CN101417293A - HRB 400 steel bar production method - Google Patents

HRB 400 steel bar production method Download PDF

Info

Publication number
CN101417293A
CN101417293A CNA2007101763698A CN200710176369A CN101417293A CN 101417293 A CN101417293 A CN 101417293A CN A2007101763698 A CNA2007101763698 A CN A2007101763698A CN 200710176369 A CN200710176369 A CN 200710176369A CN 101417293 A CN101417293 A CN 101417293A
Authority
CN
China
Prior art keywords
rolling
controlled
temperature
production method
reinforcing bar
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2007101763698A
Other languages
Chinese (zh)
Inventor
王全礼
鲁丽燕
周玉丽
张永青
杨雄
李艳平
***
熊万平
刘健
张崴
胡晓宏
刘建明
李睿英
董现春
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shougang Corp
Original Assignee
Shougang Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shougang Corp filed Critical Shougang Corp
Priority to CNA2007101763698A priority Critical patent/CN101417293A/en
Publication of CN101417293A publication Critical patent/CN101417293A/en
Pending legal-status Critical Current

Abstract

The invention relates to a production method of an HRB400 steel bar, and the material of steel bloom is 20MnSi by component optimization. The technical process comprises bessemerizing, argon-blowing refinement, continuous casting, lower-temperature rolling, rolling control among machines and stepping cooling control after rolling; and recovering sections are arranged among cooling sections. The adoption of the technology for producing the HRB400 steel bar, not only can greatly reduce cost, but also can degrade the requirements on the capacity of rolling mills and cooling control equipment among the machines so as to improve the applicability thereof. The product specifications range phi 10-phi40mm, the produced HRB400 steel bar has stable structure property and good welding and anti-quake properties.

Description

A kind of production method of HRB400 reinforcing bar
Technical field
The present invention relates to a kind of production method of HRB400 reinforcing bar, be specially adapted to the method that controlled rolling and controlled cooling is produced the HRB400 reinforcing bar.
Background technology
The national standard " Code for design of concrete structures " that played enforcement on April 1st, 2002 is clearly with the main force reinforcing bar of HRB400 grade reinforcing steel as Chinese reinforced concrete structure, wherein can weld, anti-seismic steel bar not only requires yield strength 〉=400Mpa, tensile strength 〉=570Mpa, but also requiring the actual measurement tensile strength and the ratio σ b/ σ s of actual measurement yield strength to be not less than 1.25, the ratio of reinforcing bar actual measurement yield strength and HRB400 reinforcing bar SMYS 400MPa is not more than 1.30.The production technology of HRB400 grade reinforcing steel mainly is to adopt 20MnSi microalloying (one or more in adding vanadium, niobium, the titanium) at present, production method as the described a kind of HRB400 reinforcing bar of patent application ZL200610081495.0, adopt the Nb microalloying and roll back grading control Nb and separate out process for cooling and produce the HRB400 reinforcing bar, technology comparative maturity and stable, but can increase substantially production cost.
Summary of the invention
The invention provides a kind of production method of HRB400 reinforcing bar, steel billet material composition is 20MnSi, technological process is that converter smelting → ar blowing refining → direct casting → steel billet inspection → heating furnace heating → controlled rolling → rolling the back grading control cools off, start rolling temperature is controlled at 900-1050 ℃, the finish rolling inlet temperature is controlled at 800-950 ℃, finishing temperature is controlled at 900-1000 ℃, roll the back and adopt the two-part grading control type of cooling, go out one cold section temperature and be controlled at 750~850 ℃, go out that cold bed temperature is controlled at 680-750 ℃ on the secondary cooling zone, one is cold, the recovery section that 8-10 rice is arranged between the secondary cooling zone.
The invention provides a kind of production method of HRB400 reinforcing bar, the composition of its steel billet material is controlled at 0.45%≤Ceq≤0.52%.
Adopt the beneficial effect of the production method of a kind of HRB400 reinforcing bar of the present invention:
(1) the present invention does not need to add any microalloy, reduces production costs significantly.
(2) the present invention guarantees that by optimizing composition welding heat affected zone intensity does not descend, and has satisfied the requirement of welding performance and anti-seismic performance.
(3) the present invention adopts lower temperature open rolling, inter-stand cooling technology, omnidistance thinning microstructure is organized homogenising with guaranteeing surface, core, and employing is rolled, and the back is rapid, the also accurate control of classification cooling final cooling temperatures at different levels, not only guaranteed the uniform and stable property of reinforcing bar structure property, and reduced requirement to control-cooling equipment ability between milling train and machine, improved the applicability of this technology.
(4) the present invention takes lower temperature distortion finish to gauge technology, and finish to gauge frame load improves less, and structure property satisfies the requirement of one-level anti-seismic steel bar.
The specific embodiment
Embodiments of the invention, technological process are that converter smelting → ar blowing refining → direct casting → steel billet inspection → heating furnace heating → controlled rolling → rolling the back grading control cools off.Tapping back soft blow argon 15 minutes; Steel billet composition C:0.22%, Si:0.51%, Mn:1.44%, P:0.012%, S:0.010%, Ceq:0.46%; Start rolling temperature 960-980 ℃, the rolling effectively refine austenite crystal grain of lower temperature; 860-870 ℃ of finish rolling inlet temperature, higher final rolling temperature can guarantee that mm finishing mill unit works in the motor load limit of power; Finishing temperature 980-990 ℃, because finishing temperature is higher, cooling control after rolling is very crucial, roll the back and adopt the two-part grading control type of cooling, it is cold that last rolling mill comes out and then to roll back one, and reinforcing bar is in time cooled off, suppress growing up of crystal grain, gone out 770~780 ℃ of one cold section temperature; Go out that cold bed temperature is controlled at 730-740 ℃ on the secondary cooling zone; One, the section of recovery is arranged in the middle of the secondary cooling zone, can reduce the reinforcing bar internal-external temperature difference, improve the inside and outside structural homogenity of reinforcing bar; Roll the back and adopt the grading control process for cooling both to guarantee the cooling target temperature, guaranteed the strength character of reinforcing bar again, avoided rebar surface cold tissue to occur.
The controlled rolling and controlled cooling HRB400 reinforcing bar that the present invention is produced has carried out tension test in enormous quantities, metallographic structure check, impact test, electroslag pressure welding, flash butt welding, overlap welding test, and the result all meets the requirement of relevant criterion.
Composition and performance statistics such as following table 1 in August, 2006 to the 2007 year batch process in May of controlled rolling and controlled cooling HRB400 reinforcing bar.
Table 1. controlled rolling and controlled cooling HRB400 reinforcing bar in August, 2006 to 2007 year production in May statistics
Figure A200710176369D00051
A kind of production method that adopts controlled rolling and controlled cooling to produce the HRB400 reinforcing bar that the present invention relates to is produced the HRB400 reinforcing bar with the Nb microalloying and is compared, and reduces cost of alloy 50-100 unit/ton steel (changing with Nb iron price change).Advantage of the present invention and effect mainly contain following 3 points, and 1, do not add microalloy, significantly reduce production costs; 2, optimize composition and technological design, guarantee to satisfy the requirement of welding and anti-seismic performance; 2, the rolling and post-rolling control cooling process of optimal control guarantees that cold tissue did not appear in rebar surface and performance satisfies under the prerequisite of standard-required, reduces the load of milling equipment as far as possible; 3, solve the specification effect problem; 4, adopt the present invention can produce φ 10~φ 40mm specification HRB400 reinforcing bar.

Claims (2)

1, a kind of production method of HRB400 reinforcing bar, steel billet material composition is 20MnSi, technological process is that converter smelting → ar blowing refining → direct casting → steel billet inspection → heating furnace heating → controlled rolling → rolling the back grading control cools off, it is characterized in that: start rolling temperature 900-1050 ℃, 800-950 ℃ of finish rolling inlet temperature, finishing temperature 900-1000 ℃, roll the back and adopt the two-part grading control type of cooling, go out one cold section temperature and be controlled at 750~850 ℃, go out that cold bed temperature is controlled at 680-750 ℃ on the secondary cooling zone, the recovery section of 8-10 rice is arranged between one cold, the secondary cooling zone.
2, as the production method of claims 1 described a kind of HRB400 reinforcing bar, it is characterized in that: the composition of steel billet material is controlled at 0.45%≤Ceq≤0.52%.
CNA2007101763698A 2007-10-26 2007-10-26 HRB 400 steel bar production method Pending CN101417293A (en)