CN101299412B - Semiconductor device and method of manufacturing the same - Google Patents
Semiconductor device and method of manufacturing the same Download PDFInfo
- Publication number
- CN101299412B CN101299412B CN2008101096222A CN200810109622A CN101299412B CN 101299412 B CN101299412 B CN 101299412B CN 2008101096222 A CN2008101096222 A CN 2008101096222A CN 200810109622 A CN200810109622 A CN 200810109622A CN 101299412 B CN101299412 B CN 101299412B
- Authority
- CN
- China
- Prior art keywords
- laser
- semiconductor film
- semiconductor device
- tft
- crystal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention provides a semiconductor device and a manufacturing method. The invention provides to a method to manufacture the semiconductor device, and a semiconductor device using the method thereof. When a laser crystallization method is used, no grain boundary is formed in a TFT channel forming area, and marked reduction of TFT mobility, reduction of the making current and increasement of turn-off current caused by grain boundary are prevented. Concaves or convexes of a bar shape or a rectangular shape are formed. Semiconductor films are formed on an insulation film using continuous wave laser along the Y direction or the X direction of concaves or convexes of the bar shape the rectangular shape. Althrough continuous wave laser is preferable, impulse wave laser can also be used.
Description
The present patent application be the present patent application people on January 28th, 2003 submit to, application number is 03102283.9, denomination of invention is divided an application for the patent application of " semiconductor device and manufacture method thereof ".
Technical field
The present invention relates to the film formed semiconductor device of semiconductor that a kind of use has crystalline texture, and relate to a kind of method of making this semiconductor device.The invention still further relates to a kind of particularly semiconductor device of thin-film transistor of field-effect transistor that comprises, wherein, the island semiconductor district that comprises channel formation region is formed by the crystal semiconductor film that is formed on the insulating surface, and relates to a kind of method of making this semiconductor device.
Background technology
In recent years, the technology that forms TFT on substrate obtained very fast progress, and its application and active matrix semiconductor display device are also developed.Particularly, owing to use field-effect mobility (the being also referred to as mobility) ratio of the TFT of polycrystal semiconductor film to use the height of conventional amorphous semiconductor film, make high-speed cruising become possibility.Therefore, might be by forming the drive circuit control pixel on the same substrate that forms pixel thereon, though the drive circuit control that pixel is provided outward by substrate usually.
Incidentally, for the substrate that is used in the semiconductor device,, think that glass substrate has more prospect than monocrystalline substrate according to cost.Equally, on the dielectric substrate of making by glass etc., form amorphous silicon film, and the technology of using laser treatment to carry out crystallization is known.The glass substrate poor heat resistance, and be easy to temperature distortion.Therefore, under multi-crystal TFT was formed on situation on the glass substrate, for fear of the thermal deformation of glass substrate, the crystallization that laser annealing is used for semiconductor film was very effective.Silicon fiml formation thin-film transistor (TFT hereinafter referred to as) with crystallization is applied to for example liquid crystal display device.
Compare with the method for annealing that adopts radiation heating or heat conduction heating, laser annealing has the characteristic such as the remarkable reduction processing time.In addition, semiconductor or semiconductor film optionally or are partly heated, and make substrate almost be subjected to less than fire damage.
Note, here term " laser anneal method " for example refers to, be used for to be formed on the affected layer technology of crystallization again in Semiconductor substrate or the semiconductor film, be used for the method that crystallization is formed on the technology of the semiconductor film on the substrate and improves the degree of crystallinity of the semiconductor film with crystal structure.This also comprises and is used for complanation or improves Semiconductor substrate or the technology of the surface quality of semiconductor film.Available laser oscillation apparatus has: the gas laser oscillation device that with the excimer laser is representative; Be the solid laser oscillation device of representative with the YAG laser.Known this device is by carrying out crystallization in about tens nanoseconds to the extremely short semi-conductive superficial layer of time internal irradiation LASER HEATING of tens microseconds.
An example by the crystallizing amorphous semiconductor film of use laser irradiation is by the patent documentation 1 disclosed a kind of technology that illustrates below, wherein laser is to be equal to or greater than the high-velocity scanning of beam spot diameter, * 5000/sec, thus, carry out the crystallization of amorphous semiconductor film, so that do not prepare polycrystal semiconductor film reaching under the state that amorphous semiconductor film melts fully.Disclose a kind of like this technology in the patent documentation of listing below 2, the laser irradiation of wherein pulling out is to the semiconductor film that forms crystal region basically that forms island.Perhaps, known a kind of method, wherein light beam is treated to linearly by the optical system that resembles disclosed laser processing apparatus in the patent documentation of listing below 3, and carries out irradiation.
In addition, the technology of a kind of TFT of manufacturing is disclosed in the patent documentation of listing below 4, wherein, with for example Nd:YVO
4Laser solid-state laser oscillation device to amorphous semiconductor film, forms the second harmonic irradiation of laser thus with the crystal semiconductor film of common formation and compares the crystal semiconductor film with big crystallite dimension.
[patent documentation 1]
JP 62-104117A (the 92nd page)
[patent documentation 2]
United States Patent (USP) 4,330,363 (Fig. 4)
[patent documentation 3]
JP 8-195357A (3-4 page or leaf, Fig. 1-5)
[patent documentation 4]
JP 2001-144027A (the 4th page)
Long ago just begun on insulating surface, to form the trial of single crystal semiconductor films,, proposed a kind of technology that is known as figure extension (graphoepitaxy) as the trial that makes progress very much.The figure extension is a kind of like this technology, wherein on quartz substrate surface, form a step, on quartz substrate, form amorphous semiconductor film or polycrystal semiconductor film, heat-treat with laser beam or heater then, become epitaxially grown layer by the step shape that is formed on the quartz substrate as karyomorphism thus.This technology is for example open by non-patent literature 1 grade.
[non-patent literature 1]
" use silicon on the fused silica of surperficial micrographics and laser crystallization method the figure extension (Grapho-Epitaxy of Siliocn on Fused Silica Using SurfaceMicropatterns and Laser Crystallization ", J.Vac.Sci.Technol.16 (6), 1979, pp1640-1643.
In addition, a kind of semiconductor film crystallization technology that is called the figure extension is for example disclosed in non-patent literature 2 equally.It is a kind of like this technology, wherein the epitaxial growth of carrying out semiconductor film by the concave-convex surface grid (relief grating) of introducing artificial formation on the amorphous substrate surface is attempted.Disclosed figure epitaxy technology is a kind of like this technology in non-patent literature 2, wherein in the surface of dielectric film, form step, by heat-treat being formed on semiconductor film on the dielectric film, laser irradiation or other handle the epitaxial growth that obtains the semiconductor film crystal.
[non-patent literature 2]
M.W.Geis waits people's " by silicon metal on the insulator of figure extension acquisition " Technical Digest of International Electron Devices Meeting, and 1979, p.210.
Be divided into two types according to the oscillation method laser beam: impulse hunting and continuous oscillation.In the pulsed oscillation laser device, the output energy is high relatively, makes to be set at several cm by the size that will restraint spot
2Or can increase the production in enormous quantities rate greatlyyer.Especially, when using optical system to handle the shape of bundle spot and make it become 10cm or longer when linear, might be effectively with laser irradiation to substrate and further improve the production in enormous quantities rate.Therefore, for the crystallization of semiconductor film, use the pulsed oscillation laser device to become main flow.
But in recent years, found when continuous wave laser is used for the crystallization semiconductor film particle size of the crystal that in semiconductor film, forms big when using pulsed oscillation laser.By the crystal of larger particle size in the semiconductor film, by the mobility increase of the film formed TFT of this semiconductor.As a result, continuous-wave laser beam receives publicity suddenly at present.
The crystal semiconductor film that uses the laser degradation method to make, this method roughly is divided into pulse wave and continuous-wave mode, is formed with the aggregation of great number of grains usually.The position of crystal grain and size are at random, and when forming the crystal semiconductor film, are difficult to regulation crystal grain position and size.Therefore there is intercrystalline interface (crystal boundary) by above-mentioned crystal semiconductor film pattern being turned in the active layer that island forms.
Opposite with crystal grain, owing to non crystalline structure, crystal defect etc., in crystal boundary, there are countless complex centres and trapping centre.Known charge carrier is captured at trapping centre, and the current potential of crystal boundary raises, and becomes potential barrier with respect to the charge carrier crystal boundary, and therefore the current transfer characteristic of charge carrier reduces.Particularly have crystal boundary in the TFT active layer, the characteristic of TFT is produced very large influence in channel formation region, wherein the TFT mobility significantly descends, because electric current flows in crystal boundary, making current reduces, and cut-off current increases.In addition, the characteristic of a plurality of TFT that make under the prerequisite that can obtain identical characteristic can be depending on the existence of crystal boundary in the active layer and changes.
Owing to position and the size of following reason to the crystal grain of semiconductor film irradiation laser acquisition becomes at random.Need the regular hour up in the liquid semiconductor film, producing solid-state nuclear, melt fully by this liquid semiconductor film of irradiation laser.As time goes at the countless nucleus of region generating that melts fully, and from each nucleus growth crystal.The position that produces nucleus is at random, so the nucleus non-uniform Distribution.Crystal growth stops when nucleus meets each other, so the position of crystal grain is at random with size.
Ideal situation is, forms the channel formation region that the TFT characteristic is produced a very large impact by single crystal grain, eliminates the influence of crystal boundary thus.But, almost be impossible by wherein not having the amorphous silicon film of crystal boundary with laser anneal method formation.Therefore can not be desirably among the TFT that uses the crystal silicon film that adopts the laser anneal method crystallization, obtain to be equivalent to the characteristic of the MOS transistor of on monocrystalline substrate, making.
By the semiconductor film on the single crystalline substrate being heated to the method for high temperature from the molten state recrystallization, be known as zone-melting process etc., be a kind of main stream approach, so that on dielectric film, form high-quality crystal semiconductor film with the orientation of aligning, less defective, less crystal boundary and less sub boundary.
Adopt the suprabasil step of similar known figure epitaxy technology, crystal is grown along step thus, but the step that is retained in the surface of single crystal semiconductor films of formation is considered to a problem.In addition, can not on glass substrate, form single crystal semiconductor films with the figure epitaxy method with low DEFORMATION POINTS.
In any case, can not form a kind of like this crystal semiconductor film, wherein do not exist the semiconductor volume that causes by crystallization shrink, because the defective that produces with the thermal stress of substrate, lattice mismatch etc., crystal boundary and sub boundary.Except the SOI (silicon-on-insulator) of bonding, on being formed on insulating surface, carry out then in the crystal semiconductor film of crystallization or recrystallization, still can not obtain and the quality that is formed on the MOS transistor equivalence on the single crystalline substrate.
Summary of the invention
Consider the problems referred to above, the object of the present invention is to provide a kind of semiconductor device that constitutes by high-speed semiconductor element with high current drives performance, wherein the crystal semiconductor film is formed on the insulating surface, and the crystal semiconductor film has the least possible crystal boundary and sub boundary of intersecting with orientation at least.
In addition, another purpose provides a kind of method of making semiconductor device, and the semiconductor device of this manufacture method manufacturing of a kind of usefulness, wherein use a kind of like this laser crystallization method, it can prevent to form crystal boundary in the TFT channel formation region, and can prevent all because remarkable decline, the minimizing of making current and the increase of cut-off current of the TFT mobility that crystal boundary causes.
Applicant of the present invention finds, if form semiconductor film on the dielectric film with depression and projection, with this semiconductor film of laser irradiation, then will optionally form crystal boundary in the crystal semiconductor membrane portions that is arranged on the projection of dielectric film.
Figure 19 A illustrates, when being formed on the thick non-single crystal semiconductor film of 200nm on the dielectric film with depression and projection with the sweep speed irradiation of 5cm/sec with continuous wave laser, along the TEM profile image perpendicular to the direction of laser scanning direction.Reference number 8001 among Figure 19 B and 8002 expressions are formed on the projection in the dielectric film.In the part of crystal semiconductor film 8004 on projection 8001 and 8002 crystal boundary 8003 is arranged.
Schematically show the TEM profile image shown in Figure 19 A among Figure 19 B.In the top of projection 8001 and 8002, form crystal boundary 8003.Applicant of the present invention thinks, the semiconductor film that is arranged on the dielectric film top shifts to the bottom volume of depression, because its temporary transient molten state that causes by laser irradiation, therefore, the semiconductor film attenuation that is arranged in top consequently can not meet with stresses, and wherein begins the crystal boundary of growing.Though the semiconductor film of crystallization forms crystal boundary selectively in the top of projection thus, crystal boundary is difficult for forming (zone that dots) in being arranged in the part of depression.Notice that the expression of term depression does not form the sunk area of projection.
So applicant of the present invention thinks, can determine the position that crystal boundary forms selectively by forming the part that stress is concentrated in the semiconductor film wittingly.On substrate, form dielectric film in the present invention, on dielectric film, form semiconductor film with depression and projection.Carrying out in the crystallization process with laser thus, in semiconductor film, forming the part that stress is concentrated selectively.Particularly, in semiconductor film, form depression and projection.Then along the depression and the protruding vertical irradiation continuous wave laser that are formed in the semiconductor film.Noting, is most preferred though use continuous wave laser this moment, also can use impulse wave laser.Noting, can be rectangle, triangle or trapezoidal at the cross section perpendicular to the direction projection of laser scanning direction.
For this structure, so, on the projection of semiconductor film, optionally form crystal boundary with in the process of laser crystallization.Be difficult to form crystal boundary in the semiconductor film on being arranged in the depression of dielectric film relatively.The semiconductor film that is arranged on the dielectric film depression has superior degree of crystallinity, but does not always comprise crystal boundary.But, even there is crystal boundary, to compare with the semiconductor film on the projection that is positioned at semiconductor film, crystal grain is also bigger, and degree of crystallinity is better.Therefore in the stage of the shape that designs dielectric film, can predict the position that in semiconductor film, forms crystal boundary to a certain extent.That is, the position that forms crystal boundary in the present invention can be determined selectively, therefore, might design active layer, makes in active layer, preferably comprises the least possible crystal boundary in channel formation region.
By the present invention, be used for the TFT active layer by the semiconductor film that will be arranged in effectively on the dielectric film depression, can prevent the formation of crystal boundary in the TFT channel formation region.Can prevent that all from being because remarkable reduction, the minimizing of making current and the increase of cut-off current of the TFT mobility that crystal boundary causes.Notice that the designer can suitably determine will be by graphically removal and part raised or sunken vicinity.
In order to address the above problem, according to the present invention, provide a kind of method of making semiconductor device, it comprises:
Form dielectric film having on the substrate of insulating surface, this dielectric film has opening portion;
Forming non-single crystal semiconductor film on the dielectric film and in opening portion;
The fusing non-single crystal semiconductor film carries out crystallization or recrystallization and forms the crystal semiconductor film of filling insulation film opening portion; And
Form gate insulating film and gate electrode, make the crystal semiconductor film of filling opening part by by gate insulating film and gate electrode.
Opening portion can form on the surface by the etching dielectric substrate, and the also available silicon oxide film of opening portion, silicon nitride film, oxygen silicon nitride membrane etc. and carry out etching thereon and form.Opening portion should be arranged in and comprise the position that thin film transistor channel forms the island semiconductor zone in district, and is preferably formed opening portion with consistent with channel formation region at least.
The amorphous semiconductor film of the polycrystal semiconductor film that forms by plasma CVD, sputter or low pressure chemical vapor deposition, the polycrystal semiconductor film that forms by solid state crystal growth etc. is applied on the semiconductor film of on-monocrystalline.Note, the term amorphous semiconductor film of Shi Yonging comprises that not only it has the strict difinition of the semiconductor film of complete non crystalline structure in the present invention, also comprises semiconductor film that is in the so-called microcrystalline semiconductor film that comprises crystallite crystal grain attitude and the semiconductor film that comprises local-crystalized structure.Usually use amorphous silicon film.In addition, also can use amorphous silicon germanium film, amorphous silicon carbide film etc.
Impulse wave that application produces as the gas laser oscillation device of light source or solid-state laser oscillation device or continuous wave laser are as the fusing non-single crystal semiconductor film and carry out the equipment of crystallization.The laser of irradiation is linear with optical system optically focused.The intensity distributions of laser vertically has homogeneous area, and also can laterally have distribution.Solid-state laser oscillation device with rectangular light beam is used as the laser oscillation apparatus that is used for light source.Particularly, advantageous applications dish type (s lab) laser oscillation apparatus.Perhaps, can use such structure, wherein the solid-state laser oscillation device adopts the rod that mixes with Nd, Yb, Tm and Ho, particularly uses by Nd, Tm and Ho doped YAG, YVO
4, YLF, YAlO
3Make up Deng the solid-state laser oscillation device of crystal and the amplifier of disk-shaped structure.Crystal Nd:YAG, Nd:GGG (Gd-Ga garnet), Nd:GSGG (gadolinium scandium gallium garnet) etc. can be used as disk material.After the disk laser is the zigzag light path, and total reflection simultaneously repeats in tabular laser medium.
In addition, also can use high light corresponding to laser.For example, also can use by using the light with high-energy-density of optically focused such as speculum, lens by the light of Halogen lamp LED, xenon lamp, high-pressure mercury lamp, metal halide lamp or Excimer lamp emission.
Expansion be that linear laser or high light is irradiated onto non-single crystal semiconductor film by optically focused, and the substrate that laser irradiation position and its are gone up the formation non-single crystal semiconductor film moves relative to each other.The part of laser scanning substrate or entire substrate melt non-single crystal semiconductor film thus, and carry out crystallization or crystallization again.Preferably carry out laser scanning in direction longitudinally vertical or channel formation region along opening portion.So crystal is grown along laser scanning direction, can prevent that crystal boundary and sub boundary and raceway groove from vertically intersecting.Notice that the present invention always is not limited to this.
The semiconductor device of the present invention of Zhi Zaoing is characterised in that it comprises as mentioned above:
Substrate with insulating surface;
Be formed on the substrate and have the dielectric film of opening portion; And
Be formed on the substrate and have the crystal semiconductor film with the channel formation region in the zone of filling of filling this opening portion.
According to another structure of the present invention, semiconductor device is characterised in that it comprises:
Substrate with insulating surface;
Be formed on the substrate and have along the dielectric film of the opening portion of raceway groove longitudinal extension; And
Be formed on the substrate and have the zone of this filling opening part and the crystal semiconductor film of the channel formation region in the zone of filling,
Wherein, opening portion has the degree of depth of the degree of depth that is equal to or greater than the crystal semiconductor film.
According to another structure of the present invention, semiconductor device is characterised in that it comprises:
Insulating surface with the opening portion that extends with rectangular shape or shape of stripes;
Be formed on the crystal semiconductor film in the opening portion;
Gate insulating film; And
By gate insulating film and the overlapping gate electrode of crystal semiconductor film.
According to another structure of the present invention, semiconductor device is characterised in that it comprises:
Have along the insulating surface of the axially extended opening portion of raceway groove;
Be formed on the crystal semiconductor film in the opening portion;
Gate insulating film; And
By gate insulating film and the overlapping gate electrode of crystal semiconductor film.
Have the identical order of magnitude by the degree of depth that makes opening portion with the thickness of semiconductor film, or greater than the thickness of semiconductor film, because surface tension will be assembled and be solidificated in the opening portion (being sunk part) by the semiconductor of laser or high light fusing.As a result, the thickness of the middle semiconductor film of opening portion (being bossing) is with attenuation, and the stress distortion can be concentrated in the there.In addition, the side surface of opening portion has the effect that limits crystal orientation to a certain extent.The angle of opening portion side surface forms 5-120 ° with respect to substrate surface, preferably at 80-100 °.
By behind irradiation laser or the high light melting semiconductor film, the zone of intersecting from the lower surface and the side surface of opening portion begins to solidify, and crystal growth from here on.For example, Figure 17 is illustrated in the result that some A, B, C and D place in the system carries out hot analysis mode, and wherein, the shape of step is formed by dielectric film (1) and dielectric film (2).Obtain characteristic curve as shown in Figure 18.Heat directly runs off from the below of dielectric film (2) and from the dielectric film (1) that is present on the side surface, therefore descends the fastest in a B temperature.Order afterwards is an A, C and D.Simulation result is to be 45 ° situation for side wall angle wherein, but is 90 ° situation for angle wherein, and can think has similar phenomena qualitatively.
That is,,, assemble in its opening portion in being formed on insulating surface, and crystal growth roughly occurs from the bottom and the sidewall intersection of opening portion owing to surface tension in case semiconductor film is in molten condition.So the distortion that crystallization is followed can be concentrated in the zone in the opening portion outside.In other words, the formed crystal semiconductor film of filling opening part can be distortionless.
Notice that near the energy density the laser beam edge is usually less than the energy density near beam center, the degree of crystallinity of corresponding semiconductor film is often relatively poor.Therefore, preferably carry out laser scanning like this, making becomes the edge of the part of TFT channel formation region and ray trajectory non-overlapping copies mutually afterwards.
By the present invention, the data (pattern-information) of the relevant dielectric film of seeing above the substrate that obtains in the design phase or the shape of semiconductor film can at first be stored in the storage device.The scanning pattern of laser subsequently by pattern-information and by laser the scanning direction, and determine at laser beam width perpendicular to the direction of scanning direction, make become at least the part of TFT channel formation region not with the imbricate of laser trace.Subsequently with mark as with reference to arranging substrate location, laser is irradiated onto semiconductor film on the substrate according to determined scanning pattern.
By said structure, laser can only be irradiated onto requisite part, rather than entire substrate.So can will not need needed time decreased on the part of laser irradiation, and can increase substrate processing speed.In addition, because laser irradiation can be prevented to the substrate damage that does not need part and caused.
Notice that mark can be by directly forming with etched substrate such as laser, and mark also can be formed in the dielectric film part when formation has the dielectric film of depression and projection.In addition, the position alignment of substrate also can be carried out like this, by using the shape that reads the dielectric film or the actual semiconductor film that forms of actual formation such as the image pickup element of CCD, with shape as storage in first storage device, the dielectric film that will obtain in the design phase or the pattern-information of semiconductor film are stored in second storage device, and the data that will be stored in first storage device are checked with the pattern-information that is stored in second storage device.
Can reduce the quantity of the mask that is used for mark by in a part of dielectric film, forming mark or serving as a mark by the shape of using dielectric film.In addition, mark can be formed in the more accurate position, and with in substrate, form mark with laser and compare, the precision of position alignment can be improved.
Notice that the energy density of laser is not exclusively even usually, but energy is with the position change in the laser beam.For the present invention, the laser irradiation that needs to have fixed energies density is to the part that becomes channel formation region at least, and preferred irradiation is on all flat surperficial or protruding all flat surfaces of depression.Therefore for the present invention, need to use laser beam with Energy distribution, make have energy density fully uniformly the zone at least with become overlapping of channel formation region, and flat surperficial or protruding all flat surperficial overlapping of all of preferred and depression.Can think that the shape of laser beam is preferably rectangle, linear etc. so that satisfy aforementioned energy density condition.
In addition, by using slit can stop that laser beam has the part of low energy densities.Arrive all flat surface or protruding all flat surfaces of depression by the laser irradiation of using slit can have relative homogeneous energy density, and can carry out crystallization equably.And can partly change the width of laser beam with slit according to dielectric film or semiconductor film pattern-information.The layout of channel formation region and other TFT active layer can be subjected to less restriction.Notice that term laser beam width means laser beam edge is perpendicular to the length of the direction of scanning direction.
In addition, the laser beam that is obtained by a plurality of laser oscillation apparatus emitted laser by combination also can be used in the laser crystallization.By using said structure, the part that energy density is low in each laser can be replenished mutually.
In addition, can be after forming semiconductor film, under the situation that is not exposed to external environment condition atmosphere, carry out laser irradiation (for example, under the particular atmosphere of inert gas, nitrogen, oxygen etc., or in reduced atmosphere), thus the crystallization semiconductor film.When carrying out crystallization with the laser with said structure, can prevent the polluter of molecular level in the clean room, for example prevent to be used for improving the boron that contains in the filter of air cleannes etc. and sneak into semiconductor film.
Note, be called as the routine techniques of the crystallization semiconductor film of figure extension, attempted being used for the epitaxial growth of introducing by the concave-convex surface grid on the artificial amorphous substrate that forms at semiconductor film.The technology that relates to the figure extension can find in aforementioned non-patent literature 2 grades.Disclosed figure extension is in aforementioned document etc., forms step in the surface of dielectric film, heats being formed on semiconductor film on the dielectric film, laser irradiation etc., makes the crystal extension ground growth in the semiconductor film thus.But the necessary temperature of epitaxial growth is at least about 700 ℃.If on glass substrate, carry out epitaxial growth, in semiconductor film, near the edge of the depression of dielectric film or projection, form crystal boundary.According to the present invention, arrange an island mask, the shape of dielectric film depression or projection with and the position at edge be designed to corresponding to the island mask so that improve degree of crystallinity in the part that becomes the island.Particularly, the shape, size etc. of depression or projection are determined near the center that makes between the edge of the edge of depression or projection and depression and projection not overlapping with the island.Thus with being designed to wittingly and optionally determine the position of crystal boundary corresponding to the dielectric film of the layout on island.Can remove the part that crystal boundary is formed selectively in the semiconductor film subsequently, and the part with superior relatively degree of crystallinity can be used as the island.Therefore disclosed in the present invention technology is consistent with conventional figure extension in the following areas: formed therein on the dielectric film of step and formed semiconductor film; And utilize this step crystallization semiconductor film.But the position of step control crystal boundary is not used in the Yanzhong outside conventional figure, and the Yanzhong does not comprise the notion that reduces crystal boundary in the island outside conventional figure.Routine techniques is only similar with the present invention and different with the present invention.
Description of drawings
In the accompanying drawing:
Fig. 1 is the perspective view that is used to explain crystallization method of the present invention.
Fig. 2 is the perspective view that is used to explain crystallization method of the present invention.
Fig. 3 is the perspective view that is used to explain crystallization method of the present invention.
Fig. 4 is the perspective view that is used to explain crystallization method of the present invention.
Fig. 5 A-5E is the longitdinal cross-section diagram that is used to explain the details of the relation between the form of the shape of crystallization process split shed part and crystal semiconductor film.
Fig. 6 A and 6B are the layouts that the embodiment of the laser irradiating device of using in the present invention is shown.
Fig. 7 A-7C is respectively applied for upper surface view and the longitdinal cross-section diagram of explaining the technology of making the TFT that makes by the present invention.
Fig. 8 A-8C is respectively applied for upper surface view and the longitdinal cross-section diagram of explaining the technology of making the TFT that makes by the present invention.
Fig. 9 A-9C is respectively applied for upper surface view and the longitdinal cross-section diagram of explaining the technology of making the TFT that makes by the present invention.
Figure 10 A-10C is respectively applied for upper surface view and the longitdinal cross-section diagram of explaining the technology of making the TFT that makes by the present invention.
Figure 11 A-11C is respectively applied for upper surface view and the longitdinal cross-section diagram of explaining the technology of making the TFT that makes by the present invention.
Figure 12 A-12C is respectively applied for upper surface view and the longitdinal cross-section diagram of explaining the technology of making the TFT that makes by the present invention.
Figure 13 A-13C is respectively applied for upper surface view and the longitdinal cross-section diagram of explaining the technology of making the TFT that makes by the present invention.
Figure 14 A-14D is respectively applied for upper surface view and longitdinal cross-section diagram and its guide wire of alternative shape of explaining the technology of making the TFT that makes by the present invention.
Figure 15 A-15C is the outline drawing of display panel.
Figure 16 is the upper surface view of structure that is used to explain the pixel parts of the display panel made from the present invention.
Figure 17 is the sectional view that is illustrated in the structure of using in the hot analysis mode.
Figure 18 is the curve that the result of hot analysis mode is shown.
Figure 19 A and 19B are respectively the TEM cross-sectional images after being formed on semiconductor film on the lobed basilar memebrane to carry out crystallization with laser irradiation, and the schematic diagram of image.
Figure 20 A-20C is the view that semiconductor film crystallization flow process of the present invention is shown.
Figure 21 A-21C is the view that the technology of making TFT of the present invention is shown.
Figure 22 A and 22B are the views that the technology of making TFT of the present invention is shown.
Figure 23 A and 23B are the views that the technology of making TFT of the present invention is shown.
Figure 24 A and 24B are the views that the technology of making TFT of the present invention is shown.
Figure 25 A-25C is the view that the technology of making TFT of the present invention is shown.
Figure 26 A and 26B are the sectional views of TFT.
Figure 27 A and 27B are the sectional views of TFT.
Figure 28 A-28D is the view that the technology of making TFT of the present invention is shown.
Figure 29 A-29D is the view that the technology of making TFT of the present invention is shown.
Figure 30 A and 30B are the upper surface view that forms a plurality of TFT on the basilar memebrane.
Figure 31 A-31E illustrates when using catalytic elements the view of the crystallization flow process of semiconductor film of the present invention.
Figure 32 is the view of laser irradiating device.
Figure 33 is the view of laser irradiating device.
Figure 34 A-34D is the view that the technology of making lobed basilar memebrane is shown.
Figure 35 A-35C is the view that the technology of making lobed basilar memebrane is shown.
Figure 36 A-36D is the view that the energy density distribution of laser beam is shown.
Figure 37 A and 37B are the views that the energy density distribution of laser beam is shown.
Figure 38 is the view that the energy density distribution of laser beam is shown.
Figure 39 is the view of optical system.
Figure 40 is the view of energy density distribution that the central axis direction of overlapped laser beam is shown.
Figure 41 be illustrate in the laser beam in the heart distance and the view of the relation between the energy difference.
Figure 42 is the view of output Energy distribution that is illustrated in the central axis direction of laser beam.
Figure 43 is the view that the structure of luminescent device is shown, and this luminescent device is an example of semiconductor device of the present invention.
Figure 44 is the view that the pixel structure of luminescent device is shown, and this luminescent device is an example of semiconductor device of the present invention.
Figure 45 A-45H is to use the view of the electronic equipment of semiconductor device of the present invention.
Figure 46 A and 46B are respectively the sectional views with TFT of laminated construction, and the example of structure that uses the semiconductor device of this TFT.
Figure 47 A-47C is the view that the frequency distribution of S value is shown.
Figure 48 A-48C is the view that the frequency distribution of threshold voltage is shown.
Figure 49 A-49C is the view that the frequency distribution of mobility is shown.
Figure 50 A-50C is the view that the frequency distribution of threshold voltage is shown.
Figure 51 A-51C is the view that the frequency distribution of mobility is shown.
Embodiment
Explain the embodiments of the invention pattern with reference to the accompanying drawings.Perspective view shown in Fig. 1 shows an embodiment, wherein, and the second dielectric film 103-105 that on substrate 101, forms first dielectric film 102 and be patterned into bar shaped.For second dielectric film, at three bar patens this illustrate, but certainly to the quantity of bar paten without limits.Substrate can be used the monocrystalline of commercial available non-alkali glass substrate, quartz substrate, Sapphire Substrate, its surface coverage dielectric film or the metal substrate of poly semiconductor substrate or its surface coverage dielectric film.
The A width W 1 that forms second dielectric film of bar shaped is made as 0.1-10 μ m (preferred 0.5-1 μ m), gap W2 between adjacent second dielectric film is set as 0.1-5 μ m (preferred 0.5-1 μ m), and the thickness d of second dielectric film be made as be formed on second dielectric film on the identical order of magnitude of the thickness of non-single crystal semiconductor film or greater than the thickness of semiconductor film.In addition, the shape of step does not need to have the periodic patterns of regulation, but can form and the layout and the shape alignment that comprise the island areas of TFT channel formation region.The length L of second dielectric film is also unrestricted, and length L can be such order of magnitude, makes for example can form the TFT channel formation region.
First dielectric film forms with silicon nitride or silicon oxynitride.In addition, second dielectric film forms with silica or silicon oxynitride.Available by mixing tetraethylorthosilicise (TEOS) and O
2Plasma CVD form silica.Can be by using SiH
4, NH
3And N
2O, or SiH
4And N
2O forms silicon oxynitride as the plasma CVD of raw material.
Preferably suitably regulating material makes that with the film formation condition etching speed of second dielectric film is relative very fast, so that, guarantee the selectivity in the etching processing forming under the situation of uneven shape by first dielectric film and second dielectric film that have as Fig. 1 shaped aperture part.The angle of sidewall by the film formed opening portion of second insulation can suitably be made as 5-120 °, preferably at 80-100 °.
As shown in Figure 2, forming thickness is that the amorphous semiconductor film 106 of 50-200nm covers the surface that is formed by first dielectric film 102 and the second dielectric film 103-105 and opening portion.But the compound of amorphous semiconductor film applying silicon, silicon and germanium or solid solution or silicon and carbon compound or solid solution.
Then, continuous wave laser irradiation amorphous semiconductor film 106 carries out crystallization.Linear shape is concentrated and expanded to available laser by optical system.The intensity distributions of laser has homogeneous area at longitudinal direction, and can have horizontal distribution.Rectangular light beam solid-state laser oscillation device is applicable as the laser oscillation apparatus as light source, especially, and advantageous applications dish type laser oscillation apparatus.Perhaps, adopt the solid-state laser oscillation device of the rod that mixes with Nd, Tm and Ho, particularly use such as by Nd, Tm and Ho doped YAG, YVO
4, YLF, YAlO
3Solid-state laser oscillation device in crystal also can make up with the amplifier of disk-shaped structure.The edge is scanned with the direction that the linear shape longitudinal direction intersects shown in arrow among the figure subsequently.Most preferably scan along being parallel to the longitudinal direction that is formed on the bar paten in the underlying insulation film this moment.Notice that used linear shape refers to the ratio of length and lateral length longitudinally, is equal to or greater than 10 here.
Can be used as disk material such as Nd:YAG, Nd:GGG (Gd-Ga garnet), Nd:GSGG crystal such as (gadolinium scandium gallium garnets).After the disk laser is the zigzag light path, and total reflection simultaneously repeats in the laser medium of flat shape.
In addition, consider the absorption coefficient of light of amorphous semiconductor film, the wavelength of preferred continuous wave laser is 400-700nm.Use second harmonic or the triple-frequency harmonics of Wavelength changing element by extracting first-harmonic to obtain light in this wave-length coverage.ADP (ammonium dihydrogen phosphate), Ba
2NaNb
5O
15(barium sodium niobate), CdSe (selenium cadmium), KDP (potassium dihydrogen phosphate), LiNbO
3(lithium niobate), Se, Te, LBO, BBO, KB5 etc. can be used as Wavelength changing element.Particularly preferably use LBO.Typical example is to use Nd:YVO
4The second harmonic (532nm) of laser oscillation apparatus (first-harmonic 1064nm).In addition, laser oscillation mode uses monotype, i.e. TEM
00Pattern.
Be chosen as the situation of only material for silicon, its absorption coefficient is 10
3-10
4Cm
-1Scope, this is near visible-range.If use substrate with high visible light transmissivity, such as glass, then form the amorphous semiconductor film that thickness is 30-200nm by silicon, but the irradiation wavelength is that the visible light of 400-700nm carries out crystallization under the situation that underlying insulation film is sustained damage then, optionally heats semiconductor regions thus.Particularly, with respect to amorphous silicon film, the seepage distance of 532nm wavelength light is near 100-1000nm, and the thickness that can fully arrive formation is the interior section of the amorphous semiconductor film 106 of 30-200nm.That is, might heat from the inside of semiconductor film, and almost whole semiconductor film can evenly be heated in the laser irradiation zone.
Because capillary effect, the semiconductor film by the laser irradiation fusing accumulates in the opening portion (depression).As shown in Figure 3, the surface almost is flat in the state that solidifies thus.In addition, on second dielectric film, form crystal growth end, crystal grain boundary and crystal sub boundary (projection is by the zone shown in the hatch mark 110 among the figure).Form crystal semiconductor film 107 thus.
Etching crystal semiconductor film 107 forms island semiconductor zone 108 and 109 as shown in Figure 4 subsequently.According to the zone 110 that growth end, crystal grain boundary and crystal sub boundary are wherein concentrated in etching and removal, can only stay the semiconductor regions of good quality.Form gate insulating film and gate electrode then, making can be by using the crystal semiconductor film location channel formation region of filling opening part (depression).So can finish TFT by each stage.
Fig. 5 A-5E be the degree of depth that is used for schematically explaining the opening portion groove (step) that forms by first dielectric film 102 and the second dielectric film 103-105, between the gap and crystal growth between the view that concerns.Notice that the reference symbol relevant with the length shown in Fig. 5 A-5E is: t01 represents the upward thickness of amorphous semiconductor film of second dielectric film (projection); T02 represents the thickness of the amorphous semiconductor film of opening portion (depression); T11 represents the upward thickness of crystal semiconductor film of second dielectric film (projection); T12 represents the thickness of the crystal semiconductor film of opening portion (depression); D represents the thickness (degree of depth of opening portion) of second dielectric film; W1 represents the width of second dielectric film; And W2 represents the width of opening portion.
Fig. 5 A is the situation of d<t02 and W1, W2≤1 μ m.If the degree of depth of opening portion groove is less than the thickness of amorphous semiconductor film 106, even through fusing and crystallization process, semiconductor is filling opening part not also, and the surface of crystal semiconductor film does not have flattened.That is, the shape of the depression of the substrate of crystal semiconductor film and projection almost obtains keeping.
Fig. 5 B is the situation of d 〉=t02 and W1, W2≤1 μ m.If the degree of depth of opening portion groove no better than or greater than the thickness of amorphous semiconductor film 106, surface tension produces and amorphous semiconductor accumulates in the opening portion (depression).As Fig. 5 B the state that solidifies thus is shown, it almost is flat that the surface becomes.In this case, t11 becomes less than t12, and stress is concentrated in having film thick part 120, and the crystal growth end is concentrated and further formed there in distortion.
Fig. 5 C be d>>t02, and the situation of W1, W2≤1 μ m.In this case, form crystal semiconductor film 107 so that the filling opening part, and on second dielectric film, almost do not stay the crystal semiconductor film.
Fig. 5 D is the situation of d 〉=t02 and W1, W2>1 μ m.If the width of opening portion expansion, though crystal semiconductor film filling opening part and have the complanation effect so, near opening portion center crystal grain boundary and the development of crystal sub boundary.In addition, stress concentrates on second dielectric film similarly, and distortion is assembled, and further forms the crystal growth end there.Can infer that this is because the Stress Release effect that is caused by wide gap is reduced.
Fig. 5 E is d 〉=t02 and W1, W2>>1 μ m, and further realizes the situation of the state of Fig. 5 D.
Explain with Fig. 5 A-5E as above, can think that the condition of Fig. 5 B is only when the formation semiconductor element particularly forms TFT.
Above-mentioned explanation shows an example of the depression and the convex shape of the substrate that is used to form the crystal semiconductor film, and wherein depression and projection are formed by first dielectric film and second dielectric film, but the embodiment pattern that illustrates here is not limited to this shape.Also can use substrate with analogous shape.For example, opening portion can be formed directly in the surface of quartz substrate, forms rough shape thus.
Fig. 6 A and 6B illustrate a kind of example that can be used to the laser machining device structure of crystallization.Fig. 6 A and 6B are front view and the end views that the laser machining device structure is shown, this device by laser oscillation apparatus 301, photochopper 302, high conversion mirror 303-306, slit 307, cylindrical lens 308 and 309, support platform 311, be used for moving the drive unit 312 and 313 of support platform 311, the control device 314 that is used for accessory drive, the information processor 315 etc. that is used for transmitting a signal to laser oscillation apparatus 301 and control device 314 and form based on program stored in advance in x direction and y direction.
Being concentrated to the cross sectional shape of irradiating surface by cylindrical lens 308 and 309 is the surface of laser oblique incidence substrate 320 on the support platform 311 of linear shape.Do making when causing the focal position to be moved like this owing to aberration such as astigmatism, can be at irradiating surface or its near zone optical surface that forms linear shape focusing.If cylindrical lens 308 and 309 is by the synthetic quartz manufacturing then can obtain high-transmission rate, and apply the surface coating that is implemented in lens, to realize being equal to or greater than 99% transmissivity with respect to optical maser wavelength.The cross sectional shape of irradiating surface is not limited to linear shape certainly, also can use the arbitrary shape such as rectangular shape, elliptical shape and oval shape.No matter use which kind of shape, be meant that all ratio with minor axis and major axis is in 1-10, shape in the 1-100 scope.In addition, prepare Wavelength changing element 310 to obtain harmonic wave with respect to first-harmonic.
As mentioned above, rectangular light beam solid-state laser oscillation device is used to laser oscillation apparatus, especially advantageous applications dish type laser oscillation apparatus.Perhaps, use by Nd, Tm and Ho doped YAG, YVO
4, YLF, YAlO
3Solid-state laser oscillation device in crystal also can make up with the amplifier of disk-shaped structure.Can be used as disk material such as Nd:YAG, Nd:GGG (Gd-Ga garnet), Nd:GSGG (gadolinium scandium gallium garnet) etc.In addition, also can use can continuous oscillation gas laser oscillation device or solid-state laser oscillation device.Adopt with Cr, Nd, Er, Ho, Ce, Co, Ti or Tm doped YAG, YVO
4, YLF, YAlO
3Laser oscillation apparatus in crystal is used as continuous wave solid-state laser oscillation device.Though dopant material difference, the fundamental wavelength of emission are 1 μ m-2 μ m.In order to obtain very high output, can use the solid-state laser oscillation device of diode excitation, and can use cascade to connect.
In addition, by moving support platform 311, may carry out the laser treatment of substrate 320 with drive unit 312 and 313 directions along two axles.For along the moving an of direction, might be with 1-200cm/sec, the constant speed of preferred 5-50cm/sec, mobile continuously support platform 311 on greater than the distance of the length of substrate one side.Might be along other direction, with the linear shape light beam longitudinally apart from the distance of same order on carry out discontinuous minute moved further.By the information processor 315 that microprocessor wherein is installed, the emission of laser oscillation apparatus 301 and support platform 311 synchronous workings.
The linear movement of the x direction that illustrates in the drawings by support platform 311 is by the whole surface that might handle substrate from the laser of fixing optical system irradiation.Position detecting device 316 detects substrate 320 and is in the position of irradiation laser, and transfers the signal to the information processor 315.The firing operation of laser oscillator and their timing are synchronous by information processor 315.That is, when substrate 320 was not in the position of laser irradiation, the laser vibration stopped, and its life-span is prolonged.
The laser that is transmitted into substrate 320 by the laser irradiating device with this kinds of structures can be handled needed zone of semiconductor film or whole surface, by its relative motion along direction of x shown in the figure and y direction.
By in underlying insulation film, forming step shape, in crystallization process, can concentrate the distortion and the stress of the crystallization of following those parts, wherein crystallization is to use continuous wave laser irradiation amorphous semiconductor film as mentioned above.Can prevent from being made into the crystal semiconductor film of active layer, to occur distortion and stress.By form TFT make channel formation region be arranged in not have distort and the crystal semiconductor film of stress in, the current drives performance in the time of might improving high speed, and also may improve the reliability of element.
Further, will explain the method for the irradiation laser that the present invention uses with Figure 20 A-20C.
At first, shown in Figure 20 A (formation non-single crystal semiconductor film), on substrate, form first basilar memebrane of making by dielectric film 9101.On first basilar memebrane 9101, form second basilar memebrane of making by the rectangle dielectric film 9102 subsequently, form the 3rd basilar memebrane 9103 so that cover first basilar memebrane 9101 and second basilar memebrane 9102.Silicon nitride is used as first basilar memebrane 9101 in the present embodiment pattern, and silica is used as second basilar memebrane 9102, and silicon oxide film is used as the 3rd dielectric film 9103.Notice that the material that is used for first dielectric film 9101, second dielectric film 9102 and the 3rd dielectric film 9103 is not limited to previous materials.Also can use other material, as long as: they are to bear the heat treated dielectric film that carries out in the treatment step in the back; They can prevent the alkali-metal pollution to the negative effect that can cause the TFT characteristic of the semiconductor film that forms subsequently; Can on them, form depression and projection.Notice that the method that is used to form this depression and projection will be explained in the back in detail.In addition, also can use other dielectric film except that these, and can use the stepped construction of two-layer or multilayer film.
Though show first dielectric film, second dielectric film and the 3rd dielectric film respectively in Figure 20 A-20C, three basilar memebranes are called as basilar memebrane 9104 generally together.Notice that though form the basilar memebrane 9104 with depression and projection with three basilar memebranes in the present embodiment pattern, the structure of the basilar memebrane that the present invention uses is not limited to this structure.
Can when forming basilar memebrane 9104, form mark with a part of basilar memebrane.
Substrate can be a kind of substrate that can bear the treatment temperature of back processing step.For example, can use quartz substrate, silicon substrate, such as the glass substrate of barium borosilicate glass and alumina-borosilicate glass, with and at the bottom of the surface goes up the metal substrate and stainless steel lining that forms dielectric film.In addition, also can use the plastic that to bear treatment temperature with heat resistance to a certain degree.
Then form semiconductor film 9105 so that cover basilar memebrane 9104.Available known method (such as sputter, LPCVD or plasma CVD) forms semiconductor film 9105.Notice that semiconductor film can be the amorphous semiconductor film, also can be microcrystalline semiconductor film or crystal semiconductor film.In addition, not only silicon can be used, also germanium can be used.In addition, be not exposed to atmosphere, can prevent impurity, to avoid to the pollution between semiconductor film and the basilar memebrane by after forming the 3rd basilar memebrane 9103, then forming semiconductor film.
Notice that the designer can suitably determine the shape and the size of the projection of basilar memebrane 9104.But the thickness that must set projection makes the semiconductor film that forms subsequently not be disconnected near raised brim at such order of magnitude.
Shown in Figure 20 B (irradiation laser), laser irradiation is to semiconductor film 9105 subsequently.Because laser irradiation, semiconductor film 9105 melts at once, and its volume is mobile to depression from the top of projection, shown in the arrow of the white heart.Formation has the semiconductor film (behind the LC) of planar surface and the degree of crystallinity that improves.Near the energy density step-down of the laser edge of laser beam, thus, crystal grain becomes less near the edge, ledge (ridge) occurs along crystal grain boundary.Therefore carrying out irradiation makes the edge of laser beam light path not with the part that becomes channel formation region be positioned at the overlapping of recess of semiconductor film 9105.
Notice that the scanning direction of setting laser makes the parallel longitudinal of projection of it and basilar memebrane 9104 like this.
The present invention can use known laser.Preferred laser is continuous wave, even but can think and use pulse wave, also can obtain effect of the present invention to a certain extent.Laser can using gases laser or solid-state laser.Excimer laser, Ar laser, Kr laser etc. are as gas laser, and YAG laser, YVO
4Laser, YLF Lasers device, YAl0
3Laser, amorphous laser, ruby laser, alaxadrite laser, Ti: sapphire laser, Y
2O
3Lasers etc. can be used as solid-state laser.Employing is such as by Cr, Nd, Er, Ho, Ce, Co, Ti, Yb or Tm doped YAG, YVO
4, YLF, YAlO
3Laser in crystal can be used as solid-state laser.Though the material difference that is used to mix can obtain to have the laser of the first-harmonic of about 1 μ m.By using nonlinear optical element can obtain harmonic wave with respect to first-harmonic.
In addition, also can use by after using nonlinear optical element to be converted to green laser the Ultra-Violet Laser that uses another nonlinear optical element to obtain by the infrared laser of solid-state laser emission.
As for semiconductor film (behind the LC) 9106, by the volume motion owing to laser irradiation, its film thickness becomes thicker on the depression of basilar memebrane 9104, and on the contrary, its film thickness becomes thinner on the projection of basilar memebrane 9104.Therefore because stress crystal boundary 9149 is easy to be created on the projection, on the contrary, on depression, obtain to have the almost state of good crystallinity.Notice that always semiconductor film (behind the LC) does not contain crystal boundary on depression.But even there is crystal boundary really, crystal grain is big, so degree of crystallinity becomes excellent relatively.
The surface of semiconductor film (behind the LC) 9106 subsequently exposes the convex upper surface of basilar memebrane 9104 thus.Note semiconductor film in the present embodiment pattern (behind the LC) 9106, the feasible convex upper surface that exposes basilar memebrane 9104.Shown in Figure 20 C (etching), in the depression of basilar memebrane 9104, form crystal semiconductor film (island) 9107 subsequently.
By using the island that obtains according to above-mentioned a series of processing step as the TFT active layer, more preferably as the TFT channel formation region, can prevent from the TFT channel formation region, to form crystal boundary, and can prevent because all TFT mobilities that crystal boundary causes significantly reduce the increase of making current minimizing and cut-off current.Notice that the designer can suitably determine will be by near the graphical part of removing concave edges or raised brim.
Example
To explain example of the present invention below.
Example 1
This example illustrates the example of making TFT, and wherein crystal silicon film is formed on the underlying insulation film with opening portion, and channel formation region is arranged in the fill area of filling opening part.
In Fig. 7 A-7C, on glass substrate 601, form thickness and be first dielectric film 602 that forms by silicon nitride of 100nm.On first dielectric film 602, form silicon oxide film, form second dielectric film 603 with photoengraving with rectangular shape pattern.With TEOS and O
2Mixture be the silicon oxide film of 150nm with plasma CYD deposition thickness, and under the condition of 400 ℃ of reaction pressure 40Pa and underlayer temperatures, with high frequency (13.56MHz) 0.6W/cm
2Electrical power density discharge, deposition thickness is the silicon oxide film of 150nm. Form opening portion 604a and 604b by etching then.
Notice that Fig. 7 A is a upper surface view, Fig. 7 B is the longitdinal cross-section diagram corresponding to Fig. 7 A middle conductor A-A ', and Fig. 7 C is the longitdinal cross-section diagram corresponding to Fig. 7 A middle conductor B-B '.Fig. 8 A-8C, 9A-9C, 10A-10C, 11A-11C and 12A-12C similarly handle.
Shown in Fig. 8 A-8C, forming thickness then is covering first dielectric film 602 of 150nm and the amorphous silicon film 605 of second dielectric film 603.Amorphous silicon film 605 is by using plasma CVD with SiH
4Form as unstrpped gas.
Carry out irradiation with continuous wave laser then, shown in Fig. 9 A-9C, carry out crystallization.Crystallization condition is: use YVO
4The continuous wave mode of laser oscillator; Assemble second harmonic (wavelength 532nm) output of 5.5W with optical system, so that obtain longitudinally Energy distribution uniformly, longitudinal size is 400 μ m and lateral dimension is 50-100 μ m; Speed with 50cm/sec scans, and carries out crystallization thus.The uniform energy density distribution of term does not mean that gets rid of energy density distribution not exclusively uniformly, but expression has ± 20% admissible energy density distribution scope.Laser machining device structure shown in Fig. 6 A and the 6B can be applicable to such laser irradiation.The laser of assembling with optical system can have in a longitudinal direction one wherein density distribution be uniform scope, and can laterally have distribution.Carry out crystallization like this and make density distribution have uniform zone in the vertical, and can be improved in the effect that is parallel to the crystal growth on the direction of laser scanning direction.
By irradiation laser under these conditions, amorphous silicon film melts at once, and along with crystallization is carried out in the motion of the striped of fusing.Surface tension works on molten silicon, and the silicon of fusion is assembled in opening portion (depression) and solidified.So the state of crystal semiconductor film filling opening part 604a and 604b forms crystal semiconductor film 606 down therein.
Shown in Figure 10 A-10C, form mask pattern then and finish etching processing, make that the crystal semiconductor film is retained among opening portion 604a and the 604b at least, form the island areas 607 and 608 that comprises channel formation region thus.
Figure 11 A-11C illustrates a kind of like this state, and wherein the upper layer side in semiconductor regions 607 and 608 forms gate insulating film 609 and gate electrode 610 and 611.Gate insulating film 609 can form by the silicon oxide film of plasma CVD with thickness 80nm.Use the alloy of tungsten or tungstenic to form gate electrode 610 and 611.By adopting this structure, channel formation region can be formed in the island semiconductor zone of filling opening part 604a and 604b.
As long as suitably form source region and drain region, low concentration drain region etc., can finish TFT subsequently.
Example 2
Example 2 illustrates the structure that forms by the processing that is similar to example 1, but shown in Figure 12 A-12C, is formed on the opening portion in second dielectric film 603, forms the zone of long and thin bar-shaped zone and the bar-shaped zone that is connected to this length and approaches.Form island semiconductor zone 620 because crystal silicon film is aimed at opening portion 604c, can finish the many channel TFT of single grid by forming gate insulating film 621 and gate electrode 622.
Example 3
Shown in Figure 13 A-13C, the thickness by forming second dielectric film for example by forming second dielectric film of 350nm, can finish by the film formed island areas 620 of crystal semiconductor being embedded among the opening portion 604d than the amorphous semiconductor thickness in the example 2.As long as form gate insulating film 621 and gate electrode 622 similarly, then can form the many channel TFT of single grid.
Example 4
Figure 14 A-14D illustrates another example of the many channel TFT of single grid.Similar with each film that in example 1-3, forms, on substrate 601, form first dielectric film 602, second dielectric film 603, island semiconductor zone 630, gate insulating film 631 and gate electrode 632.Different parts is the opening portion 604e that is formed by second dielectric film 603 among Figure 14 A-14D, in addition, after forming island semiconductor zone 630, remove second dielectric film from the periphery of the semiconductor regions that wherein forms channel formation region, so form second opening portion 625.
Near the zoomed-in view of the example the channel formation region shown in Figure 14 D.Form gate electrode 631 and contact with upper surface, form gate electrode 632 covering gate dielectric films 631 with the side surface in island semiconductor zone 630.In this case, on the top 634 of semiconductor regions 630 and side surface portion 635, form channel formation region.Can increase the zone that exhausts thus, TFT current drives performance can be improved.
Example 5
The present invention can be applicable to various types of semiconductor device, and explains the example of the display panel of making based on example 1-4.
In Figure 15 A-15C, preparation pixel parts 902, gate signal line drive circuit 901a and 901b on substrate 900, source signal line drive circuit 901c, input 935, wiring or wiring group 917.Seal pattern 940 can be overlapping with a wiring that is connected driving circuit section with input 935 or the part in the wiring group 917 with 901b, source signal line drive circuit 901c with gate signal line drive circuit 901a.Can reduce the surface area of the frame area (neighboring area of pixel parts) of display panel thus.FPC 936 is fixed in input 935.
In addition, also can usefulness mounted thereto the chip 950 of TFT of the present invention microprocessor, memory or the Media Processor/DSP (digital signal processor) etc. that form.By using the design rule different to form these functional circuits with pixel parts 902, gate signal line drive circuit 901a and 901b and source signal line drive circuit 901c.Particularly, use 1 μ m or less than the design rule of 1 μ m.For installation method without limits, can use COG method etc.
TFT shown in the example 1-4 can be used as the switch element of pixel parts 902, in addition, can be used as the function element of structure gate signal line drive circuit 901a and 901b and source signal line drive circuit 901c.
Figure 16 is the example of structure that a pixel of pixel parts 902 is shown, and preparation TFT801-803.These TFT be used for controlling preparation in the switching TFT of the light-emitting component of pixel or liquid crystal cell, TFT and drive TFT reset.
Comprise these TFT channel formation region island semiconductor zone 812-814 be formed on the semiconductor regions below layer in underlying insulation film in opening 809-811 form with aiming at.Can form island semiconductor zone 812-814 according to example 1-5.On the 812-814 of island semiconductor zone, form grid wiring 815-817, and form the wiring 820 and 821 and pixel capacitors 823 of holding wire 818, power line 819, other type by passivating film and leveling film.
So the present invention can finish display panel under the situation that display panel is not produced any influence.
Example 6
Pass the technology of using semiconductor device of the present invention to make so-called many channel TFT in the example 6 through discussion, these many channel TFT have a plurality of channel formation regions that are separated from each other mutually.
At first, shown in Figure 21 A, on insulating surface, form lobed basilar memebrane 9120.Notice that Figure 21 B illustrates along the sectional view of Figure 21 A middle conductor A-A ', and Figure 21 C illustrates along the sectional view of the line segment B-B ' of Figure 21 A.
Used basilar memebrane 9120 has and the identical structure of structure shown in the embodiment pattern in the example 6.Basilar memebrane 9120 is made up of three basilar memebranes.At first, form second basilar memebrane of forming by the silica of rectangular shape 9122 on first basilar memebrane 9121 forming, and form the 3rd basilar memebrane 9123 formed by silica so that cover first basilar memebrane 9121 and second basilar memebrane 9122 by silicon nitride.Basilar memebrane 9120 is formed by first basilar memebrane 9121, second basilar memebrane 9122 and the 3rd basilar memebrane 9123 in the example 6.The projection 9124 of basilar memebrane 9120 is by rectangular shape second dielectric film 9122 and do not contacted part the 3rd dielectric film 9123 structure of first dielectric film 9121 by contact second dielectric film 9122.
Note, though the designer can suitably set the shape and the size of depression 9124, need be with thickness setting at such order of magnitude, make the disconnection of the semiconductor film that forms later not appear near the edge of projection 9124.The height setting of depression 9124 is about 0.1-1 μ m in example 6.
Notice that the distortion of substrate causes the influence to the shape of the basilar memebrane that forms later.The distortion of basilar memebrane becomes the reason to the inhomogeneity interference of the degree of crystallinity of the semiconductor film that forms in the back, therefore, the surperficial available cmp method of substrate (CMP method) polishing, make distortion difference be suppressed in the level that is equal to or less than 10nm, and can be before forming basilar memebrane heated substrate in advance, make substrate not be out of shape because of the heat treatment process in the processing step of back.
Form the amorphous semiconductor film 9125 that covers basilar memebrane 9120 subsequently.Can form non-single crystal semiconductor film 9125 by using known method (such as sputter, LPCVD or plasma CVD).Forming thickness with plasma CVD in example 6 is the non-single crystal semiconductor film 9125 of 300nm.
Shown in Figure 22 A, laser irradiation is carried out crystallization thus to non-single crystal semiconductor film 9125 subsequently.Notice that Figure 22 B is corresponding to the sectional view along the phantom line segments A-A ' of Figure 22 A.Use continuous wave YVO in the example 6
4Laser carries out irradiation with the sweep speed of 50cm/sec.This moment, the laser scans direction was such, and its direction identical with carrier moving direction in the channel formation region that forms is later aimed at.As have shown in the arrow of the white heart, in example 6 at the longitudinal direction of the projection 9124 of scanning direction and rectangular shape to punctual irradiation laser.Since laser irradiation, semiconductor film 9125 fusings of on-monocrystalline, and its volume to the depression motion, forms crystal semiconductor film 9126 from projection 9124 thus.
Graphical crystal semiconductor film 9126 shown in Figure 23 A forms sub-island (sub-island) 9127 thus subsequently.Notice that Figure 23 B is corresponding to the sectional view along Figure 23 A of phantom line segments A-A '.Sub-island 9127 parts are present on the projection that forms between the depression 9124.Be positioned at part on the depression with crystal semiconductor film 9126, form the channel formation region of the many channel TFT of target, therefore, determine that by quantity, channel length and the channel width of considering channel formation region the position relation between sub-island 9127 and the projection 9124 is necessary.
Subsequently, shown in Figure 24 A, by remove the degree formation island 9128 of sub-island 9127 from upper surface to the upper surface that exposes projection 9124.Notice that Figure 24 B is corresponding to the sectional view along the phantom line segments A-A ' of Figure 24 A.Can for example can remove by using any method sub-island 9127 of surface removal from it, also can use the CMP method to remove by using etching.
Remove the part that on projection 9124, has crystal boundary by the upper surface of removing sub-island 9127.On depression, there is crystal boundary hardly, and becomes in the back in the part of channel formation region, keep crystal semiconductor film with excellent degree of crystallinity corresponding to the interval between the projection 9124.Shown in Figure 24 A and 24B, form slit-type island 9128, wherein only form channel formation region separately.Notice that the same with channel formation region, because the degree of crystallinity of semiconductor film, the part that becomes source region or drain region does not influence the characteristic of TFT.Therefore, compare with the part that becomes channel formation region and have bad degree of crystallinity even become the part in source region or drain region, this part does not become problem yet.
Under look like shown in Figure 25 A, make TFT with island 9128.Note that the method for various TFT structure and manufacturing TFT is arranged.Figure 25 B is corresponding to the sectional view along Figure 25 A phantom line segments A-A ', and Figure 25 C is corresponding to the sectional view along the phantom line segments B-B ' of Figure 25 A.Figure 26 A is corresponding to the sectional view along the phantom line segments C-C ' of Figure 25 A, and Figure 26 B is corresponding to the sectional view along Figure 25 A phantom line segments D-D '.
Form first interlayer dielectric 9134 subsequently and cover island 9128, gate insulating film 9131 and gate electrode 9132.Form second interlayer dielectric 9135 then and cover first interlayer dielectric 9134.Notice that first interlayer dielectric 9134 is inorganic insulating membranes.And can be prevented from entering island 9128 such as the impurity of the carbon in second interlayer dielectric 9135.In addition, second interlayer dielectric 9135 is organic resin films, and has the effect of planar surface, makes the wiring that forms later not be cut off.
On second interlayer dielectric 9135, form subsequently,, be connected to the wiring 9136 of impurity range 9133 by being formed on the contact hole in gate electrode 9131, first interlayer dielectric 9134 and second interlayer dielectric 9135.
So finish TFT by above-mentioned manufacturing process with a plurality of separated channel formation regions.By using such structure, the heat that is produced by drive TFT can be dissipated effectively.
Notice that the TFT structure is not limited to the structure shown in Figure 25 A-25C among the present invention.In addition, the quantity of channel formation region is not limited to four, and at present the quantity of channel formation region can be other quantity beyond one, four or four.
In addition, the structure of TFT is not limited to said structure.For example, the TFT structure can have and resembles the structure shown in Figure 27 A and the 27B.TFT shown in Figure 27 A has by two- layer conducting film 9140 and 9141 gate electrodes of forming.The sidewall of being made up of dielectric film 9142 forms the upper surface of contact conducting film 9140 and the side surface of conducting film 9141.For example, TaN can be used as conducting film 9140, and W can be used as conducting film 9141 and SiO
2Deng can be used as sidewall 9142.TFT shown in Figure 28 B has by two- layer conducting film 9144 and 9145 gate electrodes of forming.Conducting film 9144 is overlapped with impurity range.
Note, to the degree of the projection 9124 of exposing basilar memebrane, can be released in the stress that produces in the semiconductor film after laser irradiation or at etching crystal semiconductor film by during about 1 minute to 60 minutes, heat-treating at 500-600 ℃.
Be used as the TFT active layer by the semiconductor film on the depression that will be positioned at dielectric film effectively, can prevent from the TFT channel formation region, to form crystal boundary, and can prevent all because remarkable reduction, the minimizing of making current and the increase of cut-off current of the TFT mobility that crystal boundary causes.
Example 7
Explain the method on the manufacturing island that process sequence wherein is different with the process sequence of example 6 in the example 7.Note, can reference example 6 for the detailed explanation of each processing step.
At first, shown in Figure 28 A (formation non-single crystal semiconductor film), form basilar memebrane, and on basilar memebrane, form non-single crystal semiconductor film 9302 with rectangular shape projection 9301.Use laser irradiation non-single crystal semiconductor film 9302 subsequently, form crystal semiconductor film 9303 (Figure 28 B irradiation laser) thus.
Then, from its surface removal part crystal semiconductor film 9303 to such degree, so that expose the upper surface of projection 9301.Note, in example 7, use etching to remove, and the crystal semiconductor film after removing becomes crystal semiconductor film (after the etching) 9304 (Figure 28 C etching).
Then, graphical crystal semiconductor film (after the etching) 9304 forms island 9305 (Figure 28 D forms the island) thus.
Note, after etching crystal semiconductor film to the projection that to a certain degree makes basilar memebrane is exposed, or after forming the island,, can be released in the stress that produces in the semiconductor film by during about 1 minute to 60 minutes, heat-treating at 500-600 ℃.
According to above-mentioned processing step, to a certain degree making that the projection of basilar memebrane is exposed, can prevent because etching is removed the marginal portion or the lateral parts on island by etching crystal semiconductor film before forming the island.
Example 8
Explain the method on the manufacturing island that process sequence wherein is different with the process sequence of example 6 and example 7 in the example 8.Note, can reference example 6 for the detailed explanation of each processing step.
At first, shown in Figure 29 A (formation non-single crystal semiconductor film), form the basilar memebrane of projection, and on basilar memebrane, form non-single crystal semiconductor film 9312 with rectangular shape 9331.
Then, graphical non-single crystal semiconductor film 9312 forms sub-island 9313 (Figure 29 B forms sub-island) thus.
Use the sub-island 9313 of laser irradiation subsequently, cause crystallization thus.Sub-island in the example 8 after the crystallization becomes sub-island (after the crystallization) 9314 (Figure 29 C irradiation laser).
Subsequently, from its surface removal parton island (after the crystallization) 9314, the degree that the upper surface of extremely feasible projection 9311 exposes.Note, in example 8, remove, form island 9315 (Figure 29 D etching) thus by etching.
Note,, after laser irradiation or after forming the island,, can be released in the stress that produces in the semiconductor film by during about 1 minute to 60 minutes, heat-treating at 500-600 ℃ according to above-mentioned processing step.
Example 9
Explain in the example 9 and use a plurality of examples that convex to form many channel TFT and only have single channel TFT of a channel formation region.
Figure 30 A illustrates the basilar memebrane with a plurality of rectangular shape projectioies 9330.Figure 30 B illustrates with the TFT that is formed on the island on the basilar memebrane.Figure 30 B has many channel TFT 9332 and single channel TFT 9333 that 9331, one of many channel TFT that four channel formation regions are arranged have two channel formation regions.
Each TFT is formed on the depression between the projection 9330.More preferably, channel formation region and LDD district are formed on the depression between the projection 9330.
Might realize example 9 with example 6-8 combination.
Example 10
Explain in the example 10, when the crystallization semiconductor film, the example of the technology of combination irradiation laser technology and use catalyst crystallization semiconductor film.When using catalyst elements, preferably use by JP 7-130652A and the disclosed technology of JP 8-78329A.
At first, shown in Figure 31 A (formation non-single crystal semiconductor film), on basilar memebrane 9351, form non-single crystal semiconductor film 9352 with projection 9350.Then, with catalytic elements crystallization non-single crystal semiconductor film 9352 (Figure 31 B NiSPC).For example, if use the technology of using in JP 7-130652A, then the nickel acetate solution of nickeliferous 10ppm is applied to non-single crystal semiconductor film 9352, so form nickeliferous layer 9353.Carry out dehydrogenation in 1 hour at 500 ℃ then and handle, thereafter the 500-650 ℃ of heat treatment of carrying out 4-12 hour, for example 550 ℃ of heat treatments 8 hours, so form the crystal semiconductor film 9354 of degree of crystallinity with improvement.Notice that except nickel (Ni), the catalytic elements that can use comprises elements germanium (Ge), iron (Fe), palladium (Pd), tin (Sn), plumbous (Pb), cobalt (Co), platinum (Pt), copper (Cu) and gold (Au).
Subsequently by laser irradiation, form by crystal semiconductor film (behind the NiSPC) 9354 and to have the further crystal semiconductor film (behind the LC) 9355 that improves degree of crystallinity through NiSPC crystallization (Figure 31 C irradiation laser).Crystal semiconductor film (behind the LC) 9355 melts at once in the laser irradiation process, during laser irradiation, is moved to hollow volume by the top of projection 9350, thus its surface of complanation.Film thickness attenuation on the projection 9350 is because stress is easy to produce crystal boundary 9356.
The process of the catalytic elements in the explained later gettering crystal semiconductor film (behind the LC) 9355.Note,, also can behind etching crystal semiconductor film (behind the LC) 9355, carry out though gettering carries out after laser irradiation in example 10.
On crystal semiconductor film (behind the LC) 9355, form subsequently and have the barrier layer 9357 (Figure 31 D gettering) of silicon as its main composition.Noticing that barrier layer 9357 can be extremely thin, can be the film oxide of self, also can be the oxidation film by the ozone oxidation of the ultraviolet ray of irradiation in oxygen containing atmosphere generation.In addition, also can use by liquid oxidation ozoniferous be called washing (hydro-washing) and for removing the oxide-film that uses in the surface treatment carry out for organic carbon.Barrier layer 9357 is main as etching stop layer.In addition, after forming barrier layer 9357, can carry out channel doping, can activate by the irradiation high light thereafter.
On barrier layer 9357, be formed for first semiconductor film 9358 of gettering subsequently.First semiconductor film 9358 that is used for gettering can be the semiconductor film with non crystalline structure, also can be the semiconductor film with crystalline texture.The film thickness that is used for first semiconductor film 9358 of gettering is set as 5-50nm, is preferably 10-20nm.In order to improve gettering efficient, (sims analysis concentration is equal to or greater than 5 * 10 preferably to introduce oxygen at the first crystal semiconductor film 9358 that is used for gettering
18Atom/cm
3, preferably be equal to or greater than 1 * 10
19Atom/cm
3).
Be used for forming the 3rd semiconductor film (gettering site) 9359 that contains inert gas elements on first semiconductor film 9358 of gettering subsequently.Second semiconductor film 9359 that is used for gettering can be the semiconductor film with non crystalline structure, or has the semiconductor film of crystal structure, and can form by using plasma CVD, low pressure hot CVD or sputter.Second semiconductor film can be the semiconductor film that contains inert gas elements in the film formation stage, and inert gas elements also can add after forming the film that does not contain inert gas elements.Example shown in the example 10 be formed for gettering and contain second semiconductor film 9359 of inert gas elements in the film formation stage, optionally add other inert gas elements thereafter, be formed for second semiconductor film 9359 of gettering thus.In addition, being used for first semiconductor film of gettering and second semiconductor film can form under the condition that is not exposed to outside atmosphere continuously.In addition, the summation of the thickness of the thickness of first semiconductor film and second semiconductor film can be made as 30-200nm, for example 50nm.
Between the crystal semiconductor film (behind the LC) 9355 and second semiconductor film 9359, prepare gaps with first semiconductor film 9358 that is used for gettering.In the gettering process, the impurity element such as metal that is present in the crystal semiconductor film (behind the LC) 9355 is tending towards easily accumulating in the gettering site boundary vicinity, and as in the example 10, preferably first semiconductor film 9358 that is used for gettering by utilization places the gettering border away from crystal semiconductor film (behind the LC) 9355 and raises the efficiency.In addition, first semiconductor film 9358 that is used for gettering also has blocking effect, make in being included in gettering site the impurity element indiffusion and arrive interface with first semiconductor film.In addition, first semiconductor film 9358 that uses in gettering has protective effect, makes the damage that does not cause under the situation of inert gas elements crystal semiconductor film (behind the LC) 9355 adding.
Then carry out gettering.Can in blanket of nitrogen, heat-treat 1-24 hour, for example 550 ℃ of heat treatments 14 hours, as the technology that is used for gettering at 450-800 ℃.In addition, but also irradiation high light and replace heat treatment.The gas that further can introduce heating is so that heated substrate.In this case, can under 600-800 ℃ temperature, heat 1-60 minute, preferred 650 ℃-750 ℃, can reduce the processing time thus.By this gettering, shown in the arrow among Figure 31 D (gettering), impurity element moves in second semiconductor film 9359.Remove the concentration that is included in the impurity element in the crystal semiconductor film (behind the LC) 9355 that covers by barrier layer 9357 or reduces impurity element thus.Form the crystal semiconductor film (behind the gettering) 9360 that comprises impurity element hardly by gettering, wherein the concentration of impurity element is equal to or less than 1 * 10
18Atom/cm
3, preferably be equal to or less than 1 * 10
17Atom/cm
3
Then, as etching stop layer, optionally remove first semiconductor film 9358 and second semiconductor film 9359 that is used for gettering with barrier layer 9357.
Thereafter, shown in Figure 31 E (etching), change etching condition and remove barrier layer 9357, crystal semiconductor film (behind the gettering) 9360 is etched into the degree of the upper surface that exposes projection 9350, forms the crystal semiconductor film 9361 in the depression thus.
Note, before crystallization, after coating on the semiconductor film contains the solution of catalytic elements, also can carry out crystal growth by irradiation laser rather than SPC.In addition, also can use at JP10-135468, the technology of record is carried out gettering among the JP 10-135469 etc.
Note,, the invention is not restricted to this structure though in example 10, after laser irradiation, carry out gettering.Also can after the etching of carrying out Figure 31 E, carry out gettering.
Might realize example 10 in conjunction with example 6-9.
Example 11
Explain the structure of the laser irradiating device that uses in the present invention below with Figure 32.Reference number 9151 expression laser oscillation apparatus.In Figure 32, use four laser oscillation apparatus, but the laser oscillation apparatus of laser irradiating device is not limited to this quantity.
Note, laser oscillation apparatus 9151 can be remained on stationary temperature by using cooler 9152.Always do not need to use cooler 9152, but, can suppress because the dispersion of the energy of the output laser that temperature causes by laser oscillation apparatus 9151 is remained on stationary temperature.
In addition, reference number 9154 expression optical systems are come convergent laser by changing from the light outgoing route of laser generation device 9151 and the shape of adjusting laser beam.In addition, the optical system 9154 in the laser irradiating device of Figure 32 overlaps each other by making the part laser beam, also can synthesize the laser beam of output from the laser of a plurality of laser oscillation apparatus 9151.
Note, also can in the light path between pending substrate 9156 and the laser oscillation apparatus 9151, be formed on the A0 modulator 9153 that changes the laser direction of advance in the very short time period.In addition, attenuator (being used to regulate the filter of light quantity) can form the substitute of AO modulator 9153, and the energy density of laser can be regulated.
In addition, be used to measure measurement mechanism (energy density measurement mechanism) 9165, can be placed in the light path between pending substrate 9156 and the laser oscillation apparatus 9151 from the laser energy density of laser oscillation apparatus 9151 outputs.In computer 9160, can observe measured energy density over time.In this case, also can increase the output of laser oscillation apparatus 9151 so that the decay of compensation laser energy density.
Synthetic laser beam arrives pending substrate 9156 by slit 9155 irradiation.Preferably, slit 9155 can stop laser, and it is formed by the material that is not changed by laser or damage.The slit width of slit 9155 is variable, and can change the width of laser beam by slit width.
Note,, according to the type of laser and difference, and so can form by optical system from the not shape of the laser beam of laser on substrate 9156 by slit 9155 of laser oscillation apparatus 9151 emissions.
On sample stage 9157, place substrate 9156. Position control 9158 and 9159 is corresponding to the device that is used to control the laser beam position on the pending sample, and the position of sample stage 9157 is controlled by position control 9158 and 9159 among Figure 32.
Among Figure 32, position control 9158 carries out the Position Control of sample stage 9157 in the x direction, and position control 9159 carries out the Position Control of sample stage 9157 in the y direction.
In addition, the laser irradiating device of Figure 32 has the computer of preparing to have such as memory and central arithmetic processing apparatus 9160.Laser beam scan path is determined in the emission of computer 9160 control laser oscillation apparatus 9151, in addition can control position control device 9158 and 9159, and make the laser beam of laser along the path scanning of determining, so that substrate is moved to preposition.
Note,, also can move, and also can adopt two kinds of methods by using optical system such as current mirror (galvano mirror) though the position of laser beam is controlled by mobile substrate among Figure 32.
In addition, control the width of slits 9155 among Figure 32 with computer 9160, but also can change the width of laser beam according to mask pattern information.Note, always must not form this slit.
In addition, laser irradiating device also can be provided for regulating the device of pending sample temperature.In addition, laser is the light with high-energy-density and directivity, and therefore can form baffle plate so that the photoirradiation that prevents to be reflected arrives unsuitable position.Preferably, baffle plate has the character that absorbs the light that is reflected, and can be in baffle plate recirculated cooling water so that prevent owing to absorb the temperature of the light trap plate that is reflected and raise.In addition, also can on sample stage 9157, be formed for the device (lining heat) of heated substrate.
Note, under the situation that forms mark with laser, also can provide the mark laser oscillation apparatus.In this case, the emission of mark laser oscillation apparatus can be by computer 9160 controls.In addition, under the situation of usage flag laser oscillation apparatus, can be provided for the optical system of optically focused output especially from the laser of mark laser oscillation apparatus.Notice that YAG laser, CO2 laser etc. can be used as the typical laser that uses when forming mark, also can use other laser to form mark naturally.
In addition, depend on environment, can form a ccd video camera 9163 or a plurality of ccd video camera 9163 and be used for usage flag and carry out position alignment.Notice that the term ccd video camera represents to use the video camera of CCD (charge coupled cell) as photograph component.
Note, can discern insulating film pattern or semiconductor film patterns by ccd video camera 9163, and can under the situation that does not form mark, carry out the position alignment of substrate.In this case, because dielectric film mask and that be input to computer 9160 or semiconductor film pattern-information compare with actual insulation film or the semiconductor film pattern-information collected by ccd video camera 9163, can differentiate the information of relevant substrate location.In this case, must not form mark especially.
In addition, incide laser on the substrate, and return along the path identical with incident by the surface reflection of substrate.Therefore the so-called light that returns has a negative impact, and exports and frequency such as changing laser, and damages laser bar.Therefore can arrange light and stable laser emission that isolator returns with removal.
Note,, also can use a laser oscillation apparatus though the structure of a plurality of laser oscillation apparatus is provided shown in Figure 32.Figure 33 illustrates the structure of the laser irradiating device with a laser oscillation apparatus.Reference number 9201 expression laser oscillation apparatus among Figure 33, reference number 9202 expression coolers.Reference number 9215 is represented the energy density measurement mechanisms in addition, reference number 9203 expression AO modulators, reference number 9204 expression optical systems, reference number 9205 expression slits, and reference number 9213 expression ccd video cameras.Substrate 9206 is arranged on the sample stage 9207, and the position of sample stage is by position control 9208 control x directions, by position control 9209 control y directions.With similar shown in Figure 32, the work of each device in the laser irradiating device is then by computer 9210 controls.Different with Figure 32 is to have a laser oscillation apparatus.In addition, different with Figure 32 is that optical system 9204 can have the function of the laser of this laser of optically focused.
Notice that laser does not scan with irradiation and arrives whole semiconductor film, but scan laser makes minimum requisite part carry out the crystallization of minimum.Can save be used for irradiation laser to behind the crystallization semiconductor film by the time on the graphical part of removing, can reduce the processing time amount of every single substrate greatly.
Might finish example 11 in conjunction with example 6-10.
Example 12
In example 12, explain the method that forms basilar memebrane with projection and depression.
At first, shown in Figure 34 A, on substrate 9250 by the insulation film formed first basilar memebrane 9251.First basilar memebrane 9251 uses silicon oxynitride in example 12, but is not limited to this material, has big optionally dielectric film in the time of can using with the second basilar memebrane etching.Use SiH with CVD equipment
4And N
2O forms first basilar memebrane 9251, and to make its thickness be 50-200nm.Notice that first basilar memebrane can be an individual layer, and also can be the stepped construction of a plurality of dielectric films.
Then shown in Figure 34 B, form second basilar memebrane 9252 that contacts with first basilar memebrane 9251 by insulating material.The thickness of second basilar memebrane 9252 is necessary for such order of magnitude, makes depression and projection to occur in the surface of carrying out the semiconductor film that forms subsequently when graphical in the step that forms depression and projection in the back.In example 12, form the silicon oxide film of 30nm-300nm as second basilar memebrane 9252 with plasma CVD.
Shown in Figure 34 C, then form mask 9253, etching second basilar memebrane 9252.Note, in example 12, carry out wet etching, use to contain 7.13% ammonium acid fluoride (NH at 20 ℃
4HF
2) and 15.4% ammonium fluoride (NH
4F) mixed solution (Stella Chemifa Corporation, name of product LAL500) is as etching agent.Has the projection 9254 of rectangular shape by this etching formation.First basilar memebrane 9251 and projection 9254 are as a basilar memebrane in this manual.
Note, aluminium nitride, aluminium oxynitride or silicon nitride as first basilar memebrane 9251 and silicon oxide film as under the situation of second basilar memebrane 9252, preferably use graphical second basilar memebrane 9252 of RF sputter.Thermal conductivity as aluminium nitride, aluminium oxynitride and the silicon nitride of first basilar memebrane 9251 is high, but the heat rapid diffusion that therefore produces can prevent that TFT from worsening.
Then form semiconductor film so that cover first basilar memebrane 9251 and projection 9254.Thickness in example 12 protrusions is 30nm-300nm, and therefore preferred thickness with semiconductor film is made as 50-200nm, is made as 60nm here.Note,, will the degree of crystallinity of semiconductor film be had a negative impact if between semiconductor film and basilar memebrane, pollute impurity.There is the possibility of characteristic variations of the TFT of manufacturing, and can increases variations in threshold voltage, therefore preferably form basilar memebrane and semiconductor film continuously.In example 12, after forming first basilar memebrane 9251 and projection 9254, on basilar memebrane, form thin silicon oxide film 9255, under the situation that is not exposed to outside atmosphere, form semiconductor film 9256 subsequently.The thickness of silicon oxide film can suitably be set by the designer, is made as about 5nm-30nm in example 12.
Then explain the method that is different from formation basilar memebrane shown in Figure 34.Shown in Figure 35 A, at first on substrate 9260, form first dielectric film of forming by dielectric film 9261.First basilar memebrane is formed by silicon oxide film, silicon nitride film, oxygen silicon nitride membrane etc.
If the use silicon oxide film can be with plasma CVD by mixing tetraethylorthosilicise (TEOS) and O
2Form, reaction pressure is 40Pa, and underlayer temperature is 300-400 ℃, is 0.5-0.8W/cm in electrical power density
2Down discharge of high frequency (13.56MHz).If the use silicon oxynitride can be used by SiH
4, N
2O and NH
3The oxygen silicon nitride membrane made of plasma CVD form, or use by SiH
4And N
2The oxygen silicon nitride membrane that the plasma CVD of O is made forms.Create conditions in this case into, reaction pressure is 20-200Pa, underlayer temperature is 300-400 ℃, high frequency (60MHz) electrical power density is 0.1-1.0W/cm
2Also can use in addition by SiH
4, N
2O and H
2Oxynitriding hydrogen silicon (the hydrogen silicon oxynitride) film of making.Similarly, can be by using SiH
4And NH
3Plasma CVD make silicon nitride film.
After forming first basilar memebrane that thickness is 20-200nm (preferred 30-60nm) on the entire substrate, shown in Figure 35 B, form mask 9262 with photoetching technique again.Remove unwanted part by etching, form the projection 9263 of rectangular shape thus.Can use the dry etching of using fluoride gas with respect to first basilar memebrane 9261, also can use wet etching with fluoride aqueous solution.Under the situation of the method for selecting the latter, can use to contain 7.13% ammonium acid fluoride (NH
4HF
2) and 15.4% ammonium fluoride (NH
4F) mixed solution (Stella Chemifa Corporation, name of product LAL500) carries out etching.
Then form second basilar memebrane of forming by dielectric film 9264 and just cover projection 9263 and substrate 9260.Similar with first basilar memebrane 9261, used thickness is that the silicon oxide film, silicon nitride film, oxygen silicon nitride membrane of 50-300nm (preferred 100-200nm) etc. forms this film.
According to above-mentioned manufacturing process, form the basilar memebrane of forming by projection 9263 and second basilar memebrane 9264.Note, after forming second basilar memebrane 9264, under situation about not exposing with atmosphere, form semiconductor film continuously, to prevent the pollution of impurity between semiconductor film and basilar memebrane.
Might be by finishing example 12 with example 6-11 independent assortment.
Example 13
In example 13, explain shape by the overlapped synthetic laser beam that changes laser beam.
Figure 36 A illustrates, for by a plurality of laser oscillation apparatus emitted laser under the situation of slit, the example of the laser beam shape on processed sample.Laser beam shown in Figure 36 A has elliptical shape.Notice that the shape by the laser beam of laser oscillation apparatus emitted laser is not limited to elliptical shape in the present invention.The shape of laser beam depends on the type of used laser and difference can be passed through the optical system shaping in addition.For example, be shaped as 10mm * 30mm (beam profile half breadth) rectangular shape by Lambda company XeCl quasi-molecule laser (wavelength 308nm, pulse duration 30ns) L3308 emitted laser.In addition, if rod be shaped as cylindricality, by the circle that is shaped as of YAG laser emitted laser, and if use dish type, then laser is shaped as rectangle.By such laser being added shaping, can form laser with desirable size with optical system.
The laser energy density that Figure 36 B illustrates the longitudinal axis Y direction of the laser beam shown in Figure 36 A distributes.Laser beam is corresponding to the 1/e that satisfies the peak value of energy density among Figure 36 B shown in Figure 36 A
2The zone of energy density.At laser beam is under the situation of elliptical shape, the energy density of laser be distributed near oval center O the time uprise.Therefore the laser beam shown in Figure 36 A has the Energy distribution of observing Gaussian Profile at central axis direction, can be judged as the zone with homogeneous energy density and diminish.
Figure 36 C illustrates the shape that wherein has the laser beam of the laser of laser beam shape shown in Figure 36 A.Notice that it is overlapping that Figure 36 C illustrates the laser beam of four laser wherein, form the situation of a linear shape laser beam thus, but the quantity of overlapping laser beam is not limited to four.
The coincidence of the longitudinal axis of each the light beam ellipse by making laser is synthesized, and the part laser beam is overlapped, forms a laser beam 9360 thus.Note, be used as the central shaft of laser beam 9360 by the straight line that connects each oval center O acquisition.
Figure 36 D (A-A ' between energy density distribution) is illustrated in the energy density distribution of the laser of synthetic back laser beam in y direction central shaft shown in Figure 36 D.Notice that the laser beam shown in Figure 36 C is corresponding to the 1/e that satisfies the peak value of energy density among Figure 36 B
2The zone of energy density.Before synthetic the energy density of the overlapping part of each laser beam add and.For example, if the energy density E1 of the overlapping light beam shown in the figure and E2 add and, then calculated value becomes the peak E 3 of beam energy density no better than, the energy density between each oval center O is evened up.
Note, if E1 and E2 add and, ideal results becomes and equals E3, but does not in fact always equal E3.The designer can suitably set add and E1 and the permissible range of the difference between E2 value and the E3 value.
If use independently laser beam, energy density is observed Gaussian Profile, and the laser irradiation that therefore is difficult to have homogeneous energy density to the complanation of semiconductor film wherein and dielectric film partly or become the entire portion that the part on island contacts.But, replenish each other by making the overlapping part that makes of a plurality of laser with low energy densities, can expand the zone of homogeneous energy density, as understanding from Figure 36 D, compare with using the nonoverlapping independent laser of wherein a plurality of laser, can improve the degree of crystallinity of semiconductor film with high efficiency.
Notice that Figure 37 A and 37B illustrate the energy density distribution that obtains by line segment B-B ' among the calculating chart 36C and C-C ' respectively.Note, among Figure 37 A and the 37B, satisfy the 1/e of the peak value of synthetic preceding laser beam
2The zone of energy density as a reference.The length of laser beam transverse axis is 37 μ m before synthetic, and the length of y direction is 410 μ m, and the distance between the center is when being 192 μ m, and the energy density among B-B ' and the C-C ' has the Energy distribution shown in Figure 37 A and 37B respectively.Be slightly smaller than along C-C ' along the Energy distribution of B-B ', but can see that the two is almost equal.The 1/e of the peak value of laser beam before satisfied synthesizing
2The zone of energy density in laser beam shape after synthetic can be expressed as linear shape.
Figure 38 A is the view that the laser beam energy distribution after synthesizing is shown.Zone by reference number 9361 expressions is the zone with uniform energy density, and the zone of being represented by reference number 9362 is the zone with low energy densities.Among Figure 38, laser beam is counted as W in the length of central axis direction
TBW, and the length of central axis direction is counted as W in the zone 9361 with uniform energy density
MaxAlong with W
MaxCompare W
TBWBecome big, do not have homogeneous energy density and can not be used in zone 9362 in the crystallization semiconductor film, become big with the ratio that has uniform energy density and can be used in the zone 9361 of crystallization.Only carry out irradiation with energy density non-uniform areas 9362, crystallite generation and degree of crystallinity are very poor in semiconductor film.Therefore must set scanning pattern and dielectric film concave and protruding layout, make that to become the zone of the semiconductor film on island not only overlapping with zone 9362.If zone 9362 becomes big with the ratio in zone 9361, then this restriction becomes big.By using slit only to prevent the semiconductor film of energy density non-uniform areas 9362 irradiation on depression that is formed on dielectric film or the projection, so the restriction of generation when recessed and protruding in layout scanning pattern and the dielectric film is diminished.
Might realize example 13 with example 6-12 combination.
Example 14
Explain the optical system of the laser irradiating device that uses among the present invention in the example 14, and the relation of the position between optical system and the slit.
Its energy density of laser with elliptical shape laser beam with the direction of scanning direction quadrature on follow Gaussian Profile, therefore compare, by having the ratio height that the low energy densities zone occupies with laser with rectangular shape or linear shape laser beam.Therefore, the preferred laser beam of laser in the present invention is rectangular shape or the linear shape with relative homogeneous energy distribution.
Figure 39 is illustrated in wherein synthetic four laser beams with the optical system under the situation that forms a laser beam.Optical system shown in Figure 39 has six cylindrical lens 9417-9422.Incide four cylindrical lens 9419-9422 respectively from four laser of direction of arrow incident.Two of shaping laser make the shaping in cylindrical lens 9417 of its laser beam once more in cylindrical lens 9419 and 9421, and irradiation is to handling sample 9423 then.On the other hand, two of shaping laser make the shaping in cylindrical lens 9418 of its laser beam once more in cylindrical lens 9420 and 9422, and irradiation is to handling sample 9423 then.
The some parts of each laser beam of laser is overlapped, so form a synthetic laser beam in handling sample 9423.
Might suitably set focal length and incidence angle for each lens for the designer, but the focal length of the cylindrical lens 9417 of the most close processing sample 9423 and 9418 is less than the focal length of cylindrical lens 9419-9422.For example, the cylindrical lens 9417 of the most close processing sample 9423 and 9418 focal length are made as 20mm, and the focal length of cylindrical lens 9419-9422 is made as 150mm.Arrange each in the lens like this, make in example 14, to be made as 25 °, and 9417 and 9418 incidence angle is made as 10 ° from cylindrical lens 9419-9422 to cylindrical lens from cylindrical lens 9417 and 9418 incidence angles to the laser of handling sample 9423.Notice that in order to get rid of the light that returns and to carry out uniform irradiation, the laser incidence angle that preferably arrive substrate is greater than 0 °, preferably 5-30 °.
Figure 39 illustrates the synthetic example that uses four laser beams, and in this case, corresponding to four laser oscillation apparatus four cylindrical lenses is arranged, and two cylindrical lenses is arranged corresponding to these four cylindrical lenses.The quantity of the laser beam that is used to synthesize is not limited to this quantity, and the quantity of the laser beam that is used to synthesize can be equal to or greater than 2, and is equal to or less than 8.Situation for using n (n=2,4,6,8) laser beam to synthesize has n cylindrical lens corresponding to n laser oscillation apparatus, and n/2 cylindrical lens is arranged corresponding to this n cylindrical lens.Under the situation of using n (n=3,5,7) laser beam, n cylindrical lens arranged corresponding to n laser oscillation apparatus, and (n+1)/2 cylindrical lens is arranged corresponding to this n cylindrical lens.
If when under the overlapped situation of five or more a plurality of laser beam is arranged, considering to place the position, interference etc. of optical system, the preferred the 5th and laser subsequently from the opposite side irradiation of substrate, and also must on the opposite side of substrate, form slit in this case.In addition, need substrate to have the transparency.
Notice that for the back light that prevents to return from along the light path of following at first, preferably the incidence angle with respect to substrate remains on greater than 0 ° and less than 90 °.
In addition, comprise the surface of minor face edge or the surface that comprises long edge and be defined as incidence surface, when this surface be irradiating surface vertical plane surface and synthetic before each light beam when being selected as rectangular shape.In order to realize uniform laser irradiation, the length when minor face that is incorporated into reflective surface or long limit is W, and when being d for the thickness that laser has the transparency and is arranged in the substrate in the irradiating surface, the incidence angle θ of preferred laser satisfies θ 〉=arctan (W/2d).Need this parameter for each laser before synthetic.Notice that when laser path was not on incidence surface, the incidence angle that is incident upon the laser path on the incidence surface was made as θ.As long as make laser, do not interfere from the light of the front surface reflection of substrate with from the light of the rear surface reflection of substrate, and can carry out uniform laser irradiation with incidence angle θ incident.Above-mentioned parameter is the substrate consideration that refractive index equals 1.In fact, the refractive index of substrate is about 1.5 usually, when considering this value, obtains the calculated value greater than the angle of being calculated by above-mentioned parameter.But, the energy attenuation at vertical two ends of restrainting spot, therefore the interference effect in these parts is little, can obtain enough interference attenuation effects by the aforementioned calculation value.Above-mentioned inequality for θ can be applicable to not have for laser beam the substrate of the transparency.
Notice that the optical system of the laser irradiating device of Shi Yonging is not limited to the structure shown in the example 14 in the present invention.
In addition, excimer laser is typically as gas laser, and disk laser is typically as solid-state laser, and under the situation that does not make up a plurality of laser beams, it can provide the laser beam of rectangular shape or linear shape.These lasers are also in the present invention available.In addition, by using optical fiber also may form linear shape or rectangular shape laser beam with homogeneous energy density.
Might combine with example 6-13 and realize example 14.
Example 15
Example 15 is explained distance between each laser beam center and the relation between the energy density when laser beam is overlapping.
Among Figure 40, solid line illustrates the energy density of the central axis direction of each laser beam, is shown in dotted line the energy density of synthetic laser beam.The value of the energy density on the laser beam central axis direction is followed Gaussian Profile usually.
Distance in the central shaft direction satisfies the 1/e that energy density is equal to or greater than peak value
2The time, each peak-to-peak distance is counted as X in the synthetic prenex spot.In addition, peak value partly is counted as Y with respect to the increase of the mean value of synthetic back peak value and valley in the He Cheng bundle spot.X that finds by simulation shown in Figure 41 and the relation between the Y.Notice that Y represents with percentage among Figure 41.
The energy difference Y that Figure 41 represents is represented by the approximate equation of following equation 1.
[equation 1]
Y=60-293X+340X
2(wherein X is two higher values in separating)
According to equation 1, should understand and can set X like this, make and for example wishing that energy difference is made as X ≌ 0.584 under about 5% the situation.Therefore ideally, Y=0 becomes really, but the length of bundle spot shortens, and can consider evenly that productivity ratio determines X.
The admissible scope of explained later Y.Figure 42 is illustrated under the situation that laser beam has elliptical shape, at the width of central axis direction with respect to laser beam, YVO
4The output of laser (W) distributes.The zone is the zone that has for the required output energy of degree of crystallinity that obtains satisfaction shown in the oblique line, and should be understood that the output energy of synthetic laser can remain on the scope of 3.5-6W.
When the minimum and maximum value of the output energy of synthetic posterior cord spot very when obtaining the required output energy range of satisfied degree of crystallinity, the energy difference Y that can obtain satisfied degree of crystallinity becomes maximum.Therefore, under situation shown in Figure 42 energy difference Y become ± 26.3%, should understand by energy difference Y is remained on above-mentioned scope, can obtain good degree of crystallinity.
Note, by judging which kind of factor constitutes good crystallinity and can change into the scope that obtains the required output energy of good crystallinity, therefore exporting Energy distribution in addition can change because of the shape of laser beam, but and always not need the allowed band of energy difference Y be above-mentioned value.The designer can suitably be set at and obtain the needed output energy range of good crystallinity, but and need be set in the allowed band of energy difference of the output Energy distribution of used laser.
Might realize example 15 in conjunction with example 6-14.
Example 16
The present invention can be applicable to various semiconductor device, explains the example of making display panel based on example 6-10 with Figure 43 and 44.
Figure 43 is illustrated in preparation pixel parts 9902, gate signal drive circuit 9901a and 9901b, data-signal drive circuit 9901c, input and output end parts 9908 and wiring or wiring group 9904 on the substrate 9901.Seal pattern 9905 and gate signal drive circuit 9901a and 9901b, data-signal drive circuit 9901c, the wiring or the wiring group 9904 that are connected with input with driving circuit section are partly overlapping.The surface area of the frame area of display panel (peripheral region of pixel parts) can be made lessly thus.FPC 9903 is fixed in input and output end parts 9908.
The present invention can be used for constituting the active element of pixel parts 9902, gate signal drive circuit 9901a and 9901b, data-signal drive circuit 9901c.
Figure 44 is the example of structure that a pixel of the pixel parts shown in Figure 43 is shown.The pixel that example 16 is explained as the luminescent device of a kind of semiconductor device of the present invention.Notice that the term luminescent device normally is used for term display panel and display module, the light-emitting component that is formed in the display panel on the substrate is enclosed between substrate and the cladding material, and TFT etc. is installed on the display panel in the display module.Notice that light-emitting component has: comprising wherein can pass applies the layer (luminescent layer) of the electroluminescent organic compound that electric field produces; Anode and negative electrode.
Note, the light-emitting component that uses in the example 16 can have such form, wherein hole injection layer, electron injecting layer, hole transport layer, electron transport layer etc. are inorganic compounds independently, or are formed by the material that inorganic compound is wherein sneaked into organic compound.Some parts also can mix mutually in these layers in addition.
Reference number 9801 expressions are used for based on the information of vision signal electric current being offered the TFT (drive TFT) of pixel capacitors with the TFT (switching TFT) of the switch element that acts on the input of controlling the vision signal that is input to pixel, reference number 9802 expressions.
Switching TFT 9801 has active layer 9803, the gate insulating film (not shown) of the channel formation region that comprises the about 1-2 μ of a plurality of channel widths m and is the gate electrode 9805 of grid lead 9804 parts.Switching TFT 9801 is by selecting to import control switch from gate signal drive circuit 9901a and 9901b to the signal of grid lead 9804.
A district of the active layer 9803 of switching TFT 9801, or source region or drain region are connected to holding wire 9806, and 9901c is input to this holding wire with vision signal by the data-signal drive circuit, and another district is connected to the wiring 9807 that is used to connect another element.
Reference number 9820 is illustrated in the projection of the basilar memebrane that uses in the process that forms active layer 9803.
On the other hand, drive TFT 9802 has the active layer 9808, gate insulating film (not shown) of the channel formation region that comprises the about 1-2 μ of a plurality of channel widths m and is the connect up gate electrode 9810 of 9809 parts of capacitor.
A district of the active layer 9808 of drive TFT 9802, or source region or drain region are connected to power line 9811, and another district is connected to pixel capacitors 9812.
Reference number 9821 is illustrated in the projection of the basilar memebrane that uses in the process that forms active layer 9808.
Reference number 9813 expression is used for the semiconductor film of capacitor, and it is 9809 overlapping and gate insulating film is clipped in therebetween that it and capacitor connect up.The semiconductor film 9813 that is used for capacitor is connected to power line 9811.Semiconductor film 9813, gate insulating film and the capacitor that wherein the is used for capacitor 9809 overlapping parts that connect up are with the gate voltage capacitor that acts on storing driver TFT 9802.This external capacitive body wiring 9809 and power line 9811 are overlapping, and the interlayer dielectric (not shown) is clipped in therebetween.The part that also wherein capacitor wiring 9809, interlayer dielectric and power line 9811 are overlapping is with the capacitor of the gate voltage that acts on storing driver TFT 9802.
Notice that unless stipulate in addition, term connection expression used in this specification is electrically connected.
As shown by arrows, wherein the direction of motion of charge carrier in the channel formation region of the active layer 9808 of the active layer 9803 of switching TFT 9801 and drive TFT 9802 is aimed at laser scanning direction respectively.
The quantity of channel formation region is greater than the quantity of active layer 9803 channel formation regions of switching TFT 9801 in the active layer 9808 of preferred drive TFT 9802.This be because drive TFT 9802 need be bigger than switching TFT 9801 current capacity, and because can increase along with the quantity of channel formation region increases making current.
Note,, also can make liquid crystal display device by the manufacturing process of use-case 16 though example 16 has been explained the structure of used TFT substrate in the luminescent device.
Might realize example 16 by independent assortment example 6-10.
Example 17
TFT in the semiconductor device of the present invention has good degree of crystallinity at its channel formation region, therefore can form the circuit of the element formation of common use monocrystalline silicon, for example use the CPU of LSI, all types of logical circuit memory element (for example SRAM), counter circuit, logic drive circuit etc.
The minimum dimension of super LSI is near sub-micrometer range, and needs the three dimensional stress of subelement so that realize further highly integrated purpose.Example 17 is explained the structure of the semiconductor device of the present invention with laminated construction.
Figure 46 illustrates the sectional view of the semiconductor device of example 17.On substrate 9700, form first dielectric film 9701.On first dielectric film 9701, form a TFT 9702.Notice that the channel width of the channel formation region of a TFT 9702 is about the 1-2 micron.
Form first interlayer dielectric 9703 so that cover a TFT 9702, the first connecting wirings 9705 and the wiring 9704 that is electrically connected with a TFT 9702 is formed on first interlayer dielectric 9703.
Form second interlayer dielectric 9706 subsequently so that cover wiring 9704 and first connecting wiring 9705.Form second interlayer dielectric 9706 with inorganic insulating membrane, use the film of the material of the laser of irradiation in the step that wherein is absorbed in the back, for example coloured dyestuff or carbon are sneaked into silica, silicon oxynitride etc.
If use the upper surface of chemical mechanical polishing method (CMP method) polishing second interlayer dielectric 9706 subsequently, then second interlayer dielectric of Xing Chenging the more complanation that becomes subsequently is formed on second dielectric film and the degree of crystallinity of the semiconductor film by laser crystallization can be improved.
On second interlayer dielectric 9706, form second dielectric film 9707 subsequently.On second dielectric film 9707, form the 2nd TFT 9708 then.The channel width of noting the channel formation region of the 2nd TFT 9709 is about the 1-2 micron.
Form the 3rd interlayer dielectric 9709 so that cover the 2nd TFT 9708, and the wiring 9710 that on the 3rd interlayer dielectric 9709, forms second connecting wiring 9711 and be electrically connected with the 2nd TFT 9708.Note, by using the wiring (plug) 9712 of formation embeddings between first connecting wiring 9705 and second connecting wiring 9711 such as damocene technology.
Form the 4th interlayer dielectric 9713 subsequently so that cover wiring 9710 and second connecting wiring 9711.
Example 17 has so-called laminated construction, and wherein a TFT 9702 and the 2nd TFT 9708 can be overlapping by interlayer dielectric.Figure 46 A illustrates the semiconductor device with two-layer laminated construction, but it also can have three layers or more multi-layered laminated construction.In this case, resemble the inorganic insulating membrane of the absorption laser of second interlayer dielectric 9706, be formed on every layer between so that prevent that laser irradiation is to the element that is formed on down in the surface layer.
Might form very high integration, and further can shorten and be used for the wiring that between each element, is electrically connected, therefore can prevent because the signal delay that wiring capacitance causes, and might realize very at a high speed operation with three-dimensional semiconductor device.
Note, use TFT of the present invention also to can be used in CAM and the RAM coexistence chip, this chip is at " the 4th new function element technical discussion meeting collection of thesis (Fourth New FunctionalElement Technology Symposium Proceedings) ", in July, 1985, the 205th page has illustrated.Figure 46 B is the areal model of the RAM coexistence chip of the memory (CAM) that is used to have content addressing, wherein arranges the processor corresponding to memory (RAM).Ground floor is the layer that forms the word processor circuit on it, and the second layer is that formation is corresponding to the processor of the 3rd layer RAM on it by using various types of logical circuits, and the 3rd layer is the layer that wherein forms ram cell.Processor by the second layer and the 3rd layer ram cell form the memory (CAM) of content addressing.In addition, the 4th layer is the RAM (data RAM) that is used for data, and with the memory coexistence that is formed on the content addressing in the second layer and the 3rd layer.
Therefore the present invention might be applied to the semiconductor device of various types of three-dimensionals.
Might realize example 17 by independent assortment example 6-11.
Example 18
The semiconductor device application of TFT is possible in various electronic equipments with having made in accordance with the present invention.These examples comprise portable data assistance (electronic notebook, mobile computer, portable phone etc.), video camera, digital camera, personal computer, television receiver, mobile phone, projection type display device etc.Figure 45 A-45H illustrates the instantiation of these electronic equipments.
Figure 45 A illustrates display device, and it comprises framework 2001, brace table 2002, display part 2003, speaker portion 2004, video inputs 2005 etc.In display part 2003, use semiconductor device of the present invention to finish display device of the present invention.Semiconductor device is an emissive type, does not therefore need backlight.Therefore compare with LCD and can obtain thin display part.Notice that this display device comprises such as personal computer, all displays spare that the information that TV broadcasting receiver and advertisement show shows.
Figure 45 B illustrates digital still camera, and it comprises, and main body 2101, display part 2102, image receiving unit 2103, operation keys 2104, external connecting divide 2105, shutter 2106 etc.In display part 2102, use semiconductor device of the present invention to finish digital still camera of the present invention.
Figure 45 C illustrates notebook-sized personal computer, and it comprises main body 2201, framework 2202, display device 2203, keyboard 2204, outside link 2205, pointer mouse 2206 etc.In display part 2203, use semiconductor device of the present invention to finish notebook-sized personal computer of the present invention.
Figure 45 D illustrates mobile computer, and it comprises main body 2301, display part 2302, switch 2303, operation keys 2304, infrared port 2305 etc.In display part 2302, realize mobile computer of the present invention with semiconductor device of the present invention.
Figure 45 E illustrate be equipped with recording medium image-reproducing means (particularly, the dvd playback device), it comprises that main body 2401, framework 2402, display device A 2403, display device B2404, recording medium (such as DVD) read in part 2405, operation keys 2406, speaker portion 2407 etc.The main displays image information of display part A2403, and the main character display information of display part B2404.Notice that home game machine etc. are included in the classification of the image-reproducing means that is equipped with recording medium.In display part A2403 and display part B2404, use semiconductor device of the present invention to finish image-reproducing means of the present invention.
Figure 45 F illustrates goggle-type display (head mounted display), and it comprises main body 2501, display part 2502 and handel 2503.In display part 2502, use semiconductor device of the present invention to finish goggle-type display of the present invention.
Figure 45 G illustrates video camera, and it comprises main body 2601, display part 2602, framework 2603, outside link 2604, remote control receiving unit 2605, visual receiving unit 2606, battery 2607, audio frequency importation 2608, operation keys 2609, eyepiece part 2610 etc.In display part 2602, use semiconductor device of the present invention to finish video camera of the present invention.
Figure 45 H illustrates mobile phone, and it comprises, and main body 2701, framework 2702, display part 2703, audio frequency importation 2704, audio frequency output 2705, operation keys 2706, external connecting divide 2707, antenna 2708 etc.Note, in display part 3703, on black background, show the wrongly written or mispronounced character symbol, can suppress the power consumption of mobile phone thus.In display part 2703, use semiconductor device of the present invention to finish mobile phone of the present invention.
As mentioned above, but range of application of the present invention is very wide, and can be applied in the electric equipment of all spectra.Also might realize example 18 in conjunction with any structure shown in the example 6-12.
Example 19
With single channel TFT be used in flat dielectric film on the film formed many channel TFT of semiconductor of crystallization compare, many channel TFT of semiconductor device of the present invention are further controlled the dispersion in S value (subthreshold value), mobility, the threshold voltage etc.
Figure 47 A illustrates the frequency distribution of the S value of the many channel TFT of n type of the present invention.Many channel TFT of the present invention are used the semiconductor film by irradiation laser crystallization on the dielectric film with depression and projection.The width of dielectric film depression and projection is respectively 1.25 μ m and 1.50 μ m, and the TFT channel length is 8 μ m and total channel width is 12 μ m.
The frequency distribution of S value that Figure 47 B is illustrated in the n type list channel TFT of crystallization on the flat dielectric film is used for comparison.The TFT channel length is 8 μ m and channel width is 8 μ m.Figure 47 C is illustrated in the frequency distribution of S value of the many channel TFT of n type of crystallization on the flat dielectric film in addition.The TFT channel length is 8 μ m and total channel width is 12 μ m, and each channel width is 2 μ m, and the gap between the raceway groove is 2 μ m.
Standard deviation=15.8mV/dec among Figure 47 C, standard deviation=19.9mV/dec among Figure 47 C, and in Figure 47 A standard deviation=8.1mV/dec, to compare this value low with other two value.Therefore should understand the dispersion of the many channel TFT control of the n type of the present invention shown in Figure 47 A S value.
The channel width of the TFT of attention Figure 47 B is shorter than total channel width of the TFT of Figure 47 A.The TFT of Figure 47 C has than the interval between long channel width of the TFT of Figure 47 A and the long raceway groove in addition.But, even consider these conditions, can think that the standard deviation of Figure 47 A significantly is lower than the standard deviation of Figure 47 B and Figure 47 C, therefore n channel TFT of the present invention can expect to have the controlled effect of S value.
Then, Figure 48 A illustrates the frequency distribution of the threshold voltage of the many channel TFT of n type of the present invention.The structure of the TFT of Figure 48 A is identical with the situation of Figure 47 A.In addition, Figure 48 B frequency distribution of being illustrated in the threshold voltage of the n type list channel TFT of crystallization on the dielectric film on plane is used for comparison.The structure of the TFT of Figure 48 B is identical with the situation of Figure 48 B.In addition, Figure 48 C is illustrated in the frequency distribution of threshold voltage of the many channel TFT of n type of crystallization on the flat dielectric film.The structure of the TFT of Figure 48 C is identical with the situation of Figure 47 B.
Standard deviation=126mV among Figure 48 B, standard deviation=153mV among Figure 48 C, and in Figure 48 A standard deviation=80mV, to compare this value low with other two value.Therefore should understand the dispersion of the many channel TFT control of the n type of the present invention shown in Figure 48 A threshold voltage.
The channel width of the TFT of attention Figure 48 B is shorter than total channel width of the TFT of Figure 48 A.The TFT of Figure 48 C has than the interval between long channel width of the TFT of Figure 48 A and the long raceway groove in addition.But, even consider these conditions, can think that the standard deviation of Figure 48 A significantly is lower than the standard deviation of Figure 48 B and Figure 48 C, therefore n channel TFT of the present invention can expect to have the controlled effect of threshold voltage.
Then, Figure 49 A illustrates the frequency distribution of the mobility of the many channel TFT of n type of the present invention.The structure of the TFT of Figure 49 A is identical with the situation of Figure 47 A.In addition, Figure 49 B frequency distribution of mobility of being illustrated in the n type list channel TFT of crystallization on the flat dielectric film is used for comparison.The structure of the TFT of Figure 49 B is identical with the situation of Figure 47 B.In addition, Figure 49 C is illustrated in the frequency distribution of mobility of the many channel TFT of n type of crystallization on the flat dielectric film.The structure of the TFT of Figure 49 C is identical with the situation of Figure 47 C.
Standard deviation among Figure 49 B=7.9%, standard deviation among Figure 49 C=9.2%, and in Figure 49 A standard deviation=5.2%, to compare this value low with other two value.Therefore should understand the dispersion of the many channel TFT control of the n type of the present invention shown in Figure 49 A mobility.The design load of noting channel width among Figure 49 A is used for the computation migration rate, therefore can think actual migration rate low about 20%.
The channel width of the TFT of attention Figure 49 B is shorter than total channel width of the TFT of Figure 49 A.The TFT of Figure 49 C has than the interval between long channel width of the TFT of Figure 49 A and the long raceway groove in addition.But, even consider these conditions, can think that the standard deviation of Figure 49 A significantly is lower than the standard deviation of Figure 49 B and Figure 49 C, therefore n channel TFT of the present invention can expect to have the controlled effect of mobility.
Then, Figure 50 A illustrates the frequency distribution of the threshold voltage of the many channel TFT of p type of the present invention.Except that different polarity, the structure of the TFT of Figure 50 A is identical with the situation of Figure 47 A.In addition, Figure 50 B frequency distribution of threshold voltage of being illustrated in the p type list channel TFT of crystallization on the flat dielectric film is used for comparison.Except that different polarity, the structure of the TFT of Figure 50 B is identical with the situation of Figure 47 B.In addition, Figure 50 C is illustrated in the frequency distribution of threshold voltage of the many channel TFT of p type of crystallization on the flat dielectric film.Except that different polarity, the structure of the TFT of Figure 50 C is identical with the situation of Figure 47 C.
Standard deviation=218mV among Figure 50 B, standard deviation=144mV among Figure 50 C, and in Figure 50 A standard deviation=77mV, to compare this value low with other two value.Therefore should understand the dispersion of the many channel TFT control of the p type of the present invention shown in Figure 50 A threshold voltage.
The channel width of the TFT of attention Figure 50 B is shorter than total channel width of the TFT of Figure 50 A.The TFT of Figure 50 C has than the interval between long channel width of the TFT of Figure 50 A and the long raceway groove in addition.But, even consider these conditions, can think that the standard deviation of Figure 50 A significantly is lower than the standard deviation of Figure 50 B and Figure 50 C, therefore p channel TFT of the present invention can expect to have the controlled effect of threshold voltage.
Then, Figure 51 A illustrates the frequency distribution of the mobility of the many channel TFT of p type of the present invention.Except that different polarity, the structure of the TFT of Figure 51 A is identical with the situation of Figure 47 A.In addition, Figure 51 B frequency distribution of mobility of being illustrated in the p type list channel TFT of crystallization on the flat dielectric film is used for comparison.Except that different polarity, the structure of the TFT of Figure 51 B is identical with the situation of Figure 47 B.In addition, Figure 51 C is illustrated in the frequency distribution of mobility of the many channel TFT of p type of crystallization on the flat dielectric film.Except that different polarity, the structure of the TFT of Figure 51 C is identical with the situation of Figure 47 C.
Standard deviation among Figure 51 B=7.6%, standard deviation among Figure 51 C=5.9%, and in Figure 51 A standard deviation=4.6%, to compare this value low with other two value.Therefore should understand the dispersion of the many channel TFT control of the p type of the present invention shown in Figure 51 A mobility.Notice that the design load of channel width is used for the computation migration rate among Figure 49 A, therefore can think actual migration rate low about 20%.
The channel width of the TFT of attention Figure 51 B is shorter than total channel width of the TFT of Figure 51 A.The TFT of Figure 51 C has than the interval between long channel width of the TFT of Figure 51 A and the long raceway groove in addition.But, even consider these conditions, can think that the standard deviation of Figure 51 A significantly is lower than the standard deviation of Figure 51 B and Figure 51 C, therefore p channel TFT of the present invention can expect to have the controlled effect of mobility.
Shown in Figure 47 A-51C, the effect that the dispersion that many channel TFT of the present invention have the TFT characteristic is suppressed.Compare with many channel TFT with single channel TFT of wherein carrying out crystallization on flat dielectric film, by many channel TFT of the present invention, the crystal orientation of each raceway groove is easy to rotation, therefore comprises various crystal orientations.Therefore can think because the dispersion of the characteristic that crystal orientation causes is easy to be evened up.
The distortion that the edge is produced by fusing and crystal semiconductor film along with crystallization accumulates in the outer zone of opening portion, makes its fill the open area that is formed on the insulating surface.That is, the crystal semiconductor film that partly forms for filling opening can not have distortion.
In other words, by in basilar memebrane, forming opening portion and forming semiconductor, in passing through the process of irradiation continuous wave laser crystallization non-single crystal semiconductor film, make its filling opening part in fusing and crystallization process, distortion, grain boundary and the crystal sub boundary of accompanying crystallization are accumulated in the zone outside the opening portion.Make its channel formation region be arranged in the crystal semiconductor film of opening portion by forming TFT subsequently, make that increasing high speed current drives performance becomes possibility, and make the reliability that increases element become possibility.
By the present invention, be used as the TFT active layer by the semiconductor film that will be positioned at effectively on the basilar memebrane depression, can prevent the formation of crystal boundary in the TFT channel formation region, and can prevent it all is because remarkable reduction, the decline of making current and the increase of cut-off current of the TFT mobility of crystal boundary.Notice that the designer can suitably determine the graphical amount of removing by bump, adjacent and concave edges.
In addition,, can adopt wide wherein channel formation region and gate electrode, gate insulating film is clipped in therebetween zone, therefore can make channel width become big by being separated from each other a plurality of TFT channel formation regions.Channel width is bigger guarantees making current by making, and the heat that is produced by drive TFT can be dissipated effectively.
Claims (14)
1. semiconductor device comprises:
The crystal semiconductor island that on insulating surface, forms, described crystal semiconductor island comprises at least the first and second parts that extend parallel to each other, each in wherein said first and second parts comprises channel formation region;
The gate insulating film that on described first and second parts, forms;
The gate electrode that above described first and second parts, forms, described gate insulating film is therebetween,
Wherein said gate insulating film contacts in described first and second parts of described semiconductor island top surface and the side surface of each, and described top surface of each and side surface form in described first and second parts of the contiguous described semiconductor island of described gate electrode, described gate insulating film is therebetween, and
In wherein said first and second parts each comprises at least one crystal, and described crystal extends along the orientation of each in described first and second parts.
2. according to the semiconductor device of claim 1, wherein, form the circuit that is selected from the group of forming by CPU, counter circuit and logic drive circuit by using described semiconductor device.
3. according to the semiconductor device of claim 1, wherein, form logical circuit by using described semiconductor device.
4. according to the semiconductor device of claim 1, wherein, described semiconductor device is installed in the electronic equipment that is selected from the group of being made up of mobile computer, portable phone, video camera, digital camera.
5. according to the semiconductor device of claim 1, wherein, described semiconductor device is installed in the display device.
6. according to the semiconductor device of claim 1, wherein, described semiconductor device is installed in the personal computer.
7. according to the semiconductor device of claim 1, wherein, described semiconductor device is installed in the image-reproducing means that is equipped with recording medium.
8. semiconductor device comprises:
The crystal semiconductor island that on insulating surface, forms, described crystal semiconductor island comprises a pair of impurity range and at least the first and second parts that extend parallel to each other between this is to impurity range, each in wherein said first and second parts comprises channel formation region;
The gate insulating film that forms above described first and second parts, wherein said gate insulating film contact in described first and second parts on described crystal semiconductor island top surface and a part of insulating surface between described first and second parts of each at least;
The gate electrode that above described first and second parts, forms, described gate insulating film is therebetween,
In wherein said first and second parts each comprises at least one crystal, and described crystal extends along the orientation of each in described first and second parts.
9. semiconductor device according to Claim 8 wherein, forms the circuit that is selected from the group of being made up of CPU, counter circuit and logic drive circuit by using described semiconductor device.
10. semiconductor device according to Claim 8 wherein, forms logical circuit by using described semiconductor device.
11. semiconductor device according to Claim 8, wherein, described semiconductor device is installed in the electronic equipment that is selected from the group of being made up of mobile computer, portable phone, video camera, digital camera.
12. semiconductor device according to Claim 8, wherein, described semiconductor device is installed in the display device.
13. semiconductor device according to Claim 8, wherein, described semiconductor device is installed in the personal computer.
14. semiconductor device according to Claim 8, wherein, described semiconductor device is installed in the image-reproducing means that is equipped with recording medium.