CN101208073A - 彩妆类化妆品 - Google Patents

彩妆类化妆品 Download PDF

Info

Publication number
CN101208073A
CN101208073A CNA2006800150248A CN200680015024A CN101208073A CN 101208073 A CN101208073 A CN 101208073A CN A2006800150248 A CNA2006800150248 A CN A2006800150248A CN 200680015024 A CN200680015024 A CN 200680015024A CN 101208073 A CN101208073 A CN 101208073A
Authority
CN
China
Prior art keywords
composition
makeup cosmetic
powder body
cosmetic
partially crosslinked
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2006800150248A
Other languages
English (en)
Other versions
CN101208073B (zh
Inventor
增渕佑二
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kose Corp
Original Assignee
Kose Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kose Corp filed Critical Kose Corp
Publication of CN101208073A publication Critical patent/CN101208073A/zh
Application granted granted Critical
Publication of CN101208073B publication Critical patent/CN101208073B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种彩妆类化妆品，其不发粘、清爽的使用感、有弹性的触感及柔软感和耐冲击性良好，具有可填充入金属制皿状容器或树脂制皿状容器中并压缩成型，将上述皿状容器装入紧凑容器中而合并使用多种颜色的简便性和便利性。该彩妆类化妆品含有：成分(A)含有长链烷基的部分交联型有机聚硅氧烷聚合物、除了成分(A)之外的成分(B)部分交联型有机聚硅氧烷聚合物、成分(C)硅油、成分(D)选自烃油和/或酯油的一种或两种以上的液状油以及成分(E)粉体，将上述由(A)－(E)组成的组合物填充入皿状器皿，并压缩成型可获得彩妆类化妆品。

Description

彩妆类化妆品
技术领域
本发明涉及彩妆类化妆品及其制备方法，更具体地，涉及一种含有由含有长链烷基的部分交联有机聚硅氧烷聚合物组成的成分(A)、由除了成分(A)之外的部分交联型有机聚硅氧烷聚合物组成的成分(B)、由硅油组成的成分(C)、由选自烃油和/或酯油的一种或两种以上的液状油组成的成分(D)以及由粉体组成的成分(E)的彩妆类化妆品及其制备方法。
背景技术
由于彩妆类化妆品等化妆品是直接涂抹在面部、指甲等的物品，因此心情愉快地进行使用、完美地完成使用、漂亮妆容的使用感，使用效果是很重要的，这决定了化妆品的价值。使用化妆品时的第一步是，首先倾斜瓶子使内容物流到手掌中、用指尖从容器内挖出、从金属管或塑料管中倒出内容物，第二步是在皮肤表面涂抹、薄薄地摊开并涂擦。在这样的过程中，化妆品的流动性将发生改变，并在从头到尾的化妆品使用中，由于皮肤吸收油及水分蒸发等原因，皮肤的感觉也将发生改变。因此，物理性质是很复杂的。用硬、柔软、水嫩、伸展、折皱、发粘、粗糙、粉似的等词汇来表现对化妆品的评价。这些表现是从开始使用化妆品到使用完结时的感觉上的反应。
按照使用化妆品的使用阶段的流动特性、使用感等进行分类。首先将外观、接触要使用的化妆品时的特性、从容器内取出化妆品的容易度等来作为使用前的评价。接触化妆品时的特性用拇指或食指按压化妆品的力量来进行评价。此外，从容器内取出化妆品的容易度根据从容器内取出化妆品时的流动阻力及变形状态等来进行评价。其次，用使用部位的粘着性、样品在皮肤上的伸展难易性及通过皮肤的渗透性的感觉等作为使用过程中的评价。伸展性、渗透性也分别进行感觉上的评价。更具体地，在涂抹了化妆品或一定间隔地涂抹后，根据触觉和视觉等，通过使用部位的皮肤样子、剩余化妆品的擦掉难易度等来作为使用后的评价。有报道为了准确地评价化妆品的流动特性、使用感、使用效果，必须使用流变学的技术(例如，参见非专利文献1)。
根据牛顿法则流动态液体称为牛顿流体，其流动行为称为牛顿流动；另一方面，不根据牛顿法则流动态液体称为非牛顿流体，并且，其流动行为称为非牛顿流动。大部分乳剂、悬浮液、高分子溶液、半固体物质等都适用于非牛顿流体。不与施加的剪断应力成一定比例，流动较快的流动形式称为伪塑性流动；不与施加的剪断应力成一定比例、难于流动的流动形式称为膨胀流动(dialantancy)(例如，参见非专利文献2)。
最近，研发出上述流动形式之一的具有膨胀性组合物作为保湿剂、按摩剂等化妆品组合成分等的适用材料，已知该组合物是由以下成分(A)、(B)及(C)组成的，也就是，含有(A)重量平均分子量10万以上的聚环氧乙烷、(B)水溶胀性粘土矿物和(C)水、的膨胀性组合物(例如，参见专利文献1)；或由以下成分(A)及(B)组成的具有相同特性的膨胀性组合物，所述组合物含有(A)油滴平均粒径0.2μm以下的含有神经酰胺类或脂肪酸的O/W型乳化物和(B)平均分子量30万以上的水溶性高分子(例如，参见专利文献2)。
另一方面，在彩妆类化妆品上尝试了多种流变学方面的改善策略。例如，油性固体化妆品组合了较多的油分，因此显得油腻和黏黏的，为了克服较差的伸展性、蔓延性以及较强的油膜感，开发了使用硅油的化妆品。由于硅油的优良特性，因此采用了多种硅油，特别是作为化妆品中有用的油性成分广泛使用。这是因为硅油具有低粘性、光滑、伸展好、清爽的接触感觉、此外富有润滑性和疏水性、且无味无臭的良好的特征和条件。这种硅油以分子量及粘度不同的链状二甲基聚硅氧烷为代表，可列举出环状八甲基环四硅氧烷、以及甲苯基聚硅氧烷。
为了改良上述硅油，获得具有光滑而且清爽感触的使用感、使用性、并且长期稳定性良好的安全性化妆品，已经出现一种聚硅氧烷凝胶组合物，虽不溶于苯，但可含有与本身重量相同重量以上的苯、由R2SiO单元及RSiO1.5单元比例为1-30∶1的具有三维交联结构的硅聚合物，与50cs以下低粘度的硅油组成，并且所述硅聚合物及低粘度硅油的重量比例为5∶95-30∶70(例如参见专利文献3)；另外还出现了一种油性固体化妆品的组合物，其不会导致化妆膜起皱或熔融填充性低下、可以除去化妆膜光泽、具有衬垫质感；其适用于油性固体化妆品、由成分(A)-(D)组成，也就是含有(A)部分交联型有机聚硅氧烷聚合物0.5-10重量％、(B)低粘度硅油5-50重量％、(C)球状粉体10-50重量％、(D)固体油和/或半固体油1-50重量％(例如，参见专利文献4)。
此外，在粉体化妆品方面，为了具有良好的密合性及光滑的铺展性、提高化状膜的均一性及经时稳定性，已知含有以下成分(a)-(e)的，也就是含有成分(a)部分交联型有机聚硅氧烷、成分(b)液状硅油、成分(c)除了成分(b)以外的液状油及成分(e)粉体的粉体化妆品(例如，参见专利文献5)；另外还已知含有至少一种粒子相及至少一种脂肪相的粉体化妆品组合物，其进一步地含有具有表面活性特性的硅弹性体型中的至少一种的凝胶化剂，且在该组合物中粒子相以相对于组合物总量来说是50-98重量％(例如，参见专利文献6)。
此外，已知由交联有机聚硅氧烷聚合物及硅油之外的油剂组成的组合物，以及含有该组合物的化妆品(例如，参见专利文献7)。
专利文献1：特开平10-182403号专利公报
专利文献2：特开2002-317124号专利公报
专利文献3：特公平8-6035号专利公报
专利文献4：特开2000-281532号专利公报
专利文献5：特开2001-278730号专利公报
专利文献6：特开2003-55150号专利公报
专利文献7：WO2003/024413号再公开专利公报
非专利文献1：日本化妆品技术者会编《化妆品事典》、平成16年9月25日第二刷，丸善株式会社发行，p215-216页
非专利文献2：日本化妆品技术者会编《化妆品事典》、平成16年9月25日第二刷，丸善株式会社发行，p217页
发明内容
以往的油性型及粉末固体型眼影等彩妆类化妆品均是填充在皿状容器中、将其装在紧凑容器中具有携带性，并且可在一个紧凑容器中装入多种颜色，从而成为具有便利性的产品。然而，其尚欠缺清爽的触感及柔软感的使用感，也欠缺弹性。另一方面，水系凝胶状型化妆品具有清爽的触感及柔软感但难以填充入皿状容器中，因此不能在一个紧凑容器中装入多种颜色，不方便。本发明要解决的问题是提供一种不发粘的、具有清爽的使用感和有弹性的触感及柔软感、良好的耐冲击性，且该可填充入金属制或树脂制的皿状容器中，将这些皿状容器装在紧凑容器中使用，能在一个紧凑容器中装入多种颜色，具有简便性和便利性的彩装化妆品。
本发明人注意了眼影等彩妆类化妆品向来使用的多种有机聚硅氧烷聚合物的特性，锐意研究物性不同的多种有机聚硅氧烷聚合物的组合获得以下结果，发现将含有特定的2种有机聚硅氧烷聚合物与选自烃油和/或酯油的一种或两种以上的液状油、硅油、粉体的组分与溶剂(例如，作为低聚合的直链二甲基聚硅氧烷的二甲硅油等硅油)添加在一起获得膏状物质，在吸收溶剂的同时将其压缩成型，将得到不发粘的、具有清爽的使用感及柔软的触感、良好的弹性和耐冲击性、且可填充在容器中的彩妆类化妆品，并且确认其在使用时还具有简便性和便利性，由此完成本发明。
换句话说，本发明涉及：(1)一种彩妆类化妆品，其特征在于该化妆品含有：由含有长链烷基的部分交联型有机聚硅氧烷聚合物组成的成分(A)、由除了成分(A)之外的部分交联型有机聚硅氧烷聚合物组成的成分(B)、由硅油组成的成分(C)、由选自烃油和/或酯油的一种或两种以上的液状油组成的成分(D)以及由粉体组成的成分(E)；(2)如上述(1)所述的彩妆类化妆品，其特征在于该化妆品是油性的；(3)如上述(1)或(2)所述的彩妆类化妆品，其特征在于成分(A)是(乙烯基二甲硅油/十二烷基二甲硅油)交联聚合物(crosspolymer)；(4)如上述(1)-(3)任一项所述的彩妆类化妆品，其特征在于成分(B)是(二甲硅油/乙烯基二甲硅油)交联聚合物；(5)如上述(1)-(4)任一项所述的彩妆类化妆品，其特征在于成分(C)是二甲硅油；(6)如上述(1)-(5)任一项所述的彩妆类化妆品，其特征在于含有30-70质量％的成分(C)；(7)如上述(1)-(6)任一项所述的彩妆类化妆品，其特征在于含有0.5-10质量％的成分(D)；(8)如上述(1)-(7)任一项所述的彩妆类化妆品，其特征在于成分(E)含有有光泽的板状粉体；(9)如上述(1)-(8)任一项所述的彩妆类化妆品，其特征在于成分(E)含有球状粉体；(10)如上述(1)-(9)任一项所述的彩妆类化妆品，其特征在于填充入皿状容器中并压缩成型，该皿状容器的至少一个被装入紧凑容器中；(11)如上述(1)-(10)任一项所述的彩妆类化妆品，其特征在于压缩成型的化妆品的插针负载值为20-120gf；(12)如上述(1)-(11)任一项所述的彩妆类化妆品，其特征在于对压缩成型的化妆品通过质构分析仪的TPA(texture profile analysis)测定的弹性值(L2/L1)是0.48-0.99；(13)如上述(1)-(12)任一项所述的彩妆类化妆品，其特征在于所述彩妆类化妆品是眼影。
此外本发明还涉及(14)彩妆类化妆品的制备方法，其特征在于将含有由含有长链烷基的部分交联型有机聚硅氧烷聚合物组成的成分(A)、由除了成分(A)之外的部分交联型有机聚硅氧烷聚合物组成的成分(B)、由硅油组成的成分(C)、由选自烃油和/或酯油的一种或两种以上的液状油组成的成分(D)以及由粉体组成的成分(E)的组合物分散在硅油等溶剂中，分散后填充入皿状容器中，在吸收上述溶剂的同时压缩成型。
附图说明
[图1]是表示本发明产品(实施例1)的动态粘弹性的测定结果的图。横轴表示变形(％)，纵轴G’表示储能弹性模量(弹性项)，G”表示损失弹性模量(粘性项)。
[图2]是表示通过质构分析仪得到的本发明产品(实施例1)的TPA测定结果。
具体实施方式
本发明的彩妆类化妆品只要是含有：由含有长链烷基的部分交联型有机聚硅氧烷聚合物组成的成分(A)、由除了成分(A)之外的、即不含长链烷基的部分交联型有机聚硅氧烷聚合物组成的成分(B)、由硅油组成的成分(C)、由选自烃油和/或酯油的一种或两种以上的液状油组成的成分(D)以及由粉体组成的成分(E)即可，没有其它的特别限制，但更优选含有上述各成分的组合物是油性的。进一步，优选在含有上述各成分的组合物中添加硅油等溶剂，在吸收溶剂的同时将其压缩成型；进一步优选在压缩成型后填充入皿状容器中的制品。该皿状容器可装入紧凑容器中，能在一个紧凑容器中装入多个使其成套装。此处皿状容器的含义是指能够收容在紧凑容器中程度的薄小型的金属制或合成树脂制的皿状容器。依据本发明，所述油性化妆品，是指在油性基质中分散粉体的制品，其不同于粉末固体化妆品、水系凝胶状化妆品、乳化型化妆品。上述彩妆类化妆品还可列举出眼影、粉底、遮瑕膏、打地料、腮红、口红、睫毛膏、眼线、眉笔等。
做为上述成分(A)的、含有长链烷基的部分交联型有机聚硅氧烷聚合物，只要是在部分呈现具有交联键的三维结构的聚硅氧烷类橡胶上含有长链烷基的化合物即可，没有其它特别限制；上述长链烷基可以优选碳原子数目8-30个的直链烷基。该成分(A)通过将有机氢化二烯聚硅氧烷与有机聚硅氧烷加成聚合获得；所述有机氢化二烯聚硅氧烷由选自例如SiO2单元、HSiO1.5单元、RSiO1.5单元、RHSiO单元、R2SiO单元、R3SiO0.5单元及R2HSiO0.5单元(其中，R是除去脂肪族不饱和基的、取代或无取代的碳原子数1-30的一价烃基)的至少一种结构单元构成，分子中含有在硅原子上结合的氢原子数平均在1.5个以上；所述有机聚硅氧烷由选自SiO2单元、(CH2＝CH)SiO1.5单元、RSiO1.5单元、R(CH2＝CH)SiO单元、R2SiO单元、R3SiO0.5单元及R2(CH2CH)SiO0.5单元(其中，R是除去脂肪族不饱和基的、取代或非取代的碳原子数1-30的一价烃基)的结构单元构成，同时分子中含有在硅原子上结合的乙烯基数平均在1.5个以上。
这种含有长链烷基的部分交联型有机聚硅氧烷，可列举出例如INCI名(International Nomenclature Cosmetic Ingredient labeling names)为(乙烯基二甲硅油/月桂基二甲硅油)交联聚合物。市售品可列举出在含有长链烷基的部分交联型有机聚硅氧烷聚合物中配合了烃油或酯油的聚硅氧烷凝胶。例如，可具体列举出含有65-75质量％(以下简写为“％”)矿物油的KSG-41；含有70-80％异十二烷的KSG-42；含65-75％三辛烷(三-2-乙基己酸甘油酯)的KSG-43；含有65-75％的角鲨烷的KSG-44(全部是信越化学工业(株)制)等。
根据目的，可使用一种或两种以上本发明的成分(A)，虽然其含有量没有特别地限制，但是优选在化妆品中含有0.001-15％，特别优选0.1-10％。配合了成分(A)后，可提高油类总体的相容性并使油类及粉体类均一混合。此外，可在与肌肤密合性较差的硅油中配合用与肌肤密合性较高的油剂。
作为上述成分(B)的除了成分(A)以外的部分交联型有机聚硅氧烷聚合物，只要其为呈现出具有部分交联键的三维结构的聚硅氧烷类弹性体即可，没有其它特别限制，可举出的例子是使有机聚硅氧烷交联键合得到的聚合物，部分含有三维交联结构，且其由R2SiO单元及RSiO1.5单元组成，也可以含有R3SiO0.5单元和/或SiO2单元的化合物(但是，各构成单元中的R可以是例如含有氢原子；甲基、乙基、丙基等烷基；苯基、甲苯基等芳基以及乙烯基等脂肪族不饱和基；氟代基、环氧乙烷基等基团的取代基、其可以为相同或不同的种类)，更具体地，可举出特公平8-6035号公报、特开2001-342255号公报等记载的聚合物。
这种成分(B)可举出例如INCI名(International Nomenclature CosmeticIngredient labeling names)为(二甲硅油/乙烯基二甲硅油)交联聚合物。而且，虽然成分(B)可以是匀聚物，但通常较多时与低粘度硅油混合使用。这种混合物例如可具体举出KSG-15(部分交联型甲基聚硅氧烷5份与十甲基环戊烷硅氧烷95份)、KSG-16(部分交联型甲基聚硅氧烷20-30份与甲基聚硅氧烷70-80份)、KSG-17(部分交联型甲基聚硅氧烷5份与八甲基环四甲基硅氧烷95份)、KSG-18(部分交联型甲基聚硅氧烷10-20份与甲基苯基聚硅氧烷80-90份)(全部由信越化学工业公司制)等市售品。
根据目的可使用一种或两种以上的成分(B)，虽然其含有量没有特别限制，但优选在化妆品中含有1-20％，特优选5-15％。通过配合成分(B)可保持化妆品的弹性，而且可保持在皿状容器中压缩成型的结构。
作为上述成分(C)的硅油可以是直链或环状的任意一种，例如粘度50cs以下；从不发粘和清爽的使用感(感觉)的目的出发，以及，从其作为为了使与彩妆类化妆品制造工艺相关的压缩成型前的组合物成膏状的优良溶剂出发，优选30cs以下低粘度的硅油。低粘度的硅油例如可列举出：低聚合皮的直链二甲基聚硅氧烷(二甲硅油)、甲苯基聚硅氧烷、二甲基聚硅氧烷·甲苯基硅氧烷共聚物、以及环状的八甲基环四甲基硅氧烷、十甲基环戊烷硅氧烷，还可举出具体的例子，如INCI名为二甲硅油的物质(シリコン KF-96(6CS)、シリコンKF-96(10CS)、シリコンKF-96(20CS)：信越化学工业公司制)，根据目的，将一种或两种以上组合使用。此外，关于硅油的配合形态，可举出与作为成分(B)的、除了成分(A)之外的部分交联型有机聚硅氧烷聚合物相配合，以KSG-16等的凝胶状聚硅氧烷使用的形态，以及单独使用的形态，优选并用这些形态。此外，作为溶剂的硅油，优选的例子作为低粘度的硅油的低聚合度的直链二甲基聚硅氧烷，更具体地是按顺序优选シリコンKF-96(6CS)、シリコンKF-96(10CS)、シリコンKF-96(20CS)。
成分(C)硅油在化妆品中的含量是30-70％，优选40-60％配合。只要配合30％以上，可保证使用中的特别清爽感、此外只要配合70％以下，可特别地使化妆持久，即使在皿状容器中压缩成型，也可以降低成型物耐冲击性受损的可能性。予以说明，在彩妆类化妆品的制备过程中，向压缩成型前的组合物中加入作为溶剂的二甲硅油等的硅油虽然可在压缩成型时被吸收，但是有时添加的成分(C)硅油的一部分也将被吸收。
作为成分(D)的选自烃油和/或酯油的液状油，无论是来自动物油、植物油、合成油等，优选25℃下的液状物质，可举出例如液体石蜡、重质液体异链烷烃、角鲨烷、聚丁烯、聚异丁烯等作为烃油，此外，可举出例如三2-乙基己酸甘油酯、对甲氧基桂皮酸2-乙基己酯、异辛酸十六烷基酯、十四烷酸异丙酯、棕榈酸异丙酯、十四烷酸辛基月桂酯、三辛酸甘油酯、二异硬脂酸聚甘油酯、异硬脂酸二甘油酯、苹果酸二异硬脂酯、二辛酸新戊二醇酯、霍霍巴油等作为酯油，还可使用这些的一种或两种以上。
通过配合成分(D)，可在使用中赋予肌肤亲合性及密合感等。虽然成分(D)的含量没有特别限制，从更多地吸收填装时所用的硅油等溶剂方面出发，优选在化妆品中含有0.5-10％，更优选含有1-8％。此外，成分(D)的配合形态，可举出例如像KSG-4 3那样，与成分(A)含有长链烷基的部分交联型有机聚硅氧烷聚合物配合使用的形态或单独使用的形态。
作为成分(E)的粉体，只要是化妆品中常用的粉体，没有特别的限制，但优选在化妆品中含有30-70％。此外，成分(E)粉体优选是含有板状粉体的物质，并且，更优选是含有有珍珠光泽等光泽的板状粉体。进一步地，更优选含有球状粉体。化状品中可配合10-50％的板状粉体，优选20-40％，更优选30％的程度。并且，优选粉体中配合30-98％比例的有光泽的板状粉体，如果在这个范围内将出现较少的粗糙堆积物，并且涂抹在皮肤上时有较好的感觉。另外，化妆品中可以配合1-10％的球状粉体，优选1-5％，粉体中优选配合0.01％-30％的球状粉体，更优选0.5％-10％。球状粉体具有粉状感，伸展和延伸性良好，可获得更好的不发粘的清爽的使用感。此外，由于使***均一化后具有将化妆品涂抹于手指、小片、海绵、毛刷等涂抹工具上难于取下的作用，优选通过与相反作用的体系不均化、良好地崩解的粉体并用，来调整手指上取下化妆品的难易。通过球状粉体与良好地崩解的粉体在0.001∶99.99-90∶10的范围内适当组合配合，容易地调整化妆品从手指的取出。球状粉体的平均粒径(激光衍射法)优选是0.1-80μm，更优选是0.5-50μm。
此外，成分(E)的材质，可以列举是用氧化钛、黑色氧化钛、深蓝、群青、绛矾、氧化铁黄、氧化铁黑、氧化锌、氧化铝、二氧化硅、氧化镁、氧化锆、碳酸镁、碳酸钙、氧化铬、氢氧化铬、炭黑、硅酸铝、硅酸镁、硅酸铝镁、云母、合成云母、绢云母、滑石粉、高岭土、碳化硅、硫酸钡、氮化硅等无机粉体类；尼龙、聚甲基丙烯酸甲酯盐、聚丙烯酸烷基酯、有机聚硅氧烷弹性体、聚甲基倍半硅氧烷、交联型聚硅氧烷·网状聚硅氧烷嵌段共聚物、聚苯乙烯、丙烯腈-甲基丙烯酸共聚物、偏氯乙烯-甲基丙烯共聚物、聚乙烯、氨基甲酸酯、羊毛、丝绸、结晶纤维素、N-酰基赖氨酸等有机粉体类；以及有机焦油类颜料、有机色素等的色淀颜料等色素粉体类；以及微粒子氧化钛被覆的云母钛、微粒子氧化锌被覆的云母钛、硫酸钡被覆的云母钛、含有氧化钛的二氧化硅、含有氧化锌的二氧化硅等复合粉体类；以及将这些粉体用氟类化合物、聚硅氧烷类化合物、金属肥皂、卵磷脂、氢化卵磷脂、胶原、烃、高级脂肪酸、高级醇、酯、蜡(wax)、蜡(ロウ)、表面活性剂等一种或两种以上进行表面处理的表面被覆粉体类等，还可以使用这些粉体的一种或两种以上。
例如，有光泽的板状粉体可列举出：氧化钛被覆的玻璃粉、氧化钛处理的合成金云母、云母钛、氧化钛被覆的羟基铋、氧化铁云母钛、群青被覆的云母钛、磷酸氢钙(カルミン)被覆的云母钛、羟基氯化铋、鱼鳞箔、氧化铁被覆的云母、有机颜料被覆的云母钛、铝粉、聚对苯二酸乙二醇酯·铝·环氧树脂叠层粉末、聚对苯二酸乙二醇酯·聚甲基丙烯酸甲酯叠层膜末、二氧化硅·绛矾处理的铝粉等。此外，球状粉体可举出：聚甲基丙烯酸甲酯、尼龙、聚苯乙烯、二氧化硅、聚硅氧烷树脂等。具有与球状粉体作用相反的良好地崩解的粉体，不是球状及板状的，可举出例如：橄榄球状、土豆状、金米糖果状等不规则形状的粉体，材质可举出：尼龙、聚甲基丙烯酸甲酯、甲基丙烯酸甲酯交联聚合物。
在本发明的彩妆类化妆品中，除了上述必须成分外，不损害本发明效果的范围内还可在配合通常化妆品中配合的成分，例如：油性成分、表面活性剂、水及多元醇、低级醇、水溶性高分子、保湿剂等水性成分、糖类、紫外线吸收剂、抗氧化剂、防腐剂、脂肪酶及蛋白酶等酶类、间苯二酚及硫磺等各种药物、清凉剂、色素、香料等。
上述油性成分，除了必须成分之外，可举出与化妆品领域通常使用的来自动物油、植物油、合成油等的固体油、半固体油、液体油、挥发性油等的性状无关的烃类、油脂类、蜡类、硬化油类、酯油类、脂肪酸类、高级醇类、硅油类、氟系油类、羊毛脂衍生物类、油性凝胶化剂类等。更具体地可举出：凡士林、聚乙烯蜡、乙烯丙烯共聚物、石蜡、褐煤蜡、费歇尔-特罗普歇合成蜡、地蜡、矿物地蜡等非液状烃类，木蜡、橄榄油、蓖麻油、水貂油、澳洲坚果树(マカデミアンナツツ)油等油脂类，蜂蜡、ゲイロウ、巴西棕榈蜡、小烛树蜡等蜡类，松香酸季戊四醇酯、胆甾醇脂肪酸酯、植物甾醇脂肪酸酯等非液状酯类，硬脂酸、月桂酸、肉豆蔻酸、山萮酸、异硬脂酸、油酸等脂肪酸类，硬脂醇、鲸蜡醇、月桂醇、油醇、异硬脂醇、山萮醇等高级醇类，三甲基硅氧烷硅酸、高聚合的甲苯基聚硅氧烷、聚氧亚烷基改性有机聚硅氧烷、交联聚醚改性甲基聚硅氧烷、甲基丙烯酸改性聚硅氧烷、硬脂(酰)基改性甲基聚硅氧烷、油基改性甲基聚硅氧烷、二十二烷基改性甲基聚硅氧烷、聚乙烯基吡咯烷酮改性甲基聚硅氧烷、高聚合的二甲基聚硅氧烷、聚氧亚烷基·烷基甲基聚硅氧烷·甲基聚硅氧烷共聚物、烷氧基改性聚硅氧烷、氟改性聚硅氧烷等非液状聚硅氧烷类，全氟癸烷、全氟辛烷、全氟聚醚等氟系油剂类、羊毛脂、醋酸羊毛脂、羊毛脂脂肪酸异丙酯、羊毛脂醇等羊毛脂衍生物、蔗糖脂肪酸酯、异硬脂酸铝、硬脂酸钙、12-羟基硬脂酸等油性凝胶化剂类等，也可将上述一种或两种以上进行合用。
上述表面活性剂，只要是化妆品中一般使用的表面活性剂，可使用任意一种，可举出：非离子表面活性剂、阴离子表面活性剂、阳离子表面活性剂、两性表面活性剂等。例如甘油脂肪酸酯及其亚烷基二醇加成物、聚甘油脂肪酸酯及其亚烷基二醇加成物、山梨糖醇酐脂肪酸酯及其亚烷基二醇加成物、蔗糖脂肪酸酯、聚氧乙烯硬化蓖麻油、聚氧亚烷基烷基共改性有机聚硅氧烷、聚醚改性有机聚硅氧烷、卵磷脂等，也可将上述一种或两种以上进行使用。
上述水溶性高分子可举出：愈疮胶、硫酸软骨素钠、透明质酸钠、***胶、海藻酸钠、角叉菜胶等天然类水溶性高分子；甲基纤维素、羟乙基纤维素、羟甲基纤维素等半合成类水溶性高分子；羧乙烯聚合物、烷基加成羧乙烯基聚合物、聚乙烯基醇、聚乙烯基吡咯烷酮、聚丙烯酸钠等合成类水溶性高分子。还可举出蛋白质、粘多糖、胶原、弹性素、角蛋白等，也可将上述一种或两种以上进行合用。
上述抗氧化剂可举出例如α-生育酚、抗坏血酸等；美容成分可举出例如维生素类、消炎药、生药等；防腐剂可举出例如对羟基苯甲酸酯、苯氧乙醇等，也可将上述一种或两种以上进行合用。
上述紫外线吸收剂可举出例如二苯甲酮类、PABA类、桂皮酸类、水杨酸类、4-叔-丁基-4’-甲氧基二苯甲酰甲烷、羟基苯酚(オキシベンゾン)等，也可将上述一种或两种以上进行合用。
本发明的彩妆类化妆品压缩成型后的插针负载值优选是20-120gf(克力)，更优选是20-70gf，在这个数值范围内使用时将获得完全不发粘的清爽的触感和良好的耐冲击性。例如，未到20gf的话虽然能得到完全不发粘的清爽的触感，但是可能具有较差的耐冲击性，如果超过120gf，虽然具有良好的耐冲击性，但是粉的感觉太强，使用时可能会缺乏弹力感。此外，将依据本发明的插针负载值是指将彩妆类化妆品填充入厚4mm的模具中作为试样，用株式会社レオテツク公司制的“RHEO TECH FUDOH RHEO METER”作为测定仪器，将硬度测定条件设定为使用适配器(adapter)3mmφ、进入距离1.5mm、上升速度2cm/min进行测定得到的数值。
此外，对本发明的彩妆类化妆品通过质构分析仪进行的TPA(testureprofile analysis)测定中的弹性值(L2/L1)优选是0.48-0.99，更优选是0.50-0.99，在这个数值范围内可获得富有弹性的化妆品。并且，本发明中通过质构分析仪进行的TPA测定中的弹性值(L2/L1)是指将彩妆类化妆品填充入厚4mm的模具作为试样，用英弘精机株式会公司制的“质构分析仪”作为测定机器，TPA测定条件为2mmφ的圆柱形探针、探针速度0.5mm/sec，在不完全破坏样品的情况下(非破坏区域)调整变形量为25％，用上述探针对试样加2次力度，第一次和第二次的时间差保持3sec，第一次变形导致的高度变化计为L1，第二次变形导致的高度变化计为L2，用L2/L1来求值所得数值，其表示因外力导致的变形当除去外力时的返回比例(参见种谷针一、林弘通、川端晶子共著的《食品物性用语辞典》(养贤堂))。
本发明的彩妆类化妆品的制备方法只要是将含有上述成分(A)、成分(B)、成分(C)、成分(D)和成分(E)的组合物分散在溶剂中，填充入容器后，在吸收溶剂的同时压缩成型即可，没有其它的限制，但是溶剂的添加量相对于化妆品100重量份优选为30-100重量份，更优选为40-90重量份，进一步优选为45-60重量份，因为在所述配比下可降低粘度使易于进行填充并得到均匀的化妆品。作为溶剂，只要能够将含有成分(A)-(E)的组合物分散于其中，然后填充入容器内，溶剂可被吸收即可，其可以选用硅油，烃油、酯油中的任意一种，但优选硅油，更优选是低聚合度的直链二甲基聚硅氧烷(二甲硅油)。所述制备方法更具体地是，将成分(E)的粉体均匀分散在亨舍尔搅拌机(三井三池公司制)中，另外将成分(A)含有长链烷基的部分交联型有机聚硅氧烷聚合物与成分(B)除了成分(A)之外的部分交联型有机聚硅氧烷聚合物用分散机预分散后，在该分散物中加入成分(C)硅油、成分(D)选自烃油及酯油的液状油，混合均匀，用亨舍尔搅拌机(三井三池公司制)搅拌均匀分散的上述成分(E)，同时向其中加入上述成分(A)-(D)，再加入二甲硅油等作为溶剂的硅油，使之均匀混合成浆状。将浆状的组合物填充入金属制皿状容器中，在吸收加入的溶剂的同时，在金属制皿状容器中压缩成型，可得到彩妆类化妆品。此外，该填装后的金属制皿状容器可装入小型容器中。
以下根据实施例更具体地说明本发明，但是本发明的保护范围不受这些示出的实施例的限制。
[含有长链烷基的部分交联型有机聚硅氧烷聚合物的合成]
在下式(1)表示的甲基氢化二烯聚硅氧烷160.8g以及下式(2)表示的甲基二烯基聚硅氧烷499.8g中加入2％氯铂酸乙醇溶液0.1g后，保持温度70-80℃进行2小时聚合，得到作为含有长链烷基的交联有机聚硅氧烷聚合物的硅氧烷聚合物(I)。
Figure S2006800150248D00121
[部分交联型有机聚硅氧烷聚合物的合成]
在三甲硅烷基末端封端的三甲基甲基氢化二烯聚硅氧烷(分子量2300、CH3HSiO∶(CH3)2SiO为1∶4(摩尔比))中适量加入氢氧化钾溶液(乙醇∶水＝2∶1)，加热，回流进行聚合反应，得到反应生成物。然后，用水洗涤反应生成物，除去碱性剂后，自然干燥得到作为部分交联型有机聚硅氧烷聚合物的硅氧烷聚合物(II)。
[实施例1-10及比较例1-3]
制备具有如表1所示组成成分的眼影，在“手指取出性”、“使用时的弹性”、“不发粘而清爽的使用感”、“肌肤密合性”、“耐水性、耐皮脂性等的化妆持久性”、“耐冲击性”方面，根据以下示出的评价方法及判断基准进行判定，结果合并表示于表1。
[表1]
                                                       (％)
 成分  实施例  比较例
 1  2  3  4  5  6  7  8  9  10  1  2  3
 1云母  余量  余量  余量  余量  余量  余量  余量  余量  余量  余量  余量  余量  余量
 2云母钛  30.0  30.0  30.0  30.0  30.0  30.0  30.0  30.0  30.0  30.0  30.0  30.0  30.0
 3二氧化硅*1  3.0  9.0  0.5  3.0  3.0  3.0  3.0  3.0  3.0  3.0  3.0  3.0  3.0
 4尼龙*2  1.0  1.0  0.5  1.0  1.0  1.0  1.0  1.0  1.0  1.0  1.0  1.0  1.0
 5氧化钛  1.0  1.0  1.0  1.0  1.0  1.0  1.0  1.0  1.0  1.0  1.0  1.0  1.0
 6绛矾  0.1  0.1  0.1  0.1  0.1  0.1  0.1  0.1  0.1  0.1  0.1  0.1  0.1
 7防腐剂  0.2  0.2  0.2  0.2  0.2  0.2  0.2  0.2  0.2  0.2  0.2  0.2  0.2
 8聚硅氧烷聚合物(I)*3  0.5  0.5  0.5  0.001  15.0  0.5  0.5  0.5  0.5  0.5  -  0.5  0.5
 9聚硅氧烷聚合物(II)*4  10.0  10.0  10.0  10.0  10.0  1.0  20.0  10.0  10.0  5.0  10.0  -  10.0
 10二甲硅油*5  45.0  43.0  50.0  45.0  34.0  50.0  39.0  44.0  50.0  45.0  45  45  45
 11液体石蜡*6  3.0  3.0  3.0  3.0  3.0  3.0  3.0  5.0  0.25  3.0  3  3  -
 12三2-乙基己酸甘油酯*7  2.0  2.0  2.0  2.0  2.0  2.0  2.0  5.0  0.25  2.0  2  2  -
 评价项目及判定结果
 手指取出性  ◎  ○  ○  ◎  ◎  ◎  ◎  ○  ◎  ◎  ◎  ○  △
 使用时的弹性  ◎  ◎  ◎  ○  ◎  ○  ◎  ◎  ◎  ○  ○  ×  ◎
 肌肤密合性  ◎  ◎  ◎  ◎  ◎  ◎  ◎  ◎  ○  ◎  ×  ◎  ×
 水嫩的使用感  ◎  ◎  ◎  ◎  ○  ◎  ○  ◎  ◎  ◎  ◎  ◎  ○
 耐水性、耐皮脂性等的化妆持久性  ◎  ◎  ◎  ◎  ◎  ◎  ◎  ◎  ◎  ◎  △  ×  ◎
 耐冲击性  ○  ○  ○  ○  ○  ○  ○  ○  ○  ○  △  ND  ○
 插针负载值  40  50  40  40  60  110  60  30  50  100  40  190  40
ND：无法观察(内容物从金属制器皿中脱落，无法观察到表面的折皱)
*1：ゴツトボ一ルD11-796C(粒径2-5μm的球状粉体：铃木油脂工业公司制)
*2：リルサンパウダ一S(粒径10-14μm的粉体：ATOFZNA日本公司制)
*3：上述合成例的聚硅氧烷聚合物(I)
*4：上述合成例的聚硅氧烷聚合物(II)
*5：KF-96(20CS)(信越化学工业公司制)
*6：ハイコ一ルK-500(カネダ公司制)
*7：TIO(N)(日清奥利友集团公司制)
(制备方法)
A、将成分1-7均匀分散在亨舍尔搅拌机(三井三池公司制)中。
B、将成分8、成分9预先分散后，加入成分10-12，均匀混合。
C、将A在亨舍尔搅拌机中搅拌的同时，加入B，均匀分散。
D、在100份C中加入作为溶剂的二甲硅油(KF-96(10CS))(信越化学工业公司制)50份，均匀混合。
E、将D填充入金属制器皿中，用纸吸取溶剂的同时压缩成型，得到眼影。
(评价方法1)：“手指取出性”、“使用时的弹性”、“不发粘而清爽的使用感”、“肌肤密合性”、“耐水性、耐皮脂性等的化妆持久性”
让化妆品评价专门研究小组成员20名使用上述实施例及比较例的眼影，分别根据以下评价基准在“手指取出性”、“使用时的弹性”、“不发粘而清爽的使用感”、“肌肤密合性”、“耐水性、耐皮脂性等的化妆持久性”方面各自进行7个等级的评价，对每种样品进行打分，并且根据以下判定基准对全部研究小组成员的评分的平均值进行判定。
评价基准
(评价)(内容)
6：非常好
5：好
4：稍好
3：普通
2：稍差
1：差
0：非常差
判定基准
(评分的平均值)       (判定)
5.0以上：            ◎(非常好)
3.5以上未到5.0：     ○(好)
2.0以上未到3.5：     △(普通)
未到2.0：×          (不好)
(评价方法2)：“耐冲击性”
将填充入金属制器皿的状态的上述实施例及比较例的眼影从50cm的高度上向丙烯板垂直方向自由落下，观察落下后的表面状态，对每个眼影通过以下3级的评价判定基准进行判定。
(评价判定基准)
(评价)                (判定)
完全无变化：          ○
表面有折皱：          △
大的表面上有折皱：    ×
(插针负载值的测定)
将彩妆类化妆品填充入厚度为4mm的模具作为试样，用株式会社レオテツク公司制“RHEO TECH FUDOH RHEO METER”作为测定机器，设定硬度测定条件为使用适配器3mmφ、进入距离1.5mm、上升速度2cm/min，进行插针负载值测定。
从表1中可以看出，作为本发明产品的实施例1-9的眼影是在“手指取出性”、“使用时的弹性”、“不发粘的清爽使用感”、“肌肤密合性”、“耐水性、耐皮脂性等的化妆持久性”、“耐冲击性”的全部项目均表现优秀。尤其是在“使用时的弹性”、“不发粘的使用感”方面，正如后面的图1说明的，最初弹性感非常好，但随着扩展开弹性感消失，缓慢地扩展，给人的触感变成粉感的质地。与此相反，没有配合成分(A)的聚硅氧烷聚合物(I)的比较例1具有较差的“肌肤密合性”及“耐水性、耐皮脂性等化妆持久性”等；此外，没有配合成分(B)的聚硅氧烷聚合物(II)的比较例2在“使用时的弹性”、“耐水性、耐皮脂性等化妆持久性”、“耐冲击性”各方面较差；以及没有配合成分(D)的比较例3是“肌肤密合性”较差的产品。
(动态粘弹性的测定)
本发明的彩妆类化妆品与以往的油性眼影、粉末固体眼影不同，其具有有弹性的独特触感的特征。因此，用フル一ド光谱计(レオトリツク公司制，RES-II)测定上述实施例1记载的眼影的动态粘弹性。用25-50mm的平行板或クェツト，主要用形变振幅依赖性(动态频率扫描，dynamic frequency sweep)的测定模式测定几何学特征。此处的变形，将用与平行板的间隔相等的形变振幅使平行板移动的情形计为100％，频率固定在1Hz，使形变振幅在10-8至103之间变化。在这种条件下进行测定，获得储能弹性模量(G’)、损失弹性模量(G”)。这样，图1示出了使用本发明化妆品(实施例1的眼影)进行测定得到的G’(储能弹性模量：弹性项)、G”(损失弹性模量：粘性项)的曲线。纵轴的G’表示储能弹性模量(弹性项)，G”表示损失弹性模量(粘性项)，横轴(％)表示变形。在图1中，由于增加了份额后弹性项显著降低，但是粘性项没有上升，较弹性项来说降低的稍少些，因此对应于触感的是，最初弹性感非常好，随着扩展开弹性感消失，缓慢地扩展给人的感触变为有粉感的质地。
(TPA的测定)
用英弘精机(株)公司制的质构分析仪对本发明产品(实施例1、6、10)、对照品(比较例2)及以往的产品的粉末眼影、乳剂眼影(油性眼影)进行TPA(texture profile analysis)测定。测定条件为2mmφ的圆柱形探针、探针速度0.5mm/sec、，在不完全破坏样品的情况下(非破坏区域)调整变形量为25％。TPA测定为用一定的探针对样品加2次力度，第一次和第二次的时间差保持3sec，将第一次变形导致的高度变化记为L1，将第二次变形导致的高度变化记为L2，以L2/L1做为弹性(springness)的指标。例如，弹簧的情形，由于其为完全弹性体，L1＝L2，由此导致弹性L2/L1＝1。表2示出了弹性(L2/L1)的结果。通过表2可以明确本发明产品具有弹性。此外，图2示出了用质构分析仪对本发明产品(实施例1)进行TPA测定的结果作为参考。
[表2]
L2/L1
本发明产品(实施例1) 0.923
本发明产品(实施例6) 0.487
本发明产品(实施例10) 0.489
对照品(比较例2) 0.470
以往的产品(粉末眼影) 0.467
以往的产品(乳剂眼影) 0.245
此外，以下示出了以往产品(粉末眼影)及以往产品(乳剂眼影)的处方及制备方法。
[粉末眼影的处方及制备方法]
(成分)                                          (％)
1、聚硅氧烷处理的云母*8                         20.0
2、聚硅氧烷处理的滑石粉*8                       余量
3、氧化钛被覆的云母                             30.0
4、氮化硼                                       5.0
5、群青                                         2.0
6、黄色401号                                    0.5
7、合成烃蜡                                     2.5
8、交联型聚硅氧烷·网状聚硅氧烷嵌段共聚物*9     2.0
9、防腐剂                                       0.2
10、液体石蜡                                    2.0
11、凡士林                                      1.0
12、二甲基聚硅氧烷                              3.0
13、香料                                        0.01
*8：3％的二甲基聚硅氧烷处理
*9：KSP-100(粒径5μm的球状粉体：信越化学工业公司制)
(制备方法)
A、将成分1-9均匀分散在亨舍尔搅拌机(三井三池公司制)中。
B、加热成分10-13，使之均匀分散。
C、用亨舍尔搅拌机搅拌A的同时，加入B，使之均匀分散。
D、在粉碎机中粉碎C。
E、向金属器皿中填充D，压缩成型，得到粉末眼影。
[乳剂眼影的处方及制备方法]
(成分)                                           (％)
1、石蜡                                          3.5
2、二硬脂酸乙二醇                                2.0
3、巴西棕榈蜡                                    1.5
4、甲基聚硅氧烷                                  15.0
5、角鲨烷                                        7.0
6、三2-乙基己酸甘油酯                            20.0
7、交联型聚硅氧烷·网状聚硅氧烷嵌段共聚物*9      5.0
8、聚硅氧烷处理的云母钛*8                        35.0
9、聚硅氧烷处理的合金云母*8                      余量
10、氧化铁                                       0.4
11、群青                                         0.1
12、石蜡                                         0.5
13、角鲨烷                                       2.5
14、香料                                         0.01
(制备方法)
A、将12-14加热溶解均匀。
B、向A中加入9-11，在滚筒中分散。
C、将1-6加热溶解均匀。
D、将B加入C中，加热溶解均匀。
E、将7、8加入D中，加热溶解均匀。
F、将E加热到80℃，填充入金属器皿，冷却后，得到乳剂眼影。
[实施例11：眼影]
(成分)                            (％)
1、云母                            余量
2、氧化钛被覆的云母(有光泽粉体)    5.0
3、二氧化硅*10                                              3.0
4、尼龙*11                                                  1.0
5、云母钛(有光泽粉体)                                       20.0
6、氧化铁黄                                                 0.1
7、氧化铁黑                                                 0.1
8、绛矾                                                     0.1
9、群青                                                     0.1
10、聚硅氧烷处理的氧化钛                                    1.0
11、对羟基苯甲酸甲基                                        0.1
12、二甲硅油*12                                             20.0
13、含有长链烷基的部分交联型有机聚硅氧烷聚合物的混合物*1    34.0
14、部分交联型有机聚硅氧烷聚合物的混合物*14                 35.0
15、重质液体异链烷烃*15                                     5.0
16、三2-乙基己酸甘油酯                                      1.0
17、香料                                                    适量
(处方外)
18、溶剂：二甲硅油*12                                     40份
*10：ゴツトボ一ルE2-824C(粒径：0.9-1.4μm的球状粉体：铃木油脂工业公司制)
*11：リルサンパウダ一L(粒径：18-25μm的异形粉体：ATOFINA 日本公司制)
*12：KF-96(10CS)(信越化学工业公司制)
*13：KSG-43(信越化学工业公司制)
*14：KSG-16(信越化学工业公司制)
*15：パ一ルリ一ム18(日本油脂公司制)
(制备方法)
A、将成分1-11均匀分散在亨舍尔搅拌机(三井三池公司制)中。
B、将成分12-17均匀混合。
C、在亨舍尔搅拌机中搅拌A的同时，加入B，使之均匀分散。
D、在100份C中加入成分18，使之均匀混合。
E、将D填充入金属制器皿中，用纸吸收溶剂的同时压缩成型，得到眼影。
本发明的眼影在“手指取出性”、“使用时的弹性”、“不发粘的清爽使用感”、“肌肤密合性”、“耐水性、耐皮脂性等的化妆持久性”、“耐冲击性”等全部方面均表现优异。
[实施例12：眼影]
(成分)                                                     (％)
1、云母                                                    余量
2、滑石粉                                                  7.0
3、交联型聚硅氧烷·网状聚硅氧烷嵌段共聚物*9                3.0
4、尼龙*2                                                  2.0
5、云母钛(有光泽粉体)                                      20.0
6、聚硅氧烷处理的氧化铁黄                                  0.1
7、聚硅氧烷处理的氧化铁黑                                  0.1
8、聚硅氧烷处理的氧化钛                                    0.1
9、对羟基苯甲酸甲基                                        0.1
10、甲苯基聚硅氧烷*16                                      20.0
11、含有长链烷基的部分交联型有机聚硅氧烷聚合物的混合物*13  4.0
12、部分交联型有机聚硅氧烷聚合物的混合物*14                35.0
13、聚丁烯                                                 5.0
14、三2-乙基己酸甘油酯                                     1.5
15、香料                                                   适量
(处方外)
16、溶剂：二甲硅油*12                            60份
*16：KF-56(信越化学工业公司制)
(制备方法)
A、将成分1-9均匀分散在亨舍尔搅拌机(三井三池公司制)中。
B、将成分10-15均匀混合。
C、在亨舍尔搅拌机中搅拌A的同时，加入B，使之均匀分散。
D、将成分16加入100份C中，使之均匀混合。
E、将D填充入金属制器皿中，用纸吸收溶剂的同时压缩成型，得到眼影。
本发明的眼影在“手指(小片)取出性”、“使用时的弹性”、“不发粘的清爽使用感”、“肌肤密合性”、“耐水性、耐皮脂性等的化妆持久性”、“耐冲击性”等全部1面均表现优异。
[实施例13：粉底]
(成分)                                                      (％)
1、云母                                                     余量
2、滑石粉                                                   5.0
3、交联型聚硅氧烷·网状聚硅氧烷嵌段共聚物*9                 3.0
4、聚苯乙烯*17                                              2.0
5、云母钛(有光泽粉体)                                       20.0
6、氟化合物处理的氧化铁黄                                   0.1
7、氟化合物处理的氧化铁黑                                   0.1
8、氟化合物处理的绛矾                                       0.1
9、氟化合物处理的微粒氧化钛                                 2.0
10、二甲硅油*5                                              25.0
11、含有长链烷基的部分交联型有机聚硅氧烷聚合物的混合物*13   5.0
12、部分交联的有机聚硅氧烷聚合物的混合物*14                 30.0
13、对甲氧基肉桂酸2-乙基己酯                                4.0
14、三2-乙基己酸甘油酯                                      1.5
15、香料                                                    适量
(处方外)
16、溶剂：二甲硅油*18                                   45份
*17：フアインパ一ル3000SP-Q(粒径5-20μm的球状粉体：松浦公司制)
*18：KF-96(6CS)(信越化学工业公司制)
(制备方法)
A、将成分1-9均匀分散在亨舍尔搅拌机(三井三池公司制)中。
B、将成分10-15均匀混合。
C、在亨舍尔搅拌机中搅拌A的同时，加入B，使之均匀分散。
D、将成分16加入100份C中，使之均匀混合。
E、将D填充入金属制器皿中，用纸吸收溶剂的同时压缩成型，得到粉底。
本发明的粉底在“手指(海绵)取出性”、“使用时的弹性”、“不发粘的清爽使用感”、“肌肤密合性”、“耐水性、耐皮脂性等的化妆持久性”、“耐冲击性”等全部方面均表现优异。
[实施例14：腮红(face color)]
(成分)                                                        (％)
1、云母                                                       余量
2、滑石粉                                                     5.0
3、尼龙*19                                                    1.0
4、甲基丙烯酸甲基交联聚合物*20                                10.0
5、云母钛(有光泽粉体)                                         10.0
6、氟化合物处理的红色226                                      0.1
7、氟化合物处理的氧化铁黑                                     0.1
8、氟化合物处理的微粒氧化钛                                   2.0
9、二甲硅油*5                                                 30.0
10、含有长链烷基的部分交联型有机聚硅氧烷聚合物的混合物*13     2.0
11、部分交联型有机聚硅氧烷聚合物的混合物*14                   30.0
12、液体石蜡                                                  2.0
13、聚丁烯                                                    2.0
14、三2-乙基己酸甘油酯                                        1.5
15、香料                                                      适量
(处方外)
16、溶剂：二甲硅油*18                                    55份
*19：东丽制尼龙粉末SP-500(粒径1-23μm的球状粉体：东丽公司制)
*20：ガンツパ一ルGMI-0804(粒径4-15μm的异形粉体：ガンツ化成公司制)
(制备方法)
A、将成分1-8均匀分散在亨舍尔搅拌机(三井三池公司制)中。
B、使成分9-15均匀混合。
C、在亨舍尔搅拌机中搅拌A的同时，加入B，使之均匀分散。
D、将成分16加入100份C中，使之均匀混合。
E、将D填充入金属制器皿中，用纸吸收溶剂的同时压缩成型，得到腮红。
本发明的腮红在“手指取出性”、“使用时的弹性”、“不发粘的清爽使用感”、“肌肤密合性”、“耐水性、耐皮脂性等的化妆持久性”、“耐冲击性”等全部方面均表现优异。
[实施例15：唇蜜]
(成分)                                                        (％)
1、氧化钛被覆的玻璃粉(有光泽粉体)                             20.0
2、二氧化硅*10                                                2.0
3、聚苯乙烯*17                                                2.0
4、二甲硅油(20cs)                                             15.0
5、含有长链烷基的部分交联型有机聚硅氧烷聚合物的混合物*13      10.0
6、部分交联型有机聚硅氧烷聚合物的混合物*14                    35.0
7、重质液体异链烷烃*15                                        4.0
8、苹果酸二异硬脂基酯                                         余量
9、三2-乙基己酸甘油酯                                         1.5
10、1，3-丁二醇                                               1.0
11、美容成分(母菊提取物)                                      0.1
12、精制水                                                    3.0
13、香料                                                      适量
(处方外)
14、溶剂：二甲硅油(6cs)                    35份
(制备方法)
A、将成分1-3均匀分散在亨舍尔搅拌机(三井三池公司制)中。
B、使成分4-13均匀混合。
C、在亨舍尔搅拌机中搅拌A的同时，加入B，使之均匀分散。
D、将成分14加入100份C中，使之均匀混合。
E、将D填充入金属制器皿中，用纸吸收溶剂的同时压缩成型，得到唇蜜。
本发明的唇蜜在“手指(刷子)取出性”、“使用时的弹性”、“不发粘的清爽使用感”、“肌肤密合性”、“耐水性、耐皮脂性等的化妆持久性”、“耐冲击性”等全部方面均表现优异。
产业实用性
本发明的彩妆类化妆品在具有不发粘的清爽使用感及柔软的触感和弹性的同时，还具有良好的耐水性、耐皮脂性、耐冲击性，此外，可在金属制器皿或合成树脂制器皿中压缩成型，然后装入小型容器成套，能使多种颜色合并使用，具有简便性和便利性。

Claims (14)

1.彩妆类化妆品，其特征在于，含有：由含有长链烷基的部分交联型有机聚硅氧烷聚合物组成的成分(A)、由除了成分(A)之外的部分交联型有机聚硅氧烷聚合物组成的成分(B)、由硅油组成的成分(C)、由选自烃油和/或酯油的一种或两种以上的液状油组成的成分(D)、以及由粉体组成的成分(E)。
2.如权利要求1所述的彩妆类化妆品，其特征在于，彩妆类化妆品是油性的。
3.如权利要求1或2所述的彩妆类化妆品，其特征在于，成分(A)是(乙烯基二甲硅油/十二烷基二甲硅油)交联聚合物。
4.如权利要求1-3任一项所述的彩妆类化妆品，其特征在于，成分(B)是(二甲硅油/乙烯基二甲硅油)交联聚合物。
5.如权利要求1-4任一项所述的彩妆类化妆品，其特征在于，成分(C)是二甲硅油。
6.如权利要求1-5任一项所述的彩妆类化妆品，其特征在于，含有30-70质量％的成分(C)。
7.如权利要求1-6任一项所述的彩妆类化妆品，其特征在于，含有0.5-10质量％的成分(D)。
8.如权利要求1-7任一项所述的彩妆类化妆品，其特征在于，成分(E)含有具有光泽性的板状粉体。
9.如权利要求1-8任一项所述的彩妆类化妆品，其特征在于，成分(E)含有球状粉体。
10.如权利要求1-9任一项所述的彩妆类化妆品，其特征在于，填充入皿状容器中并压缩成型，该皿状容器的至少一个装在紧凑容器中。
11.如权利要求1-10任一项所述的彩妆类化妆品，其特征在于，压缩成型的彩妆类化妆品的插针负载值为20-120gf。
12.如权利要求1-11任一项所述的彩妆类化妆品，其特征在于，对压缩成型的彩妆类化妆品通过质构分析仪的TPA(texture profile analysis)测定的弹性值(L2/L1)是0.48-0.99。
13.如权利要求1-12任一项所述的彩妆类化妆品，其特征在于，所述化妆品是眼影。
14.彩妆类化妆品的制备方法，其特征在于，将含有由含有长链烷基的部分交联型有机聚硅氧烷聚合物组成的成分(A)、由除了成分(A)之外的部分交联型有机聚硅氧烷聚合物组成的成分(B)、由硅油组成的成分(C)、由选自烃油和/或酯油的一种或两种以上的液状油组成的成分(D)、以及由粉体组成的成分(E)的组合物分散在溶剂中，分散后填充入皿状容器中，在吸收上述溶剂的同时压缩成型。
CN2006800150248A 2005-05-02 2006-04-24 彩妆类化妆品 Active CN101208073B (zh)