CN101481465B - 一种高气温适应的破碎机用塑性填料 - Google Patents
一种高气温适应的破碎机用塑性填料 Download PDFInfo
- Publication number
- CN101481465B CN101481465B CN2008100100860A CN200810010086A CN101481465B CN 101481465 B CN101481465 B CN 101481465B CN 2008100100860 A CN2008100100860 A CN 2008100100860A CN 200810010086 A CN200810010086 A CN 200810010086A CN 101481465 B CN101481465 B CN 101481465B
- Authority
- CN
- China
- Prior art keywords
- crusher
- mixed solvent
- plastic filler
- high temperature
- ethylene glycol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明属于化工技术领域，涉及一种高气温适应的破碎机用塑性备衬。其特征在于：在塑性备衬双组分配方中，改变树脂的混合溶剂：选择乙二醇，二乙二醇，环己酮，丁基溶纤剂，邻苯二甲酸二丁酯，醋酸正戊酯和醋酸丁酯中三种或三种以上的组合作为混合溶剂；树脂溶液是环氧树脂，混合溶剂，增强剂，增韧剂按一定配比混合均匀的稳定粘稠流体；并与固化剂体系一起组成塑性填料。本发明一种高气温适应的破碎机用塑性填料，可在35℃气温下在破碎机衬板维护中应用，无硬泡产生，满足和保证了破碎机夏季更换维护的要求。
Description
技术领域
本发明属于化工技术领域，涉及一种多组份树脂浇注体，应用在采、选矿生产中作破碎机衬板，特别涉及一种高气温适应的破碎机用塑性填料。
背景技术
目前，国内在采、选矿的破碎作业中，为使破碎机定锥与支架间和动锥与锥体间紧密结合，必须浇注备衬，其形式主要有：一是在空腔中灌注水泥、无机粘结剂和水的混合物；在浇注前将其混合均匀自流灌入，养生达强后进行使用；二是铅锌合金浇注；首先将合金用加热炉和坩埚熔化，在可操作时间内用镏子将熔融的合金导入空腔；三是塑性填料浇注；在浇注前将塑性填料的双组分混合均匀倒入空腔，塑性填料固化达强后即可使用。第一种方法成本极低，但备衬强度低、收缩率大、无法二次浇注等无法满足新式破碎机生产需要，第二种灌注铅锌合金耗能大成本高，污染环境，操作危险性大；第三种塑性填料因成本，操作，能耗，安全等优势正逐步替代铅锌合金。
塑性填料在破碎机上的应用于保护支架和锥体，并使衬板与之紧密结合，是破碎机的主要备衬方法。目前，在矿山领域应用的塑性填料主要由树脂液态的主剂和相应的固化剂体系构成在两者混均后，浇入空腔使之固化，进而达到紧密结合衬板与支架式锥体的作用。在实际生产中基本能够满足破碎机作业要求，但其在温度适应方面存在不足，主要缺点在夏季高气温条件下，多出现发泡现象，在浇注体内留有大量气泡，使浇注体成硬泡沫状，大大降低了浇注体强度，收缩率也加大无法满足使衬板与支架式锥体紧密结合的要求。
发明内容
本发明克服了上述存在的缺陷，目的是为解决在夏季高气温条件下塑性备衬发泡使浇注体呈硬泡状，危害破碎机使用的问题，提供一种高气温适应的破碎机用塑性填料。
本发明一种高气温适应的破碎机用塑性填料内容简述：
本发明一种高气温适应的破碎机用塑性填料，其特征在于：在塑性填料双组分配方中，选择乙二醇，二乙二醇，环己酮，丁基溶纤剂，邻苯二甲酸二丁酯，醋酸正戊酯和醋酸丁酯中三种或三种以上的组合作为混合溶剂。
所述混合溶剂的原料配比是：混合溶剂每100份中：乙二醇7-10份、醋酸正戊酯63-75份、邻苯二甲酸二丁酯2-3份、乙酸正丁酯10-15份。
所述混合溶剂的原料配比是：混合溶剂每100份中：二乙二醇3-5份、醋酸丁酯35-40份、邻苯二甲酸二丁酯2-3份、丁基溶纤剂30-55份、环己酮10-15份。
所述混合溶剂的原料配比是：混合溶剂每100份中：环己酮20-30份、乙二醇5份、醋酸正戊酯65-75份。
本发明一种高气温适应的破碎机用塑性填料，可在35℃气温下在破碎机衬板维护中应用，无硬泡产生，满足和保证了破碎机夏季更换维护的要求。
具体实施方式
本发明一种高气温适应的破碎机用塑性填料是这样实现的，下面做具体说明。
在塑性填料双组分配方中本发明改变树脂的混合溶剂：
根据挥发度和沸点选择溶剂，大大减少塑性填料中易挥发物质和低沸点物质含量：本发明选择乙二醇，二乙二醇，环己酮，丁基溶纤剂，邻苯二甲酸二丁酯，醋酸正戊酯和醋酸丁酯中三种或三种以上的组合作为混合溶剂。
本发明确立的双组分体系中没有沸点低于130℃的物质，完全适应高气温条件下浇注需要，是性能良好的一种塑性填料。
本发明中塑性填料的双组分是指：
树脂溶液是指环氧树脂，混合溶剂，增强剂，增韧剂按一定配比混合均匀的稳定粘稠流体。
固化剂体系：
通过提前释热和品种选择使塑性备衬在浇注时温升适当，无可沸物质释出的目的，从而阻止了硬泡状的发生。
使用合成胺类固化剂和树脂在混合溶剂中恒温予反应并用乙二醇稀释至一定粘度。
实施例1
选择的原料配比是：
环氧树脂或改性环氧树脂100份
混合溶剂10-15份
增强剂130-170份
增韧剂1-2份
固化剂10-20份
其中：混合溶剂每100份中：乙二醇7-10份、醋酸正戊酯63-75份、邻苯二甲酸二丁酯2-3份、乙酸正丁酯10-15份。
实施例2
选择的原料配比是：
环氧树脂或改性环氧树脂100份
混合溶剂10-15份
增强剂130-170份
增韧剂1-2份
固化剂10-20份
混合溶剂每100份中：二乙二醇3-5份、醋酸丁酯35-40份、邻苯二甲酸二丁酯2-3份、丁基溶纤剂30-55份、环己酮10-15份。
实施例3
选择的原料配比是：
环氧树脂或改性环氧树脂100份
混合溶剂10-15份
增强剂130-170份
增韧剂1-2份
固化剂10-20份
混合溶剂原料配比是：混合溶剂每100份中：环己酮20-30份、乙二醇5份、醋酸正戊酯65-75份。
Claims (4)
1.一种高气温适应的破碎机用塑性填料，其特征在于：在塑性填料双组分配方中，选择乙二醇，二乙二醇，环己酮，丁基溶纤剂，邻苯二甲酸二丁酯，醋酸正戊酯和醋酸丁酯中三种以上的组合作为混合溶剂；
塑性填料的双组分是指：
树脂溶液：是指环氧树脂，混合溶剂，增强剂，增韧剂按一定配比混合均匀的稳定粘稠流体；
固化剂体系。
2.根据权利要求1所述的高气温适应的破碎机用塑性填料，其特征在于：所述混合溶剂的原料配比是：混合溶剂每100份中：乙二醇7-10份、醋酸正戊酯63-75份、邻苯二甲酸二丁酯2-3份、乙酸正丁酯10-15份。
3.根据权利要求1所述的高气温适应的破碎机用塑性填料，其特征在于：所述混合溶剂的原料配比是：混合溶剂每100份中：二乙二醇3-5份、醋酸丁酯35-40份、邻苯二甲酸二丁酯2-3份、丁基溶纤剂30-55份、环己酮10-15份。
4.根据权利要求1所述的高气温适应的破碎机用塑性填料，其特征在于：所述混合溶剂的原料配比是：混合溶剂每100份中：环己酮20-30份、乙二醇5份、醋酸正戊酯65-75份。