CN101041567A - 利用建筑垃圾生产蒸压砖 - Google Patents

利用建筑垃圾生产蒸压砖 Download PDF

Info

Publication number
CN101041567A
CN101041567A CNA2006100712637A CN200610071263A CN101041567A CN 101041567 A CN101041567 A CN 101041567A CN A2006100712637 A CNA2006100712637 A CN A2006100712637A CN 200610071263 A CN200610071263 A CN 200610071263A CN 101041567 A CN101041567 A CN 101041567A
Authority
CN
China
Prior art keywords
building waste
fly ash
technology
autoclaved fly
ash brick
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2006100712637A
Other languages
English (en)
Inventor
李秋义
张纪刚
朱亚光
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNA2006100712637A priority Critical patent/CN101041567A/zh
Publication of CN101041567A publication Critical patent/CN101041567A/zh
Pending legal-status Critical Current

Abstract

本发明利用建筑垃圾生产蒸压砖就是以建筑垃圾、粉煤灰、石灰(或电石渣)和外加剂等为主要原材料，研制生产蒸压粉煤灰垃圾砖的技术。蒸压粉煤灰垃圾砖是一种环保节约型产品。该产品不仅可以使工业废弃物和建筑垃圾减量化和资源化，而且还具有就地取材，就地消化，废物变宝，节约土地，保护环境的作用。因此，发展节能、节地、利废的绿色垃圾砖，不仅是墙体材料改革的需要，同时也是建筑业、国民经济、社会环境和资源协调发展的需要。该技术将建筑垃圾(废弃混凝土、砂浆、砖、瓦及石料)破碎成粒度小于10mm的连续级配颗粒，用作蒸压粉煤灰砖的骨料，以粉煤灰、石灰质材料等为胶结料，利用水热合成工艺生产建筑垃圾蒸压粉煤灰砖。其中建筑垃圾的用量为15％～55％，最佳范围为20％～35％。水热合成工艺是将制品置于100℃以上的饱和蒸汽中进行处理。

Description

利用建筑垃圾生产蒸压砖
技术领域
本发明涉及一种生产蒸压粉煤灰砖的技术，尤其是利用建筑垃圾生产蒸压粉煤灰砖的技术。
背景技术
随着全国各地城市化进程的推进，城市建设中的旧房改造、楼房拆迁、改建、扩建工程所带来的建筑垃圾已成为各地建筑部门和城管部门十分头痛的问题。除了需要交纳大量的征地费用及运输费用外，还会污染环境和破坏人文景观。建筑垃圾作为一种新型污染源，其治理工作正日益受到人们的重视。另外，工业高度发展的同时，也带来了城市环境的恶化，如何有效治理建筑垃圾、电石渣、粉煤灰等污染源，已是十分迫切的问题。利用石灰质材料、粉煤灰、建筑垃圾等为主要原材料，研制生产建筑墙体材料不仅可以使工业废弃物和建筑垃圾减量化和资源化，而且还具有就地取材、就地消化、废物变宝、节约土地、保护环境的作用。是墙体材料改革的需要，同时也是建筑业、国民经济、社会环境和资源协调发展的需要。
发明内容
本发明是一种利用建筑垃圾生产蒸压粉煤灰砖的技术。该技术将建筑垃圾(废弃混凝土、砂浆、砖、瓦及石料)破碎成粒度小于10mm的连续级配颗粒，用作蒸压粉煤灰砖的骨料，并以粉煤灰、石灰质材料等为胶结料，采用水热合成工艺生产建筑垃圾蒸压粉煤灰砖。建筑垃圾的用量为15％~55％，最佳范围为20％~35％。水热合成工艺是将制品置于100℃以上的饱和蒸汽中进行处理。主要组份如下：
骨料：  15％～55％
粉煤灰：35％～55％
石灰：  12％～25％
外加剂：1％～4％
水：    15％～25％
具体实施方式
实施例1
碎混凝土骨料：35％
粉煤灰：      35％
石灰：        12％
外加剂：      2％
水：          16％
首先对建筑垃圾进行人工分捡，然后将其破碎成粒径小于8mm的骨料。按照上述配合比进行配料，物料经轮碾、搅拌后，进行高压成型(压强为25MPa)制成240mm×15mm×53mm的标准砖。将砖置于蒸压釜内，采用0.8MPa的蒸汽恒压6小时，自然降温后出蒸压釜即为成品。
实施例2
碎砖、废砂浆骨料：30％
粉煤灰：          36％
石灰：            13％
外加剂：          3％
水：              18％
首先对建筑垃圾进行人工分捡，然后将其破碎成粒径小于5mm的骨料。按照上述配合比进行配料，物料经轮碾、搅拌后，进行高压成型(压强为25MPa)制成240mm×15mm×53mm的标准砖。将砖置于蒸压釜内，采用0.8MPa的蒸汽恒压6小时，自然降温后出蒸压釜即为成品。

Claims (6)

1.一种利用建筑垃圾生产蒸压粉煤灰砖的技术。该技术的主要特征是以建筑垃圾为骨料，以粉煤灰、石灰质材料等为胶结料，利用水热合成工艺生产建筑垃圾蒸压粉煤灰砖。
2.根据权利要求1所述的利用建筑垃圾生产蒸压粉煤灰砖的技术，其特征在于将建筑垃圾破碎成粒度小于10mm的连续级配颗粒，用作蒸压粉煤灰砖的骨料。
3.根据权利要求1所述的利用建筑垃圾生产蒸压粉煤灰砖的技术，其特征在于建筑垃圾包括废弃混凝土、砂浆、砖、瓦及石料。
4.根据权利要求1所述的利用建筑垃圾生产蒸压粉煤灰砖的技术，其特征在于建筑垃圾的用量为15％～55％，最佳范围为20％～35％。
5.根据权利要求1所述的利用建筑垃圾生产蒸压粉煤灰砖的技术，其特征在于蒸压工艺是将制品置于100℃以上的饱和蒸汽中进行处理；
6.根据权利要求1所述的利用建筑垃圾生产蒸压粉煤灰砖的技术，其特征在于主要组份如下：
    骨料：15％～55％
    粉煤灰：35％～55％
    石灰：12％～25％
    外加剂：1％～4％
    水：15～25％。
CNA2006100712637A 2006-03-23 2006-03-23 利用建筑垃圾生产蒸压砖 Pending CN101041567A (zh)