CN101629657B - 一种保形消防水管及制造方法 - Google Patents
一种保形消防水管及制造方法 Download PDFInfo
- Publication number
- CN101629657B CN101629657B CN2008100405642A CN200810040564A CN101629657B CN 101629657 B CN101629657 B CN 101629657B CN 2008100405642 A CN2008100405642 A CN 2008100405642A CN 200810040564 A CN200810040564 A CN 200810040564A CN 101629657 B CN101629657 B CN 101629657B
- Authority
- CN
- China
- Prior art keywords
- layer
- backing layer
- polyurethane
- shape
- prevention pipe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种保形消防水管,由骨架层和衬里层复合构成,衬里层呈管状,骨架层固定包覆在衬里层的外周,骨架层由纤维编织构成,衬里层由薄壁聚氨酯粘结层和聚氨酯防水层双挤共模构成。一种制造保形消防水管的方法,包括制作衬里层和骨架层的过程,骨架层由经线和纬线编织构成,最后将衬里层穿入骨架层,向衬里层注入压缩空气,将衬里层与骨架层内壁均匀结合,然后向衬里层注入蒸汽加热加压,将骨架层和衬里层粘结在一起。薄壁聚氨酯粘结层和聚氨酯防水层的厚度比为1∶2~1∶3。水管可弯曲变形,最小曲率半径达10厘米,抗水解,耐酸碱,老化寿命达8年以上,使用时出水快,无需展开拉直。骨架层支撑衬里层,***压力大,重量轻,便于运输和使用。
Description
技术领域:
本发明涉及流体输送技术,尤其涉及消防供水装置,特别是一种保形消防水管及制造方法。
背景技术:
消防用保形水管使用时需要承受较高的水压,而在不使用时需要容易存放,以节约空间。现有技术中,消防用保形水管采用橡胶管制作,但是橡胶管不耐高压,易被腐蚀,容易老化,重量偏重,质地偏硬,口径偏小,使用范围和领域受到限制。
发明内容:
本发明的目的在于提供一种保形消防水管,所述的这种保形消防水管要解决现有技术中消防保形水管不耐高压、易被腐蚀、容易老化、重量偏重、质地偏硬以及口径偏小的技术问题。
本发明的这种保形消防水管由骨架层和衬里层复合构成,其中,所述的衬里层呈管状,所述的骨架层固定包覆在衬里层的外周,骨架层由纤维编织构成,所述的纤维是合股涤纶纱、聚酯单丝和喷流长丝,衬里层由薄壁聚氨酯粘结层和聚氨酯防水层双挤共模构成。
进一步的,所述的骨架层由经线和纬线编织构成,所述的经线是合股涤纶纱,所述的纬线是聚酯单丝和喷流长丝。
进一步的,所述的薄壁聚氨酯粘结层和聚氨酯防水层的厚度比为1∶2~1∶3。
进一步的,所述的薄壁聚氨酯粘结层的厚度为0.1~0.12mm,聚氨酯防水层的厚度为0.25~0.30mm。
本发明还提供了一种制造上述保形消防水管的方法,所述的方法中包括一个制作衬里层的过程和一个制作骨架层的过程,其中,在所述的制作 衬里层的过程中,首先采用无色透明的聚氨酯颗粒制作软管备料,薄壁聚氨酯粘结层的材料牌号为T-6075N,聚氨酯防水层的材料牌号为T-8190AN,其中,牌号为T-6075N的材料流动点温度为120~125℃,牌号为T-8190AN的材料流动点温度为170~185℃,然后形成聚氨酯防水层的聚氨酯颗粒中加入2%的色母料,色母料的牌号E5744L,并将其拌匀,之后将挤出机预热2~3小时,设定预热温度比成形温度高10~20℃,最后通过双挤共模方法在薄壁聚氨酯粘结层和聚氨酯防水层各自形成膜的状态下相互合成,并启动动力装置,调整温度至成形温度,所述的成形温度在120~180℃之间,然后启动牵引装置,将粘结层和防水层粘合在一起,在所述的制作骨架层的过程中,将合股涤纶纱作为经线,将聚酯单丝和喷流长丝作为纬线,通过圆织机编织成管状,所述的合股涤纶纱采用SE20/6股涤纶纱,所述的纬线采用一根直径为1.3mm的聚酯单丝和一根AJY1111T/4股喷流长丝,在制作衬里层的过程和制作骨架层的过程完成之后,将衬里层穿入骨架层,向衬里层注入压缩空气,将衬里层与骨架层内壁均匀结合,然后向衬里层注入蒸汽,蒸汽压力控制在0.18~0.20Mpa,有效时间为2分钟,将骨架层和衬里层粘结在一起。
本发明的工作原理是:水管可弯曲变形,在弯曲时的最小曲率半径可达10厘米,抗水解,耐酸碱,老化寿命可达8年以上,使用时手感舒适,出水快,无需将其展开拉直,一个能提起20公斤力的人就可单人使用。骨架层给衬里层提供强度,其***压力可达6Mpa以上,同时减轻重量,每米的保形消防水管长度重量不超过250克或者160克。
本发明和已有技术相对比,其效果是积极和明显的。本发明利用骨架层和衬里层复合构成消防保形水管,骨架层由纤维编织构成,固定包覆在衬里层的外周,起到支撑作用,衬里层由薄壁聚氨酯粘结层和聚氨酯防水层双挤共模构成,抗水解,耐酸碱,老化寿命可达8年以上,使用时手感舒适,无需将其展开拉直,出水快,同时,重量轻,便于运输使用。
附图说明
图1是本发明的一个实施例中局部管壁的剖面结构示意图。
图2是本发明的另一个实施例中局部管壁的剖面结构示意图。
具体实施方式
实施例1:
如图1所示,本发明的保形消防水管由骨架层1和衬里层2复合构成,其中,所述的衬里层2呈管状,所述的骨架层1固定包覆在衬里层2的外周,骨架层1由纤维编织构成,衬里层2由薄壁聚氨酯粘结层和聚氨酯防水层双挤共模构成。
进一步的,所述的骨架层1由经线13和纬线11、纬线12编织构成。
进一步的,所述的薄壁聚氨酯粘结层和聚氨酯防水层的厚度比为1:2~1∶3。
进一步的,所述的薄壁聚氨酯粘结层的厚度为0.1~0.12mm,聚氨酯防水层的厚度为0.25~0.30mm。
进一步的,所述的经线13是合股涤纶纱,所述的纬线11喷流长丝,所述的纬线12是聚酯单丝。
本实施例的工作原理是:水管可弯曲变形,在弯曲时的最小曲率半径可达10厘米,抗水解,耐酸碱,老化寿命可达8年以上,使用时手感舒适,出水快,无需将其展开拉直,一个能提起20公斤力的人就可单人使用。骨架层1给衬里层2提供强度,其***压力可达6Mpa以上,同时减轻重量,每米的保形消防水管长度重量不超过250克或者160克。
具体的,本发明的保形消防水管可通过以下方法制作:
制作衬里层2:
1.制作软管备料:采用无色透明的聚氨酯颗粒,粘结层牌号T-6075N,防水层牌号T-8190AN,其中,粘结层牌号T-6075N的流动点温度为120~125℃,防水层牌号T-8190AN的流动点温度为170~185℃;
2.添加材料:在防水层聚氨酯颗粒中加入2%的色母料,牌号E5744L,并将其拌匀;
3.挤出机预热:挤出机在开机前预热2~3小时,其设定温度比成形温度高10~20℃;
4.双挤共模成形:通过双挤共模在各自形成膜的状态下相互合成,启动动力装置,调整温度至成形温度,原料成形温度在120~180℃之间,然后启动牵引装置,粘结层和防水层粘合在一起.
制作骨架层1:
1.骨架层1由合股涤纶纱作为经线13,由聚酯单丝和喷流长丝作为纬线11通过圆织机编织而成1#保形管,其合股涤纶纱用SE20/6股涤纶纱,纬线11一根用直径Φ1.3mm聚酯单丝,另一根用AJY1111T/4股喷流长丝;
2.编织:将合股涤纶纱作为经线,将聚酯单丝和喷流长丝作为纬线,通过圆织机编织成管状,然后将其牵引出来;
然后,将衬里层2穿入骨架层1;向衬里层2注入压缩空气,使衬里层2与骨架层1内壁均匀结合,然后向衬里层2注入蒸汽,蒸汽压力控制在0.18~0.20Mpa,有效时间为2分钟,使骨架层1和衬里层2紧密粘结在一起。
实施例2:
如图2所示,骨架层1由AJY1111T/2股蓝色喷流长丝14作为经线13、两根直径Φ1.0mm聚酯单丝15作为纬线11,通过圆织机编织而成。
Claims (5)
1.一种保形消防水管,由骨架层和衬里层复合构成,其特征在于:所述的衬里层呈管状,所述的骨架层固定包覆在衬里层的外周,骨架层由纤维编织构成,所述的纤维是合股涤纶纱、聚酯单丝和喷流长丝,衬里层由薄壁聚氨酯粘结层和聚氨酯防水层双挤共模构成。
2.如权利要求1所述的保形消防水管,其特征在于:所述的骨架层由经线和纬线编织构成,所述的经线是合股涤纶纱,所述的纬线是聚酯单丝和喷流长丝。
3.如权利要求1所述的保形消防水管,其特征在于:所述的薄壁聚氨酯粘结层和聚氨酯防水层的厚度比为1∶2~1∶3。
4.如权利要求1所述的保形消防水管,其特征在于:所述的薄壁聚氨酯粘结层的厚度为0.1~0.12mm,聚氨酯防水层的厚度为0.25~0.30mm。
5.一种制造如权利要求1所述的保形消防水管的方法,包括一个制作衬里层的过程和一个制作骨架层的过程,其特征在于:在所述的制作衬里层的过程中,首先采用无色透明的聚氨酯颗粒制作软管备料,薄壁聚氨酯粘结层的材料牌号为T-6075N,聚氨酯防水层的材料牌号为T-8190AN,其中,牌号为T-6075N的材料流动点温度为120~125℃,牌号为T-8190AN的材料流动点温度为170~185℃,然后形成聚氨酯防水层的聚氨酯颗粒中加入2%的色母料,色母料的牌号E5744L,并将其拌匀,之后将挤出机预热2~3小时,设定预热温度比成形温度高10~20℃,最后通过双挤共模方法在薄壁聚氨酯粘结层和聚氨酯防水层各自形成膜的状态下相互合成,并启动动力装置,调整温度至成形温度,所述的成形温度在120~180℃之间,然后启动牵引装置,将粘结层和防水层粘合在一起,在所述的制作骨架层的过程中,将合股涤纶纱作为经线,将聚酯单丝和喷流长丝作为纬线,通过圆织机编织成管状,所述的合股涤纶纱采用SE20/6股涤纶纱,所述的纬线采用一根直径为1.3mm的聚酯 单丝和一根AJY1111T/4股喷流长丝,在制作衬里层的过程和制作骨架层的过程完成之后,将衬里层穿入骨架层,向衬里层注入压缩空气,将衬里层与骨架层内壁均匀结合,然后向衬里层注入蒸汽,蒸汽压力控制在0.18~0.20Mpa,有效时间为2分钟,将骨架层和衬里层粘结在一起。