gloss oil, can add a certain amount of small molecules solvent, as methyl alcohol, ethanol, Virahol etc.And common ACRYLIC EMULSION and water-base resin and small molecules solvent can't be compatible, so the ACRYLIC EMULSION that the conventional emulsion polymerization method makes can't satisfy the requirement of high-performance water-based oil polish.
Summary of the invention
The preparation method who the purpose of this invention is to provide a kind of high smooth high abrasion water lustering oil.
The high light high abrasion of purpose of the present invention water lustering oil is realized in the following manner, is to be made by the raw material of following weight part:
ACRYLIC EMULSION 400-500 part, alkali soluble resins liquid 300-400 part, wax emulsion 35-55 part, defoamer 5-10 part, wetting agent 5-10 part, film coalescence aid 10-15 part, deionized water 80-120 part;
Preparation process is as follows:
ACRYLIC EMULSION is placed in the container that high speed dispersor is housed by formula rate, the deionized water of adding 1/3rd mixes, dispersing speed 800r/min, disperse to add in about 10 minutes alkali soluble resins liquid, rotating speed is increased to 1200r/min, disperses 10 minutes, and ratio adds wax emulsion, defoamer, film coalescence aid, wetting agent and remaining deionized water successively again, improved revolution 2000r/min high speed dispersion 1 hour, 200 eye mesh screens filter and promptly get highlight wear-resistant water-based glaze oil.
Oil polish of the present invention compared with prior art, excellent effect is that high gloss, wear resistance are good, is base material with blank enamelled paper, 60 degree vancometers are measured, gloss can reach 87.2 degree, under 4 pounds of pressure, wear-resisting reaching 1000 times.
Embodiment
Embodiment 1
High light high abrasion water lustering oil of the present invention is to be made by following raw materials in weight portion:
400 parts of ACRYLIC EMULSION, alkali soluble resins liquid 300-part, 35 parts of wax emulsions, 5 parts of defoamers, 5 parts of wetting agents, 10 parts of film coalescence aid, 80 parts of deionized waters;
Preparation process is as follows:
ACRYLIC EMULSION is placed in the container that high speed dispersor is housed by formula rate, the deionized water of adding 1/3rd mixes, dispersing speed 800r/min, disperse to add in about 10 minutes alkali soluble resins liquid, rotating speed is increased to 1200r/min, disperses 10 minutes, and ratio adds wax emulsion, defoamer, film coalescence aid, wetting agent and remaining deionized water successively again, improved revolution 2000r/min high speed dispersion 1 hour, 200 eye mesh screens filter and promptly get highlight wear-resistant water-based glaze oil.
Embodiment 2
High light high abrasion water lustering oil of the present invention is to be made by following raw materials in weight portion:
500 parts of ACRYLIC EMULSION, 400 parts of alkali soluble resins liquid, 55 parts of wax emulsions, 10 parts of defoamers, 10 parts of wetting agents, 15 parts of film coalescence aid, 120 parts of deionized waters;
Preparation process is identical with embodiment 1:
Embodiment 3
High light high abrasion water lustering oil of the present invention is to be made by following raw materials in weight portion:
450 parts of ACRYLIC EMULSION, 320 parts of alkali soluble resins liquid, 40 parts of wax emulsions, 6 parts of defoamers, 6 parts of wetting agents, 11 parts of film coalescence aid, 90 parts of deionized waters.
Embodiment 4
High light high abrasion water lustering oil of the present invention is to be made by following raw materials in weight portion:
480 parts of ACRYLIC EMULSION, 380 parts of alkali soluble resins liquid, 50 parts of wax emulsions, 8 parts of defoamers, 9 parts of wetting agents, 14 parts of film coalescence aid, 110 parts of deionized waters.
Embodiment 5
High light high abrasion water lustering oil of the present invention is to be made by following raw materials in weight portion:
460 parts of ACRYLIC EMULSION, 350 parts of alkali soluble resins liquid, 45 parts of wax emulsions, 7 parts of defoamers, 8 parts of wetting agents, 12 parts of film coalescence aid, 100 parts of deionized waters.
Raw material in the present invention's prescription is market public offering product.
Claims (3)
1. the preparation method of highlight wear-resistant water-based glaze oil is characterized in that it being that raw material by following weight part is made:
ACRYLIC EMULSION 400-500 part, alkali soluble resins liquid 300-400 part, wax emulsion 35-55 part, defoamer 5-10 part, wetting agent 5-10 part, film coalescence aid 10-15 part, deionized water 80-120 part;
Preparation process is as follows:
ACRYLIC EMULSION is placed in the container that high speed dispersor is housed by formula rate, the deionized water of adding 1/3rd mixes, dispersing speed 800r/min, disperse to add in about 10 minutes alkali soluble resins liquid, rotating speed is increased to 1200r/min, disperses 10 minutes, and ratio adds wax emulsion, defoamer, film coalescence aid, wetting agent and remaining deionized water successively again, improved revolution 2000r/min high speed dispersion 1 hour, 200 eye mesh screens filter and promptly get highlight wear-resistant water-based glaze oil.
2. according to the method under the claim 1, it is characterized in that, is to be made by the raw material of following weight part:
ACRYLIC EMULSION 450-480 part, alkali soluble resins liquid 320-380 part, wax emulsion 40-50 part, defoamer 6-8 part, wetting agent 6-9 part, film coalescence aid 11-14 part, deionized water 90-110 part.
3. according to the method under the claim 1, it is characterized in that, is to be made by the raw material of following weight part:
460 parts of ACRYLIC EMULSION, 350 parts of alkali soluble resins liquid, 45 parts of wax emulsions, 7 parts of defoamers, 8 parts of wetting agents, 12 parts of film coalescence aid, 100 parts of deionized waters.