CN101229967A - 一种不定型复合保温材料及其制备方法 - Google Patents
一种不定型复合保温材料及其制备方法 Download PDFInfo
- Publication number
- CN101229967A CN101229967A CNA2008100591877A CN200810059187A CN101229967A CN 101229967 A CN101229967 A CN 101229967A CN A2008100591877 A CNA2008100591877 A CN A2008100591877A CN 200810059187 A CN200810059187 A CN 200810059187A CN 101229967 A CN101229967 A CN 101229967A
- Authority
- CN
- China
- Prior art keywords
- insulating material
- composite heat
- form composite
- indefinite form
- wetting agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种不定型复合保温材料，它含有40－55％重量含量的膨胀珍珠岩、10－20％重量含量的石棉、10－20％重量含量的硅酸铝纤维、1－2％重量含量的粘接剂、10－20％重量含量的陶土。所述陶土是凹凸棒土、膨润土、硅澡土的一种或几种。所述粘接剂是聚丙烯酰胺或甲基纤维素。上述不定型复合保温材料的使用方法：将润湿剂和水混合后、加入所述不定型复合保温材料、搅拌，所述润湿剂、水、不定型复合保温材料重量比为：1∶10－20∶10－20。本发明的不定型复合保温材料添增了陶土组分，其可塑性好。在其使用过程中，加入润湿剂，使各组分均匀，提高了施工效率。
Description
技术领域
本发明涉及一种保温材料及其制备方法，更具体说是一种不定型复合保温材料及其制备方法。
背景技术
传统的保温材料大多为湿型，产品在工厂生产后运输到使用场地使用，由于其产品含水量为50％作用，因此导致运输成本高的不足，另外该类产品还存在保存时间短、施工周期长问题。
国家知识产权局2007年9月5日公开的“一种不定型复合保温材料的生产方法”(公开号CN10128968A)专利文献，该文献介绍的不定型复合保温材料的生产方法，为干拌混合料，它是以天然硅酸盐类纤维、轻质功能填料及助剂经混合、干燥、搅拌而成的，所述天然硅酸盐包括有水镁石、海泡石、石棉，所述轻质功能填料包括有膨胀膨胀珍珠岩、聚苯乙烯颗粒、聚胺脂硬泡颗粒，所述助剂包括有石膏、石灰、分散剂S、胶粉、纤维素、增稠剂。该方法生产的干拌混合料具有储存时间长、运输方便，可以在施工现场加水搅拌成复合硅酸盐保温隔热涂料，凝结固化快等特点。但其配方尤待于进一步优化，进一步提高保温效果和施工效率。
发明内容
针对上述情况，本发明拟解决的问题是提供一种组分优化，保温效果好、施工效率高的不定型复合保温材料及其制备方法。
为达到上述目的，本发明采用了以下技术方案：一种不定型复合保温材料，它含有40-55％重量含量的膨胀珍珠岩、10-20％重量含量的石棉、10-20％重量含量的硅酸铝纤维、1-2％重量含量的粘接剂、10-20％重量含量的陶土。
所述陶土是凹凸棒土、膨润土、硅澡土的一种或几种。所述粘接剂是聚丙烯酰胺或甲基纤维素。
上述不定型复合保温材料的使用方法：将润湿剂和水混合后、加入所述不定型复合保温材料、搅拌，所述润湿剂、水、不定型复合保温材料重量比为：1∶10-20∶10-20。
所述润湿剂是HLB值7-9的表面活性剂，可以是渗透剂JFC或斯潘20。
由于采用了上述技术方案，与现有技术相比，本发明的不定型复合保温材料添增了陶土组分，其可塑性好，另外通过各组分的优化，提高了保温效果。在其使用过程中，加入润湿剂，使各组分均匀，提高了施工效率。
具体实施方式
本发明的不定型复合保温材料，它含有膨胀珍珠岩、石棉、硅酸铝纤维、粘接剂和陶土。其生产方法是将上述物质混合搅拌即得到成品，其搅拌可在搅拌机中进行。
先对个组分进行介绍。
膨胀珍珠岩、石棉、硅酸铝纤维，可采用市售产品。
粘接剂：可采用市售聚丙烯酰胺或甲基纤维素。
陶土：采用凹凸棒土、膨润土、硅澡土的一种或几种。
具体各实施例的各组分配比见下表：
| 实施例 | 膨胀珍珠岩 | 石棉 | 硅酸铝纤维 | 粘接剂 | 陶土 | 使用效果 |
| 1 | 40Kg | 18kg | 20Kg | 2Kg | 20Kg | 好 |
| 2 | 55Kg | 20Kg | 15Kg | 1.5Kg | 18.5Kg | 好 |
| 3 | 48Kg | 20Kg | 20Kg | 2Kg | 10Kg | 较好 |
| 4 | 49Kg | 20Kg | 10Kg | 1Kg | 20Kg | 好 |
| 5 | 50Kg | 10Kg | 20Kg | 2Kg | 18Kg | 好 |
| 6 | 53Kg | 15Kg | 15Kg | 2Kg | 15kg | 较好 |
| 7 | 45Kg | 20Kg | 20Kg | 2Kg | 13Kg | 较好 |
上述七个实施例均能得到100Kg产品，经多次试验，其凝结固化时间、高保温效果等使用综合效果也可以上表中看出。
本发明的不定型复合保温材料的使用方法
先对润湿剂进行介绍。润湿剂是HLB值7-9的表面活性剂。如渗透剂JFC、斯潘20等。不定型复合保温材料的具体使用方法为：
将润湿剂和水混合后，取实施例1-7中任意一种得到的不定型复合保温材料产品，将不定型复合保温材料产品加入到润湿剂和水混合后，搅拌，即可直接施工。上述润湿剂、水、不定型复合保温材料重量比见下表：
| 实施例 | 水 | 不定型复合保温材料 | 润湿剂 |
| 8 | 20Kg | 20Kg | 1Kg |
| 9 | 15Kg | 15Kg | 1Kg |
| 10 | 20Kg | 10Kg | 1Kg |
| 11 | 10Kg | 20KG | 1Kg |
Claims (6)
1.一种不定型复合保温材料，其特征在于它含有40-55％重量含量的膨胀珍珠岩、10-20％重量含量的石棉、10-20％重量含量的硅酸铝纤维、1-2％重量含量的粘接剂、10-20％重量含量的陶土。
2.根据权利要求1所述的不定型复合保温材料，其特征在于所述陶土是凹凸棒土、膨润土、硅澡土的一种或几种。
3.根据权利要求1所述的不定型复合保温材料，其特征在于所述粘接剂是聚丙烯酰胺或甲基纤维素。
4.根据权利要求1所述的不定型复合保温材料的使用方法，其特征在于：将润湿剂和水混合后、加入所述不定型复合保温材料、搅拌，所述润湿剂、水、不定型复合保温材料重量比为：1∶10-20∶10-20。
5.根据权利要求4所述的不定型复合保温材料的使用方法，其特征在于所述润湿剂是HLB值7-9的表面活性剂。
6.根据权利要求5所述的不定型复合保温材料的使用方法，其特征在于所述润湿剂是渗透剂JFC或斯潘20。