CN105384411B - 一种可释放负离子的功能砂浆的制备方法 - Google Patents
一种可释放负离子的功能砂浆的制备方法 Download PDFInfo
- Publication number
- CN105384411B CN105384411B CN201510920183.3A CN201510920183A CN105384411B CN 105384411 B CN105384411 B CN 105384411B CN 201510920183 A CN201510920183 A CN 201510920183A CN 105384411 B CN105384411 B CN 105384411B
- Authority
- CN
- China
- Prior art keywords
- powder
- component
- preparation
- negative ion
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Description
检测项目 | 单位 | 实施例1 | 实施例2 | 实施例3 | 实施例4 |
28d抗压强度 | Mpa | 28.5 | 26.6 | 24.2 | 25.3 |
抗折强度 | Mpa | 18 | 16 | 13 | 15 |
粘结强度 | Mpa | 0.68 | 0.60 | 0.56 | 0.58 |
负离子发生量 | 个/cm2 | 26300 | 23500 | 20100 | 25500 |
Claims (5)