CN101386506A - 轻质保温砂浆 - Google Patents

轻质保温砂浆 Download PDF

Info

Publication number
CN101386506A
CN101386506A CNA2008100513134A CN200810051313A CN101386506A CN 101386506 A CN101386506 A CN 101386506A CN A2008100513134 A CNA2008100513134 A CN A2008100513134A CN 200810051313 A CN200810051313 A CN 200810051313A CN 101386506 A CN101386506 A CN 101386506A
Authority
CN
China
Prior art keywords
percent
mortar
water
good
heat preservation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2008100513134A
Other languages
English (en)
Other versions
CN101386506B (zh
Inventor
刘红
董艳辉
陶忠谦
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGCHUN CONSTRUCTION ENGINEERING GROUP Co Ltd
Original Assignee
CHANGCHUN CONSTRUCTION ENGINEERING GROUP Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGCHUN CONSTRUCTION ENGINEERING GROUP Co Ltd filed Critical CHANGCHUN CONSTRUCTION ENGINEERING GROUP Co Ltd
Priority to CN2008100513134A priority Critical patent/CN101386506B/zh
Publication of CN101386506A publication Critical patent/CN101386506A/zh
Application granted granted Critical
Publication of CN101386506B publication Critical patent/CN101386506B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种保温砂浆，包括粘结材料中各组分的配比，以及粘结材料和水的配比。粘结材料各组分的配比(按重量百分比计)为：玻化微珠∶陶砂∶粉煤灰∶普通硅酸盐水泥∶木纤维∶羟丙基甲基纤维素∶可再分散性乳胶粉∶减水剂＝30～50％∶5～20％∶1～5％∶35～50％∶3～5％∶1～2％∶2～5％∶0.4～0.5％；粘结材料与水的配合比例(按重量计)为：粘结材料∶水＝1∶0.6～0.65。本发明所述的轻质保温砂浆具有良好的粘合性、保水性、抗裂性和保温隔热性能，适用于墙体材料的砌筑和抹灰施工，尤其是对蒸压加气混凝土砌块的砌筑和抹灰施工，保温节能效果突出。

Description

轻质保温砂浆
技术领域
本发明涉及一种轻质保温砂浆，特别是涉及一种保温、保水、抗裂性能良好的砌筑和抹灰砂浆。
背景技术
目前，墙体施工中使用的保温砂浆种类繁多，性能参差不齐，其中常见的有：EPS颗粒保温砂浆、膨胀珍珠岩保温砂浆、玻化微珠保温砂浆。其中EPS颗粒保温砂浆虽然具有保温隔热性能良好、耐腐蚀性较好等优点，但由于EPS为有机轻质材料，造成砂浆的和易性差，施工难度大，粘结力较小，防火性能差，特别是有机材料会释放出有害物质，不宜大范围推广使用；膨胀珍珠岩保温砂浆由于膨胀珍珠岩的开孔结构，其缝隙在砂浆搅拌过程中被水泥填塞，使其保温性能大大降低；另外，此种砂浆吸水率大，抗冻融能力差，砂浆在凝结硬化过程中容易失水而产生收缩裂缝；玻化微珠的保温砂浆保温性能良好，但由于玻化微珠的粒径小、强度差，造成砂浆的强度较低，难以应用到对砌体强度要求较高的工程项目中。
自从禁止使用实心粘土砖以来，蒸压加气混凝土砌块是国内大力推广应用替代实心粘土砖的墙体材料之一，由于它具有容重轻、保温、防火、吸音、抗震性能好，现场加工方便，易于施工以及大量使用工业废渣，节能节地等特点，深受建筑各方的欢迎。据了解，蒸压加气混凝土砌块是目前国内唯一一种在严寒地区能够满足建筑节能65％设计要求的单一墙体材料。但是，由于这种墙材有其吸水率大的特点，使用普通水泥砂浆砌筑和抹灰容易出现空鼓、开裂、剥落、内墙面出现网格状黑框等现象。因此，只有加大灰缝热阻，提高砂浆的保温、保水性能，使之与砌体材料的热阻相匹配，才能降低灰缝修正系数、杜绝热桥现象等对墙体保温性能的影响，从整体上提高***护结构的保温隔热性能。
发明内容
本发明的目的在于提供一种具有保温性好、保水性好、不空鼓开裂、强度高，抗老化、防火和耐腐蚀性能的轻质保温砂浆。本发明适用于其导热系数与之相匹配的墙体材料砌筑和抹灰施工。
为了达到上述目的，本发明采用如下技术方案：其组成及配比(按重量百分比计)为：玻化微珠：陶砂：粉煤灰：普通硅酸盐水泥：木纤维：羟丙基甲基纤维素：可再分散性乳胶粉：减水剂＝30～50％：5～20％：1～5％：35～50％：3～5％：1～2％：2～5％：0.4～0.5％。
其中：玻化微珠起保温、吸音、防火、降低容重和改善级配的作用；陶砂的粒径为0.3～0.5mm，在保温砂浆中起骨料的作用，提高砂浆强度；粉煤灰提高砂浆的和易性，减少水泥用量，降低砂浆成本；羟丙基甲基纤维素起增稠保水的作用；可再分散性乳胶粉在砂浆中形成一层液膜，提高砂浆的保水性能，从而保证了砂浆能够充分水化，确保砂浆强度。
上述保温砂浆制备方法如下：按比例称量各组分，依次将玻化微珠、陶砂、粉煤灰、普通硅酸盐水泥、木纤维、羟丙基甲基纤维素、可再分散性乳胶粉、减水剂倒入滚筒式搅拌机中混合均匀；加水(按粘结材料：水＝1：0.6～0.65的比例)搅拌均匀即得到本发明所述的轻质保温砂浆。
本发明保温砂浆的优点在于：1、砂浆强度高、粘结能力强；2、砂浆密度低，导热系数低，灰缝修正系数小，保温性能好；3、保水性好，最大限度的控制了因砂浆失水造成的空鼓、开裂现象的发生。
具体实施方式
实施例1：一种高效轻质保温砂浆，其组分配比为：玻化微珠：陶砂：粉煤灰：普通硅酸盐水泥：木纤维：羟丙基甲基纤维素：可再分散性乳胶粉：减水剂＝35kg：15kg：3kg：40kg：3kg：1kg：2kg：0.4kg。
上述轻质保温砂浆的制备方法如下，按上述比例称量各组分，先将玻化微珠、陶砂、粉煤灰、普通硅酸盐水泥、木纤维、羟丙基甲基纤维素、可再分散性乳胶粉、减水剂倒入滚筒式搅拌机中混合均匀；加水60kg搅拌均匀即得到本发明所述的轻质保温砂浆。
实施例2：一种高效轻质保温砂浆，其组分配比(重量比)为：玻化微珠：陶砂：粉煤灰：普通硅酸盐水泥：木纤维：羟丙基甲基纤维素：可再分散性乳胶粉：减水剂＝30kg：17kg：5kg：40kg：3kg：1kg：3kg：0.5kg。
上述轻质保温砂浆的制备方法如下：按上述比例称量各组分，先将玻化微珠、陶砂、粉煤灰、普通硅酸盐水泥、木纤维、羟丙基甲基纤维素、可再分散性乳胶粉、减水剂倒入滚筒式搅拌机中混合均匀；加水60kg搅拌均匀即得到本发明所述的轻质保温砂浆。
上述实施例中所使用的水泥为普通硅酸盐P.O42.5水泥。

Claims (4)

1、一种轻质保温砂浆，其特征在于：其组份配比(按重量百分比计)为：玻化微珠：陶砂：粉煤灰：普通硅酸盐水泥：木纤维：羟丙基甲基纤维素：可再分散性乳胶粉：减水剂＝30～50％：5～20％：1～5％：35～50％：3～5％：1～2％：2～5％：0.4～0.5％。
2、根据权利要求1所述的轻质保温砂浆，其特征在于陶砂粒径为0.3～0.5mm，容重400～600kg/m3。
3、根据权利要求1所述的轻质保温砂浆，其特征在于玻化微珠粒径为0.1～0.5mm，容重150～170kg/m3。
4、根据权利要求1所述的轻质保温砂浆，其特征在于减水剂为萘系高效减水剂的粉剂。
CN2008100513134A 2008-10-23 2008-10-23 轻质保温砂浆 Active CN101386506B (zh)