CN101649670A - Decoration plate with inorganic texture mortar like facing bricks being coated on surface - Google Patents
Decoration plate with inorganic texture mortar like facing bricks being coated on surface Download PDFInfo
- Publication number
- CN101649670A CN101649670A CN200910167415A CN200910167415A CN101649670A CN 101649670 A CN101649670 A CN 101649670A CN 200910167415 A CN200910167415 A CN 200910167415A CN 200910167415 A CN200910167415 A CN 200910167415A CN 101649670 A CN101649670 A CN 101649670A
- Authority
- CN
- China
- Prior art keywords
- layer
- mortar
- decoration plate
- coated
- insulation layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a decoration plate with inorganic texture mortar like facing bricks being coated on the surface. The decoration plate is made by compounding three layers of materials, whereinthe surface layer of the decoration plate is an inorganic texture mortar layer with facing bricks being coated on the surface, the middle layer is a calcium silicate plate, and the inner layer is a thermal insulation layer; and the thermal insulation layer takes polystyrene resin as raw material, diagonal braces arranged inside the thermal insulation layer are in diagonal tensioning, and the diagonal angle is 45 degrees. The invention has the advantages of uneasy cracking, uneasy water seepage, good insulation effect, and the like.
Description
Technical field
The present invention relates to a kind of decorative panel of external coating face brick-imitation inanimate matter texture mortar, mainly use at heat preservation and decoration of outer wall such as buildings.
Technical background
Be in the building trade high-speed developing period at present, but the development of construction material lags behind comparatively.Usually, building inside and outside wall will be finished insulation earlier, carries out decoration construction again.Because of factors such as technology, operation, selection, constructions, very big to the construction quality influence.Problems occur through regular meeting, FAQs has the following aspects: the subitem construction, and contradiction is many; Operation is various, and is long in time limit; Technology falls behind, and is of poor quality.Use the material tradition, load-bearing is big; Wet work, weak effect; Waste of material, the cost height.Tradition insulation, decorate two the work itemss, need two professional work posts, nearly ten procedures construction exists operation many, and is time-consuming, take material, the difficult control of construction quality.Add wet construction materials such as insulation adhesives, plastering mortar, putty, coating, in work progress because of science, the stability of material prescription and on-the-spot proportioning, the correctness of constructor's operation, the capital impacts construction quality, metope also just is difficult to avoid cracking, infiltration, problems such as insulation and decoration weak effect to occur.
Summary of the invention
The object of the present invention is to provide the decorative panel of the external coating face brick-imitation inanimate matter texture mortar of a kind of infiltration not easy to crack, difficult, high insulating effect.
The object of the invention solves by the following technical programs, and this decorative panel is that trilaminate material is composited, and the top layer of decorative panel is an external coating face brick-imitation inanimate matter texture mortar layer, and the intermediate layer is a calcium silicate board with microporous, and nexine is an insulation layer.
Described insulation layer is to be raw material with the polystyrene resin, and the inner brace that is provided with is that diagonal member draws, and angle is 45 °.
External coating face brick-imitation inanimate matter texture mortar be by the aggregate of inorganic mineral type cementitious material, various optimization gratings, special architectural chemistry additive and various inorganic/decoration mortar that organic pigment forms through allotment meticulously.By selecting the aggregate of different-grain diameter for use, and in work progress, adopt different construction appliances and construction gimmick, can simulate and moulding goes out multiple different pattern structure, have fairly obvious texture and good decoration effect.Such product surface clean mark may compare favourably in true stone material exterior wall.The overall weight of product is controlled at 10～12kg/m
2In, can guarantee that the product installation is convenient and cheap.System surfaces is through after the PROCESS FOR TREATMENT, and also advantage is outstanding aspect efflorescence prevention performance, antifouling property, particularly can provide more design inspiration and space imagination aspect the processing at abnormity, negative and positive angle.Calcium silicate board with microporous is to be raw material by siliceous material, calcareous material, fortifying fibre etc., through slurrying, become operations such as base, HTHP are steam-cured, sanding surface to make.Because siliceous, calcareous material is under the condition of HTHP, reaction generates holder shellfish mullite crystal, and its performance is very stable, thus with this crystal be Main Ingredients and Appearance have fire prevention, protection against the tide, durable, deformation rate is low.Warming plate is to be raw material with the polystyrene resin, hard plate material via the continuous foam shaping by extrusion of special process, it is inner to be closed bubble structure independently, be a kind of high resistance to compression that has, do not absorb water, the environment-friendly type heat insulating material of excellent properties such as moistureproof, airtight, lightweight, corrosion-resistant, long service life, coefficient of thermal conductivity are low.Brace be high density extrusion molding lath by miter angle tiltedly draw mode, thoroughly solve plate distortional stress, improve the general safety coefficient of system.
Description of drawings
Fig. 1 is a structural representation of the present invention.
Fig. 2 is the brace schematic diagram in the insulation layer of the present invention.
1, external coating face brick-imitation inanimate matter texture mortar layer 2, calcium silicate board with microporous 3, insulation layer 4, brace
The specific embodiment
The present invention is described in further detail in conjunction with the accompanying drawings.
From Fig. 1, Fig. 2 as can be seen, this decorative panel is that trilaminate material is composited, the top layer of decorative panel is an external coating face brick-imitation inanimate matter texture mortar layer 1, the intermediate layer is a calcium silicate board with microporous 2, nexine is an insulation layer 3, insulation layer 3 is to be raw material with the polystyrene resin, and the inner brace (4) that is provided with is for diagonal member draws, and angle is 45 °.
The performance indications of insulation layer
It is a raw material with siliceous material, calcareous material, fortifying fibre etc. for calcium silicate board with microporous, through slurrying, become operations such as base, HTHP are steam-cured, sanding surface to make.Because siliceous, calcareous material is under the condition of HTHP, reaction generates holder shellfish mullite crystal, its performance is very stable, thus with this crystal be Main Ingredients and Appearance have fire prevention, protection against the tide, durable, deformation rate is low. main performance index: rupture strength: 〉=11MPa, density:＜1.4g/cm
3
The wet rate that rises:＜0.25%, percent thermal shrinkage:＜1%
Face brick-imitation inanimate matter texture mortar be by the aggregate of inorganic mineral type cementitious material, various optimization gratings, special architectural chemistry additive and various inorganic/decoration mortar that organic pigment forms through allotment meticulously.By selecting the aggregate of different-grain diameter for use, such product color is abundant, outward appearance can customize by design effect, broken through surface brick adherence technology causes in the conventional way cracking, hollowing, come off, common fault such as infiltration, the accumulation of salt in the surface soil, because that installs is convenient, more construction period can be shortened, be convenient to the overall progress arrangement of engineering.
Face brick-imitation inanimate matter texture mortar physical and mechanical property
Claims (2)
1, a kind of decorative panel of external coating face brick-imitation inanimate matter texture mortar is characterized in that:
Decorative panel is that trilaminate material is composited, and the top layer of decorative panel is an external coating face brick-imitation inanimate matter texture mortar layer (1), and the intermediate layer is calcium silicate board with microporous (2), and nexine is insulation layer (3).
2, according to the decorative panel of the described a kind of external coating face brick-imitation inanimate matter texture mortar of claim 1, it is characterized in that:
Insulation layer (3) is to be raw material with the polystyrene resin, and the inner brace (4) that is provided with is for diagonal member draws, and angle is 45 °.