CN101787152A - 一种含有间甲树脂的帘布胶料 - Google Patents
一种含有间甲树脂的帘布胶料 Download PDFInfo
- Publication number
- CN101787152A CN101787152A CN 201010119210 CN201010119210A CN101787152A CN 101787152 A CN101787152 A CN 101787152A CN 201010119210 CN201010119210 CN 201010119210 CN 201010119210 A CN201010119210 A CN 201010119210A CN 101787152 A CN101787152 A CN 101787152A
- Authority
- CN
- China
- Prior art keywords
- sizing material
- cord fabric
- glue stock
- cord
- glue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种含有间甲树脂的帘布胶料，所述帘布胶料由生胶、炭黑、活性剂、软化剂、防老剂、硫化剂、粘合剂按比例混合制作而成，其特征在于：所述帘布胶料中含有质量百分比为1～3％的间甲树脂。本发明的优点在于：对于纯间苯二酚，高温下易挥发。为保证其在胶料的含量，往往将其放于终炼胶中加入，导致其在胶料中混炼不均匀。而对于间甲树脂，完全可以摒除其挥发的忧虑，将其放入段胶中混炼，保证其分散均匀性。
Description
技术领域
本发明涉及一种帘布胶料，具体涉及一种橡胶轮胎用的，其成分中含有间甲树脂的帘布胶料。
背景技术
目前市场上的橡胶轮胎用帘布胶料由生胶、炭黑、活性剂、软化剂、防老剂、硫化剂、粘合剂和纯间苯二酚混合制得，该成分的帘布胶料由于含有纯间苯二酚，因此在混炼中有挥发现象，其在混炼中所产生的游离酚挥发物对环境形成污染，不利于环保；另外，以上成分的帘布胶料在存放过程中还易发白，且帘布粘性相对不能得到很好的保证。
发明内容
本发明的主要任务在于提供一种含有间甲树脂的橡胶轮胎用帘布胶料，具体是一种混炼时对环境友好，保证帘布年度、杜绝帘布在存放中发白现象的含有间甲树脂的帘布胶料。
为了解决以上技术问题，本发明的一种含有间甲树脂的帘布胶料，所述帘布胶料由生胶、炭黑、活性剂、软化剂、防老剂、硫化剂、粘合剂按比例混合制作而成，其特征在于：所述帘布胶料中含有质量百分比为1～3％的间甲树脂。
本发明的优点在于：对于纯间苯二酚，高温下易挥发。为保证其在胶料的含量，往往将其放于终炼胶中加入，导致其在胶料中混炼不均匀。而对于间甲树脂，完全可以摒除其挥发的忧虑，将其放入段胶中混炼，保证其分散均匀性。
附图说明
图1为本发明的胶料硫化结束后，降温至60℃，10HZ的应变扫描图；
图2为本发明的胶料的动态粘弹应变扫描图。
具体实施方式
实施例1
从以上表格可见，试验胶料的定伸应力为17——18，但对于帘布胶料比较重要的粘合性能为800——900。
第二步、动态性能测试：
测试条件：胶料150℃硫化结束后，降温至60℃，10HZ；其应变扫描如图1所示，从胶料的动态粘弹理论出发，应变扫描图如图2所示，从其结论可知：试验胶料在应变过程中粘性损失，滞后损失比正常胶料低，生热低。
对比实施例1：
该试验TP397胶料用于现场压延：
现场试验效果图：(1)试验TP397压延部件(压延后三天)；胶料日期：2008-10-27；压延日期：2008-11-5；注：压延时胶料已过期。试验结果表明：试验的压延部件丝毫没有发白现象。
(2)正常TP397压延部件：
胶料日期：2008-11-3；压延日期：2008-11-5注：压延时胶料在有效期范围内。试验结果表明：正常的压延部件一旦裸露在空气中，部件与空气接触就会产生白点。
总结：试验的压延部件丝毫没有发白现象，而正常的压延部件一旦裸露在空气中，部件与空气接触就会产生白点，大大影响了胶料粘性，情况严重的将会造成帘布不粘，更有甚者产生胎面压空。
对比实施例2
将试验胶料用于轧S3045B帘布，裁断后用于11.00R20 RLB11 2#与3#带束层中：
1、现场压延现状：
| 辊筒 | 1# | 2# | 3# | 4# |
| 温度 | 82 | 80 | 82 | 84 |
| 冷喂料 | 螺杆 | 机身 | 机头 |
| 温度 | 70 | 60 | 70 |
压延速度：30m/min；
2、试验帘布检测数据：
3、机床结果(11.00R20 RLB11结构调整前)：
| 年份 | 试验帘布 | 08年上半年 |
| 机床平均寿命 | 121h16min | 110h |
| 损坏后病象 | 胎肩*** | 胎冠脱层 |
由试验结果可见：试验胶料制得的轮胎寿命相当长。
Claims (1)
1.一种含有间甲树脂的帘布胶料，所述帘布胶料由生胶、炭黑、活性剂、软化剂、防老剂、硫化剂、粘合剂按比例混合制作而成，其特征在于：所述帘布胶料中含有质量百分比为1～3％的间甲树脂。