CN101063008A - 一种纳米二氧化钛光催化杀菌降解涂料 - Google Patents
一种纳米二氧化钛光催化杀菌降解涂料 Download PDFInfo
- Publication number
- CN101063008A CN101063008A CN 200610012636 CN200610012636A CN101063008A CN 101063008 A CN101063008 A CN 101063008A CN 200610012636 CN200610012636 CN 200610012636 CN 200610012636 A CN200610012636 A CN 200610012636A CN 101063008 A CN101063008 A CN 101063008A
- Authority
- CN
- China
- Prior art keywords
- titanium oxide
- nano titanium
- coating
- paint
- water glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种纳米二氧化钛光催化杀菌降解涂料,按质量百分比包括下列组分:纳米二氧化钛0.5~5%、六偏磷酸钠0.001~0.125%、水玻璃中的硅酸盐20~50%、无机固化剂1.2~7.5%,其余为水。本发明还提供上述纳米二氧化钛光催化杀菌降解涂料的制备方法:用晶型为锐钛矿型为主的纳米级二氧化钛添加六偏磷酸钠作分散剂后与水玻璃用砂磨均匀混合后,加入无机固化剂并混合均匀后制成涂料。其特征是:该涂料主要原料来源丰富,价格低廉。该涂料制备工艺较简单,工艺参数易控制。该涂料的杀菌、降解功能强,应用广泛。该涂料可在室温固化、施工方便,便于室外施工。
Description
技术领域 本发明涉及一种纳米二氧化钛光催化杀菌降解涂料及其制备方法。
背景技术 利用纳米二氧化钛的光催化性质来制备杀菌和降解污染物涂料的方法主要是利用氟涂料或氟塑料作粘合剂与纳米二氧化钛混合制备涂料,该涂料能成本高,难以大量生产使用。
发明内容 本发明所要解决的问题是提供一种价格低廉的纳米二氧化钛光催化杀菌降解涂料,该涂料既具有较强光催化杀菌降解功能,便于制备及室外施工的优点。
本发明提供的技术方案是:一种纳米二氧化钛光催化杀菌降解涂料,按质量百分比包括下列组分:纳米二氧化钛0.5~5%、六偏磷酸钠0.001~0.125%、水玻璃中的硅酸盐20~50%、无机固化剂1.2~7.5%,其余为水。
上述纳米二氧化钛中,晶型为锐钛矿型的纳米二氧化钛占纳米二氧化钛总量的70~100%(质量百分比),一次粒子粒径为8~90nm。
上述无机固化剂为:氟硅酸钠。
本发明还提供上述纳米二氧化钛光催化杀菌降解涂料的制备方法:用晶型为锐钛矿型为主的纳米级二氧化钛添加六偏磷酸钠作分散剂后与水玻璃用砂磨均匀混合后,再加入无机固化剂并混合均匀后制成涂料。
上述涂料的施工后固化方法可室温陈放50小时,也可用80℃左右的热风固化1小时。
本发明制备的涂料的突出特点是:
1.该涂料主要原料的大部分来源丰富,价格低廉。
2.该涂料制备工艺简单,工艺参数易控制。
3.该涂料的杀菌、降解功能强应用广泛,故性价比高。
4.该涂料可在室温固化、施工方便,便于室外刷、喷等方法施工。
具体实施方式 本发明提供的纳米二氧化钛光催化杀菌降解涂料的按质量百分比包括下列组分:纳米二氧化钛0.5~5%、六偏磷酸钠0.001~0.125%、水玻璃20~50%、无机固化剂1.2~7.5%。
按上述配比,用晶型为锐钛矿型为主的纳米级二氧化钛添加六偏磷酸钠作分散剂后与水玻璃用砂磨均匀混合后,再加入无机固化剂并混合均匀后制成涂料。
晶型为锐钛矿型或锐钛矿型大于等于70%的纳米级二氧化钛在紫外光或阳光中紫外线照射下,会产生较多的自由电子,自由基和空穴,它们有很好地氧化还原能力,能杀菌、降解有机物,消除汽车尾气中或空气中的氮氧化物、硫化物、一氧化碳等,也可降解废水中的有机物。二氧化钛自身对人体无毒无害、耐碱耐酸,是环境友好材料。
水玻璃的分子式的通式为M2O·mSiO2·nH2O,M可以是钠、钾、铵三种离子,m为模数。它加入一定量的氟硅酸钠或氟硅酸钠与缩合磷酸盐(AL、Mg、Ca盐)混合物后,可以制得低温固化的无机涂料,该涂料与各种金属、玻璃、水泥、各种砖、石有较好地结合力,有较强耐酸、耐腐、耐候、耐高温、阻燃、无环境与健康毒害、价格低廉、易涂装等优点。
本发明各流程具体工艺如下:
1.纳米二氧化钛最好采用晶型为锐钛矿型或者是锐钛矿型含量大于、等于70%的纳米级二氧化钛,一次粒子粒径为8~90nm。
2.所用的水玻璃的分子式的通式为M2O、mSiO2、nH2O,其中M可以是钾、钠或铵等离子,模数m为1~4.5,n随生产厂家不同而不同。
3.将上述水玻璃投入到搅拌容器中加水搅拌均匀,配成硅酸盐浓度为25~60%(质量百分浓度)水玻璃溶液。
4.将六偏磷酸钠溶于水配制成浓度为20%(质量百分浓度)的溶液。
5.按本发明所述比例将上述纳米二氧化钛和六偏磷酸钠溶液加入到上述水玻璃溶液中,然后经砂磨机研磨均匀分散在水玻璃中。
6.将氟硅酸钠溶于水配成10%(质量百分浓度)的溶液。
7.将已均匀分散了纳米二氧化钛的水玻璃溶液与上述配好的氟硅酸钠溶液搅拌混合均匀,混合的质量比例为:氟硅酸钠∶硅酸盐=1.2~7.5∶20~50,这样就制成了涂料。
8.制好的涂料在1~5小时内均匀地涂在所需涂覆的水泥、玻璃或金属上,室温固化50小时或用80C左右的热风吹1小时后,就可制成具有光催化杀菌降解功能的涂料膜。
9.参照中华人民共和国国家标准《食品卫生微生物学检验大肠菌群测定》(GB4789.3-94),按照***《消毒技术规范》,测试该涂料膜杀菌能力,经室内非直射阳光(辐照度为255~645μm/cm2)光照1.5小时后,大肠杆菌杀灭率大于90%。
下面通过实施例,进一步阐明本发明的突出特点和显著进步。
实施例
按质量百分取晶型为锐钛矿型70%,金红石型30%,占总涂料质量5%,一次粒子粒径为60~80nm的二氧化钛,加入六偏磷酸钠溶液(其中六偏磷酸钠的质量为二氧化钛质量的0.5%),一起加入到硅酸钾重量占总质量45%模数为4浓度为55%的钾型硅酸盐水玻璃中,砂磨,使之分散均匀,再加入浓度为10%的氟硅酸钠溶液使氟硅酸钠占总质量3%,同时加入缩合磷酸钙饱和溶液,使缩含磷酸钙占总质量的3%,其余加水,再以60转/每分钟的转速搅拌10分钟就制得这种特殊涂料,将此涂料均匀地涂覆在瓷砖上,用80℃左右的热风将之吹干1小时后,用水洗不掉,按照***《消毒技术规范》将活化的大肠杆菌菌液接种到涂料膜上,阴干后,在辐照度为448μw/cm2的室内非直射光辐照1.5小时后,按规范检查,样片上洗下并经一定时间培养的大肠杆菌仅为95个,而同等条件下空白瓷片上洗下并同样培养的大肠杆菌为1503个,杀菌率为94%。
Claims (5)
1.一种纳米二氧化钛光催化杀菌降解涂料,按质量百分比包括下列组分:纳米二氧化钛0.5~5%、六偏磷酸钠0.001~0.125%、水玻璃20~50%、无机固化剂1.2~7.5%,其余为水。
2.据权利要求1所述的涂料,其特征是:晶型为锐钛矿型的纳米二氧化钛占纳米二氧化钛总量的70~100%,一次粒子粒径为8~90nm。
3.根据权利要求1所述的涂料,其特征是:使用的无机固化剂为氟硅酸钠。
4.根据权利要求1所述涂料的制备方法,其特征是:用晶型为锐钛矿型为主的纳米级二氧化钛添加六偏磷酸钠作分散剂后与水玻璃用砂磨均匀混合后,再加入无机固化剂并混合均匀后制成涂料。
5.根据权利要求4所述的制备方法,其特征是:固化方法为室温固化50小时,或用80℃左右的热风固化1小时。