CN101705064A - 环保无醛净味建筑胶水 - Google Patents
环保无醛净味建筑胶水 Download PDFInfo
- Publication number
- CN101705064A CN101705064A CN200910211167A CN200910211167A CN101705064A CN 101705064 A CN101705064 A CN 101705064A CN 200910211167 A CN200910211167 A CN 200910211167A CN 200910211167 A CN200910211167 A CN 200910211167A CN 101705064 A CN101705064 A CN 101705064A
- Authority
- CN
- China
- Prior art keywords
- glue
- kilograms
- building glue
- urea
- phosphoric acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
环保无醛净味建筑胶水,它涉及一种建筑胶水。它是由聚乙烯醇60%-80%、磷酸6%-10%、尿素2%-5%、氢氧化钠、聚丙烯酸钠0.5%-1%、防腐剂0.1%和水补足100制备而成;采用聚乙烯醇在尿素的催化作用下和磷酸进行第一次酯化,磷酸作为一种无机多元酸,能和聚乙烯醇中的羟基进行酯化,同时加入的尿素也能增强胶水的抗冻性和存储性;无色无味,透明稠度好,存储时间长,低温不凝胶,粘结力强,可以和白水泥、双飞粉、滑石粉、石膏粉等混合使用、易施工、不脱粉、不卷皮。
Description
技术领域:
本发明涉及一种建筑胶水,尤其是涉及一种环保无醛净味建筑胶水。
背景技术:
现有建筑工程和室内装修用的建筑胶水,主要是聚乙烯醇缩醛类胶水(如107、801胶)和丙烯酰胺类胶水。聚乙烯醇缩醛类建筑胶水主要是聚乙烯醇在酸性催化剂下和甲醛(或乙二醛)反应而成,其特点是粘接强度高,抗冻性好,但胶水醛类残留量高,刺激性气味大,严重影响生产使用者的身心健康。丙烯酰胺类胶水主要是采用聚乙烯醇和丙烯酰胺为主要原料在引发剂作用下进行共聚而成,生产出来的胶水具有无色透明,施工性能好,性价比高,但丙烯酰胺为有毒物质,长期接触可引起各种神经***疾病,如肌肉麻木、萎缩,严重时可致癌。
针对以上情况,许多发明专利采用了淀粉、硼酸、水玻璃、纤维素等材料来对聚乙烯醇进行改性,或通过各种途径来消除反应后残留的醛类。但多少存在一些不足,具体使用不理想。
发明内容:
本发明的目的是提供一种环保无醛净味建筑胶水,它能采用对聚乙烯醇进行双重酯化改性,减少聚乙烯醇中的亲水性羟基,从而提高胶水的耐水性和粘接力。生产中参与反应的物质为无毒,无味,无挥发有害气体、不污染环境透明无色的环保净醛净味胶水。
为了解决背景技术所存在的问题,本发明是采用以下技术方案:它是由聚乙烯醇60%-80%、磷酸6%-10%、尿素2%-5%、氢氧化钠、聚丙烯酸钠0.5%-1%、防腐剂0.1%和水补足100制备而成,在反应釜或制胶罐中,加入600公斤水,然后开始搅拌加热,加热到40-50度时,加入聚乙烯醇60公斤,升温至95-95℃,保温搅拌半小时,使聚乙烯醇完全溶解;第二步,将温度降至90℃左右,在加入6公斤磷酸(分析纯),搅拌5分钟,然后加入5公斤尿素,搅拌反应1小时左右;第三步,加冷水100公斤,使反应釜内温度降低至60-70℃,慢慢加入10%氢氧化钠溶液,将PH调至7-8;第四步,加入1%聚丙烯酸钠溶液100公斤,保温反应30-60分钟;第五步,加入剩余的水量,补足1吨胶水,将温度降至40度以下,加入1公斤防腐剂,搅拌均匀后,包装、出料。
本发明具有以下有益效果:采用聚乙烯醇在尿素的催化作用下和磷酸进行第一次酯化,磷酸作为一种无机多元酸,能和聚乙烯醇中的羟基进行酯化,同时加入的尿素也能增强胶水的抗冻性和存储性;无色无味,透明稠度好,存储时间长,低温不凝胶,粘结力强,可以和白水泥、双飞粉、滑石粉、石膏粉等混合使用、易施工、不脱粉、不卷皮。
具体实施方式:
本具体实施方式采用以下技术方案:由聚乙烯醇60%-80%、磷酸6%-10%、尿素2%-5%、氢氧化钠、聚丙烯酸钠0.5%-1%、防腐剂0.1%和水补足100制备而成。
在反应釜或制胶罐中,加入600公斤水,然后开始搅拌加热,加热到40-50度时,加入聚乙烯醇60公斤,升温至95-95℃,保温搅拌半小时,使聚乙烯醇完全溶解。
第二步,将温度降至90℃左右,在加入6公斤磷酸(分析纯),搅拌5分钟,然后加入5公斤尿素,搅拌反应1小时左右。
第三步,加冷水100公斤,使反应釜内温度降低至60-70℃,慢慢加入10%氢氧化钠溶液,将PH调至7-8。
第四步,加入1%聚丙烯酸钠溶液100公斤,保温反应30-60分钟。
第五步,加入剩余的水量,补足1吨胶水,将温度降至40度以下,加入1公斤防腐剂,搅拌均匀后,包装、出料。
本具体实施方式采用聚乙烯醇在尿素的催化作用下和磷酸进行第一次酯化,磷酸作为一种无机多元酸,能和聚乙烯醇中的羟基进行酯化,同时加入的尿素也能增强胶水的抗冻性和存储性;无色无味,透明稠度好,存储时间长,低温不凝胶,粘结力强,可以和白水泥、双飞粉、滑石粉、石膏粉等混合使用、易施工、不脱粉、不卷皮。
Claims (1)
1.环保无醛净味建筑胶水,其特征在于它是由聚乙烯醇60%-80%、磷酸6%-10%、尿素2%-5%、氢氧化钠、聚丙烯酸钠0.5%-1%、防腐剂0.1%和水补足100制备而成,在反应釜或制胶罐中,加入600公斤水,然后开始搅拌加热,加热到40-50度时,加入聚乙烯醇60公斤,升温至95-95℃,保温搅拌半小时,使聚乙烯醇完全溶解;第二步,将温度降至90℃左右,在加入6公斤磷酸(分析纯),搅拌5分钟,然后加入5公斤尿素,搅拌反应1小时左右;第三步,加冷水100公斤,使反应釜内温度降低至60-70℃,慢慢加入10%氢氧化钠溶液,将PH调至7-8;第四步,加入1%聚丙烯酸钠溶液100公斤,保温反应30-60分钟;第五步,加入剩余的水量,补足1吨胶水,将温度降至40度以下,加入1公斤防腐剂,搅拌均匀后,包装、出料。