CN101643351B - Process for preparing chromatic ceramics - Google Patents
Process for preparing chromatic ceramics Download PDFInfo
- Publication number
- CN101643351B CN101643351B CN2009100236738A CN200910023673A CN101643351B CN 101643351 B CN101643351 B CN 101643351B CN 2009100236738 A CN2009100236738 A CN 2009100236738A CN 200910023673 A CN200910023673 A CN 200910023673A CN 101643351 B CN101643351 B CN 101643351B
- Authority
- CN
- China
- Prior art keywords
- earthenware
- described step
- parts
- soil
- chromatic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention belongs to the technical field of ceramics, in particular to a process for preparing chromatic ceramics. In recent years, cold-toned celadon products can not meet the requirement of modern people because of the enhancement of the living level and the change of the appreciation concept of people and the abundance of market substances. The process for preparing the chromatic ceramics comprises the following steps: (1) proportioning raw materials to prepare glaze materials; (2) preparing slurry molding materials; (3) drawing figures and engraving ; (4) proportioning chromatic slurry to prepare glaze materials; (5) filling the chromatic slurry; (6) carrying out bisque firing to 800 DEG C; (7) applying transparent glaze; and (8) firing and forming; preparing an artwork of the chromatic ceramics according to the technological steps by a certain mixture ratio of the raw materials. The ceramics prepared by the invention has abundant changes of figures and colors which more approach to the effect of a substance, and has hierarchy and good visual effect of three-dimension.
Description
Technical field
The invention belongs to the ceramic technology field, be specifically related to a kind of preparation technology of chromatic ceramics.
Background technology
Pottery is the greatness invention of China name family, and ceramics is consummate especially excellent, and credit state celadon is produced the yellow castle town in Tongchuan, Xing Yutang; Sheng Yusong is destroyed in unit, and last century, the seventies was able to recover; Produce today and prosperity is jewel the most effulgent in the history culture of Tongchuan, credit state celadon glaze colours is superior to dodge Huang in the olive-green; Homophony is green, belongs to cool tone, texturing, stamp etc. under glaze; But along with the development of society and the continuous change of people's aesthetic conceptions, original ceramic color and luster is dim, the dullness that shows, outmoded, old-fashioned and inflexible.
Summary of the invention
The object of the invention provides a kind of pattern color to change abundant, outstanding effect chromatic ceramics step of preparation process.
Technical scheme of the present invention: a kind of preparation technology of chromatic ceramics is characterized in that: the step of preparation process of described chromatic ceramics is:
1., proportioning raw materials is processed the tire material; 2., make pug moulding material;
3., draw pattern, texturing; 4., colored pug proportioning is processed the tire material;
5., insert colored mud; 6., biscuiting to 800 ℃;
7., execute transparent; 8., fire shaping.
Described step raw material 1. forms and weight part is: go up the shop earthenware 35-40 part white mausoleum of earthenware 20-25 part electroceramics mud 10-15 part, level ground, earthenware 20-25 part ocean earthenware 5-10 part of cultivating people of ability.
Described step 4. raw material is formed and weight part is: Dongshan earthenware soil 20-30 part is gone up the shop earthenware soil 20-25 part on the spot sloping earthenware soil 5-10 part Jing Dezhen white mausoleum of mud 10-15 part earthenware 5-10 part feldspar 10-15 part quartz 10-15 part cupric oxide 1-5 part or powder blue 1-5 part or zirconium white 1-5 part.
The texturing of described step in 3. are meant the 1mm-2mm that is that carves the pattern thickness that is plotted in the pug moulding.
Described step is inserted colored mud in 5., is meant that the tire material that 4. step is processed inserts in the groove that 3. step carve.
The described step raw material of executing transparent 7. forms and weight part is: the quartzy 10-15 part of feldspar 35-45 part Dongshan earthenware soil 5-10 Fen ?medicine soil 20-30 part glass 0.5-1 part Fuping glaze stone 20-25 part.
The described step 7. proportion of middle transparent is 1.6.
8. described step is meant with the Sweet natural gas reducing flame burns base to 1300 ℃.
Advantage of the present invention is that the ceramic pattern color change prepared is abundant, effect obviously, have levels, the stereoscopic sensation good visual effect.
Embodiment
Colored credit state celadon is the change to traditional carcass as the term suggests be exactly on credit porcelain green glaze color base plinth, to have increased color such as white, red, yellow, orchid, and glaze colours is that new system forms, and it does basic with existing tire material; Add the material that is easy to the fusion of multicolour raw material, process new carcass, on new carcass, drawing a design with writing brush earlier, go out pattern utilization right angle graduating with cutter; According to design requirements, insert the groove the inside that carves to coloured pugs such as fresh white, red, yellow, orchids, with cutter careful mix flat; The whole one integrated mass of degree and carcass, the transparent credit enamel look of executing development newly after the biscuiting burns till, and various colors promptly appear in kiln discharge; Pattern color changes abundant, and effect is obvious, more approaches effect in kind; And have levels, relief visual effect arranged, and reach the author the theme that will show.
Embodiment 1:
A kind of preparation technology of chromatic ceramics is characterized in that: the step of preparation process of described chromatic ceramics is:
1., proportioning raw materials is processed the tire material; 2., make pug moulding material;
3., draw pattern, texturing; 4., colored pug proportioning is processed the tire material;
5., insert colored mud; 6., biscuiting to 800 ℃;
7., execute transparent; 8., fire shaping.
Described step raw material 1. forms and weight part is: go up cultivate people of ability 5 parts of 10 parts of white mausoleums of 25 parts of electroceramics mud of earthenware, 20 parts of foreign level grounds of earthenware earthenwares of 35 parts of shop earthenwares.
Described step raw material 4. forms and weight part is: 20 parts in Dongshan earthenware soil is gone up 2 parts of 5 parts of 15 parts of cupric oxide of 25 parts of on the spot sloping earthenware soil 5 parts of Jing Dezhen mud, 10 parts of quartz of 10 parts of feldspars of 15 parts of white mausoleums earthenware of shop earthenware soil or 3 parts of powder blues or zirconium whites.
The 3. middle texturing of described step are meant and carve the 1mm-2mm that is plotted in the pattern thickness in the pug moulding.
Described step is inserted colored mud in 5., is meant that the tire material that 4. step is processed inserts in the groove that 3. step carve.
The raw material that described step is executed transparent in 7. forms and weight part is: 10 parts of Dongshan of 40 parts of quartz of feldspar earthenware soil, 5 Fen ?20 parts in 1 part of Fuping of medicine 24 parts of glass of soil glaze stone.
The described step 7. proportion of middle transparent is 1.6.
8. described step is meant with the Sweet natural gas reducing flame burns base to 1300 ℃.
Embodiment 2:
A kind of preparation technology of chromatic ceramics is characterized in that: the step of preparation process of described chromatic ceramics is:
1., proportioning raw materials is processed the tire material; 2., make pug moulding material;
3., draw pattern, texturing; 4., colored pug proportioning is processed the tire material;
5., insert colored mud; 6., biscuiting to 800 ℃;
7., execute transparent; 8., fire shaping.
Described step raw material 1. forms and weight part is: go up cultivate people of ability 5 parts of 15 parts of white mausoleums of 20 parts of electroceramics mud of earthenware, 20 parts of foreign level grounds of earthenware earthenwares of 40 parts of shop earthenwares.
Described step raw material 4. forms and weight part is: 26 parts in Dongshan earthenware soil is gone up 3 parts of 4 parts of 12 parts of cupric oxide of 20 parts of on the spot sloping earthenware soil 10 parts of Jing Dezhen mud, 10 parts of quartz of 8 parts of feldspars of 14 parts of white mausoleums earthenware of shop earthenware soil or 2.5 parts of powder blues or zirconium whites.
The 3. middle texturing of described step are meant and carve the 1mm-2mm that is plotted in the pattern thickness in the pug moulding.
Described step is inserted colored mud in 5., is meant that the tire material that 4. step is processed inserts in the groove that 3. step carve.
The raw material that described step is executed transparent in 7. forms and weight part is: 12 parts of Dongshan of 38 parts of quartz of feldspar earthenware soil, 5 Fen ?20 parts in 1 part of Fuping of medicine 24 parts of glass of soil glaze stone.
The described step 7. proportion of middle transparent is 1.6.
8. described step is meant with the Sweet natural gas reducing flame burns base to 1300 ℃.
Embodiment 3:
A kind of preparation technology of chromatic ceramics is characterized in that: the step of preparation process of described chromatic ceramics is:
1., proportioning raw materials is processed the tire material; 2., make pug moulding material;
3., draw pattern, texturing; 4., colored pug proportioning is processed the tire material;
5., insert colored mud; 6., biscuiting to 800 ℃;
7., execute transparent; 8., fire shaping.
Described step raw material 1. forms and weight part is: go up cultivate people of ability 8 parts of 13 parts of white mausoleums of 23 parts of electroceramics mud of earthenware, 23 parts of foreign level grounds of earthenware earthenwares of 38 parts of shop earthenwares.
Described step raw material 4. forms and weight part is: 25 parts in Dongshan earthenware soil is gone up 5 parts of 5 parts of 13 parts of cupric oxide of 23 parts of on the spot sloping earthenware soil 8 parts of Jing Dezhen mud, 13 parts of quartz of 8 parts of feldspars of 13 parts of white mausoleums earthenware of shop earthenware soil or 5 parts of powder blues or zirconium whites.
The 3. middle texturing of described step are meant and carve the 1mm-2mm that is plotted in the pattern thickness in the pug moulding.
Described step is inserted colored mud in 5., is meant that the tire material that 4. step is processed inserts in the groove that 3. step carve.
The raw material that described step is executed transparent in 7. form and weight part be 13 parts of Dongshan of 42 parts of quartz of feldspar earthenware soil 8 Fen ?23 parts in 0.8 part of Fuping of medicine 28 parts of glass of soil glaze stone.
The described step 7. proportion of middle transparent is 1.6.
8. described step is meant with the Sweet natural gas reducing flame burns base to 1300 ℃.
Claims (1)
1. the preparation technology of a chromatic ceramics, it is characterized in that: the step of preparation process of described chromatic ceramics is:
1., proportioning raw materials is processed the tire material; 2., make pug moulding material;
3., draw pattern, texturing; 4., colored pug proportioning is processed the tire material;
5., insert colored mud; 6., biscuiting to 800 ℃;
7., execute transparent; 8., fire shaping;
Described step raw material 1. forms and weight part is: go up shop earthenware 35-40 part, level ground, the earthenware 20-25 part ocean earthenware 20-25 part of cultivating people of ability, electroceramics mud 10-15 part, white mausoleum earthenware 5-10 part;
Described step raw material 4. forms and weight part is: Dongshan earthenware soil 20-30 part; Last shop earthenware soil 20-25 part; On the spot sloping earthenware soil 5-10 part; Jing Dezhen mud 10-15 part, white mausoleum earthenware 5-10 part, the quartzy 10-15 part cupric oxide 1-5 part of feldspar 10-15 part or powder blue 1-5 part or zirconium white 1-5 part;
The 3. middle texturing of described step are meant and carve the 1mm-2mm that is plotted in the pattern thickness in the pug moulding;
Described step is inserted colored mud in 5., is meant that the tire material that 4. step is processed inserts in the groove that 3. step carve;
The raw material that described step is executed transparent in 7. forms and weight part is feldspar 35-45 part, quartzy 10-15 part, Dongshan earthenware soil 5-10 part, black powder soil 20-30 part, glass 0.5-1 part, Fuping glaze stone 20-25 part;
The described step 7. proportion of middle transparent is 1.6;
8. described step is meant with the Sweet natural gas reducing flame burns base to 1300 ℃.