CN101684615A - 一种环保型气相防锈无纺布 - Google Patents

一种环保型气相防锈无纺布 Download PDF

Info

Publication number
CN101684615A
CN101684615A CN200910075251A CN200910075251A CN101684615A CN 101684615 A CN101684615 A CN 101684615A CN 200910075251 A CN200910075251 A CN 200910075251A CN 200910075251 A CN200910075251 A CN 200910075251A CN 101684615 A CN101684615 A CN 101684615A
Authority
CN
China
Prior art keywords
woven fabric
percent
gas
phase
environment
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN200910075251A
Other languages
English (en)
Inventor
黄红军
伍志强
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN200910075251A priority Critical patent/CN101684615A/zh
Publication of CN101684615A publication Critical patent/CN101684615A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高效、环保、防锈效果好的气相防锈无纺布。本气相防锈无纺布的组成及含量(质量百分比)为：无纺布85－93％；气相缓蚀剂4－13％；聚乙烯醇1－2％；铝酸酯偶联剂1－3％。其中：无纺布由聚酯(PET)、聚乙烯、聚丙烯、尼龙或聚乙烯醇等树脂拉丝压合而成，气相缓蚀剂是由15－30％苯甲酰环己胺、2－10％苯甲酸钠、10－20％苯***或羟基苯***或苯***和羟基苯***的混合物、28－45％癸二酸钠或癸二酸铵、10－20％吸氧剂、10－35％铬酸叔丁酯组成，其中吸氧剂是连二亚硫酸钠或硫酸亚铁。本气相防锈无纺布的主要生产工艺包括：气相缓蚀剂固体组分经研磨、过筛后，在纯净水中溶解后，加入铝酸酯偶联剂，溶解，放置24小时，然后用涂布机在无纺布上涂布，视使用要求调整涂布量在4－13％。

Description

一种环保型气相防锈无纺布
技术领域
本发明涉及一种环保型气相防锈无纺布，属于金属防锈技术领域。
背景技术
气相缓蚀剂是一类挥发性缓蚀剂，在常温下自动挥发出的气体可在金属表面形成一种保护膜，起到抑制金属腐蚀的作用。
二次世界大战期间，由于军械装备防锈的需要，气相防锈技术开始应用和发展。近年来，许多发达国家在国防和民用方面都大量采用气相缓蚀剂用于金属防锈。在工业领域，国外一些大企业将气相缓蚀剂广泛用于金属产品生产、运输、使用以及储存过程中的防锈。美国岩岛兵工厂从1950年开始，应用气相缓蚀剂对火炮、枪械等军械装备进行了长达10年的防锈效果试验验证，证明气相缓蚀剂对武器装备具有很好的防锈效果。目前，国内外许多单位的科研工作者开发成功了多种形式的气相防锈产品，有气相防锈膜、气相防锈纸、气相防锈涂料等产品，这些产品具有优异的防锈性能，解决了金属零备件出口和运输过程中防锈问题。但是对于钢铁企业来说，这些产品均不方便应用，如冷轧钢板从生产线下线温度在100℃以上，而且钢板边缘有一些锋利的毛刺，这样一来，上述提到的气相防锈膜由于基材为聚乙烯，当温度＞90℃就呈熔融态，无法使用，气相防锈纸较脆，易破。在生产线上使用气相防锈涂料污染严重。所以冷轧钢板的防锈是当前困扰钢铁企业的重要难题。
因此，应开发一种在冷轧钢板生产线上应用方便的环保型气相防锈产品是非常必要的。
发明内容
本发明的目的是提供一种高效、环保、防锈效果好的气相防锈无纺布。
本气相防锈无纺布的组成及含量(质量百分比)为：
无纺布          85-93％
气相缓蚀剂      4-13％
聚乙烯醇        1-2％
铝酸酯偶联剂    1-3％
其中：无纺布由聚酯(PET)、聚乙烯、聚丙烯、尼龙或聚乙烯醇等树脂拉丝压合而成，气相缓蚀剂是由15-30％苯甲酰环己胺、2-10％苯甲酸钠、10-20％苯***或羟基苯***或苯***和羟基苯***的混合物、28-45％癸二酸钠或癸二酸铵、10-20％吸氧剂、10-35％铬酸叔丁酯组成，其中吸氧剂是连二亚硫酸钠或硫酸亚铁。
本气相防锈无纺布的主要生产工艺包括：气相缓蚀剂固体组分经研磨、过筛后，在纯净水中溶解后，加入铝酸酯偶联剂，溶解，放置24小时，然后用涂布机在无纺布上涂布，视使用要求调整涂布量在4-13％。
本气相防锈无纺布的主要优点是：
①可适用于各种钢铁、铜、铝、镀铬等多种金属的保护，尤其适合板材加工流水线上使用；
②强度高，不会因为毛刺或板材边缘的其他尖锐部位而发生破裂；
③环保低毒，对人体和环境无不良影响；
④防锈效果好，在密闭条件下，可以达到5年以上。
实施例1：取无纺布85份，气相缓蚀剂(由5％苯甲酰环己胺、7％苯甲酸钠、15％苯***、35％癸二酸盐、28％铬酸叔丁酯(液体)、11％吸氧剂按照前述的生产方法生产)13份，聚乙烯醇1份，铝酸酯偶联剂1份，按照上述气相防锈无纺布的生产工艺，得到产品。
实施例2：取无纺布93份，气相缓蚀剂(由5％苯甲酰环己胺、7％苯甲酸钠、15％苯***、35％癸二酸盐、28％铬酸叔丁酯(液体)、11％吸氧剂按照前述的生产方法生产)5份，聚乙烯醇1份，铝酸酯偶联剂1份，按照上述气相防锈无纺布的生产工艺，得到产品。
对上述各实施例防锈性能的试验验证
1、静态不接触加速试验
此试验用于验证实施例1-2在静态潮湿状况下的防锈效果。实验装置见附图1，其中附图标记1为橡胶塞，标记2为试管(φ30×200mm)，标记3为试片，标记4为气相防锈无纺布，标记5为恒温槽，标记6为电解质溶液。
试验说明：气相防锈无纺布为120mm×100mm，电解质溶液分别含HCO3 -1000mg/L、SO4 2-2500mg/L、Cl-1500mg/L，将金属试片(50mm×25mm×2mm)按GB/T4879-1999规定的方法处理后不需预膜直接置于装置中，将水浴温度设置为40℃，实验期为15天。
与实施例对照的比较例为：
比较例1：取无纺布98份，聚乙烯醇1份，铝酸酯偶联剂1份，按照上述气相防锈无纺布的生产工艺，进行生产。
试验结果见表1。
表1静态不接触加速试验结果
  金属试片   A3钢  45#钢  20#钢   铝   黄铜   紫铜   镀锌   镀铬
  比较例1   ▲  ▲  ▲   ▲   ●   ●   ▲   ▲
  实施例1   ○  ○  ○   ○   ○   ○   ○   ○
  实施例2   ○  ○  ○   ○   ○   ○   ○   ○
注1：上表中，▲——严重锈蚀，●——完全变色，○——光亮无锈；
比较例1中钢类试片5h即出现锈点，很快严重全面锈蚀；铝试片表面4h失去金属光泽，24h出现白色粉状物；铜类试片20h发生变色现象，镀锌和镀铬试片15h表面失去金属光泽，24小时出现鼓泡现象。
结果表明：本发明涉及的气相防锈无纺布是一类防锈效果好，应用方便的新型气相防锈产品，对钢铁企业生产线的防锈手段的改进具有重要意义。
附图说明
图1是静态不接触实验装置图。

Claims (3)

1、一种环保型气相防锈无纺布，其特征在于各组分及其含量(质量百分比)为：
无纺布        85-93％
气相缓蚀剂    4-13％
聚乙烯醇      1-2％
铝酸酯偶联剂  1-3％
其中：无纺布由聚酯(PET)、聚乙烯、聚丙烯、尼龙或聚乙烯醇等树脂拉丝压合而成，气相缓蚀剂是由15-30％苯甲酰环己胺、2-10％苯甲酸钠、10-20％苯***或羟基苯***或苯***和羟基苯***的混合物、28-45％癸二酸钠或癸二酸铵、10-20％吸氧剂、10-35％铬酸叔丁酯组成，其中吸氧剂是连二亚硫酸钠或硫酸亚铁。
2、根据权利要求1所述的环保型气相防锈无纺布，其特征在于：无纺布是由聚酯(PET)、聚乙烯、聚丙烯、尼龙或聚乙烯醇等树脂拉丝压合而成。
3、根据权利要求1所述的环保型气相防锈无纺布，其特征在于：所述环保型气相防锈无纺布的主要生产工艺包括：气相缓蚀剂固体组分经研磨、过筛后，在纯净水中溶解后，加入铝酸酯偶联剂，溶解，放置24小时，然后用涂布机在无纺布上涂布，视使用要求调整涂布量在4-13％。
CN200910075251A 2009-08-28 2009-08-28 一种环保型气相防锈无纺布 Pending CN101684615A (zh)