CN101649175A - 紫外光固化聚氨酯丙烯酸酯胶粘剂及其制备方法 - Google Patents

紫外光固化聚氨酯丙烯酸酯胶粘剂及其制备方法 Download PDF

Info

Publication number
CN101649175A
CN101649175A CN200910060346A CN200910060346A CN101649175A CN 101649175 A CN101649175 A CN 101649175A CN 200910060346 A CN200910060346 A CN 200910060346A CN 200910060346 A CN200910060346 A CN 200910060346A CN 101649175 A CN101649175 A CN 101649175A
Authority
CN
China
Prior art keywords
formula ratio
adhesive
add
ultraviolet curing
acrylate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN200910060346A
Other languages
English (en)
Other versions
CN101649175B (zh
Inventor
陈格德
钟安永
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHENGDU AEROSPACE MINGJIANG TECHNICAL INDUSTRY Co Ltd
Sichuan University
Original Assignee
CHENGDU AEROSPACE MINGJIANG TECHNICAL INDUSTRY Co Ltd
Sichuan University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHENGDU AEROSPACE MINGJIANG TECHNICAL INDUSTRY Co Ltd, Sichuan University filed Critical CHENGDU AEROSPACE MINGJIANG TECHNICAL INDUSTRY Co Ltd
Priority to CN200910060346XA priority Critical patent/CN101649175B/zh
Publication of CN101649175A publication Critical patent/CN101649175A/zh
Application granted granted Critical
Publication of CN101649175B publication Critical patent/CN101649175B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

紫外光固化聚氨酯丙烯酸酯胶粘剂及其制备方法，公开了一种获取环保型胶粘剂的途径。该胶粘剂主要作为电子电器的粘接剂，可应用在PDP、LED、OLED、FPD显示器的粘接上。该胶粘剂是以活性稀释剂丙烯酸异冰片酯作溶剂，来代替甲苯和苯，并将甲苯二异氰酸酯滴加入聚醚中的方法，反应中使用扩链剂，在3小时内完成反应而获取。该胶粘剂不论是在生产还是使用过程中都不会产生有毒有害物质，对环境没有污染；同时它反应时间短，反应温度低，能达到节能的目的。

Description

紫外光固化聚氨酯丙烯酸酯胶粘剂及其制备方法
所属技术领域
本发明属化工技术领域，是一种环境友好，低黏度，高效节能的UV固化胶粘剂。它可以作为电子电器的粘接剂，如应用在PDP、LED、OLED、FPD显示器的粘接；也可以用于制造光学膜材料，如PET防划伤膜、防反射膜、防眩光膜和隔离膜等。
背景技术
目前，已有的光固化型聚氨酯丙烯酸酯胶粘剂主要用于木器涂料和油墨等的制造中，但它的粘接强度、延伸率、收缩率、防潮性以及电性能等，达不到电子行业中使用的标准。随着电子工业的迅猛发展，对高性能UV固化胶粘剂的需求越来越大。但现有产品的生产中多使用甲苯，苯等有毒溶剂，严重浸染环境。总之，现有同类产品无论在环保、节能、性能和功能方面尚存缺陷，不能充分满足实际应用中的要求。
发明内容
本发明的目的在于克服现有光固化型聚氨酯丙烯酸酯胶粘剂的缺陷，提供一种绿色环保，性能高且无毒害的应用于PDP等领域的紫外光固化聚氨酯丙烯酸酯胶粘剂。
本发明的目的是通过以下技术措施来实现的：以活性稀释剂丙烯酸异冰片酯(IBOA)代替甲苯和苯，作为溶剂。采用将甲苯二异氰酸酯(TDI)滴加入聚醚(PPG-2000)中的方法，并在反应中使用扩链剂，于3小时内完成反应，最终得到低表观黏度(小于3000MPa·s)，固化膜延伸率大于150％的聚氨酯丙烯酸酯胶粘剂。其配方按重量百分比计如下：
聚醚(PPG-2000)           35～40％
甲苯二异氰酸酯(TDI)      5～8％
丙烯酸羟乙酯(HEA)        15～30％
丙烯酸羟丙酯(HPA)        15～30％
丙烯酸异冰片酯(IBOA)     10～25％
乙氧基化三羟甲基丙烷三丙烯酸酯(EO-TMPTA)1～3％
1，4-丁二醇              0.1～0.5％
对苯二酚                 0.05～0.1％
二月桂酸二丁基锡         0.05～0.1％
二苯甲酮(BP)             1～2％
1-羟基环己基苯甲酮(184)  2～3％
本发明的制备过程中先按上述配方比备好各原料按如下工艺步骤进行：首先向反应釜中注入配方量的聚醚，然后加热至60℃的温度条件下滴加配方量的甲苯二异氰酸酯和二月桂酸二丁基锡，并开动搅拌均匀之后，再加入配方量的丙烯酸异冰片酯和对苯二酚，并保温反应0.3～0.7小时；接着再加入配方量的1，4-丁二醇，再保温反应0.3～0.7小时；之后再加入配方量的丙烯酸羟乙酯、丙烯酸羟丙酯和乙氧基化三羟甲基丙烷三丙烯酸酯，并搅拌0.3～0.7小时，至体系均匀透明；最后降至室温，再加入配方量的二苯甲酮和1-羟基环己基苯甲酮，混合均匀后即得成品。
本发明相比现有技术的有益效果是：该胶粘剂不论是在生产还是使用过程中都不会产生有毒有害物质，对环境没有污染；同时它反应时间短，反应温度低，能达到节能的目的。
具体实施方式
下面结合实施例对本发明作进一步的描述，以生产100公斤该产品为例。
一、原料及其用量
聚醚(PPG-2000)                             40kg
二月桂酸二丁基锡                           0.1kg
甲苯二异氰酸酯(TDI)                        7kg
丙烯酸异冰片酯(IBOA)                       10kg
对苯二酚                                   0.1kg
1，4-丁二醇                                0.3kg
丙烯酸羟乙酯(HEA)                          15kg
丙烯酸羟丙酯(HPA)                          21.5kg
乙氧基化三羟甲基丙烷三丙烯酸酯(EO-TMPTA)   1kg
二苯甲酮(BP)                               2kg
1-羟基环己基苯甲酮(184)                    3kg
二、生产流程
1.取40kg的聚醚加入反应釜中，开动搅拌并升温到60℃，再加入0.1kg的二月桂酸二丁基锡，然后开始滴加7kg的甲苯二异氰酸酯；
2.甲苯二异氰酸酯滴加完后，加入10kg的丙烯酸异冰片酯和0.1kg的对苯二酚，并保温反应0.5小时；
3.加入0.3kg的1，4-丁二醇后，再保温反应0.5小时；
4.接着加入15kg的丙烯酸羟乙酯，21.5kg的丙烯酸羟丙酯和1kg的乙氧基化三羟甲基丙烷三丙烯酸酯，并搅拌0.5小时，至体系均匀透明；
5.最后降至室温，再加入2kg的二苯甲酮和3kg的1-羟基环己基苯甲酮，混匀即得产品。

Claims (2)

1.一种以活性稀释剂丙烯酸异冰片酯作溶剂，代替甲苯和苯，采用将甲苯二异氰酸酯滴加入聚醚中的方法，来生产的紫外光固化聚氨酯丙烯酸酯胶粘剂，其特征是配方按重量百分比计如下：
聚醚(PPG-2000)                              35～40％
甲苯二异氰酸酯(TDI)                         5～8％
丙烯酸羟乙酯(HEA)                           15～30％
丙烯酸羟丙酯(HPA)                           15～30％
丙烯酸异冰片酯(IBOA)                        10～25％
乙氧基化三羟甲基丙烷三丙烯酸酯(EO-TMPTA)    1～3％
1，4-丁二醇                                 0.1～0.5％
对苯二酚                                    0.05～0.1％
二月桂酸二丁基锡                            0.05～0.1％
二苯甲酮(BP)                                1～2％
1-羟基环己基苯甲酮(184)                     2～3％
2.根据权利要求1所述的紫外光固化聚氨酯丙烯酸酯胶粘剂的制备方法，其特征是按上述配方比备好各原料按如下工艺步骤进行：
(1)向反应釜中注入配方量的聚醚，然后加热至60℃的温度条件下，滴加配方量的甲苯二异氰酸酯和二月桂酸二丁基锡，并开动搅拌使之均匀；
(2)再加入配方量的丙烯酸异冰片酯和对苯二酚，并保温反应0.3～0.7小时；
(3)接着再加入配方量的1，4-丁二醇后，再保温反应0.3～0.7小时；
(4)之后再加入配方量的丙烯酸羟乙酯、丙烯酸羟丙酯和乙氧基化三羟甲基丙烷三丙烯酸酯，并搅拌0.3～0.7小时，至体系均匀透明；
(5)最后降至室温，再加入配方量的二苯甲酮和1-羟基环己基苯甲酮，混合均匀后即得成品。
CN200910060346XA 2009-08-14 2009-08-14 紫外光固化聚氨酯丙烯酸酯胶粘剂及其制备方法 Expired - Fee Related CN101649175B (zh)