CN101284979A - Water-proofing material for adhesive joint between solid objects - Google Patents
Water-proofing material for adhesive joint between solid objects Download PDFInfo
- Publication number
- CN101284979A CN101284979A CNA200710010931XA CN200710010931A CN101284979A CN 101284979 A CN101284979 A CN 101284979A CN A200710010931X A CNA200710010931X A CN A200710010931XA CN 200710010931 A CN200710010931 A CN 200710010931A CN 101284979 A CN101284979 A CN 101284979A
- Authority
- CN
- China
- Prior art keywords
- plastic
- mass content
- solid
- adhesive joint
- steel mud
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a waterproof material for bonding solids, namely plastic-steel mud, which is characterized in that: the waterproof material for bonding solids, namely the plastic-steel mud, comprises an A component and a B component; the A component comprises the following contents in percentage by mass: 25 to 45 percent of epoxy resin, 1 to 5 percent of phthalic acid ester, and the rest additive being the combination or one of calcium carbonate, CCR, talcum powder and extra fine talc powder; the B component comprises the following contents in percentage by mass: 20 to 35 percent of polyamide curing agent, and the rest additive being the combination or one of calcium sulphate, calcium carbonate and talcum powder. The plastic-steel mud has waterproof and mildewproof performance, high adhesive force and tough structural strength, applies to the bond of ceramics, metal, rigid plastics, glass, concrete, stone and various materials, as well as the water prevention of lines, hides no dirt, and is resistant to wear, acid, alkali, corrosion and high-low temperature. In construction process, the plastic-steel mud has no pollution source or pungent odor, and does no harm to human body, which is a novel waterproof material for indoor decoration design.
Description
Technical field
The present invention relates to the Industrial buildings field of waterproof materials, a kind of water-proof material that is used for adhesive joint between solid---plastic-steel mud is provided especially.
Background technology
The modern life, finishing has generally entered the focus that common people family, particularly kitchen guarding's sanitary equipment have become people and paid close attention to.We are enjoying the while easily that high-grade sanitary appliance brought, and the consequent has also increased many worries.For example: the local jaundice in the anti-waterside of usual general glass cement, blackout; The burn into of acid, alkali and oily matter is mouldy, fracture etc., and these inevitably have a strong impact on overall appearance and use.At this phenomenon, urgent need is a kind of on the market can replace glass cement, becomes the waterproof material of interior decoration design.
Summary of the invention
The objective of the invention is in order to replace glass cement, become the waterproof material of interior decoration design, the spy provides a kind of water-proof material that is used for adhesive joint between solid---plastic-steel mud.
A kind of water-proof material that is used for adhesive joint between solid---plastic-steel mud, it is characterized in that: the described water-proof material that is used for adhesive joint between solid---plastic-steel mud drum is drawn together A, B two-pack, the A component comprises that mass content is the Resins, epoxy of 25%-45%, mass content is the phthalic ester of 1%-5%, the additive of surplus be lime carbonate, CCR, talcum powder, the strong powder of magnesium combination or one of; The B component comprises that mass content is the polyamides Ammonia solidifying agent of 20%-35%, the additive of surplus be calcium sulfate, lime carbonate, talcous combination or one of.
Described B component comprises that mass content is the acetone class thinner of 1%-5%.
Described A component comprises that mass content is the Resins, epoxy of 25%-45%, and mass content is the phthalic ester of 1%-5%, surplus lime carbonate.
The Resins, epoxy that comprises mass content 30%-40% in the described A component.
The phthalic ester that comprises mass content 2%-4% in the described A component.
In the described A component additive comprise 40%-60% lime carbonate, surplus be CCR, talcum powder, the strong powder of magnesium combination or one of.
Additive in the described A component comprise mass content 10%-20% talcum powder, surplus be CCR, lime carbonate, the strong powder of magnesium combination or one of.
Additive in the described B component comprises mass content 20%-40% calcium sulfate, and surplus is a talcum powder, the combination of lime carbonate or one of.
The described water-proof material that is used for adhesive joint between solid---plastic-steel mud is to be used in the bonding that has between the solid under the waterproof requirement, particularly the bonding of kitchen guarding's sanitary equipment.This product is a kind of bi-component reaction-type high-strength structure batch cover material material, is the clay shape before the curing.
Described Resins, epoxy is selected from Dongguan dimension star trade Co., Ltd (numbering 14270), blue star chemical industry stock company (F-48), Tianjin, Tianjin and chemical company limited (TS-650), the red precious resin company (651,650) in Zhenjiang.
Described phthalic ester is selected from Luoyang huge loose commerce and trade company limited, Wuhan City's ocean mouth Raw Materials Company of Chemical Industry.
Described polyamides Ammonia solidifying agent is selected from Jiang Qiao chemical plant, Shanghai (6101 solidifying agent, 650 solidifying agent), the auspicious strange chemical industry company limited in Guangzhou (R-2210 solidifying agent), synthetic materials company of Guangzhou Unionsun (1424B).
Described acetone class thinner is selected from good sharp chemical plant, Jiangdu, ocean mouth Raw Materials Company of Chemical Industry, day woods chemical industry.
The local jaundice in the anti-waterside of usual general glass cement, blackout; The burn into of acid, alkali and oily matter is mouldy, fracture etc., and these inevitably have a strong impact on overall appearance and use.At this phenomenon, urgent need is a kind of on the market can replace glass cement, becomes the waterproof material of interior decoration design.
This material behavior national building materials product quality supervision and inspection center test proof, service check is reported as follows:
Advantage of the present invention:
Have the clinging power of 100% waterproof, mildew-resistant, humidity resistance, high strength degree and tough and tensile structural strength, be applicable to various materials such as pottery, metal, rigid plastics, glass, concrete, stone material; Fix, plug into various pipe fittings, pipeline, circuit not only seal but also insulate, and repair tracheae, water pipe, tank, water-proof repairing etc.
Be specially adapted to the lines waterproof, after this material is handled side seam, can make the seam both sides form an integral body, any surface finish, hard, do not hide dirt, and independent one-tenth line, performance wearable, antiacid alkali, corrosion-resistant, high-low temperature resistant do not shrink, do not wear out, never degenerate, and the material environment friendly performance is good.In construction process, pollution-free source, have no irritating odor, harmless.After construction was finished, spontaneous curing did not have carcinogenic composition, can use in 2-4 hour.
Embodiment
Embodiment 1
The described water-proof material that is used for adhesive joint between solid of present embodiment---plastic-steel mud comprises A, B two-pack, wherein the ratio of mass content:
The A component, Resins, epoxy: lime carbonate: talcum powder: phthalic ester=4: 5: 1: 1
The B component, polyamides Ammonia solidifying agent: calcium sulfate: lime carbonate: talcum powder=3: 3: 1: 3.
Embodiment 2
The described water-proof material that is used for adhesive joint between solid of present embodiment---plastic-steel mud comprises A, B two-pack, wherein the ratio of mass content:
The A component, Resins, epoxy: talcum powder: phthalic ester=3: 6: 1
The B component, polyamides Ammonia solidifying agent: talcum powder: acetone class thinner=3: 6: 1
Embodiment 3
The described water-proof material that is used for adhesive joint between solid of present embodiment---the plastic-steel mud drum is drawn together A, B two-pack, wherein:
The A component comprises that mass content is 25% Resins, epoxy, and mass content is 1% phthalic ester, and the additive mass content of surplus is than being lime carbonate: CCR: talcum powder: the strong powder of magnesium=1: 1: 1: 1;
The B component comprises that mass content is 20% polyamides Ammonia solidifying agent, and the additive of surplus is 80% talcum powder.
Embodiment 4
The described water-proof material that is used for adhesive joint between solid of present embodiment---the plastic-steel mud drum is drawn together A, B two-pack, wherein:
The A component comprises that mass content is 25% Resins, epoxy, and mass content is 1% phthalic ester, and the additive of surplus is a lime carbonate;
The B component comprises that mass content is 20% polyamides Ammonia solidifying agent, 1% acetone class thinner, and the additive of surplus is a calcium sulfate.
Embodiment 5
The described water-proof material that is used for adhesive joint between solid of present embodiment---the plastic-steel mud drum is drawn together A, B two-pack,
The A component comprises that mass content is 35% Resins, epoxy, and mass content is 3% phthalic ester, and the additive of surplus is CCR;
The B component comprises that mass content is 28% polyamides Ammonia solidifying agent, 3% acetone class thinner, and the additive of surplus is a lime carbonate.
Embodiment 6
The described water-proof material that is used for adhesive joint between solid of present embodiment---the plastic-steel mud drum is drawn together A, B two-pack,
The A component comprises that mass content is 45% Resins, epoxy, and mass content is 5% phthalic ester, and the additive of surplus is a talcum powder;
The B component comprises that mass content is 35% polyamides Ammonia solidifying agent, 5% acetone class thinner, and the additive of surplus is a talcum powder.
Embodiment 7
The described water-proof material that is used for adhesive joint between solid of present embodiment---the plastic-steel mud drum is drawn together A, B two-pack,
The A component comprises that mass content is 25% Resins, epoxy, and mass content is 3% phthalic ester, and the additive of surplus is a talcum powder;
The B component comprises that mass content is 20% polyamides Ammonia solidifying agent, and the additive of surplus is a talcum powder.
Embodiment 8
The described water-proof material that is used for adhesive joint between solid of present embodiment---the plastic-steel mud drum is drawn together A, B two-pack,
The A component comprises that mass content is 25% Resins, epoxy, and mass content is 5% phthalic ester, and the additive of surplus is the combination of lime carbonate, CCR, talcum powder, the strong powder of magnesium;
The B component comprises that mass content is 25% polyamides Ammonia solidifying agent, and the additive of 2% acetone class thinner surplus is a talcum powder.
Embodiment 9
The described water-proof material that is used for adhesive joint between solid of present embodiment---the plastic-steel mud drum is drawn together A, B two-pack,
The A component comprises that mass content is 35% Resins, epoxy, and mass content is 4% phthalic ester, and the additive of surplus is the strong powder of magnesium;
The B component comprises that mass content is 20% polyamides Ammonia solidifying agent, and the additive of surplus is a talcum powder.
Embodiment 10
The described water-proof material that is used for adhesive joint between solid of present embodiment---the plastic-steel mud drum is drawn together A, B two-pack,
The A component comprises that mass content is 45% Resins, epoxy, and mass content is 1% phthalic ester, and the additive of surplus is the combination of lime carbonate, CCR, talcum powder, the strong powder of magnesium;
The B component comprises that mass content is 35% polyamides Ammonia solidifying agent, 1% acetone class thinner, and the additive of surplus is a talcum powder.
Embodiment 11
The described water-proof material that is used for adhesive joint between solid of present embodiment---the plastic-steel mud drum is drawn together A, B two-pack,
The A component comprises that mass content is 45% Resins, epoxy, and mass content is 4% phthalic ester, and the additive of surplus is a talcum powder;
The B component comprises that mass content is 35% polyamides Ammonia solidifying agent, 5% acetone class thinner, and the additive of surplus is a talcum powder.
Embodiment 12
The described water-proof material that is used for adhesive joint between solid of present embodiment---the plastic-steel mud drum is drawn together A, B two-pack,
The A component comprises that mass content is 45% Resins, epoxy, and mass content is 5% phthalic ester, and the additive of surplus is the strong powder of magnesium;
The B component comprises that mass content is 35% polyamides Ammonia solidifying agent, and the additive of surplus is a calcium sulfate.
Embodiment 13
The described water-proof material that is used for adhesive joint between solid of present embodiment---the plastic-steel mud drum is drawn together A, B two-pack,
The A component comprises that mass content is 45% Resins, epoxy, and mass content is 2% phthalic ester, and the additive of surplus is a talcum powder;
The B component comprises that mass content is 30% polyamides Ammonia solidifying agent, 3% acetone class thinner, and the additive of surplus is a talcum powder.
Embodiment 14
The described water-proof material that is used for adhesive joint between solid of present embodiment---the plastic-steel mud drum is drawn together A, B two-pack,
The A component comprises that mass content is 40% Resins, epoxy, and mass content is 3% phthalic ester, and the additive of surplus is the combination of lime carbonate, CCR, talcum powder, the strong powder of magnesium;
The B component comprises that mass content is 30% polyamides Ammonia solidifying agent, and the additive of surplus is a calcium sulfate.
Embodiment 15
The described water-proof material that is used for adhesive joint between solid of present embodiment---the plastic-steel mud drum is drawn together A, B two-pack,
The A component comprises that mass content is 40% Resins, epoxy, and mass content is 2% phthalic ester, and the additive of surplus is the strong powder of magnesium;
The B component comprises that mass content is 32% polyamides Ammonia solidifying agent, 5% acetone class thinner, and the additive of surplus is a talcum powder.
Embodiment 16
The described water-proof material that is used for adhesive joint between solid of present embodiment---the plastic-steel mud drum is drawn together A, B two-pack,
The A component comprises that mass content is 45% Resins, epoxy, and mass content is 1% phthalic ester, and the additive of surplus is lime carbonate, talcous combination;
The B component comprises that mass content is 20% polyamides Ammonia solidifying agent, 1% acetone class thinner, and the additive of surplus is a talcum powder.
Claims (9)
1, the plastic-steel mud drum is drawn together A, B two-pack to a kind of water-proof material that is used for adhesive joint between solid---plastic-steel mud is characterized in that: the described water-proof material that is used for adhesive joint between solid---,
The A component comprises that mass content is the Resins, epoxy of 25%-45%, and mass content is the phthalic ester of 1%-5%, the additive of surplus be lime carbonate, CCR, talcum powder, the strong powder of magnesium combination or one of;
The B component comprises that mass content is the polyamides Ammonia solidifying agent of 20%-35%, the additive of surplus be calcium sulfate, lime carbonate, talcous combination or one of.
2, according to the described water-proof material that is used for adhesive joint between solid of claim 1---plastic-steel mud is characterized in that: described B component comprises that mass content is the acetone class thinner of 1%-5%.
3, according to the described water-proof material that is used for adhesive joint between solid of claim 1---plastic-steel mud is characterized in that: described A component comprises that mass content is the Resins, epoxy of 25%-45%, and mass content is the phthalic ester of 1%-5%, surplus lime carbonate.
4, according to the described water-proof material that is used for adhesive joint between solid of claim 1---plastic-steel mud is characterized in that: the Resins, epoxy that comprises mass content 30%-40% in the described A component.
5, according to the described water-proof material that is used for adhesive joint between solid of claim 1---plastic-steel mud is characterized in that: the phthalic ester that comprises mass content 2%-4% in the described A component.
6, according to the described water-proof material that is used for adhesive joint between solid of claim 1---plastic-steel mud is characterized in that: in the described A component additive comprise mass content 40%-60% lime carbonate, surplus be talcum powder, CCR, the strong powder of magnesium combination or one of.
7, according to the described water-proof material that is used for adhesive joint between solid of claim 1---plastic-steel mud is characterized in that: the additive in the described A component comprise mass content 10%-20% talcum powder, surplus be CCR, lime carbonate, the strong powder of magnesium combination or one of.
8, according to the described water-proof material that is used for adhesive joint between solid of claim 1---plastic-steel mud is characterized in that: the additive in the described B component comprises mass content 20%-40% calcium sulfate, and surplus is a talcum powder, the combination of lime carbonate or one of.
9,---plastic-steel mud is characterized in that: the described water-proof material that is used for adhesive joint between solid---plastic-steel mud is to be used in the bonding that has between the solid under the waterproof requirement according to the described water-proof material that is used for adhesive joint between solid of claim 1.