CN100429261C - Organic polysiloxane composition cured at atmosphere - Google Patents
Organic polysiloxane composition cured at atmosphere Download PDFInfo
- Publication number
- CN100429261C CN100429261C CNB2005100628806A CN200510062880A CN100429261C CN 100429261 C CN100429261 C CN 100429261C CN B2005100628806 A CNB2005100628806 A CN B2005100628806A CN 200510062880 A CN200510062880 A CN 200510062880A CN 100429261 C CN100429261 C CN 100429261C
- Authority
- CN
- China
- Prior art keywords
- composition
- formula
- integer
- changing
- mass parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention provides a room temperature-curable organopolysiloxane composition excellent in fluidity, storage stability and adhesiveness and slight in odor. The room temperature-curable organopolysiloxane composition comprises the components (A), (B), (C) and (D), wherein the components (A) and (B) are blended with each other under heating in advance. The component (A) is at least one of organopolysiloxanes of formulas (1) to (4) shown in formula A( wherein, R is Me or Et; R<SP>1</SP>is a monovalent hydrocarbon group; Y is an alkylene group; Z is an alkenyl group; N is an integer of 0 or 1; a is an integer of >=10; b is an integer of >=1; and R<SP>2</SP>is a branched chain containing a hydrolyzable group and represented by the formula shown in formula (B). The component (B) is surface-nontreated fumed silica. The component (C) is an organoxysilane compound having two or more on average of hydrolyzable groups bound to Si and a boiling point of >=150[deg.]C at ordinary pressures and/or its partial hydrolyzate. The component (D) is a titanium chelate catalyst and/or an organoxytitanium of formula (5) (wherein, R<SP>3</SP>is a tertiary hydrocarbon group; R<SP>4</SP>is a monovalent hydrocarbon group except R<SP>3</SP>; and c is an integer of 2-4).
Description
Technical field
The present invention relates to normal temperature cured organic polysiloxane composition, especially relate to mobile stable, storage stability, viscosity stability, binding property is good and the remarkable few normal temperature cured organic polysiloxane composition of foul smell (especially silane is smelly).
Technical background
As everyone knows, in the prior art, by contacting the normal temperature cured organic polysiloxane composition that at room temperature is cured all types are arranged with airborne moisture, wherein emit alcohol and be cured the organopolysiloxane composition of type and since do not corrode metal species usually mainly as sealing usefulness, the bonding usefulness of electric/electronic device etc., apply with use.
As the typical example of this pure type, can enumerate special public clear 39-27643 communique (Patent Document 1), this communique discloses the composition that C-terminal end-blocking organopolysiloxane and organoalkoxysilane and organic titanic compound are formed.In addition, the spy opens clear 55-43119 communique (Patent Document 2) and discloses the composition that organoalkoxysilane end-capped organopolysiloxane and organoalkoxysilane and titan-alkoxide are formed.In addition, special open 7-39547 communique (Patent Document 3) has been put down in writing the good composition of storage stability that uses under the hydrophobic silica sealed state, and puts down in writing when using untreated silica, can not obtain the good composition of storage stability.
Yet, special public clear 39-27643 communique (Patent Document 1), the spy opens clear 55-43119 communique (Patent Document 2) and has problems aspect storage stability, in the special fair 7-39547 communique (Patent Document 3), the hydrophobic silica price expensive and mobile through the time change, can not obtain stable flowability, and also have problems aspect the binding property (especially resin bond), confirm to have the smelly unhappy foul smell that causes of silane when using lower boiling organoalkoxysilane in addition.
[Patent Document 1] special public clear 39-27643 communique
[Patent Document 2] spy opens clear 55-43119 communique
[Patent Document 3] special fair 7-39547 communique
Summary of the invention
The present invention is the research of finishing in view of above-mentioned condition, its purpose is to solve aforesaid shortcoming, flowability, storage stability are provided, binding property is good and foul smell (especially silane is smelly) less, do not have the normal temperature cured organic polysiloxane composition of discomfort in using.
The result that the inventor studies with great concentration in order to achieve the above object, at least a kind with the organopolysiloxane of following general formula (1)～(4) expression is passed through in discovery, carry out premix with the untreated smoke-like silicon-dioxide in surface, after implementing thermal treatment, in this mixture and 1 molecule water-disintegrable base that combines with Siliciumatom more than 2 or 2 is arranged on average, and the boiling point under the normal pressure is alkoxysilane compound containing trialkylsilyl group in molecular structure and/or its partial hydrolystate more than 150 ℃ or 150 ℃, mix with titanium chelate catalyzer and/or organic oxygen base titanium of having tertiary carbon atom to combine with organic oxygen base with Sauerstoffatom, can obtain flowability, storage stability, binding property is good, and foul smell (especially silane is smelly) is few, do not have the normal temperature cured organic polysiloxane composition of discomfort in the use, thereby finished the present invention.
Therefore, the invention provides with (A)～(D) is neccessary composition, and (A) composition heats the normal temperature cured organic polysiloxane composition that mixes as feature in advance with (B) composition.
(A) 100 mass parts are selected from more than a kind or 2 kinds or 2 kinds of organopolysiloxane shown in following general formula (1)～(4)
[changing 1]
In the formula, R is methyl or ethyl, R
1Be C
1～C
10Displacement or non-metathetical monovalence alkyl, a is the integer more than 10 or 10.Y is C
1～C
5Alkylidene group, N is respectively 0 or 1 integer.
[changing 2]
In the formula, R, R
1, a, N such as above-mentioned.Z is C
2～C
5Alkenyl.
[changing 3]
In the formula, R, R
1, a, Y, N such as above-mentioned, and, R
2Be the side chain that contains water-disintegrable base shown in the following general formula, b is the integer more than 1 or 1.
[changing 4]
Wherein, R, R
1, Y, N such as above-mentioned.
[changing 5]
In the formula, R, R
1, R
2, Y, Z, N, a, b such as above-mentioned.
(B) the surperficial untreated smoke-like silicon-dioxide of 5～50 mass parts
(C) on average have in 1 of 3～30 mass parts molecule more than 2 or 2 and the Siliciumatom bonded
Water-disintegrable
Base, and the boiling point under the normal pressure is the partial hydrolystate of the organic TMOS compound more than 150 ℃ or 150 ℃, organic TMOS compound or these mixture
(D) the organic alkoxy titanium of the titanium chelate catalyzer of 0.1-15 mass parts and/or following general formula (5) expression
[changing 6]
(R
3O)
cTi(OR
4)
4-c(5)
In the formula, R
3Be with Sauerstoffatom bonded carbon atom be the C of tertiary carbon atom
4～C
10The tertiary hydrocarbon base, R
4Be to remove R
3Outer C
1～C
10Displacement or non-displacement monovalence alkyl, c is 2～4 integer.
It is qualitative to adopt the present invention can make flowability, storage stability, viscosity number, and the good and foul smell (especially silane is smelly) of binding property is few normal temperature cured organic polysiloxane composition significantly.
Embodiment
(A) composition that the present invention uses is the composition of the base polymer of this composition, in order to obtain storage stability, must be to be selected from more than a kind or 2 kinds or 2 kinds of organopolysiloxane shown in following general formula (1)～(4).
[changing 7]
In the formula, R is methyl or ethyl, R
1Be C
1～C
10Displacement or non-metathetical monovalence alkyl.Y is C
1～C
5Alkylidene group, Z is C
2～C
5Alkenyl.N is respectively 0 or 1 integer, and a is the integer more than 10 or 10, and b is the integer more than 1 or 1.And R
2It is the side chain that contains water-disintegrable base shown in the following general formula.
[changing 8]
In the formula, R, R
1, Y, N such as above-mentioned.
In above-mentioned general formula (1)～(4), R is methyl or ethyl, preferable methyl.R
1Be C
1～C
10, C particularly
1～C
6Displacement or non-metathetical monovalence alkyl, for example, can enumerate the alkyl of methyl, ethyl, propyl group etc., the cycloalkyl of cyclohexyl etc., and with these basic carbon atom bonded hydrogen atoms partly by metathetical bases such as halogen atoms, for example 3,3,3-trifluoro propyl etc., wherein preferable methyl, ethyl, vinyl, phenyl, 3,3,3-trifluoro propyl, most preferable.A plurality of R in above-mentioned general formula (1)～(4)
1Can be that identical base also can be different base.
In addition, Y is C
1～C
5Alkylidene group, as alkylidene group, can enumerate methylene radical, ethylidene, propylidene, butylidene etc., preferred ethylidene.Moreover, know the polymkeric substance that Y is a Sauerstoffatom, but keeping quality is insufficient when Y is Sauerstoffatom among the present invention.
Z is C
2～C
5Alkenyl, can enumerate vinyl, allyl group, butenyl, pentenyl etc., wherein preferred vinyl as alkenyl.
(A) preferred viscosities of composition is 100～1 under 25 ℃ condition, 000, and 000mPas.The physical properties that this viscosity might be able to not be given good springiness after solidifying during less than 100mPas especially can not be given flexibility and high elongation, and greater than 1,000, the viscosity increased of composition during 000mPas, flowability might reduce significantly.For this reason, be more preferably 300～20,000mPas.Moreover this viscosity is the value of rotary viscosity design determining.
As the untreated smoke-like silicon-dioxide in (B) composition surface that the present invention uses, be to give the neccessary composition that appropriateness flowability, rubber rerum natura, binding property are used to this composition.
(B) composition must be that the surface is untreated, if the smoke-like silicon-dioxide that uses treatment agent (silane, silazane etc.) to handle then can not obtain mobile stable composition, and binding property reduces also.
As the smoke-like silicon-dioxide of the present invention (B) composition, the specific surface area that preferred BET method is measured is 30～300m
2/ g, most preferably be 100～200m
2/ g.Specific surface area is less than 30m
2During/g, can not obtain enough mechanical characteristicies sometimes, the rubber rerum natura, binding property, on the contrary surpass 300m
2Sometimes can not obtain enough stability of flow, storage stability during/g.
(B) addition of composition is 5～50 mass parts with respect to (A) composition 100 mass parts usually, preferably 10～30 mass parts.Stability of flow reduced and the viscosity of composition rises when addition was too many, mix and discharge property variation, and the rubber rerum natura of addition after solidifying very little the time, poor adhesion.
Here, the present invention carries out pre-mixing with (A), (B) composition, implements heat-treating methods.(A) composition and (B) composition are carried out premix, and when not implementing heat treatment step, not only storage stability reduces but also owing to can not obtain the composition of steady flow, so thermal treatment is necessary operation.Thermal treatment was preferably carried out 10～300 minutes in the scope of 100～250 ℃ of temperature, more preferably carried out 60～120 minutes in the scope of 120～150 ℃ of temperature.Be lower than the occasion of 100 ℃ of temperature, can not obtain enough storage stabilities sometimes, surpass the occasion of 250 ℃ of temperature, (A) composition might go bad.And heat treatment time can not obtain enough storage stabilities too in short-term sometimes, otherwise might take place rotten by (A) composition when heat treatment time is oversize.
(C) composition that the present invention uses, be on average to have more than 2 or 2 in 1 molecule, particularly more than 3 or 3 with water-disintegrable base of Siliciumatom bonded (organic alkoxies of alkoxyl group etc.) and normal pressure under boiling point be organic TMOS compound and/or its partial hydrolystate more than 150 ℃ or 150 ℃.With other the group of Siliciumatom bonded except that water-disintegrable base so long as C
1～C
10The monovalence alkyl then do not have particular determination, particularly, can enumerate the alkyl of methyl, ethyl, propyl group etc., the alkenyl of vinyl etc., aryl of phenyl etc. etc., but be that boiling point under the normal pressure is more than 150 ℃ or 150 ℃ as the condition that satisfies.If methyltrimethoxy silane (b.p.102 ℃), Union carbide A-162 (b.p.143 ℃), the boiling point under vinyltrimethoxy silane (b.p.123 ℃) and so on normal pressure is less than the then residual sometimes intensive foul smell of 150 ℃ organoalkoxysilane.
Concrete example as (C) composition, can enumerate tetraethoxysilane (b.p.168.8 ℃), (b.p.150 ℃/the four functional alkoxysilanes classes that 3mmHg) wait of methyl Cellosolve ortho-silicate, ethyl triethoxysilane (b.p.160 ℃), vinyltriethoxysilane (b.p.158 ℃), normal-butyl Trimethoxy silane (b.p.164.8 ℃), propyl trimethoxy silicane, phenyltrimethoxysila,e (b.p.130 ℃/45mmHg), the octyl group Trimethoxy silane (b.p.100 ℃/2mmHg), 3 functional alkoxysilanes classes of butyl trimethoxy Ethoxysilane etc. and partial hydrolysis condenses thereof etc.Even the boiling point under the above-mentioned normal pressure is less than 150 ℃ silane, if but the dipolymer of hydrolytic condensation or trimer then also can use.These can use a kind individually, also can use mixing more than 2 kinds or 2 kinds.
In addition, in order to give low modulus to the rubber elastomer after solidifying, also can addition ground add dimethoxydiphenylsilane (b.p.161 ℃/15mmHg), (b.p.167 ℃/15mmHg) etc. 2 functional alkoxysilanes classes of phenylbenzene diethoxy silane.
(C) use level of composition with respect to the scope of (A) composition 100 mass parts in 3～30 mass parts, is preferably used in the scope of 5～15 mass parts.Can not obtain crosslinkedly fully, rare to the composition with desired caoutchouc elasticity during less than 3 mass parts, the cured article mechanical characteristics of gained reduces when surpassing 30 mass parts, and the solidification delay of composition, foul smell deterioration.
(D) composition that the present invention uses is for solidifying the catalyzer that this composition is used, and is the organic oxygen base titanium that has shown in titanium chelate catalyzer and/or the following general formula (5) with Sauerstoffatom bonded tertiary carbon atom.
[changing 9]
(R
3O)
CTi(OR
4)
4-C(5)
In the formula, R
3Be with Sauerstoffatom bonded carbon atom be the C of tertiary carbon atom
4～C
10The tertiary hydrocarbon base, R
4Be R
3C in addition
1～C
10Displacement or non-metathetical monovalence alkyl, c is 2～4 integer.
As the concrete example of titanium chelate catalyzer, can enumerate diisopropoxy two (methyl aceto acetate) titanium, diisopropoxy bis(acetylacetonate) titanium etc.
In addition, the R in the general formula (5)
3Be C
4～C
10The tertiary hydrocarbon base, the preferred tertiary butyl.R
4Be R
3C in addition
1～C
10Displacement or non-displacement monovalence alkyl, preferable methyl, ethyl, n-propyl, sec.-propyl, normal-butyl, isobutyl-etc.
As the concrete example of organic oxygen base titanium of above-mentioned formula (5) expression, can enumerate four tert.-butoxy titaniums, isopropoxy three tert.-butoxy titaniums, butoxy three tert.-butoxy titaniums, diisopropoxy three tert.-butoxy titaniums etc.These can use a kind separately, also can use mixing more than 2 kinds or 2 kinds.
(D) addition of composition is scopes of 0.1～15 mass parts with respect to (A) composition 100 mass parts, preferably the scope of 1～10 mass parts.Addition can not obtain good storage stability after a little while, and it is long to make time of cured article of this composition.Otherwise surface cure too soon or the deep solidified nature is poor or storage stability is poor sometimes when too many.
Normal temperature cured organic polysiloxane composition of the present invention, preferred (E) the non-reacted silicone oil that cooperates, fits best two is terminal with the end capped polydimethylsiloxane of TMS.By cooperate this composition can influence liquidity, rubber rerum natura after solidifying.
(E) viscosity of composition (25 ℃) is 5～50, and 000mPas most preferably is 50～5,000mPas.Viscosity rubber rerum natura too hour sometimes reduces, or oil excessively separates out, and viscosity is when too big, and the viscosity of composition rises, operation reduction sometimes.Moreover this viscosity is to use the value of rotary viscosity design determining.
(E) use level of composition is 0～100 mass parts with respect to (A) composition 100 mass parts, most preferably is 5～80 mass parts.During greater than 100 mass parts, the rubber rerum natura reduces sometimes.
In addition, can cooperate (F) composition silane coupling agent in the normal temperature cured organic polysiloxane composition of the present invention.This composition is that the composition of further giving the effect of binding property composition is arranged in normal temperature cured organic polysiloxane composition of the present invention.Preferably use known silane coupling agent as silane coupling agent, can enumerate (methyl) propenyl silane coupling agent, epoxy silane coupling agent, amino silicane coupling agent, mercaptosilane coupling agents etc., can enumerate γ-methacryloxypropyl trimethoxy silane particularly, β-(3, the 4-epoxycyclohexyl) ethyl trimethoxy silane, γ-glycidoxypropyltrime,hoxysilane, γ-glycidoxy propyl group Union carbide A-162, N-β-(aminoethyl) γ-An Bingjisanjiayangjiguiwan, γ-An Jibingjisanyiyangjiguiwan, γ-Qiu Jibingjisanjiayangjiguiwan etc.
The use level of this silane coupling agent is preferably used 0～10 mass parts with respect to (A) composition 100 mass parts, more preferably uses 0.1～5 mass parts.Even when not using silane coupling agent also bonding, also can not use silane coupling agent according to weighting agent and clung body, during use if unfavorable on price when surpassing 10 mass parts.
Normal temperature cured organic polysiloxane composition of the present invention can add organic solvent, mould inhibitor, fire retardant, heat-resistant agent, softening agent, adhesion promotor, curing catalyst, pigment etc. as required in the scope of not destroying the object of the invention.
Normal temperature cured organic polysiloxane composition of the present invention can be heat-treated under above-mentioned condition by at first (A), (B) composition being mixed.Then, below 60 ℃, preferred cool to room temperature～40 ℃, again will (C)～(F) composition under the state of moisture-barrier and as required various additives are carried out mixed must.The composition that makes directly is kept in the encloses container, can be used as when using by being exposed to and is solidified into rubber-like elastic body in the airborne moisture, and so-called single package-type normal temperature cured organic polysiloxane composition uses.
Normal temperature cured organic polysiloxane composition of the present invention is applicable to using as the coating agent of sealing material, tackiness agent or the dampproof coating agent of electric and electronic device, fibre product, glasswork, metal products, plastics etc. or the purposes of tackiness agent.
Embodiment
Below enumerate synthesis example and embodiment and comparative example, specifically describe the present invention, but the present invention is not limited by following embodiment.Moreover, part expression mass parts in the following example, viscosity is the result of the measured value of the rotary viscosity design determining under representing 25 ℃.
[synthesis example 1]
In the there-necked flask of internal volume 15 liters that have thermometer, stirrer, water cooler, add the α of viscosity 600mPas, ω-dimethyl vinyl-dimethyl based polysiloxane 10,000g, Trimethoxy silane 136g and as 50% toluene solution 4.0g of the Platinic chloride of catalyzer, at N
2Mixed at room temperature is 9 hours under the air-flow.Then, under the decompression of 10mmHg, be heated to 100 ℃, heat up in a steamer remaining Trimethoxy silane, make viscosity 720mPas, the colourless transparent liquid 9 of non-volatile content 99.9%, 860g.Sneak into the metatitanic acid orthocarbonate in 100: 1 ratios (mass ratio) in the liquid that makes, the result is tackify immediately not, is cured after 1 day.Can confirm thus that on the vinyl of polymer ends addition has methyltrimethoxy silane.In addition, adopt
29The result that Si-NMR measures Trimethoxy silane importing rate is about 75%.This polymkeric substance as polymer A.
[synthesis example 2]
In the there-necked flask of internal volume 15 liters that have thermometer, stirrer, water cooler, adding viscosity 600mPas side chain has the α of 2 vinyl, ω-dimethyl vinyl-dimethyl based polysiloxane 10,000g, Trimethoxy silane 400g and as 50% toluene solution 4.0g of the Platinic chloride of catalyzer, at N
2Mixed at room temperature is 9 hours under the air-flow.Then, under the decompression of 10mmHg, be heated to 100 ℃, heat up in a steamer thinner toluene and remaining Trimethoxy silane, make viscosity 750mPas, the colourless transparent liquid 9 of non-volatile content 99.9%, 960g.Sneak into tetrabutyl titanate in 100: 1 ratios (mass ratio) in the liquid that makes, the result is tackify immediately not, is cured after 1 day.Can confirm thus on the vinyl contained in polymkeric substance that addition has methyltrimethoxy silane.In addition, adopt
29The result that Si-NMR measures Trimethoxy silane importing rate is about 100%.This polymkeric substance as polymer B.
[embodiment 1]
With 100 parts of specific surface areas that detect with the BET method of polymer A is 130m
2The untreated smoke-like silicon-dioxide of/g (ェ ロ ジ Le 130, Japan ァ ェ ロ ジ Le corporate system) 25 parts are mixed equably, 150 ℃ of following thermal treatments after 120 minutes, cool to room temperature, then under moisture-barrier two 25 parts of the terminal methyl group end-blocking polydimethylsiloxanes of remix viscosity 100mPas, octyl group Trimethoxy silane (b.p.100 ℃/2mmHg) 1.5 parts of 9 parts and diisopropoxy bis(acetylacetonate) titaniums make composition up to mixing.
[embodiment 2]
100 parts of specific surface areas that detect with the BET method of polymer B are about 130m
2The untreated smoke-like silicon-dioxide of/g (ェ ロ ジ Le 130, Japan ァ ェ ロ ジ Le corporate system) 25 parts are mixed equably, 150 ℃ of following thermal treatments after 120 minutes, cool to room temperature, then under moisture-barrier two 25 parts of the terminal methyl group end-blocking polydimethylsiloxanes of remix viscosity 100mPas, octyl group Trimethoxy silane (b.p.100 ℃/2mmHg) 1.5 parts of 9 parts and diisopropoxy bis(acetylacetonate) titaniums make composition up to mixing.
[embodiment 3]
With 100 parts of specific surface areas that detect with the BET method of polymer A is 130m
2The untreated smoke-like silicon-dioxide of/g (ェ ロ ジ Le 130, Japan ァ ェ ロ ジ Le corporate system) 25 parts are mixed equably, 150 ℃ of following thermal treatments after 120 minutes, cool to room temperature, then under moisture-barrier two 25 parts of the terminal methyl group end-blocking polydimethylsiloxanes of remix viscosity 100mPas, octyl group Trimethoxy silane (b.p.100 ℃/2mmHg) 1.5 parts of 9 parts and four tert.-butoxy titaniums make composition up to mixing.
[embodiment 4]
100 parts of specific surface areas that detect with the BET method of polymer A are about 200m
2The untreated smoke-like silicon-dioxide of/g (ェ ロ ジ Le 200, Japan ァ ェ ロ ジ Le corporate system) 25 parts are mixed equably, 150 ℃ of following thermal treatments after 120 minutes, cool to room temperature, then under moisture-barrier two 25 parts of the terminal methyl group end-blocking polydimethylsiloxanes of remix viscosity 100mPas, octyl group Trimethoxy silane (b.p.100 ℃/2mmHg) 1.5 parts of 9 parts and diisopropoxy bis(acetylacetonate) titaniums make composition up to mixing.
[comparative example 1]
Among the embodiment 1, except saving 150 ℃ of following thermal treatments 120 minutes, other adopt method similarly to Example 1 to make composition.
[comparative example 2]
Among the embodiment 1, except the smoke-like that uses the surface to handle with dimethylsilyl is handled silicon-dioxide (R972, Japanese ァ ェ ロ ジ Le corporate system, the specific surface area that the BET method detects: about 110m
2/ g) substituting beyond the untreated smoke-like silicon-dioxide, other adopt method similarly to Example 1 to make composition.
[comparative example 3]
Among the embodiment 1, except smoke-like silicon-dioxide (R812, Japanese firm's system, the specific surface area that the BET method detects: about 260m of using the surface to handle with TMS
2/ g) substituting beyond the untreated smoke-like silicon-dioxide, other adopt method similarly to Example 1 to make composition.
[comparative example 4]
Among the embodiment 1, except using the alternative octyl group Trimethoxy silane of methyltrimethoxy silane (b.p.102 ℃), other adopt method similarly to Example 1 to make composition.
[comparative example 5]
Among the embodiment 1, except using the alternative diisopropoxy bis(acetylacetonate) titanium of tetraisopropoxy titanium, other adopt method similarly to Example 1 to make composition.
The composition of these embodiment, comparative example is processed into the thick sheet of 2mm, solidifies 7 days under 23 ± 2 ℃, the ambiance of 50 ± 5%RH, presses JIS K6249 standard test solidified rubber rerum natura (hardness, elongation, tensile strength).At this moment, hear the foul smell of composition, confirm whether to send offending smell.In addition, side by side the composition that makes is coated on the thick resin clung body of 25 * 100 * 2mm, after at room temperature placement forms rubber elastomer, by the binding property of Visual Confirmation clung body that the cured article that makes is stretched.Here, clung body is selected glass, Resins, epoxy, nylon resin, copper for use.As fluidity test, carry out the 1g composition is coated on the sheet glass, measure then composition expansion diameter (expanding value) method and use two kinds of tests of the method for viscosity under the ambiance of 23 ± 2 ℃ of rotary viscosity design determinings.Storage stability test adopts the form of the uncured composition of wound packages heat 7 days in 70 ℃ drying machine, and then, at 23 ± 2 ℃, curing is 7 days under the ambiance of 50 ± 5%RH, similarly carries out rubber rerum natura and fusible mensuration with the composition at initial stage.The table 1 that the results are shown in of embodiment 1～4, the table 2 that the results are shown in of comparative example 1～5.
Table 1
* 1Resin bond; Zero: good; △: part is peeled off; *: can not survey
* 2Foul smell; Zero: good; *: discomfort
Table 2
* 1Resin bond; Zero: good; △: part is peeled off; *: can not survey
* 2Foul smell; Zero: good; *: discomfort
Claims (5)
1. a normal temperature cured organic polysiloxane composition is characterized in that, is neccessary composition with following (A)～(D), (A) composition and (B) composition is preheated mix:
(A) 100 mass parts are selected from more than a kind or 2 kinds or 2 kinds of organopolysiloxane shown in following general formula (1)～(4)
[changing 1]
In the formula, R is methyl or ethyl, R
1Be C
1～C
10Replacement or the monovalence alkyl of non-replacement, a is the integer more than 10 or 10; Y is C
1～C
5Alkylidene group, N is respectively 0 or 1 integer;
[changing 2]
In the formula, R, R
1, a, N such as above-mentioned, Z are C
2～C
5Alkenyl;
[changing 3]
In the formula, R, R
1, a, Y, N such as above-mentioned, R
2Be the side chain that contains water-disintegrable base shown in the following general formula, b is the integer more than 1 or 1;
[changing 4]
Wherein, R, R
1, Y, N such as above-mentioned;
[changing 5]
In the formula, R, R
1, R
2, Y, Z, N, a, b such as above-mentioned;
(B) the untreated smoke-like silicon-dioxide in 5～50 mass parts surface
(C) on average have in 1 molecule of 3～30 mass parts more than 2 or 2 and the water-disintegrable base of Siliciumatom bonded, and the boiling point under the normal pressure is the partial hydrolystate of the organic TMOS compound more than 150 ℃ or 150 ℃, organic TMOS compound or their mixture;
(D) organic oxygen base titanium of the titanium chelate catalyzer of 0.1-15 mass parts and/or following general formula (5) expression;
[changing 6]
(R
3O)
cTi(OR
4)
4-c (5)
In the formula, R
3Be with Sauerstoffatom bonded carbon atom be the C of tertiary carbon atom
4～C
10The tertiary hydrocarbon base, R
4Be R
3C in addition
1～C
10Replacement or non-replacement monovalence alkyl, c is 2～4 integer.
2. the described normal temperature cured organic polysiloxane composition of claim 1 is characterized in that, the specific surface area that untreated smoke-like silicon-dioxide adopts the BET method to detect is 30～300m
2The scope of/g.
3. claim 1 or 2 described normal temperature cured organic polysiloxane compositions is characterized in that, also contain (E) non-reactive silicone oil.
4. claim 1 or 2 described normal temperature cured organic polysiloxane compositions is characterized in that, (A) composition heats under 100～250 ℃ temperature in advance with (B) composition and mixes.
5. the described normal temperature cured organic polysiloxane composition of claim 3 is characterized in that, (A) composition heats under 100～250 ℃ temperature in advance with (B) composition and mixes.