CN101077077A - 纳米银抗菌合剂 - Google Patents
纳米银抗菌合剂 Download PDFInfo
- Publication number
- CN101077077A CN101077077A CN 200710023843 CN200710023843A CN101077077A CN 101077077 A CN101077077 A CN 101077077A CN 200710023843 CN200710023843 CN 200710023843 CN 200710023843 A CN200710023843 A CN 200710023843A CN 101077077 A CN101077077 A CN 101077077A
- Authority
- CN
- China
- Prior art keywords
- nano
- siller
- nanometer silver
- solid content
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种纳米银抗菌合剂,由纳米银溶液、水乳型聚氨酯树脂PU-50、力威龙Nivelon、渗透剂m-1038C、水混合而成,本发明合剂制成喷雾剂,喷洒到物体表面,具有很强的附着力,纳米银离子可长期保存,杀菌效果持续时间较长。可用于喷洒轿车、各种客车及货车的驾驶室,还可用于喷洒宾馆、医院、家庭、托儿所、幼儿园、老年公寓等公共场所的桌椅、床具、地毯、床单、被套、枕巾、窗帘、内衣、沙发、鞋袜等,一般可以在6秒内杀灭细菌。
Description
技术领域
本发明属于一种纳米银抗菌制剂,具体是一种含有纳米银溶液的抗菌合剂。
背景技术
纳米银颗粒的粒径为1-100纳米之间,纳米银具有杀菌作用。纳米银粒子能源源不断地释放出银离子,银离子通过以下三种途径抑制细菌的繁殖:1、银离子攻击细菌内部的代谢酶中的-SH基团,使细菌的代谢酶失去活性,阻碍细菌的正常代谢;2、银离子与细菌细胞壁上暴露的肽聚糖反应,使其不能将能量转运进细胞内,阻碍了细菌的正常生理活动;3、银离子与细菌DNA碱性基结合改变了细菌DNA结构,抑制了DNA转录。经由以上三种途径,从根源上彻底阻碍了细菌的繁殖。
金属银用于抗菌有着几千年历史,安全可靠。
纳米银具有更高的表面能与更多接触表面积,使得纳米银具有更高的抗菌活性,可以在更低的浓度下达到桌越的抗菌效果。纳米银能效杀灭650多种细菌,能有效祛除细菌引起的各种异味,有效率达到80%,由于银的独特的抗菌机理,不会象其他抗菌剂一样,使细菌产生抗药性,因此可以保证持续稳定的用药量和抗菌效果。
纳米银释放远红外线促进血液循环,新陈代谢有益健康。
纳米银在高温下有超强的稳定性,能承受1400℃的高温,具有良好化学稳定性,与各种抗菌产品兼容性好。
但是纳米银对物体的附着力不强,难以在物体表面持久的发挥杀菌抗菌作用。
发明内容
本发明的目的是提供一种对物体附着力强,能在物体表面长期附着,长期发挥杀菌抗菌作用的纳米银抗菌合剂。
本发明的技术方案如下:
纳米银抗菌合剂,其特征在于其各组分的重量百分比为:
纳米银溶液1-5%,以溶液中重量固含量为0.65-3.3%计
水乳型聚氨酯树酯PU-50 1-10%,以重量固含量30%计
力威龙Nivelon 1-5%
渗透剂m-1038C 1-5%
其余为水。
所述的纳米银抗菌合剂,其特征在于其各组分的重量百分比为:
纳米银溶液1-3%,以溶液中重量固含量为0.65-3.3%计
水乳型聚氨酯树酯PU-50 4-8%,以重量固含量30%计
力威龙Nivelon 2-4%
渗透剂m-1038C 2-4%
其余为水。
各组分简介:
1、纳米银溶液:
络合态银溶液
Ag含量浓度:
Ag颗粒粒径≤0.5nm
状态:无色透明液体。
PH值=7
2、渗透剂m-1038C
化学组成:高级醇磷酸酯盐的复合物
离子性:阴/非离子
外观:无色透明的液体
水溶性:易溶于水
PH:6-8
安定性:耐强碱、耐高温、氧化剂
3、力威龙Nivelon:
化学组成:高分子聚合物
离子性:非离子
外观:透明或白色乳液
水溶性:易溶于水
特殊性质:
(1)、对纤维具有防污、防静电,吸水及柔软性多方面的效果,并耐长久家庭洗涤;
(2)、可防止静电堆积,对汗水所引起的斑点有显著的降低能力;
(3)、可作为聚酯及其混纺织物吸湿排汗加工整理剂使用。
3、水乳型聚氨酯树脂PU-50
类型:脂肪族聚氨酯树脂
外观:无机械杂质、无凝聚物的乳液,干后透明状
固含量:29-31%
PH:6-9
胶体电荷:阴离子
硬度:软
性能特点:
成膜柔软,粘着力强
耐光、耐黄变性能佳
优异的延伸及耐曲挠性、定型性能优异
极佳的耐水性、耐溶剂性能
手感舒适,丰满有弹性,耐候性能优异
纳米银抗菌合剂制成喷雾剂,可用于喷洒轿车、各种客车及货车的驾驶室,还可用于喷洒宾馆、医院、家庭、托儿所、幼儿园、老年公寓等公共场所的桌椅、床具、地毯、床单、被套、枕巾、窗帘、内衣、沙发、鞋袜等,一般可以在6秒内杀灭细菌。
本发明的优点:
1、解决了纳米银离子在物体表面、纤维组织内部的固定问题,纳米银离子虽然杀菌功能好,但是它在物体表面及纤维组织内部不耐水洗及磨擦,一般经过几次冲洗后就流失掉,而本发明合剂的纳米银离子可长期保存,杀菌效果持续时间较长。
2、可快速渗透到物体表面的毛细孔内、纤维类织物的内部被固定,耐水冲洗。
3、良好的自洁性能。由于加入了抗静电材料,所以被喷涂过纳米银抗菌合剂的物体表面对尘埃具有抗吸附作用。
4、具有对650多种细菌的抗菌功能,有效的解决了其它抗菌剂对细菌的选择性。
5、本发明抗菌合剂可用在棉、麻、化纤、毛纺等纺织品上,可用在金属、木制、竹制物体表面,可用于轿车厢内纺织品、皮革、塑料等表面,喷上去后杀菌效果、附着力一样。
6、除异味功能,可以杜绝由细菌引起的异味。
具体实施方式
纳米银抗菌合剂,由以下各组分混合配制而成,各组分的重量百分比为:
纳米银溶液1-3%,溶液中重量固含量为0.65-3.3%
水乳型聚氨酯树酯PU-50(固含量30%)4-8%
力威龙Nivelon 2-4%
渗透剂m-1038C 2-4%
其余为水。
力威龙Nivelon、渗透剂m-1038C由杭州美高化工有限公司生产,纳米银溶液由上海得富纳米技术有限公司生产,水乳型聚氨酯树酯PU-50由合肥安科精细化工有限公司生产。
Claims (2)
1、纳米银抗菌合剂,其特征在于其各组分的重量百分比为:
纳米银溶液 1-5%,以溶液中重量固含量为0.65-3.3%计
水乳型聚氨酯树酯PU-50 1-10%,以重量固含量30%计
力威龙Nivelon 1-5%
渗透剂m-1038C 1-5%
其余为水。
2、根据权利要求1所述的纳米银抗菌合剂,其特征在于其各组分的重量百分比为:
纳米银溶液 1-3%,以溶液中重量固含量为0.65-3.3%计
水乳型聚氨酯树酯PU-50 4-8%,以重量固含量30%计
力威龙Nivelon 2-4%
渗透剂m-1038C 2-4%
其余为水。