CN101003882A - Two-phase stainless steel - Google Patents
Two-phase stainless steel Download PDFInfo
- Publication number
- CN101003882A CN101003882A CN 200610022589 CN200610022589A CN101003882A CN 101003882 A CN101003882 A CN 101003882A CN 200610022589 CN200610022589 CN 200610022589 CN 200610022589 A CN200610022589 A CN 200610022589A CN 101003882 A CN101003882 A CN 101003882A
- Authority
- CN
- China
- Prior art keywords
- weight
- stainless steel
- molybdenum
- chromium
- phase stainless
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
This invention discloses corrosion-resistant binary phase stainless steel, which comprises: C 0-0.03 wt.%, Cr 20-25 wt.%, Ni 3.5-7.5 wt.%, Mo 1.5-4.5 wt.%, Mn 0-2 wt.%, Si 0-1 wt.%, N 0.08-0.2 wt.%, P 0-0.03 wt.%, and S 0-0.028 wt.%. The stainless steel has such advantages as high strength, good corrosion resistance, stable quality, no deformation and high processability, and can be used to manufacture rotary drums of centrifuges.
Description
Technical field
The present invention relates to a kind of stainless steel, especially relate to a kind of high-strength stainless steel.
Background technology
At present, stainless steel has a variety of, but still exists intensity not reach design requirement.Such as, to make stainless steel that centrifuge drum adopts and have 321,316,316L is several, these steel capital exist intensity low, the defective that deflection is big, just because the restriction of this material, it is bigger that the diameter of rotary drum can not be done, otherwise will be out of shape severity, can't works better.
Summary of the invention
Based on above-mentioned need of practice, the technical problem that the present invention solves is: the high chromium of a kind of low-carbon (LC) is provided and corrosion-resistant, the high strength of an amount of nickel, molybdenum, nitrogen are arranged, stable material quality is indeformable and the novel duplex stainless steel of excellent machinability arranged.
Technical scheme of the present invention is: a kind of duplex stainless steel, contain 0~0.03% (weight) carbon, 20~25% (weight) chromium,~7.5% 3.5 (weight) nickel, 1.5~4.5% (weight) molybdenum, 0~2% (weight) manganese, 0~1% (weight) silicon,~0.2% 0.08 (weight) nitrogen, 0~0.03% (weight) phosphorus, 0~0.028% (weight) sulphur.
Wherein, the characteristics of steel of the present invention are chromium content height, help improving the intensity of steel; Carbon mainly is the machinability that improves steel; Molybdenum is the rotproofness that improves steel.
Technique effect of the present invention is: good corrosion resistance, and the intensity height, stable material quality is indeformable and excellent machinability arranged; Especially be suitable for making the rotary drum of super-magnum centrifuge.
The present invention is further described below in conjunction with embodiment.
Embodiment
Embodiment 1:
A kind of duplex stainless steel, containing chromium is 20% (weight), and nickel is 3.5% (weight), and molybdenum is 1.5% (weight), and nitrogen is 0.08% (weight).
Embodiment 2:
A kind of duplex stainless steel, contain: carbon is 0.03% (weight), and chromium is 25% (weight), and nickel is 7.5% (weight), molybdenum is 4.5% (weight), and manganese is 2% (weight), and silicon is 1% (weight), nitrogen is 0.2% (weight), and phosphorus is 0.03% (weight), and sulphur is 0.028% (weight).
Embodiment 3:
A kind of duplex stainless steel, the component and the weight percent thereof that contain are as follows: carbon is 0.02%, and chromium is 21%, and nickel is 4.5%, and molybdenum is 2.5%, and manganese is 1%, and silicon is 0.5, and % nitrogen is 0.1%, and phosphorus is 0.02%, and sulphur is 0.02%.
Embodiment 4:
A kind of duplex stainless steel, contain: carbon is 0.02% (weight), and chromium is 23% (weight), and nickel is 6.5% (weight), molybdenum is 3.5% (weight), and manganese is 0.5% (weight), and silicon is 0.8% (weight), nitrogen is 0.05% (weight), and phosphorus is 0.01% (weight), and sulphur is 0.01% (weight).
Embodiment 5:
A kind of duplex stainless steel, contain: carbon is 0.01% (weight), and chromium is 22% (weight), and nickel is 5% (weight), molybdenum is 3% (weight), and manganese is 1% (weight), and silicon is 0.8% (weight), nitrogen is 0.05% (weight), and phosphorus is 0.015% (weight), and sulphur is 0.015% (weight).
Claims (1)
1, a kind of duplex stainless steel, it is characterized in that, contain 0~0.03% (weight) carbon, 20~25% (weight) chromium, 3.5~7.5% (weight) nickel,~4.5% 1.5 (weight) molybdenum, 0~2% (weight) manganese, 0~1% (weight) silicon, 0.08~0.2% (weight) nitrogen, 0~0.03% (weight) phosphorus, 0~0.028% (weight) sulphur.