CN101457015A - Dicyclopentadiene modified unsaturated polyester resin glass fiber reinforcement molding composition - Google Patents
Dicyclopentadiene modified unsaturated polyester resin glass fiber reinforcement molding composition Download PDFInfo
- Publication number
- CN101457015A CN101457015A CNA2009100580171A CN200910058017A CN101457015A CN 101457015 A CN101457015 A CN 101457015A CN A2009100580171 A CNA2009100580171 A CN A2009100580171A CN 200910058017 A CN200910058017 A CN 200910058017A CN 101457015 A CN101457015 A CN 101457015A
- Authority
- CN
- China
- Prior art keywords
- unsaturated polyester
- polyester resin
- parts
- modified unsaturated
- thickening
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a dicyclopentadiene modified unsaturated polyester resin fiberglass enhancement mode plastic combination which is characterized in that the composition by weight is that: the unsaturated polyester resin is 18 to 23 portions, 666D polystyrene is 7 to 10 portions, the aluminum hydroxide is 40 to 50 portions, the ankali-free and twist-free fiberglass roving is 21 to 30 portions, the peroxide t-butyl perbenzoate is 0.2 to 0.4 portion, the zinc stearate is 1 to 1.5 portions, the pigment paste is 2 to 4 portions and the active magnesium oxide is 0.2 to 0.4 portion. The unsaturated polyester resin is modified unsaturated polyester resin where the dicyclopentadiene can be thickened or the thickenable dicyclopentadiene modified unsaturated polyester resin and the thickenable isophthalic or the o-benzene typed polyester resin are mixed in a weight proportion of 9:1 to 9. After being hot press molded, the combination of the invention has the characteristics of high surface hardness, low shrinking percentage and high mechanical strength, which can be used for being pressed and molded into wall plates of train coach bodies, sanitary ware and insulating barriers.
Description
Technical field
The invention belongs to dicyclic pentylene modified unsaturated polyester resin is the glass fibre reinforced mould plastic composition of matrix resin, relates to a kind of dicyclopentadiene modified unsaturated polyester resin glass fiber reinforcement molding composition.The unsaturated polyester resin glass fibre reinforced mould plastic composition product of this method preparation is applicable to fields such as the wallboard, sanitary ware, insulating barrier of compression moulding train casing.
Background technology
In the existing unsaturated polyester glass fiber sheet molding compound (being called for short SMC), the prescription of unsaturated polyester resin glass fibre reinforced mould plastic generally by the aluminium hydroxide of unsaturated polyester resin, polystyrene, particle diameter 1~23 μ m or/and the non-twist fibre glass roving of alkali-free of lime carbonate, length 25~50mm, peroxidized t-butyl perbenzoate, Zinic stearas, pigment paste, activated magnesia etc. form.Fields such as that the product that makes is widely used in is electric, transport facility, building, sanitary ware.But used unsaturated polyester resin was thickening O-phthalic acid type (being called for short adjacent benzene type) unsaturated polyester resin and m-phthalic acid type (abbreviation metaphenylene) unsaturated polyester resin during prescription was formed.Shrinking percentage height after this resinoid solidifies causes the surface hardness of goods low simultaneously, and the mechanical property of goods is relatively poor.The shrinking percentage of common SMC unsaturated polyester resin glass fibre reinforced mould plastic is 0.1~0.5%, and Barcol hardness is lower, below 48, and flexural strength is less than 180MPa.
Reclaim in the byproduct of dicyclopentadiene (dicyclopentadiene is called for short DCPD) for raw gasline steam cracking production ethylene process and make (C5 fraction), price is low.Owing to have performances such as good dry air, erosion resistance, low contractions as starting material synthetic resin, so become the problem that many in recent years production of resins producer competitively develops as starting material production unsaturated polyester resin with dicyclopentadiene with dicyclopentadiene.
The Yang Kai of South China Science ﹠ Engineering University etc. has inquired into various influence factors of dicyclic pentylene modified unsaturated polyester resin synthetic and main technique condition thereof; This resin does not have thickening properties as the matrix resin of hand paste glass reinforced plastic.
China Patent No. ZL96119856.7 disclosed " a kind of preparation method of dicyclic pentylene modified unsaturated polyester resin " provides a kind of method for preparing dicyclic pentylene modified unsaturated polyester resin (DCPD modification UPR) (UPR is a unsaturated polyester resin).The resin that this method makes is water-fast, resistance to chemical corrosion good, but does not possess thickening properties.
Chinese patent application 200510026882.X disclosed " a kind of preparation method of dicyclic pentylene modified unsaturated polyester resin " provides the preparation method of a kind of dicyclic pentylene modified unsaturated polyester resin (DCPD modification UPR).The advantage of the resin that this method makes is that goods have more excellent thermotolerance, is higher than the state of the art of currently available products.But this resin is also stuck with paste the matrix resin of glass reinforced plastic as hand, do not have thickening properties equally.
Summary of the invention
Purpose of the present invention is intended to overcome above-mentioned deficiency of the prior art, and a kind of dicyclopentadiene modified unsaturated polyester resin glass fiber reinforcement molding composition is provided; This unsaturated polyester resin glass fibre reinforced mould plastic composition has that surface hardness height, physical strength height, shrinking percentage are low, characteristics such as cost is low, and product is applicable to fields such as the wallboard, sanitary ware, insulating barrier of compression moulding train casing.
Content of the present invention is: a kind of dicyclopentadiene modified unsaturated polyester resin glass fiber reinforcement molding composition, it is characterized in that weight consists of: 18~23 parts of unsaturated polyester resins, 7~10 parts of 666D polystyrene, particle diameter is 40~50 parts in the aluminium hydroxide of 8-15 μ m, length is 21~30 parts of the non-twist fibre glass rovings of the alkali-free of 25mm, 0.2~0.4 part of peroxidized t-butyl perbenzoate, 1~1.5 part of Zinic stearas, 2~4 parts of pigment paste, and 0.2~0.4 part of activated magnesia;
But described unsaturated polyester resin is thickening dicyclic pentylene modified unsaturated polyester resin (adopting Chinese patent application numbers 200710051048.5, publication number CN101230131A to provide " preparation method of thickenable dicyclopentadiene unsaturated polyester resin " to make), but but or thickening dicyclic pentylene modified unsaturated polyester resin and other common thickening metaphenylene or adjacent benzene type unsaturated polyester resin mix the hybrid resin that forms with the weight proportion of 9:1~9, to realize thickening properties.
In the content of the present invention: but described pigment paste is to get any one or any two kinds of different ratios toners in titanium dioxide, carbon black, red iron oxide, the phthalocyanine blue, add the mixture that an amount of thickening metaphenylene or adjacent benzene type unsaturated polyester resin form through grinding again, it is formed and the same prior art of preparation method, can select as required.
Composition described in the content of the present invention is put in slaking 24-48h promptly makes the moulding compound product between constant temperature 42-50 ℃ slaking.
Compared with prior art, the present invention has following characteristics and beneficial effect:
(1) but the present invention is that to adopt with the thickening dicyclic pentylene modified unsaturated polyester resin be the glass fibre reinforced mould plastic composition of matrix resin, its thickening property is good, constant product quality, technology is simple, is easy to industry and enlarges and produce, and is practical; Product is applicable to that compression moulding is wallboard, sanitary ware, electric insulation dividing plate of train casing etc.;
(2) molding compound composite of the present invention has the surface hardness height after hot-forming, and shrinking percentage is low, the characteristics that physical strength is high; Its Barcol hardness is generally between 50~57; Shrinking percentage generally can be controlled between 0.010%~0034%, and flexural strength is between 176~282MPa;
(3) molding compound composite of the present invention adopts the industrial by-products dicyclic pentylene modified unsaturated polyester resin to make starting material, and price is lower, help reducing cost, but than similar thickening unsaturated polyester resin cost low about 8%;
Embodiment
The following examples of the present invention are only as the further specifying of content of the present invention, can not be as scope perhaps in the qualification of the present invention.The invention will be further described below in conjunction with embodiment.
Embodiment 1:
A kind of dicyclic pentylene modified glass fiber reinforced unsaturated polyester plastic composition, be made up of by weight following material: dicyclic pentylene modified unsaturated polyester resin (adopts Chinese patent application numbers 200710051048.5, " preparation method of thickenable dicyclopentadiene unsaturated polyester resin " that publication number CN101230131A provides makes, 18 parts afterwards together), 7 parts of 666D polystyrene, 50 parts in the aluminium hydroxide of particle diameter 8 μ m, 21 parts of the non-twist fibre glass rovings of the alkali-free of length 25mm, 0.2 part of peroxidized t-butyl perbenzoate, 1 part of Zinic stearas, 2.6 parts of pigment paste, 0.2 part of activated magnesia.Said composition is put in slaking 48h promptly makes the moulding compound product between the slaking of 45 ℃ of constant temperature.Product shrinking percentage 0.012%, the Barcol hardness 54 of goods, flexural strength 194MPa.
Embodiment 2:
A kind of dicyclic pentylene modified glass fiber reinforced unsaturated polyester plastic composition, form by weight by following material: 20 parts of dicyclic pentylene modified unsaturated polyester resins, 8 parts of 666D polystyrene, 46 parts in particle diameter 8 μ m aluminium hydroxides, 23 parts of the non-twist fibre glass rovings of length 25mm alkali-free, 0.25 part of peroxidized t-butyl perbenzoate, 1 part of Zinic stearas, 2.5 parts of pigment paste, 0.25 part of activated magnesia.Said composition is put in slaking 48h promptly makes the moulding compound product between the slaking of 45 ℃ of constant temperature.Product shrinking percentage 0.014%, the Barcol hardness 56 of goods, flexural strength 227MPa.
Embodiment 3:
A kind of dicyclic pentylene modified glass fiber reinforced unsaturated polyester plastic composition, form by weight by following material: 23 parts of dicyclic pentylene modified unsaturated polyester resins, 10 parts of 666D polystyrene, 42 parts in particle diameter 8 μ m aluminium hydroxides, 27 parts of the non-twist fibre glass rovings of length 25mm alkali-free, 0.4 part of peroxidized t-butyl perbenzoate, 1 part of Zinic stearas, 2.2 parts of pigment paste, 0.4 part of activated magnesia.Said composition is put in slaking 48h promptly makes the moulding compound product between the slaking of 45 ℃ of constant temperature.Product shrinking percentage 0.017%, the Barcol hardness 55 of goods, flexural strength 243MPa.
Embodiment 4:
A kind of dicyclic pentylene modified glass fiber reinforced unsaturated polyester plastic composition, form by weight by following material: 18 parts of dicyclic pentylene modified unsaturated polyester resins, 7 parts of 666D polystyrene, 40 parts in particle diameter 8 μ m aluminium hydroxides, 30 parts of the non-twist fibre glass rovings of length 25mm alkali-free, 0.2 part of peroxidized t-butyl perbenzoate, 1.5 parts of Zinic stearass, 3 parts of pigment paste, 0.2 part of activated magnesia.Said composition is put in slaking 48h promptly makes the moulding compound product between the slaking of 45 ℃ of constant temperature.Product shrinking percentage 0.010%, the Barcol hardness 57 of goods, flexural strength 282MPa.
Embodiment 5:
A kind of dicyclic pentylene modified glass fiber reinforced unsaturated polyester plastic composition, form by weight by following material: 18 parts of dicyclic pentylene modified unsaturated polyester resins, but 2 parts of thickening metaphenylene unsaturated polyester resins, 8 parts of 666D polystyrene, 45 parts in particle diameter 8 μ m aluminium hydroxides, 22 parts of the non-twist fibre glass rovings of length 25mm alkali-free, 0.3 part of peroxidized t-butyl perbenzoate, 1.4 parts of Zinic stearass, 4 parts of pigment paste, 0.3 part of activated magnesia.Said composition is put in slaking 48h promptly makes the moulding compound product between the slaking of 45 ℃ of constant temperature.Product shrinking percentage 0.016%, the Barcol hardness 53 of goods, flexural strength 197MPa.
Embodiment 6:
A kind of dicyclic pentylene modified glass fiber reinforced unsaturated polyester plastic composition, be made up of by weight following material: dicyclic pentylene modified unsaturated polyester resin reduces to 15 parts, but the thickening metaphenylene unsaturated polyester resin increases to 5 parts, 8 parts of 666D polystyrene, 45 parts in particle diameter 8 μ m aluminium hydroxides, 22 parts of the non-twist fibre glass rovings of length 25mm alkali-free, 0.3 part of peroxidized t-butyl perbenzoate, 1.4 parts of Zinic stearass, 4 parts of pigment paste, 0.3 part of activated magnesia.Said composition is put in slaking 48h promptly makes the moulding compound product between the slaking of 45 ℃ of constant temperature.Product shrinking percentage 0.021%, the Barcol hardness 52 of goods, flexural strength 193MPa.
Embodiment 7:
Dicyclic pentylene modified unsaturated polyester resin is reduced to 10 parts, but the thickening metaphenylene unsaturated polyester resin increases to 10 parts, other is with embodiment 5 (summary).Product shrinking percentage 0.026%, the Barcol hardness 51 of goods, flexural strength 184MPa.
Embodiment 8:
But but the thickening metaphenylene unsaturated polyester resin is changed to the adjacent benzene type of thickening unsaturated polyester resin, other is with embodiment 5 (summary).Product shrinking percentage 0.017%, the Barcol hardness 53 of goods, flexural strength 186MPa.
Embodiment 9:
But but the thickening metaphenylene unsaturated polyester resin is changed to the adjacent benzene type of thickening unsaturated polyester resin, other is with embodiment 7 (summary).Product shrinking percentage 0.024%, the Barcol hardness 50 of goods, flexural strength 176MPa.
In the various embodiments described above: described dicyclic pentylene modified unsaturated polyester resin adopts Chinese patent application numbers 200710051048.5, " preparation method of thickenable dicyclopentadiene unsaturated polyester resin " that publication number CN101230131A provides makes, but the manufacturer of thickening metaphenylene unsaturated polyester resin is Changzhou China resin company limited of section etc., but the manufacturer of the adjacent benzene type of thickening unsaturated polyester resin is Nanjing, Nanjing DSM company limited etc., the manufacturer of 666D polystyrene is a Beijing Yanshan Petrochemical Company etc., the manufacturer of aluminium hydroxide is Central Region company of Chalco group etc., the manufacturer of the non-twist fibre glass roving of alkali-free is a Chongqing Polycomp International Co., Ltd etc., the manufacturer of peroxidized t-butyl perbenzoate is auxiliary reagent factory, Lanzhou etc., the manufacturer of Zinic stearas is Rui Feng chemical plant, Shijiazhuang etc., and the manufacturer of activated magnesia produces etc. for Israel.
In the various embodiments described above: but described pigment paste can be to get any one or any two kinds of different ratios toners in titanium dioxide, carbon black, red iron oxide, the phthalocyanine blue, add the mixture that an amount of thickening metaphenylene or adjacent benzene type unsaturated polyester resin form through grinding again, it is formed and the same prior art of preparation method, can select as required.
In the various embodiments described above: composition can be placed on that slaking 24-48h promptly makes the moulding compound product between constant temperature 42-50 ℃ slaking.
The invention is not restricted to the foregoing description, content of the present invention is described all can implement and have described good result.
Claims (2)
1, a kind of dicyclopentadiene modified unsaturated polyester resin glass fiber reinforcement molding composition, it is characterized in that weight consists of: 18~23 parts of unsaturated polyester resins, 7~10 parts of 666D polystyrene, particle diameter is 40~50 parts in the aluminium hydroxide of 8-15 μ m, length is 21~30 parts of the non-twist fibre glass rovings of the alkali-free of 25mm, 0.2~0.4 part of peroxidized t-butyl perbenzoate, 1~1.5 part of Zinic stearas, 2~4 parts of pigment paste, and 0.2~0.4 part of activated magnesia;
But described unsaturated polyester resin is the thickening dicyclic pentylene modified unsaturated polyester resin, but but or thickening dicyclic pentylene modified unsaturated polyester resin and thickening metaphenylene or adjacent benzene type unsaturated polyester resin mix the hybrid resin that forms with the weight proportion of 9:1~9.
2,, it is characterized in that by the described dicyclopentadiene modified unsaturated polyester resin glass fiber reinforcement molding composition of claim 1: but described pigment paste be get in titanium dioxide, carbon black, red iron oxide, the phthalocyanine blue one or both, add the mixture that thickening metaphenylene or adjacent benzene type unsaturated polyester resin form through grinding again.