CN101348689B - 水性弹点漆 - Google Patents
水性弹点漆 Download PDFInfo
- Publication number
- CN101348689B CN101348689B CN2008101204585A CN200810120458A CN101348689B CN 101348689 B CN101348689 B CN 101348689B CN 2008101204585 A CN2008101204585 A CN 2008101204585A CN 200810120458 A CN200810120458 A CN 200810120458A CN 101348689 B CN101348689 B CN 101348689B
- Authority
- CN
- China
- Prior art keywords
- percent
- paint
- water
- agent
- emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种应用在木制品、层压板等表面的水性弹点漆。现有的油漆产品为二液型油漆,需现配现用,超过10小时以上会固化,多余下的油漆不能重复使用。本发明包括按重量百分比计的下列组分:水性聚氨酯乳液30%—50%,有机硅改性丙烯酸酯乳液20%—40%,成膜助剂十二酯醇1%—10%,聚丙烯酸钠盐类分散剂0.5%—5.0%,消泡剂0.3%—0.5%,填料10%—25%,颜料1%—10%,pH值调节剂0.1%—1.0%,增稠剂0.1%—1.0%,水1%—10%。本发明符合环保的要求,不会快速固化,可重复使用。
Description
技术领域
本发明涉及一种应用在木制品、层压板等表面的油漆。
背景技术
目前木制品表面涂装用的油漆产品存在以下问题:a)不符合环保要求,油漆中含有40%以上的有机溶剂,对施工人员及产品消费者的健康造成极大的伤害;b)为二液型油漆,需现配现用,超过10小时以上会固化,多余下的油漆不能重复使用。
发明内容
本发明所要解决的技术问题是克服上述现有技术存在的缺陷,提供一种符合环保要求的水性弹点漆,其不会快速固化,可重复使用。
为此,本发明采用如下的技术方案:水性弹点漆,其包括按重量百分比计的下列组分:
水性聚氨酯乳液 30%—50%
有机硅改性丙烯酸酯乳液 20%-40%
成膜助剂十二酯醇 1%—10%
聚丙烯酸钠盐类分散剂 0.5%—5.0%
消泡剂 0.3%—0.5%
填料 10%—25%
颜料 1%—10%
PH值调节剂 0.1%—1.0%
增稠剂 0.1%—1.0%
水 1%—10%。
本发明中,水性聚氨酯乳液无毒、无味、无污染环境、无腐蚀。有机硅改性丙烯酸酯乳液具有耐化学品性好,干燥好,光泽度高等特点。十二酯醇(Texanol)是新一代的成膜助剂,化学名为2,2,4—三甲基—1,3—戊二醇单异丁酸酯,它能被吸附在乳液粒子上,可以有效的聚结,软化融合乳液粒子,使乳液的成膜温度大大降低,起到低温下即能成膜的特性,有利于弹点漆的施工应用,十二酯醇具有良好的水解稳定性,低的凝固点,适宜挥发速率,高效的聚结效率;分散剂用于生产过程中使各助剂在乳液中分散均匀;消泡剂用于消除生产过程中产生的气泡;填料有利于提高涂膜的硬度和降低成本;颜料可根据不同的颜色要求选用不同的颜料,提供涂膜的不同色彩;PH值调节剂用于调节乳液的PH值在8.0-9.0之间,中性及偏碱性条件易于储存和包装并且有利于碱溶性增稠剂增稠;增稠剂用于控制粘度在1000-3000mps,在此粘度下有利于施工。
本发明的水性弹点漆优选的配方如下(以重量百分比计):
水性聚氨酯乳液 30%—50%
有机硅改性丙烯酸酯乳液 20%—40%
成膜助剂十二酯醇 1%—10%
分散剂SOLSPERSE27000 0.5%—5.0%
消泡剂F111 0.3%—0.5%
重质碳酸钙 10%—20%
聚四氟乙烯蜡粉 0.1%—5.0%
碳黑 1%—10%
N,N二甲基乙醇胺 0.1%—1.0%
增稠剂TT615 0.1%—1.0%
水 1%—10%。
本发明具有以下有益效果:水性聚氨脂酯乳液、改性丙烯酸酯乳液均无毒,采用水作溶剂,没有采用有机溶剂,不影响施工人员及产品消费者的身体健康,符合了环保的要求;采用水性聚氨脂酯乳液调节了水性漆固化后的物理性能,改性丙烯酸酯乳液提高了成膜物的耐化学性和光泽和硬度;为单组份体系,易于储存,可重复使用。
下面结合具体实施方式对本发明作进一步的说明。
具体实施方式
实施例1
本发明的各组分如下(按重量百分比计):
水性聚氨酯乳液 30%
有机硅改性丙烯酸酯乳液 40%
十二酯醇(成膜助剂) 1%
SOLSPERSE27000(分散剂) 2%
F111(消泡剂) 0.5%
800目重质碳酸钙(填料) 20%
N5223(聚四氟乙烯蜡粉,填料) 0.1%
Printexu碳黑(颜料) 1%
DMAE(N,N二甲基乙醇胺)(PH值调节剂)1%
TT615(改性碱溶胀缔合型增稠剂) 1%
水 至100%。
实施例2
本发明的各组分如下(按重量百分比计):
水性聚氨酯乳液 35%
有机硅改性丙烯酸酯乳液 25%
十二酯醇(成膜助剂) 10%
SOLSPERSE27000(分散剂) 0.5%
F111(消泡剂) 0.3%
800目重质碳酸钙(填料) 10%
N5223(填料) 5%
Printexu碳黑(颜料) 10%
DMAE(N,N二甲基乙醇胺)(PH值调节剂) 0.1%
TT615(增稠剂) 0.1%
水 至100%。
实施例3
本发明的各组分如下(按重量百分比计):
水性聚氨酯乳液 50%
有机硅改性丙烯酸酯乳液 20%
十二酯醇(成膜助剂) 5%
SOLSPERSE27000(分散剂) 5%
F111(消泡剂) 0.5%
800目重质碳酸钙(填料) 10%
N5223(填料) 1.5%
Printexu碳黑(颜料) 6%
DMAE(N,N二甲基乙醇胺)(PH值调节剂) 0.4%
TT615(增稠剂) 0.4%
水 至100%。
上述实施例的制备方法如下:
先按比例加入水性聚氨酯乳液、有机硅改性丙烯酸酯乳液,在搅拌下加入成膜助剂十二酯醇,搅匀后测试成膜性能,合格后依次加入SOLSPERSE27000、F111、800目重质碳酸钙、N5223、Printexu碳黑搅拌均匀,用DMAE调节PH值在8.0—9.0之间,加入配方量的水后高速搅拌下加入TT615增稠剂调节粘度在1000—3000mps;然后砂磨机研磨一遍至细度10um以下,送检合格后包装。
上述实施例制得的产品性能如下:
固含量:>45%,
干燥速度:4小时表干,48小时实干,
涂膜硬度:>1H,
喷涂性能:能均匀喷涂无障碍。
Claims (2)
1.水性弹点漆,其包括按重量百分比计的下列组分:
水性聚氨酯乳液 30%-50%
有机硅改性丙烯酸酯乳液 20%-40%
成膜助剂十二酯醇 1%-10%
聚丙烯酸钠盐类分散剂 0.5%-5.0%
消泡剂F111 0.3%-0.5%
重质碳酸钙 10%-20%
聚四氟乙烯蜡粉 0.1%-5.0%
颜料 1%-10%
PH值调节剂 0.1%-1.0%
增稠剂 0.1%-1.0%
水 1%-10%。
2.根据权利要求1所述的水性弹点漆,其包括按重量百分比计的下列组分:
水性聚氨酯乳液 30%-50%
有机硅改性丙烯酸酯乳液 20%-40%
成膜助剂十二酯醇 1%-10%
分散剂SOLSPERSE 27000 0.5%-5.0%
消泡剂F111 0.3%-0.5%
重质碳酸钙 10%-20%
聚四氟乙烯蜡粉 0.1%-5.0%
碳黑 1%-10%
N,N二甲基乙醇胺 0.1%-1.0%
增稠剂TT615 0.1%-1.0%
水 1%-10%。