CN101353242A - 一种机制砂自密实混凝土 - Google Patents

一种机制砂自密实混凝土 Download PDF

Info

Publication number
CN101353242A
CN101353242A CNA2008100460739A CN200810046073A CN101353242A CN 101353242 A CN101353242 A CN 101353242A CN A2008100460739 A CNA2008100460739 A CN A2008100460739A CN 200810046073 A CN200810046073 A CN 200810046073A CN 101353242 A CN101353242 A CN 101353242A
Authority
CN
China
Prior art keywords
machine
made sand
compacting concrete
self
cobble
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2008100460739A
Other languages
English (en)
Inventor
高育欣
向卫平
郑广军
简晓军
修晓明
胡建平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
China Construction Third Engineering Bureau Co Ltd
China Construction Ready Mixed Concrete Co Ltd
Original Assignee
Concrete Service Station of China Construction Third Bureau Co Ltd Chengdu Branch
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Concrete Service Station of China Construction Third Bureau Co Ltd Chengdu Branch filed Critical Concrete Service Station of China Construction Third Bureau Co Ltd Chengdu Branch
Priority to CNA2008100460739A priority Critical patent/CN101353242A/zh
Publication of CN101353242A publication Critical patent/CN101353242A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种机制砂自密实混凝土，按照重量组分计算，包括水泥100份、粉煤灰25－45份、矿粉0－30份、聚羧酸减水剂0.8－1.5份、机制砂220－250份、卵石130－150份、碎石130－150份混合组成。本发明在节约天然资源的基础上，不仅具有高流动性、高稳定性和低坍落度损失，而且相比同等效果，成本更加低廉，生产更加简便，同时由于本发明中没有使用硅灰，因此操作人员的身体健康更有保障。

Description

一种机制砂自密实混凝土
技术领域
本发明属于建筑材料类，涉及一种用于工业与民用建筑的混凝土，特别是涉及一种免振捣的机制砂自密实混凝土。
背景技术
自密实混凝土要求混凝土拌合物具有“液化”性质，具备较好的流动性能和稳定性能，施工时无须振捣。当前制备自密实混凝土的技术，一般使用河砂，利用其优良的级配和颗粒粒形，比较容易实现“自密实”。目前，机制砂已经成为普通混凝土中的一种常规材料，应用相对比较成熟；但是与河砂相比，机制砂颗粒粒形差，级配差，往往会降低新拌混凝土的流动性能和稳定性能。然而，随着河砂等天然资源的不断枯竭，探索机制砂等人工加工资源在自密实混凝土中的应用成为一种趋势。
公告号为CN1323049C的发明专利，公开了一种机制砂自密实混凝土，由水泥、粉煤灰、硅灰、其他矿物掺合料、聚羧酸减水剂、增粘剂、消泡剂、机制砂和碎石混合组成。该发明使用了硅灰、消泡剂、增粘剂等目前在普通混凝土中还没有得到广泛运用的组分，有效地提高了混凝土体系的流动性能和稳定性能，但是由于硅灰等特殊材料的价格相对比较昂贵，使得该发明存在应用成本相对较高，生产操作相对较复杂等缺陷；同时由于硅灰是一种超细材料，人若吸入易患吸肺病，受商品混凝土搅拌站生产工艺所限制，目前生产时一般采用人工添加，极易对操作人员造成身体伤害。
发明内容
本发明的目的就是针对现有技术的不足，提供一种免振捣，具有高流动性、高稳定性和低坍落度损失的机制砂自密实混凝土，不仅节约天然资源，而且相比同等效果，成本低廉，生产简便，对人体无害。
为实现上述目的，本发明的技术方案如下：
一种机制砂自密实混凝土，按照重量组分计算，包括水泥100份、粉煤灰25-45份、矿粉0-30份、聚羧酸减水剂0.8-1.5份、机制砂220-250份、卵石130-150份、碎石130-150份混合组成。使用时，将45-60份的水和上述材料混合，根据不同的水灰比分布情况，所述机制砂自密实混凝土的28d强度可达到50-70Mpa。所述机制砂自密实混凝土中没有使用硅灰、增粘剂、消泡剂等特殊材料，而是运用普通混凝土中广泛使用的常规材料，有利于简化生产和质量控制；而且上述特殊材料价格相对昂贵，其中硅灰价格约为水泥的8-10倍，因此本发明具有更加低廉的成本。
所述机制砂为所述机制砂自密实混凝土的细集料，以卵石为原料破碎而成，细度模数2.5-3.0，级配达到II区中砂边缘要求，石粉含量8％-10％。细集料全部使用机制砂，不仅对自密实混凝土的使用材料进行了拓展，更重要的是对河砂资源具有一种保护作用，对改善生态环境有着积极的意义。
所述卵石和碎石按重量比例1∶1混合，构成所述机制砂自密实混凝土的粗集料，其中卵石为5-16mm连续级配，碎石为10-20mm连续级配，卵石和碎石均经过水洗，含泥量均小于0.5％。所述水泥为普通硅酸盐水泥，强度≥42.5强度等级。所述粉煤灰为I级或II级粉煤灰，其需水比≤100％。所述矿粉是S75级，比表面积330m2/kg-390m2/kg，流动度比大于105％。所述聚羧酸减水剂是一种含有高效减水组分和徐放型高分子的聚羧酸系减水剂，具有良好的工作度保持性能，固含量为20％。
本发明具有以下有益效果：在节约天然资源的基础上，不仅具有高流动性、高稳定性和低坍落度损失，而且相比同等效果，成本更加低廉，生产更加简便，同时由于本发明中没有使用硅灰，因此操作人员的身体健康更有保障。
具体实施方式
实施例一
制所述机制砂自密实混凝土1m3，取水泥400kg、粉煤灰150kg、矿粉0kg、聚羧酸减水剂4kg、机制砂920kg、卵石560kg、碎石560kg。所述机制砂以卵石为原料破碎而成，细度模数2.8，级配达到II区中砂边缘要求，石粉含量9％。所述卵石为5-16mm连续级配，碎石为10-20mm连续级配，卵石和碎石均经过水洗，含泥量为0.4％。所述水泥为普通硅酸盐水泥，强度为42.5强度等级。所述粉煤灰为I级粉煤灰，其需水比为100％。所述矿粉是S75级，比表面积360m2/kg，流动度比110％。所述聚羧酸减水剂固含量为20％。
使用时，将200kg的水和上述材料混合，即可制得所述机制砂自密实混凝土。该机制砂自密实混凝土拌合物的坍落度、坍落扩展度、倒坍落度流出时间见表1；该机制砂自密实混凝土不同龄期的抗压强度见表2。
实施例二
制所述机制砂自密实混凝土1m3，取水泥350kg、粉煤灰100kg、矿粉100kg、聚羧酸减水剂2.8kg、机制砂770kg、卵石525kg、碎石525kg。所述机制砂以卵石为原料破碎而成，细度模数2.5，级配达到II区中砂边缘要求，石粉含量8％。所述卵石为5-16mm连续级配，碎石为10-20mm连续级配，卵石和碎石均经过水洗，含泥量为0.35％。所述水泥为普通硅酸盐水泥，强度为52.5强度等级。所述粉煤灰为II级粉煤灰，其需水比为95％。所述矿粉是S75级，比表面积330m2/kg，流动度比108％。所述聚羧酸减水剂固含量为20％。
使用时，将157.5kg的水和上述材料混合，即可制得所述机制砂自密实混凝土。该机制砂自密实混凝土拌合物的坍落度、坍落扩展度、倒坍落度流出时间见表1；该机制砂自密实混凝土不同龄期的抗压强度见表2。
实施例三
制所述机制砂自密实混凝土1m3，取水泥400kg、粉煤灰100kg、矿粉50kg、聚羧酸减水剂6kg、机制砂1000kg、卵石520kg、碎石520kg。所述机制砂以卵石为原料破碎而成，细度模数3.0，级配达到II区中砂边缘要求，石粉含量10％。所述卵石为5-16mm连续级配，碎石为10-20mm连续级配，卵石和碎石均经过水洗，含泥量为0.45％。所述水泥为普通硅酸盐水泥，强度为42.5R强度等级。所述粉煤灰为II级粉煤灰，其需水比为98％。所述矿粉是S75级，比表面积390m2/kg，流动度比115％。所述聚羧酸减水剂固含量为20％。
使用时，将240kg的水和上述材料混合，即可制得所述机制砂自密实混凝土。该机制砂自密实混凝土拌合物的坍落度、坍落扩展度、倒坍落度流出时间见表1；该机制砂自密实混凝土不同龄期的抗压强度见表2。
实施例四
制所述机制砂自密实混凝土1m3，取水泥300kg、粉煤灰135kg、矿粉90kg、聚羧酸减水剂3.9kg、机制砂720kg、卵石435kg、碎石435kg。所述机制砂以卵石为原料破碎而成，细度模数2.7，级配达到II区中砂边缘要求，石粉含量8.5％。所述卵石为5-16mm连续级配，碎石为10-20mm连续级配，卵石和碎石均经过水洗，含泥量为0.3％。所述水泥为普通硅酸盐水泥，强度为42.5强度等级。所述粉煤灰为I级粉煤灰，其需水比为90％。所述矿粉是S75级，比表面积380m2/kg，流动度比120％。所述聚羧酸减水剂固含量为20％。
使用时，将165kg的水和上述材料混合，即可制得所述机制砂自密实混凝土。该机制砂自密实混凝土拌合物的坍落度、坍落扩展度、倒坍落度流出时间见表1；该机制砂自密实混凝土不同龄期的抗压强度见表2。
表1机制砂自密实混凝土拌合物性能
表2不同龄期机制砂自密实混凝土的抗压强度
Figure A20081004607300081

Claims (7)

1.一种机制砂自密实混凝土，其特征在于：按照重量组分计算，所述机制砂自密实混凝土包括水泥100份、粉煤灰25-45份、矿粉0-30份、聚羧酸减水剂0.8-1.5份、机制砂220-250份、卵石130-150份、碎石130-150份混合组成。
2.如权利要求1所述的机制砂自密实混凝土，其特征在于：所述机制砂为所述机制砂自密实混凝土的细集料，以卵石为原料破碎而成，细度模数2.5-3.0，级配达到II区中砂边缘要求，石粉含量8％-10％。
3.如权利要求1所述的机制砂自密实混凝土，其特征在于：所述卵石和碎石按重量比例1∶1混合，构成所述机制砂自密实混凝土的粗集料，其中卵石为5-16mm连续级配，碎石为10-20mm连续级配，卵石和碎石均经过水洗，含泥量小于0.5％。
4.如权利要求1至3任一所述的机制砂自密实混凝土，其特征在于：所述水泥为普通硅酸盐水泥，强度≥42.5强度等级。
5.如权利要求1至3任一所述的机制砂自密实混凝土，其特征在于：所述粉煤灰为I级或II级粉煤灰，其需水比≤100％。
6.如权利要求1至3任一所述的机制砂自密实混凝土，其特征在于：所述矿粉是S75级，比表面积330m2/kg-390m2/kg，流动度比大于105％。
7.如权利要求1至3任一所述的机制砂自密实混凝土，其特征在于：所述聚羧酸减水剂固含量为20％。
CNA2008100460739A 2008-09-16 2008-09-16 一种机制砂自密实混凝土 Pending CN101353242A (zh)