CN101407573A - 聚氨酯跑道胶 - Google Patents

聚氨酯跑道胶 Download PDF

Info

Publication number
CN101407573A
CN101407573A CNA2008101792712A CN200810179271A CN101407573A CN 101407573 A CN101407573 A CN 101407573A CN A2008101792712 A CNA2008101792712 A CN A2008101792712A CN 200810179271 A CN200810179271 A CN 200810179271A CN 101407573 A CN101407573 A CN 101407573A
Authority
CN
China
Prior art keywords
rubber
runway rubber
modified polyether
polyurethane
runway
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2008101792712A
Other languages
English (en)
Inventor
罗植春
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
AOSHUNDA INDUSTRY Co LTD SHENZHEN CITY
Original Assignee
AOSHUNDA INDUSTRY Co LTD SHENZHEN CITY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by AOSHUNDA INDUSTRY Co LTD SHENZHEN CITY filed Critical AOSHUNDA INDUSTRY Co LTD SHENZHEN CITY
Priority to CNA2008101792712A priority Critical patent/CN101407573A/zh
Publication of CN101407573A publication Critical patent/CN101407573A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种聚氨酯跑道胶，该跑道胶包括有改性聚醚、增加跑道胶粘性的填料和二苯基甲烷二异氰酸酯，重量配比为45～53∶45～53∶5～7。本发明采用化工生产中产生的废弃物加工而成的改性聚醚，所制的胶粘结强度好，流动性好，摊铺时平整度好，保证了施工质量。简化了生产工艺，缩短了生产周期，成本大幅降低，提高了竞争力；不含有毒的游离TDI和MOKA，为环保型产品。

Description

聚氨酯跑道胶
技术领域
本发明涉及一种聚氨酯跑道胶。
背景技术
通用型聚氨酯跑道胶，是通过两种组分混合搅拌得到的，其中甲组分为聚丙二醇-甲苯二异氰酸酯(TDI)予聚体，异氰酸根(-NCO％)；乙组分为聚醚二元醇、聚醚三元醇、硫化剂亚甲基双邻氯苯胺(MOKA，需110℃熔化)、催化剂、填料、颜料搅拌均匀经研磨而成。现场使用时是将甲组分和乙组分按照一定比例混合搅拌均匀即可摊铺塑胶跑道。这种传统生产跑道胶的过程成本高、对环境有污染；原料品种多，生产工艺复杂，生产周期长，施工程序繁琐，效率不高。
发明内容
本发明所要解决的技术问题是提供一种聚氨酯跑道胶，该跑道胶成分简单，生产工艺简化，缩短了生产周期，施工成本大大降低。
为解决上述技术问题，本发明所提供的技术方案是：一种聚氨酯跑道胶，该跑道胶包括有改性聚醚、增加跑道胶粘性的填料和二苯基甲烷二异氰酸酯，重量配比为45～53∶45～53∶5～7。
该跑道胶还包括有颜料，添加的重量比例为改性聚醚的1.5％。
所述改性聚醚为从含有聚氨酯成分的废料中提取的聚醚多元醇。
所述改性聚醚、填料和二苯基甲烷二异氰酸酯的重量配比为50∶50∶6。
本发明具有的优点：采用化工生产中产生的废弃物加工而成的改性聚醚，第一，成本低，另外该聚醚为四官能团，分子量高，所制的胶粘结强度好，流动性好，摊铺时平整度好，保证了施工质量；第二，简化了生产工艺，缩短了生产周期，成本大幅降低，提高了竞争力；第三，一步法使施工效率大大提高；第四，不含有毒的游离TDI和MOKA，为环保型产品。
具体实施方式：
实施例1
一种聚氨酯跑道胶，该跑道胶包括有改性聚醚、增加跑道胶粘性的填料和二苯基甲烷二异氰酸酯，重量配比为50∶50∶6。该跑道胶还包括有颜料，添加的重量比例为改性聚醚的1.5％。可根据不同要求，调配各种颜料。
其中，改性聚醚为从含有聚氨酯成分的废料中提取的聚醚多元醇。填料采用是指为增加产品的粘性和其它性能，在生产过程中增加的粉料，比如双飞粉之类的物质。
实施例2
一种聚氨酯跑道胶，该跑道胶包括有改性聚醚、增加跑道胶粘性的填料和二苯基甲烷二异氰酸酯，重量配比为45∶45∶5。该跑道胶还包括有颜料，添加的重量比例为改性聚醚的1.5％。可根据不同要求，调配各种颜料。
其中，改性聚醚为从含有聚氨酯成分的废料中提取的聚醚多元醇。填料采用是指为增加产品的粘性和其它性能，在生产过程中增加的粉料，比如双飞粉之类的物质。
实施例3
一种聚氨酯跑道胶，该跑道胶包括有改性聚醚、增加跑道胶粘性的填料和二苯基甲烷二异氰酸酯，重量配比为53∶53∶7。该跑道胶还包括有颜料，添加的重量比例为改性聚醚的1.5％。可根据不同要求，调配各种颜料。
其中，改性聚醚为从含有聚氨酯成分的废料中提取的聚醚多元醇。填料采用是指为增加产品的粘性和其它性能，在生产过程中增加的粉料，比如双飞粉之类的物质。
本发明聚氨酯跑道胶的施工方法为“一步法”，即现场施工时不再是甲乙料按照一定比例混合搅拌均匀即可摊铺塑胶跑道，而是在主剂中按照一定比例添加催干剂，然后直接摊铺成胶。
本发明聚氨酯跑道胶由催干剂和主剂组成，催干剂不是传统含游离TDI的予聚体，而使用的是无毒的单纯二苯基甲烷二异氰酸酯(MDI)，不需合成。主剂由改性聚醚、填料、颜料组成，混合搅拌均匀经研磨即成，不加硫化剂MOKA，不加催化剂，不需加热，简化了生产工艺，缩短了生产周期。改性聚醚是由化工生产中产生的边角料加工而成，所以成本大大降低。
本发明采用化工生产废弃物加工而成的改性聚醚，变废为宝，成本大幅降低，并且简化了生产工艺，缩短了生产周期。使用MDI，将现场施工由传统的两步法变为一步法。
以上所述，仅是本发明的较佳实施例，并非对本发明作任何形式上的限制，虽然本发明已以较佳实施例揭露如上，然而并非用以限定本发明，任何熟悉本专业的技术人员，在不脱离本发明技术方案范围内，当可利用上述揭示的技术内容作出些许更动或修饰为等同变化的等效实施例，但凡是未脱离本发明技术方案的内容，依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与修饰，均仍属于本发明技术方案的范围内。

Claims (4)

1、一种聚氨酯跑道胶，其特征在于：该跑道胶包括有改性聚醚、增加跑道胶粘性的填料和二苯基甲烷二异氰酸酯，重量配比为45～53∶45～53∶5～7。
2、根据权利要求1所述的聚氨酯跑道胶，其特征在于：该跑道胶还包括有颜料，添加的重量比例为改性聚醚的1.5％。
3、根据权利要求1或2所述的聚氨酯跑道胶，其特征在于：所述改性聚醚为从含有聚氨酯成分的废料中提取的聚醚多元醇。
4、根据权利要求1所述的聚氨酯跑道胶，其特征在于：所述改性聚醚、填料和甲苯二异氰酸酯的重量配比为50∶50∶6。
CNA2008101792712A 2008-12-04 2008-12-04 聚氨酯跑道胶 Pending CN101407573A (zh)