CN101240369A - 一种提高镁合金力学性能的方法 - Google Patents
一种提高镁合金力学性能的方法 Download PDFInfo
- Publication number
- CN101240369A CN101240369A CNA200710010339XA CN200710010339A CN101240369A CN 101240369 A CN101240369 A CN 101240369A CN A200710010339X A CNA200710010339X A CN A200710010339XA CN 200710010339 A CN200710010339 A CN 200710010339A CN 101240369 A CN101240369 A CN 101240369A
- Authority
- CN
- China
- Prior art keywords
- magnesium alloy
- pulsed current
- sup
- handled
- mechanical property
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及镁合金性能的改进技术,具体为一种提高镁合金力学性能的方法。对镁合金进行脉冲电流处理,脉冲电流放电周期1μs~1000μs,最大峰值电流密度103~105A/mm2,单个脉冲的持续时间1μs~10000μs。本技术的特点在于:经过脉冲电流处理后,可以提高镁合金的塑性,而基本不降低其强度。并且本发明操作简单,效率高,成本低,便于推广应用。
Description
技术领域:
本发明涉及镁合金性能的改进技术,具体为一种提高镁合金力学性能的方法。
背景技术:
镁合金作为一种结构材料,具有密度低、比强度高、比硬度高等特点,已被广泛应用于航空航天、汽车工业、空间与国防领域,以及电子与通信等行业。但是由于镁合金是密排六方(hcp)结构,塑性变形能力和压力加工成形性能都较差,所以目前提高镁合金的力学性能成为了研究者们主要的研究方向。而利用脉冲电流方法来提高镁合金的综合力学性能,目前还尚未见报道。
发明内容:
本发明的目的在于提供一种提高镁合金力学性能的方法。经过本方法处理后,镁合金的塑性得到提高,而且强度基本不降低。
为了实现上述目的,本发明的技术方案是:处理方法为脉冲电流处理。脉冲电流的放电周期1μs~1000μs,最大峰值电流密度103~105A/mm2,单个脉冲的持续时间1μs~10000μs,脉冲电流处理的时间为单个脉冲的持续时间。本发明提供的提高镁合金力学性能的方法,其脉冲电流的较佳参数为:放电周期为50μs~500μs,最大峰值电流密度为3×103~4×104A/mm2,单个脉冲的持续时间200μs~2500μs。
本发明的原理是:利用脉冲电流对不同状态的镁合金进行处理,使处理后的镁合金晶粒尺寸仅稍微长大,织构不发生明显的变化,从而使处理后的样品强度基本不降低。而脉冲电流处理后增加了镁合金内部大角晶界的比例,并且脉冲电流能够降低材料内部的缺陷密度,如:降低位错密度,减少孔洞,愈合裂纹等等。所以处理后的镁合金塑性能够明显提高。
本发明的优点在于:
1、经过脉冲电流处理后,可以提高镁合金的塑性,而基本不降低其强度。
2、采用本发明操作简单,周期短,效率高,成本低,便于推广应用。
附图说明:
图1为脉冲电流处理过程的装置示意图。
图2为处理试样所用脉冲电流的波形图。
图3为实施例1试样处理后与处理前的拉伸曲线。
图4为实施例2试样处理后与处理前的拉伸曲线。
图5为实施例3试样处理后与处理前的拉伸曲线。
图6为实施例4试样处理后与处理前的拉伸曲线。
具体实施方式:
下面通过实施例详述本发明。
实施例1
所用材料是经过4次等通道转角挤压处理的AZ31镁合金,试样有效部分尺寸为:6mm×4mm×1.5mm。如图1所示,将试样1两端夹持在铜电极2之间,再将两个铜电极2分别与脉冲电流发生器(电容器组)输出的正负电极相连,脉冲电流是由10台MWF15-36电容器放电产生的,脉冲电流的波形和基本参数由TDS3012型示波器测定。
图2为本实施例处理试样所用的脉冲电流波形图,其中脉冲电流的放电周期约为tp=110μs,最大峰值电流密度约为jm=1.05×104A/mm2,单个脉冲的持续时间约为800μs。如图3所示,脉冲电流处理后样品的延伸率与脉冲电流处理之前相比明显提高,由原来的约37%提高到约57%,而屈服强度和最大拉伸强度没有降低。脉冲电流处理后样品的平均晶粒尺寸由处理前的约2.1μm长大到2.5μm,织构未发生明显变化。
实施例2
与实施例1不同的是:最大峰值电流密度约为jm=0.98×104A/mm2。其脉冲电流处理前后拉伸曲线的变化如图4所示,脉冲电流处理后样品的延伸率由处理前的约37%提高到了约46%,而屈服强度和最大拉伸强度都未降低。平均晶粒尺寸由处理前的约2.1μm稍微长大到2.2μm,织构未发生明显变化。
实施例3
与实施例1不同的是:最大峰值电流密度约为jm=1.08×104A/mm2。其脉冲电流处理前后拉伸曲线的变化如图5所示,脉冲电流处理后样品的延伸率由处理前的约37%提高到了约45%,而屈服强度和最大拉伸强度稍微降低。平均晶粒尺寸由处理前的约2.1μm长大到2.6μm,织构未发生明显变化。
实施例4
与实施例1不同的是:所用材料是工业挤压态的AZ31镁合金,试样有效部分尺寸为18mm×4mm×2mm。脉冲电流的放电周期约为tp=220μs,最大峰值电流密度约为jm=0.72×104A/mm2,单个脉冲的持续时间约为1100μs。其脉冲电流处理前后拉伸曲线的变化如图6所示,脉冲电流处理后样品的延伸率由处理前的约15%提高到了约21%,而屈服强度和最大拉伸强度都没降低。平均晶粒尺寸和织构未发生明显变化。
Claims (2)
1. 一种提高镁合金力学性能的方法,其特征在于:处理方法为脉冲电流处理,脉冲电流放电周期1μs~1000μs,最大峰值电流密度103~105A/mm2,单个脉冲的持续时间1μs~10000μs,脉冲电流处理的时间为单个脉冲的持续时间。
2. 按照权利要求1所述的提高镁合金力学性能的方法,其特征在于:脉冲电流的放电周期为50μs~500μs,最大峰值电流密度为3×103~4×104A/mm2,单个脉冲的持续时间200μs~2500μs。