CN101062477A - Cracking product sulfur-lowing catalyst - Google Patents
Cracking product sulfur-lowing catalyst Download PDFInfo
- Publication number
- CN101062477A CN101062477A CN 200610076196 CN200610076196A CN101062477A CN 101062477 A CN101062477 A CN 101062477A CN 200610076196 CN200610076196 CN 200610076196 CN 200610076196 A CN200610076196 A CN 200610076196A CN 101062477 A CN101062477 A CN 101062477A
- Authority
- CN
- China
- Prior art keywords
- catalyst
- weight
- zinc
- content
- slurries
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The disintegration product odinagogue comprises zinc bloom 0. 1-50%, alumina 20-99. 9%. It is made by mixing alumina, zinc bloom, deionized water mixed with acid, with PH value ranging 2-5, weighing 5-25%, mixing the generated serum and zinc alloy, spraying and drying the serum to bake 0. 5 to 10 hours in 400-800deg.C. With the contact under the catalyst reaction conditions, it can better lower the content of sulfur in the fission product.
Description
Technical field
The present invention relates to a kind of catalytic cracking production sulfur-lowing catalyst, more specifically say so about a kind of be used for catalytic cracking process contain the zinc cracking product sulfur-lowing catalyst.
Background technology
The product that combustion of sulfur in the gasoline forms is important atmosphere pollution, and for this reason, the content of strict standard of fuel restriction sulfur in gasoline has all been formulated in countries in the world.Because about sulphur more than 80% is from catalytically cracked gasoline in China's gasoline product, therefore, the content that reduces sulphur in the catalytically cracked gasoline becomes the key that reduces the finished product content of sulfur in gasoline.
At present the catalytically cracked gasoline desulfur technology has three classes: the preliminary treatment of FCC raw material hydrogenation, directly handle and the hydrogenation post processing in the FCC process.Slough sulphur in the FCC charging by hydrotreatment before cracking, although this method is very effective, equipment investment is big, and the hydrogen consumption is high; Remove sulphur in the crackate by the hydrogenation post processing, although also effective, alkene is saturated, and the product octane number descends; Take all factors into consideration, direct desulfurization in cracking process promptly adds sulfur-lowing catalyst or sulfur prodegradant in FCC apparatus, and by changing the cracking mode of sulfide in the FCC raw material, to fall the sulphur purpose be a desirable approach thereby reach.
US 5807475 and US 5164076 propose to exchange molecular sieve with transition metal ions, can improve the suction-operated of molecular sieve to sulfide.As the low silicon FAU of zinc exchange and the USY of silver exchange, the X type molecular sieve and the Y zeolite of Cu, La, Ni, Mo ion-exchange can make the sulphur in the gasoline reduce by 40%.
CN 1049678C discloses a kind of catalytic cracking catalyst compositions, said composition comprises that (a) is dispersed in the molecular sieve in the inorganic oxide matrix, (b) the salic Lewis-acidic components of 1-50% (weight), described component mainly is made up of the lewis acid of representing with oxide by the total weight 1-50% (weight) of lewis acid in the component and aluminium oxide, and described lewis acid is selected from nickel, copper, zinc, silver, cadmium, indium, tin, mercury, thallium, lead, bismuth, boron, aluminium (Al
2Except the O) and the element and the compound of gallium, and described lewis acid is stated from the aluminium oxide.The alumina component that contains Lewis acid wherein is by itself being had lewis acid character and having about 30~400m
2The alumina host of/g surface area with/be selected from Ni, Cu, Zn, Ag, Cd, In, Sn, Hg, Tl, Pb, Bi, B, Al (is not Al
2O
3), the method preparation of " second " component reaction/dipping of one group element/compound of forming of Ca and composition thereof or prepare by method with aluminium oxide and crucial Lewis-acidic components co-precipitation.
CN1281887A provides a kind of gasoline desulfur catalyst of the FCC of being used for process, and its molecular sieve comprises oxidation state metal component (preferred vanadium) and improves the rare earth component (preferred cerium) of catalyst cracking activity.For effective to desulfurization, metal is present in the cavernous structure inside of molecular sieve, for fear of produce too much coke and hydrogen in cracking process, the metal that adds should not have significant hydrogenation activity, and therefore, vanadium, zinc, iron, cobalt and gallium are desirable components, wherein, vanadium is the preferable alloy composition.MAT estimates and shows, vanadium exchange molecular sieve is very effective to gasoline desulfur, adds 10% V/ZSM-5, V/MCM-49, V/ β and V/USY in the benchmark agent, observes content of sulfur in gasoline and reduces by 10%, 17%, 41% and 75% respectively.
The described sulfur reduction catalyst of CN1261618A contains a kind of porous molecular screen, this molecular sieve contains first metal component and second metal component, first metal component is positioned at Molecular Sieve Pore inside and oxidation state greater than zero, and second metal component comprises at least a rare earth element that is positioned at Molecular Sieve Pore inside.Described first metal component is selected from periodic table of elements period 4 and IIB, VB, IIIA, the metal, particularly vanadium of VIII family, zinc, iron, gallium.The amount of metal component is 0.2~5 weight % in the catalyst.
WO 01/21732A1 discloses a kind of method that reduces sulfur content in the cracking petroleum fraction, this method is included in the temperature of raising and a kind of Cracking catalyst and a kind of additive that reduces the product sulfur content and exists down, with the petroleum distillate catalytic cracking, obtain having liquid crackate than low sulfur content.Wherein, the additive of described reduction product sulfur content contains a kind of non-molecular sieve carrier of vanadium that contains, and described non-molecular sieve carrier can be the organic or inorganic carrier, preferred carrier is amorphous or the para-crystal inorganic oxide, as aluminium oxide, silica, clay or their mixture.
CN1552802A provides a kind of cracking additive with desulfidation and preparation method thereof, this auxiliary agent contains a kind of heat-resistant inorganic oxide, clay and a kind of metal component, contain or do not contain molecular sieve, with the auxiliary agent total amount is benchmark, the content of heat-resistant inorganic oxide is 2~68 weight %, the content of clay is 30~80 weight %, the content of molecular sieve is 0~40 weight %, metal oxide in described highest price attitude, the content of metal component is 0.1~30 weight %, described metal component exists with the reduction valence state, and it is selected from the non-aluminum metal of periodic table of elements IIIA family, IVA family metal, VA family metal, IB family metal, IIB family metal, VB family metal, the group vib metal, VIIB family metal, in the VIII family base metal one or more.This auxiliary agent has higher desulphurizing activated, and the catalyst mixture that contains this auxiliary agent and Cracking catalyst has higher cracking activity.
Summary of the invention
The objective of the invention is on the basis of existing technology, provide a kind of have higher the sulphur activity falls and contain the zinc cracking product sulfur-lowing catalyst.
Cracking product sulfur-lowing catalyst provided by the invention, contain zinc oxide, aluminium oxide, gross weight with catalyst is a benchmark, the content of aluminium oxide is 20~99.9 weight %, the content of zinc oxide is 0.1~50 weight %, and satisfy that each components contents sum is 100 weight % in the catalyst, catalyst provided by the present invention is by the method preparation that may further comprise the steps:
(1) aluminium oxide and/or aluminium hydroxide, deionized water and acid are mixed, it is 2~5 that each amounts of components makes the pH value of slurries, and solid content is 5~25 weight %;
(2) step (1) gained slurries are mixed with zinc compound;
(3) with step (2) gained slurries spray-drying, roasting 0.5~10 hour in 400~800 ℃ of air afterwards.
The present invention also provides a kind of method of catalytic cracking production desulfurization, be included under the catalytic cracking reaction condition, the sulfur-bearing oil raw material is contacted with catalyst, described catalyst is the mixture of catalyst provided by the present invention and catalytic cracking catalyst, and the content of catalyst of the present invention is 0.1~20 weight % in the described mixture.
Sulfur-lowing catalyst provided by the present invention is compared with existing sulfur-lowing catalyst, has higher desulphurizing activated.
For example, miscella with Zhenghai wax oil and the normal slag of grand celebration (20: 80) is a raw material, with catalyst C1 provided by the present invention and the trade mark is that the Industrial Catalysis Cracking catalyst (production of catalyst Shandong branch company of China petroleum chemical engineering Stock Co., Ltd) of GOR-II is mixed with 10: 90 weight ratio, at 500 ℃, oil ratio is 4, and WHSV is 16h
-1Condition under, on the small fixed flowing bed device, carry out catalytic cracking reaction, conversion ratio is 70.5 weight %, sulfur in gasoline content is 375.4 mg/litre, and contrast medium D2 carries out catalytic cracking reaction under same reaction condition, conversion ratio is 64.5 weight %, and the sulfur content in the gasoline is 610.1 mg/litre.As seen, catalyst of the present invention has the higher sulphur activity of falling.
The specific embodiment
Catalyst provided by the present invention is a benchmark with the gross weight of catalyst, and preferred alumina content is 40~90 weight %, and zinc oxide content is 5~45 weight %, and satisfies that each components contents sum is 100 weight % in the catalyst.
It is 2.5~4.0 that the consumption of each component of catalyst preparation step of the present invention (1) makes the pH value of slurries, and solid content is 6~15 weight %.
The mixed method of each component of the present invention is the known method of one of ordinary skill in the art, there is not special requirement, preferred steps (1) is mixed slurries that the back forms and ℃ was stirred 10~120 minutes down in room temperature~90, and more preferably slurries stirred 30~90 minutes down in 40~80 ℃.
Aluminium oxide described in the catalyst preparation step of the present invention (1) is selected from can be by in the aluminium oxide of sour peptization one or more, as gama-alumina, η-aluminium oxide, θ-aluminium oxide, χ-aluminium oxide, and preferred gama-alumina; Described aluminium hydroxide can be selected from one or more in boehmite, boehmite, gibbsite, the promise diaspore, preferred boehmite.
Used acid can be selected from one or more in inorganic acid, the organic acid in the sulfur-lowing catalyst preparation process of the present invention (1), for example, described inorganic acid can be one or more in hydrochloric acid, sulfuric acid, nitric acid, the phosphoric acid, described organic acid can be one or more in formic acid, acetate, oxalic acid or the citric acid, preferred hydrochloric acid or nitric acid wherein.
Catalyst preparation step of the present invention (2) be mixed into existing method, do not have special requirement, stirred 10~120 minutes under the temperature of room temperature~90 ℃ the preferred back of mixing, more preferably the temperature in room temperature~60 ℃ stirred 30~60 minutes.Described zinc compound can be selected from its water soluble compound, as zinc nitrate, zinc chloride, zinc sulfate, zinc acetate; Also can be selected from its water-insoluble compound, as basic zinc carbonate, zinc oxide.When zinc compound is water-insoluble compound, it directly can be mixed with product that step (1) obtains, mix with step (1) products therefrom again after also itself and water can being made into certain density slurries, join slurries solid content can be arbitrary value, preferably be not less than 5 weight %; When zinc compound is water soluble compound, described mixing can be that the product that step (1) obtains is directly mixed with it, mix with the product that described step (1) obtains again after also it can being made into the certain density aqueous solution, institute joins that compound concentrations is an arbitrary value in the solution, preferably is not less than 5 weight %.
Catalyst preparation step of the present invention (3) spray-drying is known by one of ordinary skill in the art, and preferably spray drying chamber inlet temperature is 200~500 ℃, and the hothouse outlet temperature is 100~150 ℃; 500~700 ℃ of the sintering temperatures of preferably spray drying rear catalyst, roasting time 1~6 hour.
Catalyst of the present invention also can contain one or more of other metal (non-zinc metal) in addition that dezincifies in IB, IIB, IIIB, IVB, VB, VIB, VIIB, VIII family or the rare earth metal, gross weight with catalyst is a benchmark, be no more than 40 weight % in its content of highest price oxide, preferred non-zinc tenor is 0.5~30 weight %.
In IB of the present invention, IIB, IIIB, IVB, VB, VIB, VIIB, VIII family or the rare earth metal one or more, be preferably in titanium, copper, cobalt, nickel, iron, manganese, gallium, zirconium, vanadium and the lanthanide series metal one or more, more preferably one or more in iron, titanium, the cobalt metal.
When containing non-zinc metal in the catalyst, in preparation process (2), introduce non-zinc metallic compound, being about to step (1) gained slurries mixes with zinc compound and non-zinc metallic compound, non-zinc metallic compound can add before zinc compound adds, and also can add simultaneously with zinc compound or add after zinc compound adds.
IB, IIB, IIIB, IVB, VB, VIB, VIIB, VIII family or rare earth compound can be selected from its water soluble compound in the Preparation of Catalyst of the present invention, one or more in the nitrate of metals such as copper, cobalt, nickel, iron, manganese, titanium, gallium, zirconium, vanadium and rare earth, chloride, the sulfate for example, also can be selected from its water-insoluble compound, for example titanium dioxide.When non-zinc metallic compound is water-insoluble compound, it directly can be mixed with product that step (1) obtains, mix with step (1) products therefrom again after also itself and water can being made into certain density slurries, join slurries solid content can be arbitrary value, preferably be not less than 5 weight %; When zinc and other transition metal element compound are water soluble compound, described mixing can be that the product that step (1) obtains is directly mixed with it, mix with the product that described step (1) obtains again after also it can being made into the certain density aqueous solution, institute joins that compound concentrations is an arbitrary value in the solution, preferably is not less than 5 weight %.
Catalyst of the present invention, its most probable aperture compared with general catalyst with specific area does not have specific (special) requirements, and preferably its most probable bore dia is 10~20nm, and specific area is 100~300m
2/ g.
Catalyst provided by the invention can mix with catalytic cracking catalyst (FCC catalyst), uses as sulfur-bearing oil raw material catalytic cracking product desulphurization catalyst, can reduce the sulfur content in crackate such as gasoline, diesel oil, the kerosene, particularly gasoline.In the mixture of catalyst provided by the invention and catalytic cracking catalyst, the amount of catalyst of the present invention accounts for 0.1~20 weight % of catalyst total amount, is preferably 5~20 weight %.Described sulfur-bearing oil raw material can be selected from contain sulfur resid, reduced crude, decompression residuum, the cured oil of decompression, the cured oil of normal pressure, the cured oil of straight run, propane light/heavy one or more in de-oiling and the cured oil of coking.
The following examples will the present invention will be further described.
Among the embodiment chemical composition of sample by x-ray fluorescence spectrometry (referring to " petrochemical industry analytical method (RIPP test method) ", Yang Cui waits volume surely, Science Press, nineteen ninety publishes), (the ASAP2400 type that U.S. Micromeritics company makes adsorbs instrument automatically) measured with static state low temperature nitrogen adsorption capacity method in specific area, most probable aperture, the small fixed flowing bed evaluation of the reactivity worth of catalyst, content of sulfur in gasoline is measured with the HPGC6890 type chromatograph of being furnished with the PFPD detector.
Embodiment 1
Present embodiment illustrates Catalysts and its preparation method provided by the invention.
With 4.8 kilograms of boehmites (solid content 60 weight %, Shandong Aluminium Industrial Corp produces) and deionized water mixing making beating, obtain the slurries of solid content 10 weight %, stirred 10 minutes down at 60 ℃, add 300 gram hydrochloric acid (concentration 36%, analyze pure), continue to stir 30 minutes, obtain the pH value and be 3.2 slurries.In above-mentioned slurries, add 2.0 kilograms of zinc oxide (analyzing pure) and the slurries that 4 kilograms of deionized water making beating form, continue to stir after 30 minutes,,, obtain catalyst C1 provided by the invention 600 ℃ of roastings 1 hour with the slurries spray-drying that obtains.The composition of C1, specific area, most probable bore dia are listed in table 1.
Embodiment 2
Present embodiment illustrates Catalysts and its preparation method provided by the invention.
With 5.8 kilograms of boehmites (solid content 60 weight %, Shandong Aluminium Industrial Corp produces) and deionized water mixing making beating, obtain the slurries of solid content 15 weight %, be warmed up to 60 ℃, under agitation add 504 gram hydrochloric acid (concentration 36%, analyze pure), continue to stir 60 minutes, obtain pH value and be 2.8 slurries.Cobalt nitrate (Co (the NO that in above-mentioned slurries, adds 1.1 kilograms
3)
26H
2O analyzes pure) and 2.1 kilograms of zinc oxide and 3 kilograms of slurries that the deionized water making beating forms, continue to stir 30 minutes down at 60 ℃.With the slurries spray-drying that obtains,, obtain catalyst C2 provided by the invention then 550 ℃ of roastings 3 hours.The composition of catalyst C2, specific area, most probable bore dia are listed in table 1.
Embodiment 3
Present embodiment illustrates Catalysts and its preparation method provided by the invention.
Method according to embodiment 2 prepares catalyst, the zinc nitrate (Zn (NO that different is with 10.5 kilograms
3)
26H
2O analyzes pure) and 335 gram manganese chloride (MnCl
24H
2O analyzes pure) replace 1.1 kilograms cobalt nitrate (Co (NO among the embodiment 2
3)
26H
2O) and 2.1 kilograms of zinc oxide.Sintering temperature is that 650 ℃, roasting time are 2 hours, obtains catalyst C3 provided by the invention.The composition of C3, specific area, most probable bore dia are listed in table 1.
Embodiment 4
Present embodiment illustrates Catalysts and its preparation method provided by the invention.
With 7.2 kilograms of boehmites (solid content 60 weight %, Shandong Aluminium Industrial Corp produces) and deionized water mixing making beating, obtain the slurries of solid content 10 weight %, at room temperature stirred 10 minutes, add 650 gram hydrochloric acid (concentration 36%, analyze pure), continue stirring at room after 90 minutes, obtain the pH value and be 2.8 slurries.Iron chloride (the FeCl that in above-mentioned slurries, adds 3.1 kilograms
36H
2O analyzes pure) and 600 gram zinc oxide and the slurries that 800 gram deionized waters making beating form, stirring 60 minutes continued.With the slurries spray-drying that obtains,, obtain catalyst C4 provided by the invention then 700 ℃ of roastings 1.5 hours.The composition of catalyst C4, specific area, most probable bore dia are listed in table 1.
Embodiment 5
Present embodiment illustrates Catalysts and its preparation method provided by the invention.
With 4.8 kilograms of boehmites (solid content 60 weight %, Shandong Aluminium Industrial Corp produces) and deionized water mixing making beating, obtain the slurries of solid content 10 weight %, stirred 10 minutes down at 80 ℃, add 300 gram hydrochloric acid (concentration 36%, analyze pure), continue to stir 30 minutes, obtain the pH value and be 3.2 slurries.In above-mentioned slurries, add 2.4 kilograms of zinc oxide (analyzing pure), 300 gram titanium oxide (analyzing pure) and 4 kilograms of slurries that the deionized waters making beating forms, continue to stir after 30 minutes, add 1200 milliliters of 270g/l (in rare earth oxide) re chlorides, continue to stir 20 minutes, with the slurries spray-drying that obtains, 750 ℃ of roastings 1 hour, obtain catalyst C5 provided by the invention.The composition of C5, specific area, most probable bore dia are listed in table 1.
Embodiment 6
Present embodiment illustrates Catalysts and its preparation method provided by the invention.
With 3.9 kilograms of boehmites (solid content 60 weight %, Shandong Aluminium Industrial Corp produces) and deionized water mixing making beating, obtain the slurries of solid content 12 weight %, be warmed up to 60 ℃, under agitation add 492 gram hydrochloric acid (mass concentrations 36%, analyze pure), continue to stir 30 minutes, obtain the pH value and be 3.0 slurries.The zinc chloride (analyzing pure) that adds 3.2 kilograms in above-mentioned slurries stirred after 10 minutes, added 1.7 kilograms of titanium dioxide (analyzing pure) and 2 kilograms of deionized waters are pulled an oar and the slurries of formation, continuation stirring 60 minutes under 60 ℃.With the slurries spray-drying that obtains,, obtain catalyst C6 provided by the invention then 600 ℃ of roastings 2 hours.The composition of catalyst C6, specific area, most probable bore dia are listed in table 1.
Comparative Examples 1
The method that provides according to CN1552802A embodiment 1 prepares catalyst, obtains contrast medium D1, and its composition, specific area, most probable bore dia are listed in table 1.
Comparative Examples 2
The method that provides according to embodiment among the CN1049678C 1 prepares catalyst, and different is to use ZnCl
2Replace nickel nitrate, obtain contrast medium agent D2, its composition, specific area, most probable bore dia are listed in table 1.
Comparative Examples 3
The method that provides according to embodiment among the CN1049678C 6 prepares the catalyst of being made up of zinc oxide/alumina, obtains contrast medium D3, and its composition, specific area, most probable bore dia are listed in table 1.
Table 1
Example number | 1 | 2 | 3 | 4 | 5 | 6 | Comparative Examples 1 | Comparative Examples 2 | Comparative Examples 3 |
The catalyst numbering | C1 | C2 | C3 | C4 | C5 | C6 | D1 | D2 | D3 |
Kinds of transition metals | - | Co | Mn | Fe | RE *+Ti | Ti | Co | - | - |
Transition metal oxide, weight % | - | 4.7 | 2.1 | 15.9 | 4.9+5.5 | 26.2 | 5.0 | - | - |
ZnO, weight % | 40.5 | 36.5 | 42.6 | 10.2 | 40.6 | 31.8 | - | 14.5 | 40.5 |
Al 2O 3, weight % | 59.5 | 58.8 | 55.3 | 73.9 | 49.0 | 42.0 | 45.0 | 85.5 | 59.5 |
Kaolin, weight % | - | - | - | - | - | - | 50.0 | - | - |
Specific surface, rice 2/ gram | 106 | 194 | 160 | 168 | 173 | 211 | 89 | 105 | 78 |
The most probable aperture, dust | 100.8 | 165.1 | 111.8 | 130.4 | 189.4 | 150.7 | 86.1 | 120.6 | 100.2 |
*RE represents rare earth metal
Embodiment 7~12
The following examples illustrate the reactivity worth of sulfur-lowing catalyst provided by the invention.
Respectively with the catalyst C1~C6 and the trade mark GOR-II industrial catalyst (Shandong, Shandong catalyst plant product) of example of the present invention 1~6 preparation, be mixed into catalyst mixture (mixed proportion see Table 3 and table 4) according to different proportion, on the small fixed flowing bed device, estimate.Feedstock oil is the miscella of Zhenghai wax oil and the normal slag of grand celebration (20: 80), and its character sees Table 2.Reaction temperature, air speed, oil ratio and evaluation result are listed in table 3,4.
Comparative Examples 4~7
The catalytic cracking performance of following Comparative Examples explanation contrast medium.
According to the method for embodiment 7~12 same feedstock oil is carried out catalytic cracking respectively, different is that evaluation result is listed in table 4 with catalyst provided by the invention in the catalyst replacement catalyst mixture of Comparative Examples 1~3 preparation.
Table 2
Feedstock oil | Zhenghai VGO | The normal slag of grand celebration |
Density (20 ℃), g/cm 3 | 0.9154 | 0.8906 |
Refractive power (70 ℃) | 1.4926 | 1.4957(20℃) |
Viscosity (100 ℃) mm 2/s | 6.962 | 24.84 |
Four components, m% saturated hydrocarbons aromatic hydrocarbons gum asphalt | 64.0 32.0 4.0 0.0 | 51.2 29.7 18.3 0.8 |
Freezing point, ℃ | 35 | 43 |
Aniline point, ℃ | 82.0 | >105 |
C m% H m% S m% N m% | 85.38 12.03 2.0 0.16 | 86.54 13.03 0.13 0.3 |
Carbon residue m% | 0.18 | 4.3 |
Boiling range, ℃ initial boiling point 5% 10% 30% 50% 70% 90% | 329 363 378 410 436 462 501 | 282 351 370 482 553 - - |
Table 3
Example number | 6 | 7 | 8 | 9 | 10 | 11 |
Catalyst mixture is formed | The heavy % GOR-II in 10 heavy %C1+90 | The heavy % GOR-II in 10 heavy %C2+90 | The heavy % GOR-II in 8 heavy %C3+92 | The heavy % GOR-II in 20 heavy %C4+80 | The heavy % GOR-II in 15 heavy %C5+85 | The heavy % GOR-II in 7 heavy %C5+93 |
Reaction temperature, ℃ | 500 | 500 | 500 | 500 | 500 | 500 |
Weight (hourly) space velocity (WHSV), h -1 | 16 | 16 | 16 | 16 | 16 | 16 |
Oil ratio | 4 | 4 | 4 | 4 | 4 | 4 |
The crackate yield, weight % | 100 | 100 | 100 | 100 | 100 | 100 |
Dry gas | 1.8 | 2 | 1.8 | 1.7 | 1.9 | 1.7 |
Liquefied gas | 13.6 | 15.6 | 13.5 | 13.6 | 13.6 | 13.7 |
Gasoline | 50.7 | 50.3 | 50.1 | 51.1 | 51.4 | 50.1 |
Diesel oil | 17.6 | 16 | 18.3 | 17.8 | 17.1 | 17.9 |
Heavy oil | 11.9 | 11.4 | 12.0 | 11.7 | 11.3 | 12.1 |
Coke | 4.4 | 4.7 | 4.3 | 4.1 | 4.7 | 4.5 |
Conversion ratio, weight % | 70.5 | 72.6 | 69.7 | 70.5 | 71.6 | 70.0 |
The gas and oil sulfur content, mg/L | 375.4 | 348.2 | 366.0 | 310.8 | 358.1 | 411.6 |
Table 4
Example number | 12 | Comparative Examples 4 | Comparative Examples 5 | Comparative Examples 6 | Comparative Examples 7 |
Catalyst mixture is formed | The heavy % GOR-II in 15 heavy %C6+85 | The heavy % GOR-II in 15 heavy %D1+85 | The heavy % GOR-II in 7 heavy %D1+93 | The heavy % GOR-II in 10 heavy %D2+90 | The heavy % GOR-II in 10 heavy %D3+90 |
Reaction temperature, ℃ | 500 | 500 | 500 | 500 | 500 |
Weight (hourly) space velocity (WHSV), h -1 | 16 | 16 | 16 | 16 | 16 |
Oil ratio | 4 | 4 | 4 | 4 | 4 |
The crackate yield, weight % | 100 | 100 | 100 | 100 | 100 |
Dry gas | 1.7 | 1.5 | 1.6 | 1.5 | 1.9 |
Liquefied gas | 13.7 | 11.3 | 11.3 | 11.3 | 10.9 |
Gasoline | 50.1 | 46.9 | 48.5 | 46.9 | 47.8 |
Diesel oil | 17.9 | 20.3 | 19.6 | 20.3 | 19.9 |
Heavy oil | 12.1 | 15.2 | 14.6 | 15.2 | 14.9 |
Coke | 4.5 | 4.8 | 4.4 | 4.8 | 4.6 |
Conversion ratio, weight % | 70.0 | 64.5 | 65.8 | 64.5 | 65.2 |
Content of sulfur in gasoline, mg/litre | 316.6 | 610.0 | 645.6 | 610.1 | 587.6 |
From table 3 and table 4 as can be seen, miscella with Zhenghai wax oil and the normal slag of grand celebration (20: 80) is a raw material, with catalyst C1 provided by the present invention and the trade mark is that the Industrial Catalysis Cracking catalyst (Shandong, Shandong catalyst plant product) of GOR-II is mixed with 10: 90 weight ratio, at 500 ℃, oil ratio is 4, and WHSV is 16h
-1Condition under, on the small fixed flowing bed device, carry out catalytic cracking reaction, conversion ratio is 70.5 weight %, sulfur in gasoline content is 375.4 mg/litre, and contrast medium D2 carries out catalytic cracking reaction under same reaction condition, conversion ratio is 64.5 weight %, and the sulfur content in the gasoline is 610.1 mg/litre.As seen, catalyst of the present invention has the higher sulphur activity of falling.
Claims (10)
1, a kind of cracking product sulfur-lowing catalyst, contain zinc oxide, aluminium oxide, gross weight with catalyst is a benchmark, the content of aluminium oxide is 20~99.9 weight %, the content of zinc oxide is 0.1~50 weight %, and satisfy that each components contents sum is 100 weight % in the catalyst, described catalyst is by the method preparation that may further comprise the steps:
(1) aluminium oxide and/or aluminium hydroxide, deionized water and acid are mixed, it is 2~5 that the consumption of each component makes the pH value of slurries, and solid content is 5~25 weight %;
(2) step (1) gained slurries are mixed with zinc compound;
(3) with step (2) gained slurries spray-drying, roasting 0.5~10 hour in 400~800 ℃ of air afterwards.
2, according to the described catalyst of claim 1, it is characterized in that, be benchmark with the gross weight of catalyst, and alumina content is 40~90 weight % in the described catalyst, zinc oxide content is 5~45 weight %, and satisfies that each components contents sum is 100 weight % in the catalyst.
3, according to the described catalyst of claim 1, it is characterized in that,
It is 2.5~4.0 that the consumption of each component of described step (1) makes the pH value of slurries, and solid content is 6~15 weight %, and described step (3) sintering temperature is 500~700 ℃, and roasting time is 1~6 hour.
According to the described catalyst of claim 1, it is characterized in that 4, it is room temperature~90 ℃ stirring 10~120 minutes in temperature that each component of described step (1) is mixed the back; The mixed slurries of described step (2) are room temperature~90 ℃ stirring 10~120 minutes in temperature.
5, according to the described catalyst of claim 1, it is characterized in that, described catalyst contains one or more of non-zinc metal in IB, IIB, IIIB, IVB, VB, VIB, VIIB, VIII family or the rare earth metal, gross weight with catalyst is a benchmark, be no more than 40 weight % in its content of oxide, the introducing method of described component is to comprise a step that step (1) gained slurries are mixed with non-zinc metallic compound in described step (2).
6, according to the described catalyst of claim 5, it is characterized in that, described non-zinc metal is selected from one or more in titanium, copper, cobalt, nickel, iron, manganese, gallium, zirconium, vanadium and the lanthanide series metal, is benchmark with the gross weight of catalyst, is 0.5~30 weight % in the non-zinc tenor of oxide.
7, according to the described catalyst of claim 5, it is characterized in that one or more in described non-zinc metal chosen from Fe, titanium or the cobalt metal.
According to each described catalyst of claim 1~7, it is characterized in that 8, described catalyst most probable bore dia is 10~20nm, specific area is 100~300m
2/ g.
9, a kind of method of catalytic cracking production desulfurization, be included under the catalytic cracking reaction condition, the sulfur-bearing oil raw material is contacted with catalyst, described catalyst is the mixture of described catalyst of claim 1 and catalytic cracking catalyst, and the content of the described catalyst of claim 1 is 0.1~20 weight % in the described mixture.
10, in accordance with the method for claim 9, it is characterized in that the ratio that the described catalyst of claim 1 accounts for total catalyst weight is 5~20 weight %.