CN101440197A - 一种玻璃纤维增强聚对苯二甲酸丁二酯组合物 - Google Patents
一种玻璃纤维增强聚对苯二甲酸丁二酯组合物 Download PDFInfo
- Publication number
- CN101440197A CN101440197A CNA2007101705565A CN200710170556A CN101440197A CN 101440197 A CN101440197 A CN 101440197A CN A2007101705565 A CNA2007101705565 A CN A2007101705565A CN 200710170556 A CN200710170556 A CN 200710170556A CN 101440197 A CN101440197 A CN 101440197A
- Authority
- CN
- China
- Prior art keywords
- raw materials
- fiber reinforced
- glass fiber
- polybutylene terephthalate
- glass fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种玻璃纤维增强热塑性聚对苯二甲酸丁二酯组合物,其特征在于,由以下重量百分比的原料制成:聚对苯二甲酸丁二酯(PBT)58-83%、玻璃纤维15-40%、相容剂1-8%、抗氧剂0.1-1%、润滑剂0.1-1%。其制备方法为:按重量百分比称取原料;除玻璃纤维外将其他原料放入高混机中混合;出料;将混合的原料加玻璃纤维放入螺杆机中挤出造粒。本发明的优点是玻璃纤维增强热塑性聚对苯二甲酸丁二酯材料,从而大大提高材料的刚性、强度和尺寸稳定性,且明显提高材料的冲击性能。
Description
技术领域
本发明涉及一种玻璃纤维增强聚对苯二甲酸丁二酯组合物,更具体地涉及一种能显著提高PBT刚性、强度和冲击强度的复合材料,属于改性聚酯技术领域。
背景技术
聚对苯二甲酸丁二酯PBT具有优良的机械性能、耐老化性能、优良的电气性能等,被广泛用于电子电器、汽车、机械设备、精密仪器的零部件,以取代金属制件及热固性树脂制件,由于PBT自身在高负载下耐热性不够,其力学性能不稳定。
发明内容
本发明的目的在于提供一种具有超高耐热,低翘曲,极高的抗冲击性能、高强度、优良的耐化学性、尺寸稳定性好、制品表面光洁的高耐热增强聚对苯二甲酸丁二酯组合物。
为实现以上目的,本发明的技术方案是提供一种高耐热增强聚对苯二甲酸丁二酯组合物,其特征在于,它由以下重量百分比的原料制成:
聚对苯二甲酸丁二酯PBT 58-83%、
玻璃纤维 15-40%、
抗氧剂 0.1-1%、
润滑剂 0.1-1%、
相容剂 1-8%。
所述的聚对苯二甲酸丁二酯相对密度为1.3-1.35g/cm3,熔点220-240℃,熔体粘度为0.6-0.9;所述的玻璃纤维为无碱玻璃纤维,其表面经硅烷偶联剂处理;所述的抗氧剂为受阻酚类1010和亚磷酸酯类抗氧剂168复配;所述的润滑剂为MB-4.所述的相容增韧剂为乙烯-丙烯酸酯接枝甲基丙烯酸缩水甘油脂,其熔融指数5-10g/10min,熔点为60℃。
一种玻璃纤维增强聚对苯二甲酸丁二酯组合物的制备方法,其特征在于,采用一步法工艺,其方法如下:
第一步.按重量百分配比秤取原料;
第二步.除玻璃纤维,将其他原料放入高混机中混合2-5分钟;
第三步.出料;
第四步.将混合的原料加玻璃纤维放入螺杆机中挤出造粒,螺杆机的转速为180—600转/分,温度为200-260℃。
聚对苯二甲酸丁二酯相对密度为1.3-1.35g/cm3,熔点为220-240℃,熔体粘度为0.6-0.9,纯的PBT在1.82MPa的载荷下热变形温度只有95℃。
无碱玻璃纤维自身的取向方向有很高的强度,经偶联剂表面处理,与PBT树脂有很好的相容性,极大地提高PBT树脂的强度、尺寸稳定性和耐热性能。
共聚聚酯具有高度透明,抗冲击性能优异,具有很高刚度、硬度和良好的韧性,甚至在低温也保持应有的韧性。
本发明采用PBT为基体树脂,制得一种高耐热增强聚对苯二甲酸丁二酯组合物,获得了一种高力学性能、高耐热、低翘曲的PBT复合材料。
本发明的优点是具有耐热性、极低的翘曲、极高的冲击性能、高强度、优良的耐化学性、尺寸稳定性好、制品表面光洁。
具体实施方案
下面结合实施例,对本发明作进一步详细说明:
玻璃纤维选用无碱玻璃纤维,抗氧剂选用168/1010,;润滑剂选用乙烯-丙烯酸酯接枝甲基丙烯酸缩水甘油脂,相容增韧剂为乙烯-丙烯酸酯接枝甲基丙烯酸缩水甘油脂。
实施例1和2配比1-2(表1)
原料名称 配比1(wt%) 配比2(wt%)
PBT 75 63
玻璃纤维 20 30
相容剂 4 6
抗氧剂(2:1) 0.6 0.6
润滑剂 0.4 0.4
按重量百分比秤取原料,除玻璃纤维将其他原料放入高混机中混合4分钟,然后与玻璃纤维一起用螺杆挤出机挤出造粒,螺杆转数在200转/分,加工温度为:(单位℃)
一区 | 二区 | 三区 | 四区 | 五区 | 六区 | 七区 | 八区 | 九区 | 十区 |
225 | 230 | 235 | 235 | 235 | 235 | 235 | 235 | 235 | 235 |
根据实施例1、实施例2制得的玻璃纤维增强聚对苯二甲酸丁二酯样品。机械性能依据ASTM测试标准
性能对比(表2)
项目 实施例1 实施例2 PBT
拉伸强度MPa 88.3 98.6 56
弯曲强度MPa 115.7 140.5 89.3
弯曲模量MPa 3801.2 5312.4 3451.2
冲击强度J/M 120.3 140.4 76.2
HDT(1.82MPa) 215 220 95
Claims (6)
1.一种玻璃纤维增强聚对苯二甲酸丁二酯组合物,其特征在于,它由以下重量百分比的原料制成:
聚对苯二甲酸丁二酯 58-83%、
玻璃纤维 15-40%、
抗氧剂 0.1-1%、
润滑剂 0.1-1%、
相容剂 1-8%。
2.根据权利要求1所述的玻璃纤维增强聚对苯二甲酸丁二酯组合物,其特征在于,所述的聚对苯二甲酸丁二酯相对密度为1.3-1.35g/cm3,熔点为220-240℃,熔体粘度为0.6-0.9。
3.根据权利要求1所述的玻璃纤维增强聚对苯二甲酸丁二酯组合物,其特征在于,所述的玻璃纤维为无碱玻璃纤维,其表面经硅烷偶联剂处理。
4.根据权利要求1所述的玻璃纤维增强聚对苯二甲酸丁二酯组合物,其特征在于,所述的的抗氧剂为受阻酚类1010和亚磷酸酯类抗氧剂168复配。
5.根据权利要求1所述的高耐热增强聚对苯二甲酸丁二酯组合物,其特征在于,所述的润滑剂为MB-4.
6.根据权利要求1所述的一种高耐热增强聚对苯二甲酸丁二酯组合物的制备方法,其特征在于,采用一步法工艺,其方法如下:
第一步.按重量百分比比秤取原料;
第二步.除玻璃纤维,将其他原料放入高混机中混合2-5分钟;
第三步.出料;
第四步.将混合的原料加玻璃纤维放入螺杆机中挤出造粒,螺杆机的转速为180—600转/分,温度为200-260℃。