CN101300202A - 磷酸盐光学玻璃 - Google Patents
磷酸盐光学玻璃 Download PDFInfo
- Publication number
- CN101300202A CN101300202A CNA2006800404174A CN200680040417A CN101300202A CN 101300202 A CN101300202 A CN 101300202A CN A2006800404174 A CNA2006800404174 A CN A2006800404174A CN 200680040417 A CN200680040417 A CN 200680040417A CN 101300202 A CN101300202 A CN 101300202A
- Authority
- CN
- China
- Prior art keywords
- glass
- optical glass
- chemical durability
- phosphate optical
- addition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明的目的在于提供具有1.45~1.65的折射率、65以上阿贝数的光学常数且化学耐久性优异的光学玻璃。本发明涉及的磷酸盐光学玻璃的特征在于,按质量%计含有P2O5:73~85、Al2O3:14~26、K2O+Li2O:1~12、SiO2:0~12、B2O3:0~12、Na2O:0~12、Y2O3:0~12、La2O3:0~12、MgO+CaO+SrO+BaO:0~12、ZrO2+TiO2+Gd2O3:0~10、Ta2O5+GeO2+Ga2O3+Nb2O5+WO3+TeO2:0~10、Sb2O3:0~2、ZnO+PbO:0~12的玻璃成分。
Description
技术领域
本发明涉及能精密加压成形的、特别是化学耐久性优异的磷酸盐光学玻璃。
背景技术
以往,作为具有高色散性的光学玻璃,已知有以P2O5为基本成分的磷酸盐光学玻璃。但以往的磷酸盐光学玻璃的耐久性、特别是化学耐久性差,在光学玻璃的研磨工序、清洗工序或作为透镜长期使用过程中存在其表面容易因为灼烧或风化作用而引起腐蚀的问题。特别是在精密加压成形的光学玻璃中,为了易于成形而含有碱金属·碱土类金属元素,使化学耐久性问题更突出。
作为用以提高磷酸盐光学玻璃的化学耐久性的技术方案,专利文献1中提出了含有特定量的Al2O3的组成,但在化学耐久性方面并不令人满意。此外,作为精密加压成形用的磷酸盐光学玻璃,专利文献2等中公开了组成,但其涵盖阿贝数为23~42的色散性低的范围,而不涵盖阿贝数为65以上的高色散性的范围。
专利文献1:日本专利特开昭57-118045号公报(发明的详细内容)
专利文献2:日本专利特开2003-238197号公报(发明的详细内容)
发明的揭示
本发明的目的在于提供具有1.45~1.65的折射率、65以上阿贝数的光学常数且化学耐久性优异的光学玻璃。
本发明者为达到上述目的进行了潜心研究,从而完成了本发明。即,本发明的技术内容如下所述。
(1)磷酸盐光学玻璃,其特征在于,按质量%计含有P2O5:73~85、Al2O3:14~26、K2O+Li2O:1~12、SiO2:0~12、B2O3:0~12、Na2O:0~12、Y2O3:0~12、La2O3:0~12、MgO+CaO+SrO+BaO:0~12、ZrO2+TiO2+Gd2O3:0~10、Ta2O5+GeO2+Ga2O3+Nb2O5+WO3+TeO2:0~10、Sb2O3:0~2、ZnO+PbO:0~12的玻璃成分。
(2)上述(1)所述的磷酸盐光学玻璃,其特征在于,按质量%计含有P2O5:74~80、Al2O3:15~25、K2O+Li2O:1~8的成分。
(3)上述(1)或(2)所述的磷酸盐光学玻璃,其特征在于,含有1~4质量%Li2O。
(4)上述(1)~(3)任一项所述的磷酸盐光学玻璃,其特征在于,折射率(nd)为1.45~1.65,且阿贝数(vd)为65~80。
(5)上述(1)~(4)任一项所述的磷酸盐光学玻璃,其特征在于,玻璃化温度(Tg)为600℃以下。
本发明的磷酸盐光学玻璃具有1.45~1.65的折射率、65以上阿贝数的光学常数,并具有以往产品未能达到的优异的化学耐久性。而且,它是易熔解、不易失透的光学玻璃,玻璃化温度低,适于加压成形。此外,不以原料价格高的Ga2O3、GeO2、Ta2O5成分为必须成分,因此是在原料价格方面也有利的光学玻璃。
实施发明的最佳方式
本发明的磷酸盐光学玻璃(以下称本玻璃)的特征在于,至少含有(1)P2O5、(2)Al2O3、(3)Li2O和/或K2O。另外,本说明书中只要无特殊说明,“%”意味着“质量%”。
本玻璃中P2O5是形成光学玻璃的主要成分(玻璃形成氧化物),含有73~85%。若P2O5不足73%,则难以得到所需的光学常数,另一方面当P2O5超过85%时,化学耐久性有可能下降。作为P2O5的上限,优选为80%以下,进一步优选为78%以下。本玻璃中若P2O5为74%以上,则光学常数和化学耐久性之间达到良好的平衡,因而成为优选,P2O5进一步优选为75%以上,P2O5特别优选为76%以上。
本玻璃中,从化学耐久性的观点出发Al2O3为必须成分,含有14~26%。若Al2O3不足14%,则有可能无法得到充分的化学耐久性,而当Al2O3超过26%时,熔解性下降,有可能无法得到所需的光学常数。本玻璃中Al2O3的下限优选为15%以上,Al2O3进一步优选为16%以上。同样,本玻璃中Al2O3的上限优选为25%以下,进一步优选为23%以下。
本玻璃中,Li2O和/或K2O是使玻璃化温度降至适合加压成形的温度时的必须成分,含有1~12%、优选1~8%。若Li2O和/或K2O不足1%,则玻璃化温度提高,加压成形性下降。若Li2O和/或K2O超过12%,则化学耐久性下降,有可能无法得到所需的光学常数。本玻璃中若含有1~4%的Li2O,则低温成形性和化学耐久性提高,因而优选。当本玻璃中不含Li2O而只含K2O时,若含有1~6%的K2O,则低温成形性和化学耐久性提高,因而优选。
可以将本玻璃中Li2O和/或K2O的一部分用Na2O置换,但当Na2O量增多时,化学耐久性下降,因此优选尽量降低Na2O含量。
本玻璃中SiO2虽不是必须成分,但具有维持低色散性(提高阿贝数)的同时提高化学耐久性的效果。不过,当添加量多时,难以得到所需的光学特性,且玻璃化温度上升,结果导致加压成形时的成形温度上升、生产率等下降。因此,在本玻璃中添加SiO2时,优选为0~12%,进一步优选为0~7%。作为本玻璃中添加SiO2时的下限,优选为1%以上,进一步优选为3%以上,特别优选为5%以上。
本玻璃中B2O3虽不是必须成分,但具有维持低色散性的效果。另一方面,当添加量增多时,难以得到所需的光学特性,因此添加B2O3时优选为0~12%,进一步优选为0~9%,特别优选为0~6%。作为本玻璃中添加B2O3时的下限,优选为2%以上,进一步优选为3%以上,特别优选为4%以上。
本玻璃中Y2O3虽不是必须成分,但能在维持低色散性的同时增加折射率,还具有提高化学耐久性的效果。不过当添加量过多时,熔解温度上升、熔解性下降,因此添加Y2O3时优选为0~12%,进一步优选为0~7%。作为本玻璃中添加Y2O3时的下限,优选为2%以上,进一步优选为4%以上,特别优选为6%以上。
本玻璃中La2O3也具有与Y2O3相同的效果,所以添加La2O3时优选0~12%,进一步优选为0~7%。作为本玻璃中添加La2O3时的下限,优选为2%以上,进一步优选为4%以上,特别优选为6%以上。
本玻璃中MgO、CaO、SrO或BaO中的任1种以上虽不是必须成分,但添加后折射率提高。不过当其添加量过多时,难以得到所需的光学常数,因此在本玻璃中的添加量优选为0~12%,进一步优选为0~11%,其添加量特别优选为0~8%。作为本玻璃中添加MgO、CaO、SrO或BaO中的任1种以上时的下限,优选为1%以上,进一步优选为2%以上,特别优选为3%以上。
本玻璃中从ZrO2、TiO2及Gd2O3中选择的任1种以上虽不是必须成分,但添加后化学耐久性提高、耐失透性提高。不过当添加量过多时,阿贝数下降。因此,其添加量优选为0~10%,进一步优选为0~5%。作为本玻璃中添加ZrO2、TiO2及Gd2O3中的任1种以上时的下限,优选为1%以上,进一步优选为2%以上,特别优选为3%以上。
本玻璃中从Ta2O5、GeO2、Ga2O3、Nb2O5、TeO2以及WO3中选择的任1种以上虽不是必须成分,但添加后折射率提高。不过当其添加量过多时,阿贝数下降,因此其添加量优选为0~10%,进一步优选为0~5%。另外,由于形成上述成分的原料的价格高,因此在注重原料价格方面时,优选尽量减少添加量。作为本玻璃中添加选自Ta2O5、GeO2、Ga2O3、Nb2O5、TeO2以及WO3的任1种以上时的下限,优选为1%以上,进一步优选为2%以上,特别优选为3%以上。
本玻璃中Sb2O3虽不是必须成分,但可作为玻璃熔融时的澄清剂而添加。其添加量优选为2%以下,进一步优选为1%以下。作为本玻璃中添加Sb2O3时的下限,优选为0.01%以上,进一步优选为0.1%以上,特别优选为0.2%以上。
若在本玻璃中添加ZnO和/或PbO,则具有降低熔融温度的效果。ZnO和/或PbO的添加量优选为0~12%,进一步优选为0~7%,但考虑到对环境方面的影响等时,优选实质上不含有。作为本玻璃中添加ZnO和/或PbO时的下限,优选为1%以上,进一步优选为3%以上,特别优选为5%以上。
另外,对于本玻璃,Ag、Cu或Fe各元素的离子导致着色,因此优选实质上不含有。
关于本玻璃的光学特性,折射率(nd)优选为1.45~1.65。折射率(nd)进一步优选为1.50以上,折射率(nd)特别优选为1.53以上。本玻璃的阿贝数(vd)优选为65~80。阿贝数(vd)进一步优选为67以上,阿贝数(vd)特别优选为70以上。本玻璃的玻璃化温度(Tg)优选为600℃以下,玻璃化温度特别优选为550℃以下。作为本玻璃的光学特性,折射率(nd)为1.45~1.65,优选为1.50~1.55,且阿贝数(vd)以65~80为宜,优选68~72。
本玻璃的制造方法不受特殊限制。例如可以将氧化物、氢氧化物、碳酸盐、硝酸盐等通常的光学玻璃中使用的原料称量·混合,装入铂坩埚内,在约1200~1300℃下熔融2~6小时,澄清、搅拌后,铸入预热至约500℃的模中等,然后退火来制造。
实施例
下面,列举实施例等更具体地说明本发明,但本发明的解释不限于以下实施例。另外,例1~例3是本发明的比较例,例4~例13是本发明的实施例。
[化学组成·样品制作法]
按表1、表2所示的化学组成(%)称量原料。关于各玻璃的原料,分别为P2O5使用H3PO4、K2O使用KNO3、Li2O使用Li2CO3、CaO使用CaCO3、B2O3使用H3BO3、Al2O3使用氧化物。将称取的原料用混合器干式混合30分钟,装入内容积约300cm3的铂坩埚内,在1200~1300℃下熔融2~6小时,澄清、搅拌后,铸入预热至约500℃的长15mm×宽50mm的长方形模中,然后以约1℃/分钟的速度退火,制得样品。
[评价方法]
折射率(nd)是相对于氦d线的折射率,阿贝数(vd)由vd=(nd-1)/(nF-nC)求得。这里,nF、nC分别是相对于氢F线和氢C线的折射率。另外,折射率用折射率计(卡鲁尼光学工业公司(カルニュ一光学工業社)制、商品名:KRP-2)测定。用热分析装置(精工仪器公司(セィコ一ィンスッル社)制、商品名:EXSTAR6000TG/DTA)通过差热分析(DTA)来测定得到的各玻璃粉末的玻璃化温度(Tg)。测定条件为以10℃/分钟升温。
关于化学耐久性,将样品在高温高湿下长时间保持,用保持前后的透射率变化来评价。具体而言,将以15mm×15mm的面为两面镜面的15mm×15mm ×10mm大小的平板状样品在温度60℃、相对湿度90%下保持336小时,用分光装置(日立制作所制、商品名:U-3500)测定保持前后的透射率,算出透射率变化Δ(%)=透射率(高温高湿保持后)-透射率(高温高湿保持前)的绝对值|Δ(%)|。透射率变化越小,化学耐久性越高。另外,例1~例3以3次的平均值、例4~例7以2次的平均值、例8~例11以1次的测定值、例12和例13以2次的平均值分别表示。
关于玻璃的熔解性等,上述样品制作时肉眼观察的结果表明:例4~例13的熔解性没有问题,得到的玻璃样品中未发现气泡、波筋。
[表1]
例1 | 例2 | 例3 | |
P2O5 | 71.0 | 73.0 | 74.0 |
B2O3 | 2.0 | 2.0 | 5.0 |
Al2O3 | 14.0 | 11.0 | 12.0 |
MgO | - | 2.0 | - |
CaO | - | - | - |
Li2O | - | - | - |
K2O | 13.0 | 12.0 | 9.0 |
折射率 | 1.51 | 1.51 | 1.52 |
阿贝数 | 71.0 | 70.5 | 70.6 |
Tg/℃ | - | - | - |
Δ/% | 0.37 | 0.26 | 0.26 |
[表2]
例4 | 例5 | 例6 | 例7 | 例8 | |
P2O5 | 77.0 | 77.4 | 77.5 | 77.4 | 77.0 |
B2O3 | - | 3.5 | 2.3 | 4.7 | 4.6 |
Al2O3 | 17.0 | 15.4 | 16.3 | 14.5 | 14.5 |
MgO | - | - | - | - | - |
CaO | 4.7 | 1.9 | 1.9 | 1.9 | 1.9 |
Li2O | 1.2 | 1.8 | 2.0 | 1.5 | 2.0 |
K2O | - | - | - | - | - |
折射率 | 1.53 | 1.53 | 1.53 | 1.53 | 1.53 |
阿贝数 | 69.8 | 70.4 | 69.8 | 70.8 | 70.5 |
Tg/℃ | - | 562 | 554 | 575 | 535 |
Δ/% | 0.01 | 0.00 | 0.00 | 0.01 | 0.01 |
[表3]
例9 | 例10 | 例11 | 例12 | 例13 | |
P2O5 | 77.4 | 77.8 | 77.4 | 74.6 | 75.0 |
B2O3 | 4.7 | 4.7 | 4.7 | 3.4 | 4.5 |
Al2O3 | 15.0 | 15.0 | 15.0 | 14.8 | 14.1 |
MgO | - | - | - | - | - |
CaO | 0.9 | - | - | 1.8 | 1.8 |
Li2O | 2.0 | 2.5 | 3.0 | - | - |
K2O | - | - | - | 5.3 | 4.6 |
折射率 | 1.53 | 1.53 | 1.53 | 1.52 | 1.52 |
阿贝数 | 70.8 | 70.8 | 70.8 | 70.5 | 70.7 |
Tg/℃ | 564 | 551 | 535 | 620 | 614 |
Δ/% | 0.01 | 0.01 | 0.01 | 0.02 | 0.02 |
产业上利用的可能性
本发明的磷酸盐光学玻璃是色散性低且折射率为所需数值的光学玻璃,化学耐久性优异,而且加压成形性优异,因此可用作精密加压成形用光学玻璃。
另外,在此引用2005年10月26日提出申请的日本专利申请2005-311293号的说明书、权利要求书以及摘要的全部内容,作为本发明说明书的揭示。
Claims (5)
1.磷酸盐光学玻璃,其特征在于,按质量%计含有P2O5:73~85、Al2O3:14~26、K2O+Li2O:1~12、SiO2:0~12、B2O3:0~12、Na2O:0~12、Y2O3:0~12、La2O3:0~12、MgO+CaO+SrO+BaO:0~12、ZrO2+TiO2+Gd2O3:0~10、Ta2O5+GeO2+Ga2O3+Nb2O5+WO3+TeO2:0~10、Sb2O3:0~2、ZnO+PbO:0~12的玻璃成分。
2.如权利要求1所述的磷酸盐光学玻璃,其特征在于,按质量%计含有P2O5:74~80、Al2O3:15~25、K2O+Li2O:1~8的玻璃成分。
3.如权利要求1或2所述的磷酸盐光学玻璃,其特征在于,含有1~4质量%的Li2O。
4.如权利要求1~3中任一项所述的磷酸盐光学玻璃,其特征在于,折射率(nd)为1.45~1.65,且阿贝数(vd)为65~80。
5.如权利要求1~4中任一项所述的磷酸盐光学玻璃,其特征在于,玻璃化温度(Tg)为600℃以下。