CN101386763B - 耐高温可剥性防腐涂料及其制备方法 - Google Patents

耐高温可剥性防腐涂料及其制备方法 Download PDF

Info

Publication number
CN101386763B
CN101386763B CN2008102280637A CN200810228063A CN101386763B CN 101386763 B CN101386763 B CN 101386763B CN 2008102280637 A CN2008102280637 A CN 2008102280637A CN 200810228063 A CN200810228063 A CN 200810228063A CN 101386763 B CN101386763 B CN 101386763B
Authority
CN
China
Prior art keywords
weight
coating
high temperature
solvent
styrene
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2008102280637A
Other languages
English (en)
Other versions
CN101386763A (zh
Inventor
梁成浩
王兴飞
黄乃宝
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dalian Maritime University
Original Assignee
Dalian Maritime University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dalian Maritime University filed Critical Dalian Maritime University
Priority to CN2008102280637A priority Critical patent/CN101386763B/zh
Publication of CN101386763A publication Critical patent/CN101386763A/zh
Application granted granted Critical
Publication of CN101386763B publication Critical patent/CN101386763B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及的是一种特种涂料，尤其涉及一种耐高温可剥性防腐涂料及其制备方法。该涂料由成膜剂、助剂和溶剂组成，各组分重量比为：成膜剂12～17％，助剂5～10％，溶剂73～83％。具体制备方法为将成膜剂、助剂及溶剂按重量比混合后在密闭容器中常温搅拌溶解30分钟即得到产品。该涂料以高分子聚合物为成膜物质，具有良好的耐酸、碱、盐性能及优异的韧性，并且耐高温性能显著，该涂料易于施涂，启封方便，固化后的涂料膜层剥离后金属表面无污染，且剥落的涂料膜层经处理后可重复使用。

Description

耐高温可剥性防腐涂料及其制备方法
技术领域
本发明涉及的是一种特种涂料，尤其涉及一种耐高温可剥性防腐涂料及其制备方法。
背景技术
金属材料在大气环境中的腐蚀最为普遍，尤其是在一些高温环境下。通常的防护措施为涂敷涂料，在使用时为除去漆膜，往往采用有机溶剂溶解涂膜，用碱水处理，或者用竹刀、刮片等物理方法处理，但这些方法难以除尽涂膜，并有损表面，费工又费时。
发明内容
本发明的目的是克服传统涂料的缺点，提供一种耐高温可剥性防腐涂料。
本发明的技术方案是：耐高温可剥性防腐涂料由成膜剂、助剂和溶剂组成，各组分重量比为：
成膜剂    12～17％
助剂      5～10％
溶剂      73～83％
其中成膜剂由乙烯基树脂和苯乙烯—丁二烯—苯乙烯嵌段共聚物(SBS)组成，各组分重量比为：
乙烯基树脂                             90～95％
苯乙烯—丁二烯—苯乙烯嵌段共聚物(SBS)  5～10％
苯乙烯—丁二烯—苯乙烯嵌段共聚物(SBS)为线形YH—792(S/B＝40/60)；
助剂由邻苯二甲酸二丁酯(DBP)、活性纳米级碳酸钙、十八胺、羊毛脂、双酚A、亚磷酸三乙酯和二月桂酸二丁基锡组成，各组分重量比为：
邻苯二甲酸二丁酯(DBP)      60～65％
活性纳米级碳酸钙           13～17％
十八胺                     5～8％
羊毛脂                     5～8％
双酚A                      2～5％
亚磷酸三乙酯               0.5～1.5％
二月桂酸二丁基锡           0.5～1.5％
活性纳米级碳酸钙的平均粒径为20～50nm；
溶剂由环己酮和四氢呋喃组成，各组分重量比为：
环己酮         50～60％
四氢呋喃       40～50％
耐高温可剥性防腐涂料具体制备步骤为：
(1)、按照上述重量比，将乙烯基树脂、双酚A、亚磷酸三乙酯混合均匀后加入到环己酮中；
(2)、按重量比，将苯乙烯—丁二烯—苯乙烯嵌段共聚物(SBS)、活性纳米级碳酸钙、十八胺、羊毛脂混合均匀后加入到四氢呋喃中；
(3)、将步骤(1)和(2)中所得的溶液混合并搅拌，按重量比加入DBP、二月桂酸二丁基锡，常温搅拌30分钟后即得产品。
本发明的有益效果是：
(1)、本发明以高分子聚合物为成膜物质，并加入了羊毛脂作为缓蚀剂，具有良好的耐酸、碱、盐性能；
(2)、加入了苯乙烯—丁二烯—苯乙烯嵌段共聚物(SBS)、活性纳米级碳酸钙作为增塑增韧剂，涂料膜层具有优异的韧性，从而起到防震防刮等效果；
(3)、由于亚磷酸三乙酯(TEP)和双酚A热稳定剂的加入，涂料膜层的耐高温性能显著，可应用于高温环境下金属表面的临时保护；
(4)、该涂料易于施涂，启封方便，固化后的涂料膜层剥离后金属表面无污染，且剥落的涂料膜层经处理后可重复使用。
具体实施方式
实施例
选取成膜剂15％，助剂8％，溶剂77％，常温搅拌30分钟制备耐高温可剥性防腐涂料。其物理性能及耐蚀性能结果见下表1和表2：
表1物理性能结果
Figure G2008102280637D00031
表2耐酸、碱、熬浸泡试验结果

Claims (3)

1.耐高温可剥性防腐涂料，其特征在于，该涂料由成膜剂、助剂和溶剂组成，各组分重量比为：
成膜剂  12～17％
助剂    5～10％
溶剂    73～83％
其中成膜剂由乙烯基树脂和苯乙烯-丁二烯-苯乙烯嵌段共聚物(SBS)组成，各组分重量比为：
乙烯基树脂                         90～95％
苯乙烯-丁二烯-苯乙烯嵌段共聚物(SBS)5～10％；
助剂由邻苯二甲酸二丁酯(DBP)、活性纳米级碳酸钙、十八胺、羊毛脂、双酚A、亚磷酸三乙酯和二月桂酸二丁基锡组成，各组分重量比为：
Figure DEST_PATH_FSB00000679646600011
其中，所述的活性纳米级碳酸钙的平均粒径为20～50nm；
溶剂由环己酮和四氢呋喃组成，各组分重量比为：
环己酮    50～60％
四氢呋喃  40～50％。
2.根据权利要求1所述的耐高温可剥性防腐涂料，其特征在于，所述的苯乙烯-丁二烯-苯乙烯嵌段共聚物(SBS)为线形YH-792，嵌段比S/B＝40/60。
3.制备权利要求1所述的耐高温可剥性防腐涂料的方法，其特征在于，(1)、按照上述重量比，将乙烯基树脂、双酚A、亚磷酸三乙酯混合均匀后加入到环己酮中；(2)、按重量比，将苯乙烯-丁二烯-苯乙烯嵌段共聚物(SBS)、活性纳米级碳酸钙、十八胺、羊毛脂混合均匀后加入到四氢呋喃中；(3)、将步骤(1)和(2)中所得的溶液混合并搅拌，按重量比加入邻 苯二甲酸二丁酯(DBP)、二月桂酸二丁基锡，常温搅拌30分钟后即得产品。 
CN2008102280637A 2008-10-11 2008-10-11 耐高温可剥性防腐涂料及其制备方法 Expired - Fee Related CN101386763B (zh)