CN101113234A - 一种pc/abs合金废料回收配方 - Google Patents
一种pc/abs合金废料回收配方 Download PDFInfo
- Publication number
- CN101113234A CN101113234A CNA200610036824XA CN200610036824A CN101113234A CN 101113234 A CN101113234 A CN 101113234A CN A200610036824X A CNA200610036824X A CN A200610036824XA CN 200610036824 A CN200610036824 A CN 200610036824A CN 101113234 A CN101113234 A CN 101113234A
- Authority
- CN
- China
- Prior art keywords
- abs
- waste
- prescription
- impact
- reclaims
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种PC/ABS合金废料回收配方,其所包括组分以重量份数表示为:PC/ABS废旧料40~50份、高抗冲PC/ABS份、水口料35~55份、增韧剂1~3份、溴系阻燃剂3~7份、锑系阻燃剂1~3份、丙烯酸类抗冲改性剂2~7份、抗氧剂0.2~0.5份。本发明的PC/ABS合金废料回收配方,其采用高抗冲PC/ABS水口料与普通PC/ABS废旧料共混,同时添加各种助剂,能使PC/ABS合金废料的各项性能均可以达到PC/ABS原料水准,因此,其在降低生产成本的同时避免了废料造成的环境污染,具有很好的社会效益和经济效益。
Description
技术领域
本发明涉及高分子材料技朮领域,特别是涉及一种高分子材料回收配方。
背景技术
PC/ABS合金是60年代中期发展起来的一种综合性能较好的工程塑料,它既具有PC的耐热性、机械强度和尺寸稳定性;又具有ABS树脂的易加工性和价廉等优点;其综合性能好、性价比合理,可在汽车工业、家用电器等领域中广泛应用。由于PC/ABS合金广泛应用于电子电器产品中,该类产品报废以后产生的废旧料数量十分巨大,为了减少环境压力和能源消耗,提高资源的应用效率,因此传统的将废旧料焚烧和掩埋的方法就不够经济实用,因而开发废旧料料的再生显得十分关键;高抗冲PC/ABS合金在生产过程中由于注塑机浇道的原因和产品成型不良会产生一些水口料,这些水口料如不加以利用,则显得相当浪费并导致污染环境。
发明内容
鉴于以上问题,本发明的目的在于提供一种PC/ABS合金废料回收配方。
为达到上述目的,本发明采用高抗冲PC/ABS水口料与普通PC/ABS废旧料共混,并在共混过程中添加增韧剂、阻燃剂、抗老化剂等助剂的方法,对PC/ABS合金废料进行环保回收利用,使PC/ABS合金废料的各项性能均可以达到PC/ABS原料水准。
本发明提供的PC/ABS合金废料的回收配方,其所包括组分以重量份数表示为:
PC/ABS废旧料 40~50
高抗冲PC/ABS水口料 35~55
增韧剂 1~3
溴系阻燃剂 3~7
锑系阻燃剂 1~3
丙烯酸类抗冲改性剂 2~7
抗氧剂 0.2~0.5
其中,所述增韧剂可为ACR(基丙烯酸酯-丙烯酸酯共聚物)、MBS(甲基丙烯酸甲酯-丁二烯-苯乙烯共聚物)、MMB(甲基丙烯酸甲酯-丁二烯共聚物)或ASA(丙烯腈-苯乙烯-丙烯酸酯共聚物)等。
所述的溴系阻燃剂可为溴化聚碳酸酯、十溴二苯醚、八溴醚、四溴双酚A、四溴双酚A聚碳酸酯齐聚物、六溴环十二烷或环保型溴系阻燃剂十溴二苯乙烷等。
所述的锑系阻燃剂可为三氧化二锑、五氧化二锑或锑酸钠等。
所述的抗氧剂可为抗氧剂1010、抗氧剂2921等。
优选的,本发明提供的PC/ABS合金废料回收配方,其组分以重量份数表示为:
PC/ABS废旧料 48.8
高抗冲PC/ABS水口料 39
MBS 2
十溴二苯乙烷 3
三氧化二锑 1
丙烯酸类抗冲改性剂 6
抗氧剂1010 0.2
优选的,本发明提供的PC/ABS合金废料回收配方,其组分以重量份数表示为:
PC/ABS废旧料 43.7
高抗冲PC/ABS水口料 43.7
MBS 2
十溴二苯乙烷 4
三氧化二锑 1.3
丙烯酸类抗冲改性剂 4
抗氧剂1010 0.3
优选的,本发明提供的PC/ABS合金废料回收配方,其组分以重量份数表示为:
PC/ABS废旧料 40
高抗冲PC/ABS水口料 52
MBS 1
十溴二苯乙烷 3
三氧化二锑 1
丙烯酸类抗冲改性剂 2.6
抗氧剂1010 0.4
本发明的PC/ABS合金废料回收配方,其采用高抗冲PC/ABS水口料与普通PC/ABS废旧料共混,同时添加各种助剂,能使PC/ABS合金废料的各项性能均可以达到PC/ABS原料水准,因此,其在降低生产成本的同时避免了废料造成的环境污染,具有很好的社会效益和经济效益。
具体实施方式
实施例1
按比例称取下列材料:
PC/ABS废旧料 48.8
高抗冲PC/ABS水口料 39
MBS 2
十溴二苯乙烷 3
三氧化二锑 1
丙烯酸类抗冲改性剂 6
抗氧剂1010 0.2
再将该共混料通过挤出机中混炼造粒,所得混炼造粒经注射成型制成成品,最后按国家标准GB13525/T-92测试所得成品的机械性能及按美国电工协会UL94标准测试其阻燃性能,并按照国家标准GB/T3682-2000测量产品的熔体质量流动速率(MFR),其结果与改善前PC/ABS废旧料及PC/ABS原料相关性能对比如表1所示。
表1:实施例1所得产品与PC/ABS废旧料和PC/ABS原料之间性能对比
项目 | PC/ABS废旧料 | 原料 | 产品 |
冲击强度(kJ/M2) | 25 | 50 | 50.23 |
拉伸强度(MPa) | 62 | 64 | 63.15 |
MFR(g/10min) | 28 | 20 | 26 |
阻燃性(UL94) | HB | V-0 | V-0 |
实施例2
按比例称取下列材料:
PC/ABS废旧料 43.7
高抗冲PC/ABS水口料 43.7
MBS 2
十溴二苯乙烷 4
三氧化二锑 1.3
丙烯酸类抗冲改性剂 4
抗氧剂1010 0.3
再将该共混料通过挤出机中混炼造粒,所得混炼造粒经注射成型制成成品,最后按国家标准GB13525/T-92测试所得成品的机械性能及按美国电工协会UL94标准测试其阻燃性能,并按照国家标准GB/T3682-2000测量产品的熔体质量流动速率(MFR),其结果与改善前PC/ABS废旧料及PC/ABS原料相关性能对比如表2所示。
表2:实施例2所得产品与PC/ABS废旧料和PC/ABS原料之间性能对比
项目 | PC/ABS废旧料 | 原料 | 产品 |
冲击强度(kJ/M2) | 25 | 50 | 57.05 |
拉伸强度(MPa) | 62 | 64 | 61.56 |
MFR(g/10min) | 28 | 20 | 25.7 |
阻燃性(UL94) | HB | V-0 | V-0 |
实施例3
按比例称取下列材料:
PC/ABS废旧料 40
高抗冲PC/ABS水口料 52
MBS 1
十溴二苯乙烷 3
三氧化二锑 1
丙烯酸类抗冲改性剂 2.6
抗氧剂1010 0.4
再将该共混料通过挤出机中混炼造粒,所得混炼造粒经注射成型制成成品,最后按国家标准GB13525/T-92测试所得成品的机械性能及按美国电工协会UL94标准测试其阻燃性能,并按照国家标准GB/T3682-2000测量产品的熔体质量流动速率(MFR),其结果与改善前PC/ABS废旧料及PC/ABS原料相关性能对比如表3所示。
表3:实施例3所得产品与PC/ABS废旧料和PC/ABS原料之间性能对比
项目 | PC/ABS废旧料 | 原料 | 产品 |
冲击强度(kJ/M2) | 25 | 50 | 60.5 |
拉伸强度(MPa) | 62 | 64 | 64.31 |
MFR(g/10min) | 28 | 20 | 27 |
阻燃性(UL94) | HB | V-0 | V-0 |
以上所述,仅是本发明较佳可行的实施例而已,不能因此即局限本发明的权利范围,对熟悉本领域的普通技术人员来说,举凡运用本发明的技术方案和技术构思做出其它各种相应的改变和变形,而所有这些改变和变形都应属在本发明权利要求的保护范围之内。
Claims (8)
1.一种PC/ABS合金废料回收配方,其特征在于,所包括组分以重量份数表示为:
PC/ABS废旧料 40~50
高抗冲PC/ABS水口料 35~55
增韧剂 1~3
溴系阻燃剂 3~7
锑系阻燃剂 1~3
丙烯酸类抗冲改性剂 2~7
抗氧剂 0.2~0.5
2.根据权利要求1所述的PC/ABS合金废料回收配方,其特征在于,所述增韧剂可为ACR(甲基丙烯酸酯-丙烯酸酯共聚物)、MBS(甲基丙烯酸甲酯-丁二烯-苯乙烯共聚物)、MMB(甲基丙烯酸甲酯-丁二烯共聚物)或ASA(丙烯腈-苯乙烯-丙烯酸酯共聚物)等。
3.根据权利要求1所述的PC/ABS合金废料回收配方,其特征在于,所述的溴系阻燃剂可为溴化聚碳酸酯、十溴二苯醚、八溴醚、四溴双酚A、四溴双酚A聚碳酸酯齐聚物、六溴环十二烷或环保型溴系阻燃剂十溴二苯乙烷等。
4.根据权利要求1所述的PC/ABS合金废料回收配方,其特征在于,所述的锑系阻燃剂可为三氧化二锑、五氧化二锑或锑酸钠等。
5.根据权利要求1所述的PC/ABS合金废料回收配方,其特征在于,所述的抗氧剂可为抗氧剂1010、抗氧剂2921等。
6.根据权利要求1-5任意一项所述的PC/ABS合金废料回收配方,其特征在于,所包括组分以重量份数表示为:
PC/ABS废旧料 48.8
高抗冲PC/ABS水口料 39
MBS 2
十溴二苯乙烷 3
三氧化二锑 1
丙烯酸类抗冲改性剂 6
抗氧剂1010 0.2
7.根据权利要求1所述的PC/ABS合金废料回收配方,其特征在于,所包括组分以重量份数表示为:
PC/ABS废旧料 43.7
高抗冲PC/ABS水口料 43.7
MBS 2
十溴二苯乙烷 4
三氧化二锑 1.3
丙烯酸类抗冲改性剂 4
抗氧剂1010 0.3
8.根据权利要求1所述的PC/ABS合金废料回收配方,其特征在于,所包括组分以重量份数表示为:
PC/ABS废旧料 40
高抗冲PC/ABS水口料 52
MBS 1
十溴二苯乙烷 3
三氧化二锑 1
丙烯酸类抗冲改性剂 2.6
抗氧剂1010 0.4.