CN101413083A - 用于压缩机滚动活塞的铸铁材料 - Google Patents

用于压缩机滚动活塞的铸铁材料 Download PDF

Info

Publication number
CN101413083A
CN101413083A CNA2007100599554A CN200710059955A CN101413083A CN 101413083 A CN101413083 A CN 101413083A CN A2007100599554 A CNA2007100599554 A CN A2007100599554A CN 200710059955 A CN200710059955 A CN 200710059955A CN 101413083 A CN101413083 A CN 101413083A
Authority
CN
China
Prior art keywords
rolling piston
cast iron
compressor
percent
iron material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2007100599554A
Other languages
English (en)
Inventor
张余
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LG Electronics Tianjin Appliances Co Ltd
Original Assignee
LG Electronics Tianjin Appliances Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LG Electronics Tianjin Appliances Co Ltd filed Critical LG Electronics Tianjin Appliances Co Ltd
Priority to CNA2007100599554A priority Critical patent/CN101413083A/zh
Publication of CN101413083A publication Critical patent/CN101413083A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种用于压缩机滚动活塞的铸铁材料，各个成分的质量百分比为：碳C为3.0％～3.6％，硅Si为1.8％～2.4％，锰Mn为0.5％～1.0％，磷P为0.1％～0.3％，硫磺S为0.15％以下，铬Cr为0.7％～1.0％，其余为铁Fe。本发明的用于压缩机滚动活塞的铸铁材料的各项性能满足固定的滚动活塞性能指标，同时不添加镍、钼等贵金属，降低了成本。

Description

用于压缩机滚动活塞的铸铁材料
技术领域
本发明涉及压缩机，尤其是以降低成本的用于压缩机滚动活塞的铸铁材料。
背景技术
如图1、2所示，现有技术的封闭型压缩机包括两端封闭的中空圆筒形密封容器1和设置在密封容器1的上边提供压缩驱动力的电动结构，以及设置在电动结构的底部，在压缩驱动力的作用下吸入并压缩制冷剂气体后输出的压缩机构构成。
电动机构包括连接电源时产生磁力的定子2和在定子2的磁力作用下旋转的转子3以及压入于转子内径内的转轴4构成。
压缩机构包括焊接固定在密封容器内，贯穿转轴4并支持转轴4的上部轴承5；上侧密封安装于上部轴承5的底部，具备吸入并压缩制冷剂气体后输出的内部压缩空间的气缸6；封闭气缸6下部的下部轴承7；贯穿上部轴承5和下部轴承7之间气缸6内部空间的偏离转轴4轴心的偏心部8；***于偏心部8的外柱面上，在气缸6内部空间里旋转的滚动活塞9；与滚动活塞9的外柱面线性接触，并将气缸6内部空间的内柱面和滚动活塞9的外柱面形成的内部压缩空间划分为吸入区和压缩区的叶片(图中未示)构成。
气缸5包括内部具备压缩空间的圆形机身6a；在机身6a的外侧延伸与密封容器1的内柱面相切的带状部6b；为了使叶片(图中未示)与滚动活塞9的外柱面相切，而将其固定成左右可移动结构的叶片槽6d；在叶片槽6d的侧面贯穿带状部6b，以向压缩空间内部引入制冷机气体的吸气端6f；在叶片槽6d的另一侧面顺着上角形成的输出压缩空间内的被压缩制冷机的输出口6c构成。并且，在机身6a的上下侧面上配备了多个固定上部轴承5和下部轴承7的装配孔6e。
图中5a表示输出口，10表示输出阀，11表示消音器，13表示输出管。
当密封容器1内上部的定子2连接电源时，转子3将旋转运动传递给压入于转子3内径的转轴中，带动***在转轴4的偏心部8外柱面的滚动活塞9进行旋转运动，并在气缸6和上部轴承5以及下部轴承7形成的空间内压缩通过储存器(图中未示)吸入的制冷机气体。
在压缩空间内被压缩的制冷剂气体通过上部轴承5的输出口5a输出至压缩机构上部后，通过密封容器1和定子2之间的间隙和转子3与定子2之间的间隙移动至压缩机上部，之后由输出管13输出到压缩机的外部。
目前世界各大压缩机制造商广泛使用镍铬钼铸铁材质制造压缩机滚动活塞，由于近年来镍钼价格节节攀升，导致活塞毛坯铸件的成本大幅度增加。
发明内容
本发明所要解决的技术问题是提供一种满足滚动活塞性能指标、成本降低的用于压缩机滚动活塞的铸铁材料。
为了解决上述技术问题，本发明采用的技术方案是：一种用于压缩机滚动活塞的铸铁材料，各个成分的质量百分比为：碳C为3.0％～3.6％，硅Si为1.8％～2.4％，锰Mn为0.5％～1.0％，磷P为0.1％～0.3％，硫磺S为0.15％以下，铬Cr为0.7％～1.0％，其余为铁Fe。
本发明的有益效果：用于压缩机滚动活塞的铸铁材料的各项性能满足固定的滚动活塞性能指标，同时不添加镍、钼等贵金属，降低了成本。
附图说明
图1是现有技术的封闭型旋转式压缩机的纵断面图。
图2是现有技术的封闭型旋转式压缩机用气缸立体图。
具体实施方式
下面结合附图和具体实施方式对本发明的用于压缩机滚动活塞的铸铁材料作进一步详细说明：
如表1所示，本发明用于压缩机滚动活塞用表1的质量百分比的铸铁进行铸造。
表1 质量百分比(％)
 
C Si Mn P S Cr Fe
3.0～3.6   1.8～2.4   0.5～1.0   0.1～0.3   <0.15 0.7～1.0   剩余
对本发明的用于压缩机滚动活塞的铸铁材料进行测试，与现有规范的活塞金相组织与性能指标要求进行比较，见表2：
 
技术标准 本发明的材料
石墨类型 以片状A型石墨为主 以片状A型石墨为主
珠光体含量 大于90％ 大于90％
磷共晶 3～6％ 5％
铸态硬度 HRB95～108 HRB107.8
抗拉强度 大于250MPa 273.8MPa
淬火后硬度 HRC46～54 HRC55
以上数据由发明人委托河北工业大学铸造研究所测试。
从上述的数据可以看出，本发明的用于压缩机滚动活塞的铸铁材料，没有添加本行业通用的镍、钼。但性能达到了规定的标准，降低了成本。

Claims (1)

1、一种用于压缩机滚动活塞的铸铁材料，其特征是各个成分的质量百分比为：碳C为3.0％～3.6％，硅Si为1.8％～2.4％，锰Mn为0.5％～1.0％，磷P为0.1％～0.3％，硫磺S为0.15％以下，铬Cr为0.7％～1.0％，其余为铁Fe。
CNA2007100599554A 2007-10-18 2007-10-18 用于压缩机滚动活塞的铸铁材料 Pending CN101413083A (zh)